Volumn 204, Issue 6-7, 2009, Pages 992-996
|
High temperature oxidation resistance of multicomponent Cr-Ti-Al-Si-N coatings
|
Author keywords
Cathodic arc evaporation; Hard coating; Oxidation
|
Indexed keywords
ARC DEPOSITION;
ARC EVAPORATION;
BONDING STATE;
CATHODIC-ARC EVAPORATION;
CHEMICAL COMPOSITIONS;
CHROMIUM OXIDES;
COATED SAMPLE;
DEPOSITED COATINGS;
HIGH TEMPERATURE OXIDATION RESISTANCE;
HIGH-TEMPERATURE OXIDATION TEST;
MIXED LAYER;
MULTICOMPONENTS;
NACL CRYSTAL;
NANO GRAINS;
OXIDATION RATES;
OXIDE SCALE;
PROTECTIVE LAYERS;
ROTATING ARCS;
SI CONTENT;
SURFACE REGION;
TIALSIN;
TIO;
ALUMINUM;
CATHODES;
CAVITY RESONATORS;
CHROMIUM;
CRYSTAL STRUCTURE;
EVAPORATION;
GRAVIMETRIC ANALYSIS;
HARD COATINGS;
INORGANIC COATINGS;
LITHIUM COMPOUNDS;
OXIDATION;
OXIDATION RESISTANCE;
OXYGEN;
SCALE (DEPOSITS);
SILICON;
SODIUM CHLORIDE;
TITANIUM;
VAPORS;
X RAY PHOTOELECTRON SPECTROSCOPY;
CHROMATE COATINGS;
|
EID: 72149099593
PISSN: 02578972
EISSN: None
Source Type: Journal
DOI: 10.1016/j.surfcoat.2009.04.009 Document Type: Article |
Times cited : (67)
|
References (36)
|