A study of compressive strength between zirconia framework and veneering ceramic as a function of thermal expansion coefficient using Shell-Nielsen test method

Journal of Adhesion Science and Technology

Volumn 29, Issue 18, 2015, Pages 1924-1936

  Gökçe, Bülent ^a   Çötert, Hamit Serdar ^a   Özcan, Mutlu ^b  

^a EGE UNIVERSITY   (Turkey)

^b UNIVERSITY OF ZURICH   (Switzerland)

Author keywords

adhesion; bond strength; chipping; veneering ceramic; zirconia

Indexed keywords

ADHESION; ADHESIVES; BOND STRENGTH (MATERIALS); COMPRESSIVE STRENGTH; TESTING; THERMAL EXPANSION; VENEERS; WEIBULL DISTRIBUTION;

ADHESIVE FAILURE; CHIPPING; THERMAL EXPANSION COEFFICIENTS; UNIVERSAL TESTING MACHINES; VARYING COEFFICIENTS; VENEERING CERAMICS; WEIBULL MODULUS; ZIRCONIA CERAMIC;

ZIRCONIA;

EID: 84930823759     PISSN: 01694243     EISSN: 15685616     Source Type: Journal    
DOI: 10.1080/01694243.2015.1046308     Document Type: Article

References (43)

1. Guazzato M, Albakry M, Ringer SP, Swain MV. Strength, fracture toughness and microstructure analysis of a selection of all-ceramic materials. Part II. Zirconia based dental ceramics. Dent. Mater. 2004; 20: 440-456.
2. Conrad Hj, Seong Wj, Pesun IJ. Current ceramic materials and systems with clinical recommendations: a systemic review. J. Prosthet. Dent. 2007; 98: 389-404.
3. Denry I, Kelly JR. State of art of zirconia for dental applications. Dent. Mater. 2008; 24: 299-307. 10.1016/j.dental.2007.05.007
4. Özkurt Z, Kazazoglu E, Ünal A. In vitro evaluation of shear bond strength of veneering ceramics to zirconia. Dent. Mater. J. 2010; 29: 138-146. 10.4012/dmj.2009-065
5. Saito A, Komine F, Blatz MB, Matsumura H. A comparison of bond strength of layered veneering porcelains to zirconia and metal. J. Prosthet. Dent. 2010; 104: 247-257. 10.1016/S0022-3913(10)60133-3
6. Isgrò G, Pallav P, van der Zel JM, Feilzer AJ. The influence of the veneering porcelain and different surface treatments on the biaxial flexural strength of a heat-pressed ceramic. J. Prosthet. Dent. 2003; 90: 465-473. 10.1016/j.prosdent.2003.08.003
7. Aboushelib MN, de Jager N, Kleverlaan CJ, Feilzer AJ. Effect of loading method on the fracture mechanics of two layered all-ceramic restorative systems. Dent. Mater. 2007; 23: 952-959. 10.1016/j.dental.2006.06.036
8. Roediger M, Gersdorff N, Huels A, Rinke S. Prospective evaluation of zirconia posterior fixed partial dentures: four-year clinical results. Int. J. Prosthodont. 2010; 23: 141-148.
9. Raigrodski AJ, Hillstead MB, Meng GK, Chung KH. Survival and complications of zirconia-based fixed dental prostheses: a systematic review. J. Prosthet. Dent. 2012; 107: 170-177. 10.1016/S0022-3913(12)60051-1
10. Raigrodski AJ, Chiche GJ, Potiket N, Hochstedler JL, Mohamed SE, Billiot S, Mercante DE. The efficacy of posterior three-unit zirconium-oxide-based ceramic fixed partial dental prostheses: a prospective clinical pilot study. J. Prosthet. Dent. 2006; 96: 237-244. 10.1016/j.prosdent.2006.08.010
11. Ozkurt Z, Kazazoglu E. Clinical success of zirconia in dental applications. J. Prosthodont. 2010; 19: 64-68. 10.1111/jopr.2010.19.issue-1
12. Al-Dohan HM, Yaman P, Dennison JB, Razzoog ME, Lang BR. Shear strength of core-veneer interface in bi-layered ceramics. J. Prosthet. Dent. 2004; 91: 349-355. 10.1016/j.prosdent.2004.02.009
13. Guazzato M, Proos K, Sara G, Swain MV. Strength, reliability, and mode of fracture of bilayered porcelain/core ceramics. Int. J. Prosthodont. 2004; 17: 142-149.
14. Rocha EP, Anchieta RB, Freitas-Junior AC, de Almeida EO, Cattaneo PM, Chang Ko C. Mechanical behavior of ceramic veneer in zirconia-based restorations: a 3-dimensional finite element analysis using microcomputed tomography data. J. Prosthet. Dent. 2011; 105: 14-20. 10.1016/S0022-3913(10)60184-9
15. Tinschert J, Zwez D, Marx R, Anusavice KJ. Structural reliability of alumina-, feldspar-, leucite-, mica-and zirconia-based ceramics. J. Dentistry. 2000; 28: 529-535. 10.1016/S0300-5712(00)00030-0
16. White SN, Miklus VG, McLaren EA, Lang LA, Caputo AA. Flexural strength of a layered zirconia and porcelain dental all-ceramic system. J. Prosthet. Dent. 2005; 94: 125-131. 10.1016/j.prosdent.2005.05.007
17. Aboushelib MN, Kleverlaan CJ, Feilzer AJ. Microtensile bond strength of different components of core veneered all-ceramic restorations Part II: zirconia veneering ceramics. Dent. Mater. 2006; 22: 857-863. 10.1016/j.dental.2005.11.014
18. Kern M. Controlled airborne-particle abrasion of zirconia ceramic restorations. J. Prosthet. Dent. 2010; 103: 127-128. 10.1016/S0022-3913(10)60016-9
19. Yang B, Barloi A, Kern M. Influence of air-abrasion on zirconia ceramic bonding using an adhesive composite resin. Dent. Mater. 2010; 26: 44-50. 10.1016/j.dental.2009.08.008
20. Tinschert J, Natt G, Mautsch W, Augthun M, Spiekermann H. Fracture resistance of lithium disilicate-, alumina-, and zirconia-based three-unit fixed partial dentures: a laboratory study. Int. J. Prosthodont. 2001; 14: 231-238.
21. Dundar M, Özcan M, Comlekoglu E, Gungor MA, Artunc C. Bond strengths of veneering ceramics to reinforced ceramic core materials. Int. J. Prosthodont. 2005; 18: 71-72.
22. Fischer H, Marx R. Fracture toughness of dental ceramics: comparison of bending and indentation method. Dent. Mater. 2002; 18: 12-19. 10.1016/S0109-5641(01)00005-7
23. Shell JS, Nielsen JP. Study of the bond between gold alloys and porcelain. J. Dent. Res. 1962; 41: 1424-1437. 10.1177/00220345620410062101
24. Ban S, Anusavice KJ. Influence of test method on failure stress of brittle dental materials. J. Dent. Res. 1990; 69: 1791-1799. 10.1177/00220345900690120201
25. Özcan M. Fracture reasons in ceramic-fused-to-metal restorations. J. Oral. Rehabil. 2003; 30: 265-269.
26. Çömlekoʇlu ME, Dündar M, Özcan M, Güngör MA, Gökçe B, Artunç C. Evaluation of bond strength of various margin ceramics to a zirconia ceramic. J. Dent. 2008; 36: 822-827. 10.1016/j.jdent.2008.05.019
27. Kotousov A, Kahler B, Swain M. Analysis of interfacial fracture in dental restorations. Dent. Mater. 2011; 27: 1094-1101. 10.1016/j.dental.2011.06.009
28. Sundh A, Sjogren G. A comparison of fracture strength of yttrium-oxide-partially-stabilized zirconia ceramic crowns with varying core thickness, shapes and veneer ceramics. J. Oral Rehabil. 2004; 31: 682-688. 10.1111/j.1365-2842.2004.01284.x
29. Guess PC, Kuliš A, Witkowski S, Wolkewitz M, Zhang Y, Strub JR. Shear bond strengths between different zirconia cores and veneering ceramics and their susceptibility to thermocycling. Dent. Mater. 2008; 24: 1556-1567. 10.1016/j.dental.2008.03.028
30. McLean JW, Sced IR. The gold alloy/porcelain bond. Trans. Brit. Ceram. Soc. 1973; 5: 229-233.
31. Aboushelib MN, Kleverlaan CJ, Feilzer AJ. Microtensile bond strength of different components of core veneered all-ceramic restorations. Part 3: double veneer technique. J. Prosthodont. 2008; 17: 9-13.
32. Taskonak B, Mecholsky J, Anusavice K, Anusavice KJ. Residual stresses in bilayer dental ceramics. Biomaterials. 2005; 26: 3235-3241. 10.1016/j.biomaterials.2004.08.025
33. Hermann I, Bhowmick S, Zhang Y, Lawn BR. Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: trilayer structures. J. Mater. Res. 2006; 21: 512-521. 10.1557/jmr.2006.0056
34. Choi JE, Waddell JN, Swain MV. Pressed ceramics onto zirconia. Part 2: indentation fracture and influence of cooling rate on residual stresses. Dent. Mater. 2011; 27: 1111-1118. 10.1016/j.dental.2011.08.003
35. Mainjot AK, Schajer GS, Vanheusden AJ, Sadoun MJ. Residual stress measurement in veneering ceramic by hole-drilling. Dent. Mater. 2011; 27: 439-444. 10.1016/j.dental.2010.12.002
36. Goracci C, Sadek FT, Monticelli F, Cardoso PE, Ferrari M. Influence of substrate, shape, and thickness on microtensile specimens structural integrity and their measured bond strengths. Dent. Mater. 2004; 20: 643-654. 10.1016/j.dental.2003.08.009
37. Sundh A, Molin M, Sjögren G. Fracture resistance of yttrium oxide partially-stabilized zirconia all-ceramic bridges after veneering and mechanical fatigue testing. Dent. Mater. 2005; 21: 476-482. 10.1016/j.dental.2004.07.013
38. von Steyern PV, Carlson P, Nilner K. All-ceramic fixed partial dentures designed according to the DC-Zirkon technique. A 2-year clinical study. J. Oral. Rehabil. 2005; 32: 180-187. 10.1111/jor.2005.32.issue-3
39. Hadavi F, Hey JH, Ambrose ER, Louie PW, Shinkewski DJ. The effect of dentin primer on the shear bond strength between composite resin and enamel. Oper. Dent. 1993; 18: 61-65.
40. Van Noort R, Noroozi S, Howard IC, Cardew G. A critique of bond strength measurements. J. Dent. 1989; 17: 61-67. 10.1016/0300-5712(89)90131-0
41. Aboushelib MN, Dejager N, Kleverlaan CJ, Feilzer AJ. Microtensile bond strength of different components of core veneered all-ceramic restorations. Dent. Mater. 2005; 21: 984-991. 10.1016/j.dental.2005.03.013
42. Leone EF, Fairhurst CW. Bond strength and mechanical properties of dental porcelain enamels. J. Prosthet. Dent. 1967; 18: 155-159. 10.1016/S0022-3913(67)80058-1
43. Isgrò G, Kleverlaan CJ, Wang H, Feilzer AJ. Thermal dimensional behavior of dental ceramics. Biomaterials. 2004; 25: 2447-2453. 10.1016/j.biomaterials.2003.09.027