Competing fracture modes in brittle materials subject to concetrated cyclic loading in liquid environments: Trilayer structures

Journal of Materials Research

Volumn 21, Issue 2, 2006, Pages 512-521

  Hermann, Ilja ^a   Bhowmick, Sanjit ^a   Zhang, Yu ^b   Lawn, Brian R ^a  

^a NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

^b NEW YORK UNIVERSITY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ALUMINA; BRITTLENESS; COATING TECHNIQUES; CRACKS; CYCLIC LOADS; FRACTURE; GLASS; MATHEMATICAL MODELS; POLYCARBONATES; VIDEO CAMERAS; WATER;

BRITTLE MONOLITHS; FRACTURE EVOLUTION; LIQUID ENVIRONMENTS; TRILAYER STRUCTURES;

MULTILAYERS;

EID: 33644505154     PISSN: 08842914     EISSN: None     Source Type: Journal    
DOI: 10.1557/jmr.2006.0056     Document Type: Article

References (24)

1. Y. Zhang, S. Bhowmick, and B.R. Lawn: Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: monoliths. J. Mater. Res. 20, 2021 (2005).
2. S. Bhowmick, Y. Zhang, and B.R. Lawn: Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: Bilayer structures. J. Mater. Res. 20, 2792 (2005).
3. J.R. Kelly, R. Giordano, R. Pober, and M.J. Cima: Fracture surface analysis of dental ceramics: Clinically failed restorations. Int. J. Prosthodont. 3, 430 (1990).
4. J.R. Kelly: Ceramics in restorative and prosthetic dentistry. Ann. Rev. Mater. Sci. 27, 443 (1997).
5. B.R. Lawn, Y. Deng, P. Miranda, A. Pajares, H. Chai, and D.K. Kim: Overview: damage in brittle layer structures from concentrated loads. J. Mater. Res. 17, 3019 (2002).
6. Y. Zhang, J-K. Kwang, and B.R. Lawn: Deep penetrating conical cracks in brittle layers from hydraulic cyclic contact. J. Biomed. Mater. Res. 73B, 186 (2005).
7. H. Chai and B.R. Lawn: Hydraulically pumped cone fractures in brittle solids. Acta Mater. 53, 4237 (2005).
8. H. Chai, B.R. Lawn, and S. Wuttiphan: Fracture modes in brittle coatings with large interlayer modulus mismatch. J. Mater. Res. 14, 3805 (1999).
9. Y-W. Rhee, H-W. Kim, Y. Deng, and B.R. Lawn: Contact-induced damage in ceramic coatings on compliant substrates: Fracture mechanics and design. J. Am. Ceram. Soc. 84, 1066 (2001).
10. Y. Deng, B.R. Lawn, and I.K. Lloyd: Characterization of damage modes in dental ceramic bilayer structures. J. Biomed Mater. Res. 63B, 137 (2002).
11. Y. Deng, P. Miranda, A. Pajares, F. Guiberteau, and B.R. Lawn: Fracture of ceramic/ceramic/polymer trilayers for biomechanical applications. J. Biomed. Mater. Res. 67A, 828 (2003).
12. B.R. Lawn, Y. Deng, and V.P. Thompson: Use of contact testing in the characterization and design of all-ceramic crown-like layer structures: A review. J. Prosthet. Dent. 86, 495 (2001).
13. Y. Zhang, B.R. Lawn, K.A. Malament, V.P. Thompson, and E.D. Rekow: Damage accumulation and fatigue life of sandblasted dental ceramics. (unpublished),
14. Y. Zhang, B.R. Lawn, E.D. Rekow, and V.P. Thompson: Effect of sandblasting on the long-term strength of dental ceramics. J. Biomed Mater. Res. 71B, 381 (2004).
15. J.R. Kelly: Clinically relevant approach to Ware testing of all-ceramic restorations. J. Prosthet. Dent. 81, 652 (1999).
16. J.H. Kim, P. Miranda, D.K. Kim, and B.R. Lawn: Effect of an adhesive interlayer on the fracture of a brittle coating on a supporting substrate. J. Mater. Res. 18, 222 (2003).
17. D.K. Kim, Y-G. Jung, I.M. Peterson, and B.R. Lawn: Cyclic fatigue of intrinsically brittle ceramics in contact with spheres. Acta Mater. 47, 4711 (1999).
18. M.G. Abrams and D.J. Green: Prediction of crack propagation and fracture in residually stressed glass as a function of the stress profile and flaw size distribution. J. Europ. Ceram. Soc. (in press).
19. M-W. He and J.W. Hutchinson: Crack deflection at an interface between dissimilar elastic materials. Int. J. Solids Struct. 25, 1053 (1989).
20. T.W. Clyne: Residual stresses in thick and thin surface coatings, in Encyclopedia of Materials Science and Technology (Elsevier, Oxford, U.K,, 2001).
21. L.B. Freund and S. Suresh: Thin Film Materials: Stress, Defect Formation and Surface Evolution (Cambridge University Press, Cambridge, UK, 2004), Chap. 2.
22. D.B. Marshall and B.R. Lawn: An indentation technique for measuring stresses in tempered glass surfaces. J. Am. Ceram. Soc. 60, 86 (1977).
23. S. Wuttiphan, B.R. Lawn, and N.P. Padture: Crack suppression in strongly bonded homogeneous/heterogeneous laminates: A study on glass/ glass-ceramic bilayers. J. Am. Ceram. Soc. 79, 634 (1996).
24. L.M. Braun, ST Bennison, and B.R. Lawn: Objective evaluation of short-crack toughness-curves using indentation flaws: Case study on alumina-based ceramics. J. Am. Ceram. Soc. 75, 3049 (1992).