Catalyst-free synthesis and structural and mechanical characterization of single crystalline Ca2B2O5·H 2O nanobelts and stacking faulted Ca2B2O 5 nanogrooves

Nano Letters

Volumn 10, Issue 1, 2010, Pages 255-262

  Bao, Lihong ^a   Xu, Zhi Hui ^a   Li, Rui ^a   Li, Xiaodong ^a  

^a University of South Carolina   (United States)

Author keywords

Elastic modulus; Nanobelts; Nanogrooves; Nanoindentation; Stacking faults

Indexed keywords

CATALYST-FREE; CATALYST-FREE SYNTHESIS; FAULT ARRAYS; HYDROTHERMAL METHODS; LOW TEMPERATURES; NANO-MATERIALS; NANOGROOVES; ORDERED STACKING; SINGLE-CRYSTALLINE; STRUCTURAL AND MECHANICAL CHARACTERIZATIONS;

CALCIUM; CATALYSIS; CATALYSTS; CRYSTALLINE MATERIALS; ELASTIC MODULI; HYDRATES; HYDRATION; MECHANICAL PROPERTIES; NANOBELTS; SYNTHESIS (CHEMICAL);

STACKING FAULTS;

EID: 74849112128     PISSN: 15306984     EISSN: None     Source Type: Journal    
DOI: 10.1021/nl9034187     Document Type: Article

References (44)

1. Yang, P. D.; Lieber, C. M. Science 1996, 273, 1836-1840.
2. Xiang, J.; Lu, W.; Hu, Y. J.; Wu, Y.; Yan, H.; Lieber, C. M. Nature 2006, 447, 489-493.
3. Pan, Z. W.; Dai, Z. R.; Wang, Z. L. Science 2001, 297, 1947-1949.
4. Craighead, H. G. Science 2000, 290, 1532-1535.
5. Banerjee, P.; Perez, I.; Henn-Lecordier, L.; Lee, S. B.; Rubloff, G. W. Nat- Nanotechnol. 2009, 4, 292-296.
6. Cao, L. Y.; White, J. S.; Park, J. S.; Schuller, J. A.; Clemens, B. M.; Brongersma, M. L. Nat- Mater. 2009, 8, 643-647.
7. Wang, Z. W.; Daemen, L. L.; Zhao, Y. S.; Zha, C. S.; Downs, R. T.; Wang, X. D.; Wang, Z. L.; Hemley, R. J. Mater Mater. 2005, 4, 922-927.
8. Hochbaum, A. I.; Chen, R. K.; Delgado, R. D.; Liang, W. J.; Garnett, E. C.; Najarian, M.; Majumdar, A.; Yang, P. D. Nature 2008, 451, 163-167.
9. Czaban. J. A.; Thompson, D. A.; LaPierre, R. R. Nano Lett. 2009, 9, 148-154.
10. Liu, F.; Tian, J. F.; Bao, L. H.; Yang, T. Z.; Shen, C. M.; Lai, X. Y.; Xiao, Z. M.; Xie, W. G.; Deng, S. Z.; Chen, J.; She, J. C.; Xu, N. S.; Giao, H. -J. Adv. Mater. 2008, 20, 2609-2615.
11. Wang, X. J.; Tian, J. F.; Yang, T. Z.; Bao, L. H.; Hui, C.; Liu, F.; Shen, C. M.; Gu, C. Z.; Xu, N. S.; Gao, H. J. Adv.Mater. 2007, 19, 4480-4485.
12. Bao, J. M.; Bell, D. C.; Capasso, F.; Wagner, J. B.; Mârtensson, T.; Tragârdh. J.; Samuelson, L. Nano Lett. 2008, 8, 836-841.
13. Algra, R. E.; Verheijen, M. A.; Borgström, M. T.; Feiner, L.-F.; Immink, G.; van Enckevort, W. J. P.; Vlieg, E.; Bakkers, E. P. A. M. Nature 2008, 456, 369-372.
14. Xiong, Q. H.; Wang, J.; Eklund, P. C. Nano Lett. 2006, 6, 2736-2742.
15. Caroff, P.; Dick, K. A. Johansson, J.; Messing, M. E.; Deppert, K.; Samuelson, L. Nat- Nanotechnol. 2009, 4, 50-55.
16. Johansson, J.; Karlsson, L. S.; Svensson, C. P. T.; Mârtensson, T.; Wacaser, B. A.; Deppert, K.; Samuelson, L.; Seifert, W. Nat. Mater. 2006, 5, 574-580.
17. Toimil-Molares, M. E.; Buschmann, V.; Dobrev, D.; Neumann, R.; Scholz, R.; Schuchert, I. U.; Vetter, J. Adv. Mater. 2001, 13, 62-65.
18. Wu, B.; Heidelberg, A.; Boland. J. J.; Sader. J. E.; Sun, X. M.; Li, Y. D. Nano Lett. 2006, 6, 468-472.
19. Schaefer, D. M.; Patil A.; Andres, R. P.; Reifenberger, R. Phys. Rev. B 1995, 57, 5322-5332.
20. Lu, L.; Shen, Y. F.; Chen, X. H.; Qian, L. H.; Lu, K. Science 2004, 304, 422-426.
21. Wang, J. G.; Tian, M. L.; Mallouk, T. E.; Chan, M. H. J. Phys. Chem. B 2004, 108, 841-845.
22. Tao, X. Y.; Li, X. D. Nano Lett. 2008, 8, 505-510.
23. Stiles, M. D.; Hamann, D. R. Phys. Rev. B 1990, 41, 5280-5282.
24. Stiles, M. D.; Hamann, D. R. Phys. Rev. B 1988, 38, 2021-2037.
25. Lopez, F. J.; Hemesath, E. R.; Lauhon, L. J. Nano Lett. 2009, 9, 2774-2779.
26. Tao, X. Y.; Wang, X. N.; Li, X. D. Nano Lett. 2007, 7, 3172-3176.
27. Li, R.; Tao, X. Y.; Li, X. D. J. Mater. Chem. 2009, 19, 983-987.
28. Zhu, Y. C.; Bando, Y.; Ma, R. Z. Adv. Mater. 2003, 15, 1377-1379.
29. Ma, R. Z.; Bando, Y.; Sato, T.; Tang, C. C.; Xu, F. F. J. Am. Chem. Soc. 2002, 124, 10668-10669.
30. Santos, C. N.; Meneses, D. D.; Echegut, P.; Neuville, D. R.; Hemandes, A. C.; Ibanez, A. Appl. Phys. Lett. 2009, 94, 151901.
31. Ishii, T.; Kokaku, H.; Nagai, A.; Nishita, T.; Kakimoto, M. Polym. Sng. Sci. 2006, 46, 799-806.
32. Guo, C. F.; Luan, L.; Shi, F. G.; Ding, X. I. Electrochem. Soc. 2009, 156, J 125-J128.
33. Kityk, I. V.; Majchrowski, A.; Michalski, E.; Kasprowicz, D.; Drozdowski, M.; Kisielewski, J.; Lukasiewicz, T.; Sahraoui, B. I. Phys. Chem. B 2006, 110, 9090-9094.
34. Hao, J. H.; Gao, J. Appl. Phys. Lett. 2004, 85, 3720.
35. Liu, H.; Hu, C. G.; Wang, Z. L. Nano Lett. 2006, 6, 1535-1540.
36. Li, X. D.; Bhushan, B. Mater. Charact. 2002, 48, 11-36.
37. Bhushan, B.; Li, X. D. Int. Mater. Rev. 2003, 48, 125-164.
38. Hu, J. T.; Odom, T. W.; Lieber, C. M. Acc. Chem. Res. 1999, 32, 435-455.
39. Trentler, T. J.; Hickman, K. M.; Geol, S. C.; Viano, A. M.; Gibbons, P. C.; Buhro, W. E. Science 1995, 270, 1791-1794.
40. Wang, Z. L.; Feng, X. D. J. Phys. Chem. B 2003, 107, 13563-13566.
41. Xia, Y. N.; Yang, P. D.; Sun, Y. G.; Wu, Y. Y.; Mayers, B.; Gates, B.; Yin, Y. D.; Kim, F.; Yan, H. Q. Adv. Mater. 2003, 15, 353-389.
42. Xu, Z. H.; Li, X. D. Acta Mater. 2006, 54, 1699-1703.
43. Manupriya; Thind, K. S.; Sharma, G.; Rajendran, V.; Singh, K.; Gayathri Devi, A. V.; Aravindan, S. Phys. Status Solidi A 2006, 203, 2356-2364.
44. Gere, J. M.; Timoshenko, S. P. Mechanics of Materials; PWS-KENT: Boston, MA, 1990.