Identifying the crystalline orientation of black phosphorus using angle-resolved polarized Raman spectroscopy

Angewandte Chemie - International Edition

Volumn 54, Issue 8, 2015, Pages 2366-2369

  Wu, Juanxia ^a,d   Mao, Nannan ^a   Xie, Liming ^c   Xu, Hua ^b   Zhang, Jin ^a  

^a PEKING UNIVERSITY   (China)

^b SHAANXI NORMAL UNIVERSITY   (China)

^c NATIONAL CENTER FOR NANOSCIENCE AND TECHNOLOGY   (China)

^d PEKING UNIVERSITY   (China)

Author keywords

Anisotropy; Black phosphorus; Crystalline orientation; Phosphorene; Polarized Raman spectroscopy

Indexed keywords

ANISOTROPY; CRYSTALLINE MATERIALS; PHOSPHORUS; POLARIZATION; RAMAN SPECTROSCOPY;

CRYSTALLINE ORIENTATIONS; NONDESTRUCTIVE METHODS; OPTICAL ANISOTROPIC; PARALLEL POLARIZATION; PHOSPHORENE; POLARIZATION ANGLE; POLARIZATION DIRECTION; POLARIZED RAMAN SPECTROSCOPY;

CRYSTAL ORIENTATION;

EID: 85027927037     PISSN: 14337851     EISSN: 15213773     Source Type: Journal    
DOI: 10.1002/anie.201410108     Document Type: Article

References (20)

1. a) H. Liu, A. T. Neal, Z. Zhu, Z. Luo, X. F. Xu, D. Tomanek, P. D. D. Ye, ACS Nano 2014, 8, 4033-4041;
2. b) L. K. Li, Y. J. Yu, G. J. Ye, Q. Q. Ge, X. D. Ou, H. Wu, D. L. Feng, X. H. Chen, Y. B. Zhang, Nat. Nanotechnol. 2014, 9, 372-377;
3. c) H. Liu, A. T. Neal, M.W. Si, Y. C. Du, P. D. Ye, IEEE Electron Device Lett. 2014, 35, 795-797.
4. J. S. Qiao, X. H. Kong, Z. X. Hu, F. Yang, W. Ji, Nat. Commun. 2014, 5, 4475.
5. M. Buscema, D. J. Groenendijk, S. I. Blanter, G. A. Steele, H. S. J. van der Zant, A. Castellanos-Gomez, Nano Lett. 2014, 14, 3347-3352.
6. A. Morita, Appl. Phys. A 1986, 39, 227-242.
7. S. Zhang, J. Yang, R. J. Xu, F.Wang,W. F. Li, M. Ghufran, Y.-W. Zhang, Z. F. Yu, G. Zhang, Q. H. Qin, et al., ACS Nano 2014, 8, 9590-9596.
8. J. Zhang, H. J. Liu, L. Cheng, J. Wei, J. H. Liang, D. D. Fan, J. Shi, X. F. Tang, Q. J. Zhang, 2014, arXiv:1405.3348.
9. H. O. H. Churchill, P. Jarillo-Herrero, Nat. Nanotechnol. 2014, 9, 330-331.
10. F. N. Xia, H. Wang, Y. C. Jia, Nat. Commun. 2014, 5, 4458.
11. a) G. Z. Qin, Q.-B. Yan, Z. Z. Qin, S. Y. Yue, H. J. Cui, Q. R. Zheng, G. Su, Sci. Rep. 2014, 4, 6946;
12. b) R. X. Fei, L. Yang, Nano Lett. 2014, 14, 2884-2889;
13. c) H. Y. Lv, W. J. Lu, D. F. Shao, Y. P. Sun, Phys. Rev. B 2014, 90, 085433;
14. d) R. X. Fei, L. Yang, Appl. Phys. Lett. 2014, 105, 083120.
15. W. L. Lu, H. Y. Nan, J. H. Hong, Y. M. Chen, C. Zhu, Z. Liang, X. Y. Ma, Z. H. Ni, C. H. Jin, Z. Zhang, Nano Res. 2014, 7, 853-859.
16. a) J. Ribeiro-Soares, R. M. Almeida, L. G. Cancado, M. S. Dresselhaus, A. Jorio, 2014, arXiv:1408.6641;
17. b) S. Sugai, T. Ueda, K. Murase, J. Phys. Soc. Jpn. 1981, 50, 3356-3361;
18. c) S. Sugai, I. Shirotani, Solid State Commun. 1985, 53, 753-755.
19. J. B. Bates, A. S. Quist, J. Chem. Phys. 1972, 56, 1528-1533.
20. Y. Y. Zhao, X. Luo, H. Li, J. Zhang, P. T. Araujo, C. K. Gan, J. Wu, H. Zhang, S. Y. Quek, M. S. Dresselhaus, et al., Nano Lett. 2013, 13, 1007-1015.