Shear bond strength comparison between conventional porcelain fused to metal and new functionally graded dental restorations after thermal-mechanical cycling

Journal of the Mechanical Behavior of Biomedical Materials

Volumn 13, Issue , 2012, Pages 194-205

  Henriques, B ^a   Goncalves S ^a   Soares, D ^a   Silva, F S ^a  

^a UNIVERSITY OF MINHO   (Portugal)

Author keywords

Functionally graded materials; Hot pressing; Metal ceramic dental restorations; Porcelain fused to metal (PFM); Shear bond strength; Thermal and mechanical cycling

Indexed keywords

CROSSHEAD SPEED; DENTAL RESTORATIONS; DWELL TIME; FATIGUE TESTING CONDITIONS; FUNCTIONALLY GRADED; METAL-CERAMIC BONDS; METAL-CERAMIC INTERFACE; METAL/CERAMIC COMPOSITES; NANOINDENTATION TESTS; PORCELAIN FUSED TO METALS; PORCELAIN-FUSED-TO-METAL RESTORATION; SEM/EDS; SHAPIRO-WILK TESTS; SHEAR BOND STRENGTH TESTS; SHEAR BOND STRENGTHS; SHEAR TESTS; SPECIAL DEVICES; SURFACE FRACTURE; THERMAL AND MECHANICAL CYCLING; THERMAL-MECHANICAL CYCLING; THERMOMECHANICAL CYCLING; UNIVERSAL TESTING MACHINES; YOUNG'S MODULUS;

BOND STRENGTH (MATERIALS); ELASTIC MODULI; FATIGUE TESTING; FILLING; FUNCTIONALLY GRADED MATERIALS; HARDNESS; HOT PRESSING; MATERIALS TESTING; METALS; NANOINDENTATION; PORCELAIN; RESTORATION;

FRACTURE;

ALLOY; CHROMIUM; COBALT; DENTAL MATERIAL; METAL; MOLYBDENUM;

ARTICLE; CERAMICS; DENTAL RESTORATION WEAR; DENTISTRY; FUNCTIONALLY GRADED MATERIALS; MATERIALS; POWDER; PRIORITY JOURNAL; PROCELAIN FUSED TO METAL RESTORATION; SHEAR STRESS; TENSILE STRENGTH;

DENTAL PORCELAIN; DENTAL RESTORATION FAILURE; DENTAL RESTORATION REPAIR; MATERIALS TESTING; MECHANICAL PROCESSES; METALS; SHEAR STRENGTH; TEMPERATURE;

EID: 84865290646     PISSN: 17516161     EISSN: 18780180     Source Type: Journal    
DOI: 10.1016/j.jmbbm.2012.06.002     Document Type: Article

References (54)

1. Anusavice K.J. Phillips' Science of Dental Materials 2006, W.B. Saunders, Philadelphia. 11th ed.
2. Anusavice K.J., Dehoff P.H., Fairhurs C.W. Comparative evaluation of ceramic-metal bond tests using finite element stress analysis. Journal of Dental Research 1980, 59:608-613.
3. Akova T., Ucar Y., Tukay A., Balkaya M.C., Brantley W.A. Comparison of the bond strength of laser-sintered and cast base metal dental alloys to porcelain. Dental Materials: Official Publication of the Academy of Dental Materials 2008, 24:1400-1404.
4. Atta O.M., Smith B.G.N., Brown D. Bond strengths of three chemical adhesive cements adhered to a nickel-chromium alloy for direct bonded retainers. The Journal of Prosthetic Dentistry 1990, 63:137-143.
5. Craig R.G., Powers J.M. Restorative dental materials 2002, Mosby, pp. 480-492. 11th ed.
6. Crim G.A., Mattingly S.L. Evaluation of two methods for assessing marginal leakage. The Journal of Prosthetic Dentistry 1981, 45:160-163.
7. de Melo R.M., Travassos A.C., Neisser M.P. Shear bond strengths of a ceramic system to alternative alloys. The Journal of Prosthetic Dentistry 2005, 93:64-69.
8. Dlouhy I., Boccaccini A.R. Preparation, microstructure and mechanical properties of metal-particulate/glass-matrix composites. Composites Science and Technology 1996, 56:1415-1424.
9. Donovan T.E., Swift.E.J Porcelain-fused-to-metal (PFM) alternatives. Journal of Esthetic and Restorative Dentistry 2009, 1:4-6.
10. dos Santos J.G., Fonseca R.G., Adabo L.G., Cruz C.A.S. Shear bond strength of metal-ceramic repair systems. The Journal of Prosthetic Dentistry 2006, 96(3):165-173.
11. Eliasson A., Arnelund C.F., Johansson A. A clinical evaluation of cobalt-chromium metal ceramic fixed partial dentures and crowns: A three-to seven-year retrospective study. The Journal of Prosthetic Dentistry 2007, 98:6-16.
12. Elsaka S.E., Hamouda I.M., Elewady Y.A., Abouelatta O.B., Swain M.V. Effect of chromium interlayer on the shear bond strength between porcelain and pure titanium. Dental Materials: Official Publication of the Academy of Dental Materials 2010, 26:793-798.
13. Elsaka S.E., Hamouda I.M., Elewady Y.A., Abouelatta O.B., Swain M.V. Influence of chromium interlayer on the adhesion of porcelain to machined titanium as determined by the strain energy release rate. Journal of Dentistry 2010, 38(8):648-654.
14. Fischer J., Zbären C., Stawarczyk B., Hämmerle C.H.F. The effect of thermal cycling on metal-ceramic bond strength. Journal of Dentistry 2009, 37:549-553.
15. Fusayama T., Katayoi T., Nomoto S. Corrosion of gold and amalgam placed in contact with each other. Journal of Dental Research 1963, 42:1183-1197.
16. Gasik M., Kawasaki A., Kang Y. Optimization of FGM TBC and their thermal cycling stability. Material Science Forum 2005, 492:9-14.
17. Gale M.S., Darvell B.W. Thermal cycling procedures for laboratory testing of dental restorations. Journal of Dentistry 1999, 27:89-99.
18. Hammad I.A., Stein R.S. A qualitative study for the bond and color of ceramometals - Part I. Journal of Prosthetic Dentistry 1990, 75:602-608.
19. Hammad I.A., Talic Y.F. Designs of bond strength tests for metal-ceramic complexes: Review of the literature. The Journal of Prosthetic Dentistry 1996, 75:602-608.
20. Hamouda I.M., Elùwaseffy N.A., Hasan A.M., Elùfalal A.A. Evaluation of an experimental dental porcelain. Journal of the Mechanical Behavior of Biomedical Materials 2010, 3:610-618.
21. Henriques B., Soares D., Silva F.S. Optimization of bond strength between gold alloy and porcelain through a composite interlayer obtained by powder metallurgy. Materials Science and Engineering A 2011, 528:1415-1420.
22. Henriques B., Soares D., Silva F. Shear bond strength of a Hot Pressed Au-Pd-Pt alloy-porcelain dental composite. J. Mech. Behav. Biomedical Materials (Bristol, England) 2011, 4(8):1718-1726.
23. Huang M., Wang R., Thompson V., Rekow D. Bioinspired design of dental multilayers. Journal of Materials Science: Materials in Medicine 2007, 18:57-64.
24. Jörn D., Waddell J.N., Swain M.V. The influence of opaque application methods on the bond strength and final shade of PFM restorations. Journal of Dentistry 2010, 38:143-149.
25. Leibrock A., Degenhart M., Behr M., Rosentritt M., Handel G. In vitro study of the effect of thermo- and load-cycling on the bond strength of porcelain repair system. Journal of Oral Rehabilitation 1999, 26:130-137.
26. Lorenzoni F.C., Martins L.M., Silva N.R.F.A., Coelho P.G., Guess P.C., Bonfante E.A., Thompson V.P., Bonfante G. Fatigue life and failure modes of crowns systems with a modified framework design. Journal of Dentistry 2010, 38:626-634.
27. Morgan M.J., James D.F., Pilliar R.M. Fractures of the fixture component of an osseointegrated implant. International Journal of Oral and Maxillofacial Implants 1993, 8:409-414.
28. Napankangas R., Salonen-Kemppi M.A., Raustia A.M. Longevity of fixed metal ceramic bridge prostheses: a clinical follow-up study. Journal of Oral Rehabilitation 2002, 29:140-145.
29. Nikaido T., Kunzelmann K.H., Chen H., Ogata M., Harada N., Yamaguchi S., Cox C.F., Hickel R., Tagami J. Evaluation of thermal cycling and mechanical loading on bond strength of a self-etching primer system to dentin. Dental Materials 2002, 18:269-275.
30. Niu X., Rahbar N., Farias S., Soboyejo W. Bio-inspired design of dental multilayers: Experiments and model. Journal of the Mechanical Behavior of Biomedical Materials 2009, 2:596-602.
31. Oyafuso D.K., Özcan M., Bottino M.A., Itinoche M.K. Influence of thermal and mechanical cycling on the flexural strength of ceramics with titanium or gold alloy frameworks. Dental Materials 2008, 24:351-356.
32. Pjetursson B.E., Tan K., Lang N.P., Brägger U., Egger M., Zwahlen M. A systematic review of the survival and complication rates of fixed partial dentures after an observation period of at least 5 years. Clinical Oral Implants Research 2004, 15:654-666.
33. Pröbster L., Maiwald U., Weber H. Three-point bending strength of ceramics fused to cast titanium. European Journal of Oral Sciences 1996, 104:313-319.
34. Rees J.S., Jacobsen P.H., Koliniotou-Kubia E. The current status of composite materials and adhesive systems. Part 4. Some clinically related research. Restorative Dentistry 1990, 6(3):4-8.
35. Rizkalla A.S., Jones D.W. Indentation fracture toughness and dynamic elastic moduli for commercial feldspathic dental porcelain materials. Dental Materials 2004, 20:198-206.
36. Rosentritt M., Behr M., Scharnagel P., Handel G., Kolbeck C. The influence of the resilient support of abutment teeth on the fracture resistance of all-ceramic fixed dental prostheses: An in vitro study. The International Journal of Prosthodontics 2011, 24:465-468.
37. Rosentritt M., Behr M., van der Zel J.M., Feilzer A.J. Approach for valuating the influence of laboratory simulation. Dental Materials: Official Publication of the Academy of Dental Materials 2009, 25:348-352.
38. Salazar M.S.M., Pereira S.M.B., Ccahuana V.Z., Passos S.P., Vanderlei A.D., Pavanelli C.A., Bottino M.A. Shear bond strength between metal alloy and a ceramic system, submitted to different thermocycling immersion times. Acta Ontolog. Latinoam. 2007, 20(2):97-102.
39. Sartori R., Corrĉa C.B., Fernandes F.R.B., Marcantonio E., Vaz L.G. Mechanical properties of dental implants submitted to fluoride ions action. Rev. Odont. 2007, 36(4):317-322.
40. Scherrer S.S., Wiskott A.H.W., Coto-Hunziker V., Belser U.C. Monotonic flexure and fatigue strength of composites for provisional and definitive restorations. The Journal of Prosthetic Dentistry 2003, 89:579-588.
41. Shimoe S., Tanoue N., Yanagida H., Atsuta M., Koizumi H., Matsumura H. Comparative strength of metal-ceramic and metal-composite bonds after extended thermocycling. Journal of Oral Rehabilitation 2004, 31:689-694.
42. Souza J.C.M., Nascimento R.M., Martinelli A.E. Characterization of dental-ceramic interfaces immersed in artificial saliva after substructural mechanical metallization with titanium. Surface and Coatings Technology 2010, 205:787-792.
43. Suresh S., Mortensen A. Fundamentals of functionally graded materials 1998, Maney publishing, London.
44. Suresh S. Graded materials for resistance to contact deformation and damage. Science (New York, NY) 2001, 292:2447-2451.
45. Tróia M.G., Henriques G.E.P., Nóbilo M.A.A., Mesquita M.F. The effect of thermal cycling on the bond strength of low-fusing porcelain to commercially pure titanium and titanium-aluminium-vanadium alloy. Dental Materials 2003, 19:790-796.
46. Upadhyay D., Panchal M.A., Dubey R.S., Srivastava V.K. Corrosion of alloys used in dentistry: A review. Materials Science and Engineering A 2006, 432(1-2):1-11.
47. Van Noort R. Introduction to Dental Materials 2007, Elsevier. 3rded.
48. Vásquez V., Ozcan M., Nishioka R., Souza R., Mesquita A., Pavanelli C. Mechanical and Thermal Cycling Effects on the flexural of glass Ceramics Fused to Titanium. Dental Materials 2008, 1(27):7-15.
49. Vásquez V.Z.C., Özcan M., Kimpara E.T. Evaluation of interface characterization and adhesion of glass ceramics to commercially pure titanium and gold alloys after thermal- and mechanical-loading. Dental Materials: Official Publication of the Academy of Dental Materials 2009, 25:221-231.
50. Vichi A., Louca C., Corciolani G., Ferrari M. Color related to ceramic and zirconia restorations: A review. Dental Materials: Official Publication of the Academy of Dental Materials 2011, 27:97-108.
51. Wagner W.C., Asgar K., Bigelow W.C., Flinn R.A. Effect of interfacial variables on metal-porcelain bonding. Journal of Biomedical Materials Research Part A 1993, 27:531-537.
52. Walter M., Reppel P.D., Böning K., Freesmeyer W.B. Six year follow-up of titanium and high-gold porcelain-fused-to-metal fixed partial dentures. Journal of Oral Rehabilitation 1999, 26:91-96.
53. Wu Y., Moser.J.B., Jameson L.M., Malone W.F.P. The effect of oxidation heat treatment on porcelain bond strength in selected base metal alloys. The Journal of Prosthetic Dentistry 1991, 66:439-444.
54. Zarone F., Russo S., Sorrentino R. From porcelain-fused-to-metal to zirconia: Clinical and experimental considerations. Dental Materials: Official Publication of the Academy of Dental Materials 2011, 27:83-96.