Evaluation of interface characterization and adhesion of glass ceramics to commercially pure titanium and gold alloy after thermal- and mechanical-loading

Dental Materials

Volumn 25, Issue 2, 2009, Pages 221-231

  Vásquez, Vanessa Zulema Ccahuana ^a   Özcan, Mutlu ^b   Kimpara, Estevão Tomomitsu ^a  

^a SÃO PAULO STATE UNIVERSITY UNESP   (Brazil)

^b UNIVERSITY MEDICAL CENTER GRONINGEN   (Netherlands)

Author keywords

Ceramic; EDS; Gold alloy; Mechanical aging; Shear bond strength; Thermal aging; Titanium

Indexed keywords

ADHESION; ALLOYS; ALUMINA; ALUMINUM; BARIUM; BOND STRENGTH (MATERIALS); CERAMIC MATERIALS; DENTAL MATERIALS; EXPLOSIVE ACTUATED DEVICES; GLASS CERAMICS; GOLD; GOLD ALLOYS; METALLIC COMPOUNDS; PALLADIUM; PORCELAIN; SCANNING ELECTRON MICROSCOPY; SHEAR STRENGTH; SILICON ALLOYS; SODIUM; STRENGTH OF MATERIALS; THERMAL AGING; TIN; TITANIUM; TITANIUM OXIDES;

ADHESIVE FAILURES; AGING CONDITIONS; AIRBORNE PARTICLES; ALLOY INTERFACES; ALUMINUM OXIDES; BOND STRENGTHS; CERAMIC; COMMERCIAL PURE TITANIUMS; COMMERCIALLY PURE TITANIUMS; CONTROL GROUPS; CROSSHEAD SPEEDS; DENTAL CERAMICS; DISTILLED WATERS; DWELL TIMES; EDS; EDS ANALYSIS; ENERGY DISPERSIVE; EXPERIMENTAL GROUPS; FAILURE TYPES; FELDSPATHIC CERAMICS; GLASSY MATRIXES; INTERFACE CHARACTERIZATIONS; INTERFACIAL ZONES; MECHANICAL AGING; METAL COMBINATIONS; OPAQUE CERAMICS; PD ALLOYS; SCANNING ELECTRON MICROSCOPES; SHEAR BOND STRENGTH; SUBSTRATE SURFACES; UNIVERSAL TESTS; WATER STORAGES;

TITANIUM ALLOYS;

ALLOY; ALUMINUM OXIDE; ALUMINUM SILICATE; BIOMEDICAL AND DENTAL MATERIALS; GLASS CERAMICS; GOLD ALLOY; PALLADIUM; POTASSIUM DERIVATIVE; SILICON; TITANIUM; TITANIUM DIOXIDE; VITA OMEGA; WATER;

ARTICLE; CERAMICS; CHEMISTRY; CLINICAL TRIAL; COMPARATIVE STUDY; CONTROLLED CLINICAL TRIAL; CONTROLLED STUDY; DENTAL BONDING; DENTAL CARE; DENTAL ETCHING; ELECTRON PROBE MICROANALYSIS; FELDSPAR; HUMAN; INSTRUMENTATION; MATERIALS TESTING; MECHANICAL STRESS; RANDOMIZED CONTROLLED TRIAL; SCANNING ELECTRON MICROSCOPY; SHEAR STRENGTH; SURFACE PROPERTY; TEMPERATURE; TOOTH PROSTHESIS;

ALUMINUM OXIDE; ALUMINUM SILICATES; CERAMICS; DENTAL BONDING; DENTAL ETCHING; DENTAL MATERIALS; DENTAL PORCELAIN; DENTAL STRESS ANALYSIS; ELECTRON PROBE MICROANALYSIS; GOLD ALLOYS; HUMANS; MATERIALS TESTING; METAL CERAMIC ALLOYS; MICROSCOPY, ELECTRON, SCANNING; PALLADIUM; POTASSIUM COMPOUNDS; SHEAR STRENGTH; SILICON; STRESS, MECHANICAL; SURFACE PROPERTIES; TEMPERATURE; TITANIUM; WATER;

EID: 58149239912     PISSN: 01095641     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.dental.2008.07.002     Document Type: Article

References (46)

1. Fradeani M., D'Amelio M., and Redemagni M. Corrado M. Five-year follow-up with Procera all-ceramic crowns. Quintessence Int 36 (2005) 105-113
2. Wang R.R., and Fenton A. Titanium for prosthodontic applications: a review of the literature. Quintessence Int 27 (1996) 401-408
3. Lautenschlager E.P., and Monaghan P. Titanium and titanium alloys as dental materials. Int Dent J 43 (1993) 245-253
4. Könönen M., and Kivilathi J. Bonding of low-fusing dental porcelain to commercially pure titanium. J Biomed Mater Res 28 (1994) 1027-1035
5. Yoda M., Konno T., Takada Y., Iijima K., Griggs J., Okuno O., et al. Bond strength of binary titanium alloys to porcelain. Biomaterials 22 (2001) 1675-1681
6. Akagi K., Okamoto Y., Matsuura T., and Hoibe T. Properties of test metal ceramic titanium alloys. J Prosthet Dent 68 (1992) 462-467
7. Kimura H., Horng C.J., Okazaki M., and Takahashi J. Oxidation effects on porcelain-titanium interface reactions and bond strength. Dent Mater J 9 (1990) 91-99
8. Adachi M., Mackert Jr. J.R., Parry E.E., and Fairhurst C.W. Oxide adherence and porcelain bonding to titanium and Ti-6Al-4V alloy. J Dent Res 69 (1990) 1230-1235
9. Könönen M., and Kivilahti J. Fusing of dental ceramics to titanium. J Dent Res 80 (2001) 840-854
10. Anusavice K.J. Philips. Science of dental materials. 11th ed. (2004), Sauders, Misouri p. 763
11. Esquivel J.F., Chai J., and Wozniak W.T. The physical properties of low-fusing porcelains for titanium. Int J Prosthodont 9 (1996) 563-571
12. Herø H., Syverud M., and Waarli M. Mold filling and porosity in castings of titanium. Dent Mater 19 (1993) 15-18
13. King A.W., Lautenschlager E., Chai J., and Gilbert J. A comparison of the hardness of different types of titanium and conventional metal ceramics. J Prosthet Dent 72 (1994) 314-319
14. Syverud M., and Herø H. Mold filling of Ti casting using investments with different gas permeability. Dent Mater 11 (1995) 14-18
15. Yilmaz H., and Dinçer C. Comparison of the bond compatibility of titanium and a NiCr alloy to dental porcelain. J Dent 27 (1999) 215-222
16. In: Powers J.M., and Sakaguchi R.L. (Eds). Craig's restorative dental materials. 12th ed. (2006), St. Louis, Mosby 632
17. Hammad I.A., and Talic Y.F. Designs of bond strength tests for metal ceramic complexes: review of the literature. J Prosthet Dent 75 (1996) 602-608
18. White S.N., Li Z.C., Yu Z., and Kipnis V. Relationship between static chemical and cyclic mechanical fatigue in a feldspathic porcelain. Dent Mater 13 (1997) 103-110
19. Poljak-Guberina R., Catovic A., Jerolimov V., Franz M., and Bergman V. The fatigue strength of the interface between Ag-Pd alloy and hydrothermal ceramic. Dent Mater 15 (1999) 417-420
20. Probster L., Maiwald U., and Weber H. Three-point bending strength of ceramics fused to cast titanium. Eur J Oral Sci 104 (1996) 313-319
21. Wang R.R., Welsch G.E., and Castro-Cedeno M. Interfacial reactions of cast titanium with mold materials. Int J Prosthodont 11 (1998) 33-43
22. Garbelini W.J., Henriques G.E.P., Tróia Jr. M., Mesquita M.F., and Dezan C.C. Evaluation of low-fusing ceramic systems combined with titanium grades II and V by bending test and scanning electron microscopy. J Appl Oral Sci 11 (2003) 354-360
23. Bondioli I.R., and Bottino M.A. Evaluation of shear bond strength at the interface of two porcelains and pure titanium injected into the casting mold at three different temperatures. J Prosthet Dent 91 (2004) 541-547
24. Itinoche K.M., Özcan M., Bottino M.A., and Oyafuso D. Effect of mechanical cycling on the flexural strength of densely sintered ceramics. Dent Mater 22 (2006) 1029-1034
25. Suansuwam N., and Swain M.V. Adhesion of porcelain to titanium and titanium alloy. J Dent 31 (2003) 509-518
26. Papazoglu E., and Brantley W.A. Porcelain adherence versus force to failure for palladium-gallium alloys: a critique of metal-ceramic bond testing. Dent Mater 14 (1998) 112-119
27. Anusavice K.J., Dehoff P.H., and Fairhurs C.W. Comparative evaluation of ceramic-metal bond tests using finite element stress analysis. J Dent Res 59 (1980) 608-613
28. Tróia Jr. M.G., Henriques G.E., Nobilo M.A., and Mesquita M.F. The effect of thermal cycling on the bond strength of low-fusing porcelain to commercially pure titanium and titanium-aluminium-vanadium alloy. Dent Mater 19 (2003) 790-796
29. Gilbert J.L., Covey D.A., and Lautenschalager E.P. Bond characteristics of porcelain fused to milled titanium. Dent Mater 10 (1994) 134-140
30. Chong M.P., Beech D.R., and Chem M.R.I.C. A simple shear test to evaluate the bond strength of ceramic fused to metal. Aust Dent J 25 (1980) 357-361
31. Hammad I.A., Goodkind R.J., and Gerberich W.W. A shear test for the bond strength of ceramometals. J Prosthet Dent 58 (1987) 431-437
32. Taira Y., Matsumura H., Yoshida K., Tanaka T., and Atsuta M. Influence of surface oxidation of titanium on adhesion. J Dent 26 (1998) 69-73
33. Melo R.M., Travassos A.C., and Neisser M.P. Shear bond strengths of a ceramic system to alternative metal alloys. J Prosthet Dent 93 (2005) 64-69
34. Cai Z., Bunce N., Nunn M.E., and Okabe T. Porcelain adherence to dental cast CP titanium: effects of surface modifications. Biomaterials 22 (2001) 979-986
35. Riley E.J. Ceramo-metal restorations. Dent Clin N Am 21 (1977) 669-682
36. Pang I.C., Gilbert J.L., Chai J., and Lautenschlager E.P. Bonding characteristics of low-fusing porcelain bonded to pure titanium and palladium-copper alloy. J Prosthet Dent 73 (1995) 17-25
37. White S.N., Caputo A.A., and Goo E. Strength of porcelain fused to titanium beams. J Prosthet Dent 75 (1996) 640-648
38. Shimoe S., Tanoue N., Yanagida H., Atsuta M., Koizumi H., and Matsumura H. Comparative strength of metal-ceramic and metal-composite bonds after extended thermocycling. J Oral Rehabil 31 (2004) 689-694
39. Suansuwan N., and Swain M.V. New approach for evaluating metal-porcelain interfacial bonding. Int J Prosthodont 12 (1999) 547-552
40. Scherrer S.S., Wiskott A.H., Coto-Hunziker V., and Belser U.C. Monotonic flexure and fatigue strength of composites for provisional and definitive restorations. J Prosthet Dent 89 (2003) 579-588
41. Teoh S.H. Fatigue of biomaterials: a review. Int Biomat Fatigue 22 (2000) 825-837
42. Gale M.S., and Darwell B.W. Thermal cycling procedures for laboratory testing of dental restorations. J Dent 27 (1999) 89-99
43. Leibrock A., Degenhart M., Behr M., Rosentritt M., and Handel G. In vitro study of the effect of thermo- and load-cycling on the bond strength of porcelain repair systems. J Oral Rehabil 26 (1999) 130-137
44. International Organization for Standardization, ISO 10477:1992/Amendment.1:1998(E).
45. Özcan M., and Niedermeier W. Clinical study on the reasons for and location of failures of metal ceramic restorations and survival of repairs. Int J Prosthodont 15 (2002) 299-302
46. Oyafuso D.K., Özcan M., Bottino M.A., and Itinoche K. Influence of thermal and mechanical cycling on the flexural strength of ceramics with titanium or gold alloy frameworks. Dent Mater 24 (2008) 351-356