Review of degradation models for progressive failure analysis of fiber reinforced polymer composites

Applied Mechanics Reviews

Volumn 62, Issue 1, 2009, Pages 1-33

  Garnich, Mark R ^a   Akula, Venkata M K ^a  

^a UNIVERSITY OF WYOMING   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

DEGRADATION MODEL; FAILURE CRITERIA; FIBER REINFORCED POLYMER COMPOSITES; FIELD VARIABLES; FINITE ELEMENT IMPLEMENTATION; MATERIAL DAMAGES; MATERIAL PROPERTY DEGRADATION; MATHEMATICAL REPRESENTATIONS; PROGRESSIVE FAILURE ANALYSIS; PROPERTY DEGRADATION; RESIDUAL PROPERTIES;

COMPOSITE STRUCTURES; DEGRADATION; FAILURE ANALYSIS; FIBER REINFORCED PLASTICS; FUNCTIONS; LAMINATES; MATHEMATICAL MODELS; POLYMER MATRIX COMPOSITES; QUALITY ASSURANCE; STRUCTURE (COMPOSITION);

FINITE ELEMENT METHOD;

EID: 69649096419     PISSN: 00036900     EISSN: None     Source Type: Journal    
DOI: 10.1115/1.3013822     Document Type: Review

References (310)

1. Sendeckyj, G. P., 1972, "A Brief Survey of Empirical Multi-Axial Strength Criteria for Composites," Composite Materials: Testing and Design (Second Conference), American Society for Testing and Materials, Philadelphia, ASTM STP 497, pp. 41-51.
2. Wu, E. M., "Phenomenological Anisotropic Failure Criterion," Mechanics of Composite Materials (Composite Materials Series), G. P. Sendeckyj, ed., Academic Press, New York and London, Vol. 2, pp. 353-431.
3. Soni, S. R., 1983, "A New Look at Commonly Used Failure Theories in Composite Laminates," Proceedings of the 24th AIAA/ASME/ASCE/AHS Structures, Structural Dynamics and Materials Conference, Lake Tahoe, NV, May 2-4, pp. 171-175.
4. Soni, S. R., 1983, "A Comparative Study of Failure Envelopes in Composite Laminates," J. Reinf. Plast. Compos., 2(1), pp. 34-42.
5. Tsai, S. W., 1984, "A Survey of Macroscopic Failure Criteria for Composite Materials," J. Reinf. Plast. Compos., 3(1), pp. 40-62.
6. Rowlands, R. E., 1985, "Strength (Failure) Theories and Their Experimental Correlation," Handbook of Composites, G. C. Sih and A. M. Skudra, eds., Elsevier Science, pp. 71-125.
7. Nahas, M. N., 1986, "Survey of Failure and Post-Failure Theories of Laminated Fiber-Reinforced Composites," J. Compos. Technol. Res., 8(4), pp. 138-153.
8. Fan, W., 1987, "On Phenomenological Anisotropic Failure Criteria," Compos. Sci. Technol., 28(4), pp. 269-278.
9. Labossiere, P., and Neale, K. W., 1987, "Macroscopic Failure Criteria for Fibre-Reinforced Composite Materials," SM Arch., 12(2), pp. 439-450.
10. Thom, H., 1998, "A Review of the Biaxial Strength of Fibre-Reinforced Plastics," Composites, Part A, 29(8), pp. 869-886.
11. Federico, P., 2001, "A Study of Failure Criteria of Fibrous Composite Materials," NASA/CR Report No. 2001-210661.
12. Soden, P. D., Hinton, M. J., and Kaddour, A. S., 1998, "A Comparison of Predictive Capabilities of Current Failure Theories for Composite Laminates," Compos. Sci. Technol., 58(7), pp. 1225-1254.
13. Hinton, M. J., Kaddour, A. S., and Soden, P. D., 2002, "A Comparison of the Predictive Capabilities of Current Failure Theories for Composite Laminates, Judged Against Experimental Evidence," Compos. Sci. Technol., 62(12-13), pp. 1725-1797.
14. Kaddour, A. S., Hinton, M. J., and Soden, P. D., 2004, "A Comparison of the Predictive Capabilities of Current Failure Theories for Composite Laminates: Additional Contributions," Compos. Sci. Technol., 64(3-4), pp. 449-476.
15. Hinton, M. J., Kaddour, A. S., and Soden, P. D., 2004, "A Further Assessment of the Predictive Capabilities of Current Failure Theories for Composite Laminates: Comparison With Experimental Evidence," Compos. Sci. Technol., 64(3-4), pp. 549-588.
16. Icardi, U., Locatto, S., and Longo, A., 2007, "Assessment of Recent Theories for Predicting Failures of Composite Laminates," Appl. Mech. Rev., 60(2), pp. 76-86.
17. Hill, R., 1950, Mathematical Theory of Plasticity, Clarendon, Oxford, pp. 317-321.
18. Azzi, V. D., and Tsai, S. W., 1965, "Anisotropic Strength of Composites," Exp. Mech., 5(9), pp. 283-288.
19. Hoffman, O., 1967, "The Brittle Strength of Orthotropic Materials," J. Compos. Mater., 1(2), pp. 200-206.
20. Chamis, C. C., 1969, "Failure Criteria for Filamentary Composites," Composite Materials: Testing and Design, American Society for Testing and Materials, Philadelphia, ASTM STP 460, pp. 336-351.
21. Tsai, S. W., and Wu, E. M., 1971, "A General Theory of Strength for Anisotropic Materials," J. Compos. Mater., 5(1), pp. 58-80.
22. Sandhu, R. S., 1976, "Nonlinear Behavior of Unidirectional and Angle Ply Laminates," J. Aircr., 13(2), pp. 104-111.
23. Hashin, Z., and Rotem, A., 1973, "A Fatigue Failure Criterion for Fiber Reinforced Materials," J. Compos. Mater., 7(4), pp. 448-464.
24. Hashin, Z., 1980, "Failure Criteria for Unidirectional Fiber Composites," ASME J. Appl. Mech., 47(2), pp. 329-334.
25. Lee, J. D., 1982, "Three-Dimensional Finite Element Analysis of Damage Accumulation in Composite Laminates," Proceedings of the Second USAUSSR Symposium, Bethlehem, PA, Mar. 9-12, pp. 291-306.
26. Christensen, R. M., 1997, "Stress Based Yield/Failure Criteria for Fiber Composites," Int. J. Solids Struct., 34(5), pp. 529-543.
27. Mayes, J. S., and Hansen, A. C., 2001, "A Multicontinuum Failure Analysis of Composite Structural Laminates," Mech. Compos. Mater. Struct., 8(4), pp. 249-262.
28. Hahn, H. T., and Williams, J. G., 1986, "Compression Failure Mechanisms in Unidirectional Composites," Composite Materials: Testing and Design, American Society for Testing and Materials, Philadelphia, ASTM STP 893, pp. 115-139.
29. Eason, T. G., and Ochoa, O. O., 1996, "Modeling Progressive Damage in Composites: A Shear Deformable Element for ABAQUS," Compos. Struct., 34(2), pp. 119-128.
30. Ye, L., 1988, "Role of Matrix Resin in Delamination Onset and Growth in Composite Laminates," Compos. Sci. Technol., 33(4), pp. 257-277.
31. Yamada, S. E., and Sun, C. T., 1978, "Analysis of Laminate Strength and Its Distribution," J. Compos. Mater., 12(3), pp. 275-284.
32. Chang, F. K., Scott, R. A., and Springer, G. S., 1984, "Failure Strength of Nonlinearly Elastic Composite Laminates Containing a Pin Loaded Hole," J. Compos. Mater., 18(5), pp. 464-477.
33. Lessard, L. B., 1991, "Bearing Failure of Composite Pinned Joints Using Progressive Damage Modeling," Proceedings of the Eighth International Conference on Composite Materials, Honolulu, HI, Jul. 15-19, pp. 9.E.1-9.E.10.
34. Griffin, O. H., Jr., 1982, "Evaluation of Finite-Element Software Packages for Stress Analysis of Laminated Composites," Compos. Technol. Rev., 4(4), pp. 136-141.
35. Saarela, O., 1994, "Computer Programs for Mechanical Analysis and Design of Polymer Matrix Components," Prog. Polym. Sci., 19(1), pp. 171-301.
36. ABAQUS Inc., 2006, ABAQUS Version 6.6, ABAQUS Inc., Providence, RI.
37. Ochoa, O. O., and Reddy, J. N., 1992, Finite Element Analysis of Composite Laminates, Kluwer Academic, Boston.
38. Robbins, D. H., Jr., and Reddy, J. N., 1993, "Modelling of Thick Composites Using a Layer-Wise Laminate Theory," Int. J. Numer. Methods Eng., 36(4), pp. 655-677.
39. Reddy, J. N., 1989, "On Refined Computational Models of Composite Laminates," Int. J. Numer. Methods Eng., 27(2), pp. 361-382.
40. Reddy, J. N., 1989, "On the Generalization of Displacement-Based Laminate Theories," Appl. Mech. Rev., 42(1), pp. S213-S222.
41. Hyer, M. W., 1998, Stress Analysis of Fiber-Reinforced Composite Materials, McGraw-Hill Science, New York.
42. Herakovich, C. T., 1998, Mechanics of Fibrous Composites, Wiley, New York.
43. Jones, R. M., 1999, Mechanics of Composite Materials, 2nd ed., Taylor & Francis, Philadelphia.
44. Chang, F. K., and Chang, Y. K., 1987, "A Progressive Damage Model for Laminated Composites Containing Stress Concentrations," J. Compos. Mater., 21(9), pp. 834-855.
45. Chou, P. C., Carleone, J., and Hsu, C. M., 1972, "Elastic Constants of Layered Media," J. Compos. Mater., 6(1), pp. 80-93.
46. Sun, C. T., and Li, S., 1988, "Three-Dimensional Effective Elastic Constants for Thick Laminates," J. Compos. Mater., 22(7), pp. 629-639.
47. Al-Khalil, M. F. S., and Soden, P. D., 1994, "Theoretical Through-Thickness Elastic Constants for Filament-Wound Tubes," Int. J. Mech. Sci., 36(1), pp. 49-62.
48. Lempriere, B. M., 1968, "Poisson's Ratio in Orthotropic Materials," AIAA J., 6(11), pp. 2226-2227.
49. Reddy, Y. S., and Reddy, J. N., 1993, "Three-Dimensional Finite Element Progressive Failure Analysis of Composite Laminates Under Axial Extension," J. Compos. Technol. Res., 15(2), pp. 73-87.
50. Vinson, J. R., and Sierakowski, R. L., 1986, The Behavior of Structures Composed of Composite Materials (Mechanics of Structural Systems), Kluwer Academic, Boston, Vol 5.
51. Chen, W. H., and Lee, S. S., 1995, "Numerical and Experimental Failure Analysis of Composite Laminates With Bolted Joints Under Bending Loads," J. Compos. Mater., 29(1), pp. 15-36.
52. Lee, J. D., 1982, "Three Dimensional Finite Element Analysis of Damage Accumulation in Composite Laminate," Comput. Struct., 15(3), pp. 335-350.
53. Lee, J. D., 1980, "Three Dimensional Finite Element Analysis of Layered Fiber-Reinforced Composite Materials," Comput. Struct., 12(3), pp. 319-339.
54. Labossiere, P., Neale, K. W., and Neglo, K., 1988, "Damage Accumulation in Fibre-Reinforced Composite Laminates," Trans. Can. Soc. Mech. Eng., 12(3), pp. 133-137.
55. Hwang, W. C., and Sun, C. T., 1989, "Failure Analysis of Laminated Composites by Using Iterative Three-Dimensional Finite Element Method," Comput. Struct., 33(1), pp. 41-47.
56. Chang, F. K., and Springer, G. S., 1986, "The Strengths of Fiber Reinforced Composite Bends," J. Compos. Mater., 20(1), pp. 30-45.
57. Nagesh, 2003, "Finite-Element Analysis of Pressure Vessels With Progressive Degradation," Def. Sci. J., 53(1), pp. 75-86.
58. Tsau, L.-R., and Plunkett, R., 1993, "Finite Element Analysis of Progressive Failure for Laminated FRP Plates With Inplane Loading," Eng. Fract. Mech., 45(4), pp. 529-546.
59. Tsau, L. R., Chang, Y. H., and Tsao, F. L., 1995, "The Design of Optimal Stacking Sequence for Laminated FRP Plates With Inplane Loading," Comput. Struct., 55(4), pp. 565-580.
60. Tsau, L. R., and Liu, C. H., 1995, "A Comparison Between Two Optimization Methods on the Stacking Sequence of Fiber-Reinforced Composite Laminate," Comput. Struct., 55(3), pp. 515-525.
61. Tsai, S. W., 1986, Composites Design, Think Composites, Dayton, OH.
62. Hu, F. Z., Soutis, C., and Edge, E. C., 1997, "Interlaminar Stresses in Composite Laminates With a Circular Hole," Compos. Struct., 37(2), pp. 223-232.
63. Pachajoa, M. E., Frances, M. K., and Lee, J. D., 1995, "Stress and Failure Analysis of Composite Structures," Eng. Fract. Mech., 50(5-6), pp. 883-902.
64. McCarthy, C. T., McCarthy, M. A., and Lawlor, V. P., 2005, "Progressive Damage Analysis of Multi-Bolt Composite Joints With Variable Bolt-Hole Clearances," Composites, Part B, 36(4), pp. 290-305.
65. Camanho, P. P., and Matthews, F. L., 1999, "A Progressive Damage Model for Mechanically Fastened Joints in Composite Laminates," J. Compos. Mater., 33(24), pp. 2248-2280.
66. Nuismer, R. J., and Tan, S. C., 1988, "Constitutive Relations of a Cracked Composite Lamina," J. Compos. Mater., 22(4), pp. 306-321.
67. Tan, S. C., and Nuismer, R. J., 1989, "A Theory for Progressive Matrix Cracking in Composite Laminates," J. Compos. Mater., 23(10), pp. 1029-1047.
68. O'Higgins, R. M., Padhi, G. S., McCarthy, M. A., and McCarthy, C. T., 2004, "Experimental and Numerical Study of the Open-Hole Tensile Strength of Carbon/Epoxy Composites," Mech. Compos. Mater., 40(4), pp. 269-278.
69. Gul Apalak, Z., Kemal Apalak, M., and Serdar Genc, M., 2007, "Progressive Damage Modeling of an Adhesively Bonded Composite Single Lap Joint Under Flexural Loads at the Mesoscale Level," J. Reinf. Plast. Compos., 26(9), pp. 903-953.
70. Kermanidis, Th., Labeas, G., Tserpes, K. I., and Pantelakis, Sp., 2000, "Finite Element Modeling of Damage Accumulation in Bolted Composite Joints Under Incremental Tensile Loading," Proceedings of the Third ECCOMAS Congress, Barcelona, Spain, Sept. 11-14.
71. Tserpes, K. I., Papanikos, P., and Kermanidis, Th., 2001, "A Three-Dimensional Progressive Damage Model for Bolted Joints in Composite Laminates Subjected to Tensile Loading," Fatigue Fract. Eng. Mater. Struct., 24(10), pp. 663-675.
72. Shokrieh, M. M., Lessard, L. B., and Poon, C., 1996, "Three-Dimensional Progressive Failure Analysis of Pin/Bolt Loaded Composite Laminates," 83rd Meeting of the AGARD SMP on Bolted Joints in Polymeric Composites, Florence, Italy, Sept, 2-3, pp. 7.1-7.10.
73. Tserpes, K. I., Labeas, G., Papanikos, P., and Kermanidis, Th., 2002, "Strength Prediction of Bolted Joints in Graphite/Epoxy Composite Laminates," Composites, Part B, 33(7), pp. 521-529.
74. Ireman, T., Ranvik, T., and Eriksson, I., 2000, "On Damage Development in Mechanically Fastened Composite Laminates," Compos. Struct., 49(2), pp. 151-171.
75. Mayes, J. S., 1999, "Multicontinuum Failure Analysis of Composite Structural Laminates," Ph.D. thesis, University of Wyoming, Laramie.
76. Mayes, J. S., and Hansen, A. C., 2004, "Composite Laminate Failure Analysis Using Multicontinuum Theory," Compos. Sci. Technol., 64(3-4), pp. 379-394.
77. Mayes, J. S., and Hansen, A. C., 2004, "A Comparison of Multicontinuum Theory Based Failure Simulation With Experimental Results," Compos. Sci. Technol., 64(3-4), pp. 517-527.
78. Waszczak, J. P., and Cruse, T. A., 1971, "Failure Mode and Strength Predictions of Anisotropic Bolt Bearing Specimens," J. Compos. Mater., 5(3), pp. 421-425.
79. Sciuva, M. D., Icardi, U., and Villani, M., 1998, "Failure Analysis of Composite Laminates Under Large Deflection," Compos. Struct., 40(3-4), pp. 239-255.
80. Pal, P., and Ray, C., 2002, "Progressive Failure Analysis of Laminated Composite Plates by Finite Element Method," J. Reinf. Plast. Compos., 21(16), pp. 1505-1513.
81. Prusty, B. G., 2005, "Progressive Failure Analysis of Laminated Unstiffened and Stiffened Composite Panels," J. Reinf. Plast. Compos., 24(6), pp. 633-642.
82. Lee, Y. J., and Chen, W. H., 1988, "Failure Process and Bolted Joint Strength of Composite Laminates," J. Chin. Soc. Mech. Eng., 9(3), pp. 169-182.
83. Chen, W. H., and Lee, Y. J., 1990, "The Effects of Clearance and Pin Elasticity on the Bearing Strength of Composite Laminates," J. Chin. Soc. Mech. Eng., 11(2), pp. 147-157.
84. Kim, Z. G., Hong, C. S., and Kim, C. G., 1995, "Postbuckling Analysis of Stringer Stiffened Composite Laminated Cylindrical Panels," J. Reinf. Plast. Compos., 14(8), pp. 827-846.
85. Kong, C. W., Lee, I. C., Kim, C. G., and Hong, C. S., 1998, "Postbuckling and Failure of Stiffened Composite Panels Under Axial Compression," Compos. Struct., 42(1), pp. 13-21.
86. Kong, C. W., Hong, C. S., and Kim, C. G., 2001, "Postbuckling Strength of Composite Plate With a Hole," J. Reinf. Plast. Compos., 20(6), pp. 466-481.
87. Hyer, M. W., Wolford, G. F., and Knight, N. F., Jr., 2003, "Damage Initiation and Progression in Internally Pressurized Noncircular Composite Cylinders," Proceedings of the 44th AIAA/ASME/ASCE/AHS Structures, Structural Dynamics, and Materials Conference, Norfolk, VA, Apr. l7-10, pp. 1702-1712.
88. Chen, J. K., Sun, C. T., and Chang, C. I., 1985, "Failure Analysis of a Graphite/Epoxy Laminate Subjected to Combined Thermal and Mechanical Loading," J. Compos. Mater., 19(5), pp. 408-423.
89. Gummadi, L. N. B., and Palazotto, A. N., 1998, "Progressive Failure Analysis of Composite Cylindrical Shells Considering Large Rotations," Composites, Part B, 29(5), pp. 547-563.
90. Kweon, J. H., Hong, C. S., and Lee, I. C., 1995, "Postbuckling Compressive Strength of Graphite/Epoxy Laminated Cylindrical Panels Loaded in Compression," AIAA J., 33(2), pp. 217-222.
91. Kweon, J. H., 1998, "Post-Failure Analysis of Composite Cylindrical Panels Under Compression," J. Reinf. Plast. Compos., 17(18), pp. 1665-1681.
92. Kweon, J. H., 2002, "Crippling Analysis of Composite Stringers Based on Complete Unloading Method," Comput. Struct., 80(27-30), pp. 2167-2175.
93. Lee, I. C., Kim, C. G., and Hong, C. S., 1997, "Buckling and Postbuckling Behavior of Stiffened Composite Panels Loaded in Compression," AIAA J., 35(1), pp. 202-204.
94. Sun, X. K., Du, S. Y., and Wang, G. D., 1999, "Bursting Problem of Filament Wound Composite Pressure Vessels," Int. J. Pressure Vessels Piping, 76(1), pp. 55-59.
95. Wang, J., Callus, P. J., and Bannister, M. K., 2004, "Experimental and Numerical Investigation of the Tension and Compression Strength of Un-Notched and Notched Quasi-Isotropic Laminates," Compos. Struct., 64(3-4), pp. 297-306.
96. Kam, T. Y., Sher, H. F., Chao, T. N., and Chang, R. R., 1996, "Predictions of Deflection and First-Ply Failure Load of Thin Laminated Composite Plates Via the Finite Element Approach," Int. J. Solids Struct., 33(3), pp. 375-398.
97. Sandhu, R. S., Sendeckyj, G. P., and Gallo, R. L., 1983, "Modeling of the Failure Process in Notched Laminates," Proceedings of IUTAM Symposium, Blacksburg, VA, pp. 179-189.
98. Griffis, C. A., Nemes, J. A., Stonesifer, F. R., and Chang, C. I., 1986, "Degradation in Strength of Laminated Composites Subjected to Intense Heating and Mechanical Loading," J. Compos. Mater., 20(3), pp. 216-235.
99. Engelstad, S. P., Reddy, J. N., and Knight, N. F., Jr., 1992, "Postbuckling Response and Failure Prediction of Graphite-Epoxy Plates Loaded in Compression," AIAA J., 30(8), pp. 2106-2113.
100. Singh, S. B., and Kumar, A., 1998, "Postbuckling Response and Failure of Symmetric Laminates Under In-Plane Shear," Compos. Sci. Technol., 58(12), pp. 1949-1960.
101. Singh, S. B., and Kumar, A., 1999, "Postbuckling Response and Strength of Laminates Under Combined In-Plane Loads," Compos. Sci. Technol., 59(5), pp. 727-736.
102. Ganesan, R., and Zhang, D., 2004, "Progressive Failure Analysis of Composite Laminates Subjected to In-Plane Compressive and Shear Loadings," Sci. Eng. Compos. Mater., 11(2-3), pp. 79-102.
103. Pandey, A. K., and Reddy, J. N., 1987, "A Post First-Ply Failure Analysis of Composite Laminates," Proceedings of the 28th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Material Conference, Monterey, CA, Apr. 6-8, pp. 788-797.
104. Gotsis, P. K., Chamis, C. C., and Minnetyan, L., 1998, "Prediction of Composite Laminate Fracture, Micromechanics and Progressive Fracture," Compos. Sci. Technol., 58(7), pp. 1137-1149.
105. Gotsis, P. K., Chamis, C. C., and Minnetyan, L., 2002, "Application of Progressive Fracture Analysis for Predicting Failure Envelopes and Stress-Strain Behaviors of Composite Laminates: A Comparison With Experimental Results," Compos. Sci. Technol., 62(12-13), pp. 1545-1559.
106. Minnetyan, L., Chamis, C. C., and Murthy, P. L. N., 1992, "Structural Durability of a Composite Pressure Vessel," J. Reinf. Plast. Compos., 11(11), pp. 1251-1269.
107. Gotsis, P. K., Chamis, C. C., and Minnetyan, L., 1996, "Computational Simulation of Damage Progression of Composite Thin Shells Subjected to Mechanical Loads," Theor. Appl. Fract. Mech., 25(3), pp. 211-224.
108. Gotsis, P. K., Chamis, C. C., and Minnetyan, L., 1997, "Progressive Fracture of Fiber Composite Build-Up Structures," J. Reinf. Plast. Compos., 16(2), pp. 182-198.
109. Minnetyan, L., and Chamis, C. C., 1997, "Progressive Fracture of Composite Cylindrical Shells Subjected to External Pressure," J. Compos. Technol. Res., 19(2), pp. 65-71.
110. Minnetyan, L., Rivers, J. M., Chamis, C. C., and Murthy, P. L. N., 1995, "Discontinuously Stiffened Composite Panel Under Compressive Loading," J. Reinf. Plast. Compos., 14(1), pp. 85-98.
111. Chamis, C. C., Gotsis, P. K., and Minnetyan, L., 1996, "Damage Tolerance of Composite Pressurized Shells," Proceedings of the 37th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference and Exhibit, Salt Lake City, UT, Apr. 15-17, pp. 2112-2121.
112. Chamis, C. C., Gotsis, P. K., and Minnetyan, L., 1998, "Progressive Fracture and Damage Tolerance of Composite Pressure Vessels," J. Adv. Mater., 30(1), pp. 22-26.
113. Huang, D., and Minnetyan, L., 1998, "Damage Progression in Carbon-Fiber Reinforced Plastic I-Beams," J. Compos. Constr., 2(1), pp. 38-45.
114. Huang, D., and Minnetyan, L., 2001, "Progressive Fracture of Stitched Stiffened Composite Shear Panels in the Postbuckling Range," J. Reinf. Plast. Compos., 20(18), pp. 1617-1632.
115. Averill, R. C., 1992, "A Micromechanics-Based Progressive Failure Model for Laminated Composite Structures," Proceedings of the 33rd AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference and Exhibit, Dallas, TX, Apr. 13-15, pp. 2898-2904.
116. Kim, Y., Davalos, J. F., and Barbero, E. J., 1996, "Progressive Failure Analysis of Laminated Composite Beams," J. Compos. Mater., 30(5), pp. 536-560.
117. Davalos, J. F., and Kim, Y., 1996, "A Layer-Wise Formulation for Progressive Failure Analysis of Laminated Composite Beams," Proceedings of the Fourth Materials Engineering Conference, Washington, DC, Nov. 10-14, pp. 1150-1159.
118. Greif, R., and Chapon, E., 1993, "Investigation of Successive Failure Modes in Graphite/Epoxy Laminated Composite Beams," J. Reinf. Plast. Compos., 12(5), pp. 602-621.
119. Yang, L., 1988, "Reliability of Composite Laminates," Mech. Struct. Mach., 16(4), pp. 523-536.
120. Zhao, H., and Zhanjun, G., 1995, "Reliability Analysis of Composite Laminates by Enumerating Significant Failure Modes," J. Compos. Mater., 14(5), pp. 427-444.
121. Thomas, D. J., and Wetherhold, R. C., 1991, "Reliability Analysis of Composite Laminates With Load Sharing," J. Compos. Mater., 25(11), pp. 1459-1475.
122. Max Yen, S. C., Chu, T. C., Teh, K. T., Wright, M. A., and Stumpff, P., 1994, "Diagnosis of the Subsequent Failure Mechanisms of Composite Laminates," Int. J. Offshore Polar Eng., 4(3), pp. 248-256.
123. Kang, T. J., Cho, Y. J., Youn, J. R., Chung, K., and Lee, K. W., 2001, "Prediction of the Ultimate Strength of Composite Laminates Under In-Plane Loading Using a Probabilistic Approach," Polym. Polym. Compos., 9(5), pp. 339-343.
124. Tsai, S. W., and Azzi, V. D., 1966, "Strength of Laminated Composite Materials," AIAA J., 4(2), pp. 296-301.
125. Chiu, K. D., 1969, "Ultimate Strengths of Laminated Composites," J. Compos. Mater., 3(3), pp. 578-582.
126. Chou, S. C., Orringer, O., and Rainey, J. H., 1976, "Post-Failure Behavior of Laminates -I. No Stress Concentrations," J. Compos. Mater., 10(4), pp. 371-381.
127. Eckold, G. C., Leadbetter, D., Soden, P. D., and Griggs, P. R., 1978, "Lamination Theory in Prediction of Failure Envelopes for Filament Wound Materials Subjected to Biaxial Loading," Composites, 9(4), pp. 243-246.
128. Kaddour, A. S., Soden, P. D., and Hinton, M. J., 1998, "Failure of ±55 Degree Filament Wound Glass/Epoxy Composite Tubes Under Biaxial Compression," J. Compos. Mater., 32(18), pp. 1618-1645.
129. Hinton, M. J., Soden, P. D., and Kaddour, A. S., 1996, "Strength of Composite Laminates Under Biaxial Loads," Appl. Compos. Mater., 3(3), pp. 151-162.
130. Schneider, W., and Bardenheier, R., 1975, "Versagenskriterien fur Kunstsoffe, Teil II: Experimentelle Ergebnisse," J. Mater. Technol., 6, pp. 339-348.
131. Huang, Z. M., 2004, "A Bridging Model Prediction of the Ultimate Strength of Composite Laminates Subjected to Biaxial Loads," Compos. Sci. Technol., 64(3-4), pp. 395-448.
132. Huang, Z. M., 2004, "Correlation of the Bridging Model Predictions of the Biaxial Failure Strengths of Fibrous Laminates With Experiments," Compos. Sci. Technol., 64(3-4), pp. 529-548.
133. Huang, Z. M., 2000, "A Unified Micromechanical Model for the Mechanical Properties of Two Constituent Composite Materials. Part V: Laminate Strength," J. Thermoplast. Compos., 13(3), pp. 190-206.
134. Huang, Z. M., 2004, "Ultimate Strength of a Composite Cylinder Subjected to Three-Point Bending: Correlation of Beam Theory With Experiment," Compos. Struct., 63(3-4), pp. 439-445.
135. Huang, Z. M., 2004, "Flexural Strength of a Composite Cylinder Incorporated With Thermal Residual Stresses," Mater. Sci. Eng., A, 366(2), pp. 367-380.
136. Hinton, M. J., 1998, "Predicting Failure in Composite Laminates: The Background to the Exercise," Compos. Sci. Technol., 58(7), pp. 1001-1010.
137. Soden, P. D., Hinton, M. J., and Kaddour, A. S., 1998, "Lamina Properties, Lay-Up Configurations and Loading Conditions for a Range of Fibre-Reinforced Composite Laminates," Compos. Sci. Technol., 58(7), pp. 1011-1022.
138. Hinton, M. J., Kaddour, A. S., and Soden, P. D., 2002, "Evaluation of Failure Prediction in Composite Laminates: Background to 'Part B' of the Exercise," Compos. Sci. Technol., 62(12-13), pp. 1481-1488.
139. Soden, P. D., Hinton, M. J., and Kaddour, A. S., 2002, "Biaxial Test Results for Strength and Deformation for a Range of E-Glass and Fibre Reinforced Composite Laminates: Failure Exercise Benchmark Data," Compos. Sci. Technol., 62(12-13), pp. 1489-1514.
140. Hinton, M. J., Kaddour, A. S., and Soden, P. D., 2004, "Evaluation of Failure Prediction in Composite Laminates: Background to 'Part C' of the Exercise," Compos. Sci. Technol., 64(3-4), pp. 321-327.
141. Soden, P. D., Kaddour, A. S., and Hinton, M. J., 2004, "Recommendations for Designers and Researchers Resulting From the World-Wide Failure Exercise," Compos. Sci. Technol., 64(3-4), pp. 589-604.
142. Harik, V. M., 2001, "Optimization of Structural Designs for a Safe Failure Pattern: Layered Material Systems," Mater. Des., 22(4), pp. 317-324.
143. Bogetti, T. A., Hoppel, C. P. R., Harik, V. M., Newill, J. F., and Burns, B. P., 2004, "Predicting the Nonlinear Response and Progressive Failure of Composite Laminates," Compos. Sci. Technol., 64(3-4), pp. 329-342.
144. Bogetti, T. A., Christopher, P. R. H., Harik, V. M., Newill, J. F., and Burns, P. B., 2004, "Predicting the Nonlinear Response and Failure of Composite Laminates: Correlation With Experimental Evidence," Compos. Sci. Technol., 64(3-4), pp. 477-485.
145. Liu, K., and Tsai, S. W., 1998, "A Progressive Quadratic Failure Criterion for a Laminate," Compos. Sci. Technol., 58(7), pp. 1023-1032.
146. Kuraishi, A., Tsai, S. W., and Liu, K. S., 2002, "A Progressive Quadratic Failure Criterion, Part B," Compos. Sci. Technol., 62(12-13), pp. 1683-1695.
147. Wolfe, W. E., and Butalia, T. S., 1998, "A Strain-Energy Based Failure Criterion for Non-Linear Analysis of Composite Laminates Subjected to Biaxial Loading," Compos. Sci. Technol., 58(7), pp. 1107-1124.
148. Liu, X., and Mahadevan, S., 2000, "Ultimate Strength Failure Probability Estimation of Composite Structures," J. Reinf. Plast. Compos., 19(5), pp. 403-426.
149. Mahadevan, S., and Liu, X., 2002, "Probabilistic Analysis of Composite Structure Ultimate Strength," AIAA J., 40(7), pp. 1408-1414.
150. Sluimer, G. M., 1998, "Ultimate Performance of GRP-Laminates Under In-Plane Biaxial Loading," Heron, 43(4), pp. 199-225.
151. Puck, A., 1965, "Zum Deformationsverhalten und Bruchmechanismus von Glasfaser/Kunstoff," Kunststoffe, 55, p. 913.
152. Tan, S. C., 1991, "A Progressive Failure Model for Composite Laminates Containing Openings," J. Compos. Mater., 25(5), pp. 556-577.
153. Tan, S. C., and Perez, J., 1993, "Progressive Failure of Laminated Composites With a Hole Under Compressive Loading," J. Reinf. Plast. Compos., 12(10), pp. 1043-1057.
154. Kwon, Y. W., and Berner, J. M., 1995, "Micromechanics Model for Damage and Failure Analysis of Laminated Fibrous Composites," Eng. Fract. Mech., 52(2), pp. 231-242.
155. Davila, C. G., Ambur, D. R., and McGowan, D. M., 2000, "Analytical Prediction of Damage Growth in Notched Composite Panels Loaded in Compression," J. Aircr., 37(5), pp. 898-905.
156. Ambur, D. R., Jaunky, N., and Hilburger, M. W., 2004, "Progressive Failure Studies of Stiffened Panels Subjected to Shear Loading," Compos. Struct., 65(2), pp. 129-142.
157. Ambur, D. R., Jaunky, N., Hillburger, M. W., and Davila, C. G., 2004, "Progressive Failure Analyses of Compression-Loaded Composite Curved Panels With and Without Cutouts," Compos. Struct., 65(2), pp. 143-155.
158. Xiao, Y., and Ishikawa, T., 2002, "Bearing Failure in Bolted Composite Joints: Analytical Tools Development," Adv. Compos. Mater., 11(4), pp. 375-391.
159. Xiao, Y., and Ishikawa, T., 2005, "Bearing Strength and Failure Behavior of Bolted Composite Joints, Part II: Modeling and Simulation," Compos. Sci. Technol., 65(7-8), pp. 1032-1043.
160. Kim, S. J., Hwang, J. S., and Kim, J. H., 1998, "Progressive Failure Analysis of Pin-Loaded Laminated Composites Using Penalty Finite Element Method," AIAA J., 36(1), pp. 75-80.
161. Feih, S., and Shercliff, H. R., 2005, "Composite Failure Prediction of Single-L Joint Under Bending," Composites, Part A, 36(3), pp. 381-395.
162. Feih, S., and Shercliff, H. R., 2005, "Quality Assessment of Curved Composite Components in Peel Joint Structures," Composites, Part A, 36(3), pp. 397-408.
163. Chang, F. K., Lessard, L. B., and Tang, J. M., 1988, "Compression Response of Laminated Composites Containing an Open Hole," SAMPE Q., 19(4), pp. 46-51.
164. Chang, F. K., and Lessard, L. B., 1991, "Damage Tolerance of Laminated Composites Containing an Open Hole and Subjected to Compressive Loadings: Part I - Analysis," J. Compos. Mater., 25(1), pp. 2-43.
165. Xie, D., and Biggers, S. B., Jr., 2003, "Postbuckling Analysis With Progressive Damage Modeling in Tailored Laminated Plates and Shells With a Cutout," Compos. Struct., 59(2), pp. 199-216.
166. Lessard, L. B., and Shokrieh, M. M., 1995, "Two-Dimensional Modeling of Composite Pinned-Joint Failure," J. Compos. Mater., 29(5), pp. 671-697.
167. Zarco-Gonzalez, J. C., Fellows, N. A., and Durodola, J. F., 2004, "A Step-Size Independent Method for Finite Element Modeling of Damage in Composites," Compos. Sci. Technol., 64(10-11), pp. 1679-1689.
168. Okutan, B., 2002, "The Effects of Geometric Parameters on the Failure Strength for Pin-Loaded Multi-Directional Fiber-Glass Reinforced Epoxy Laminate," Composites, Part B, 33(8), pp. 567-578.
169. Okutan, B., and Karakuzu, R., 2002, "The Failure Strength for Pin-Loaded Multi-Directional Fiber-Glass Reinforced Epoxy Laminate," J. Compos. Mater., 36(24), pp. 2695-2712.
170. Okutan, B., and Karakuzu, R., 2003, "The Strength of Pinned Joints in Laminated Composites," Compos. Sci. Technol., 63(6), pp. 893-905.
171. Kang, T. J., and Lee, K. W., 1997, "Strength Prediction for Mechanical Joints in Laminated Composite Plate Using Progressive Failure Analysis," Polym. Polym. Compos., 5(5), pp. 343-351.
172. Lee, K. W., and Kang, T. J., 2000, "Strength Prediction of Mechanical Joints in Laminated Composite Plates," Key Eng. Mater., 183-187, pp. 1165-1170.
173. Dano, M. L., Gendron, G., and Picard, A., 2000, "Stress and Failure Analysis of Mechanically Fastened Joints in Composite Laminates," Compos. Struct., 50(3), pp. 287-296.
174. Padhi, G. S., Shenoi, R. A., Moy, S. S. J., and Hawkins, G. L., 1998, "Progressive Failure and Ultimate Collapse of Laminated Composite Plates in Bending," Compos. Struct., 40(3/4), pp. 277-291.
175. Kress, G., Siau, M., and Ermanni, P., 2005, "Iterative Solution Methods for Damage Progression Analysis," Compos. Struct., 69(1), pp. 21-33.
176. Tolson, S., and Zabaras, N., 1991, "Finite Element Analysis of Progressive Failure in Laminated Composite Plates," Comput. Struct., 38(3), pp. 361-376.
177. Spottswood, S. M., and Palazotto, A. N., 2001, "Progressive Failure Analysis of a Composite Shell," Compos. Struct., 53(1), pp. 117-131.
178. Ochoa, O. O., and Engblom, J. J., 1987, "Analysis of Progressive Failure in Composites," Compos. Sci. Technol., 28(2), pp. 87-102.
179. Engblom, J. J., and Ochoa, O. O., 1986, "Finite Element Formulation Including Interlaminar Stress Calculations," Comput. Struct., 23(2), pp. 241-249.
180. Greszczuk, L. B., 1975, "Microbuckling Failure of Circular Fiber-Reinforced Composites," AIAA J., 13(10), pp. 1311-1318.
181. Singh, S. B., Kumar, A., and Iyengar, N. G. R., 1997, "Progressive Failure of Symmetrically Laminated Plates Under Uni-Axial Compression," Struct. Eng. Mech., 5(4), pp. 433-450.
182. Singh, S. B., Kumar, A., and Iyengar, N. G. R., 1998, "Progressive Failure of Symmetric Laminates Under In-Plane Shear: I-Positive Shear," Struct. Eng. Mech., 6(2), pp. 143-159.
183. Singh, S. B., Kumar, A., and Iyengar, N. G. R., 1998, "Progressive Failure of Symmetric Laminates Under In-Plane Shear: II-Negative Shear," Struct. Eng. Mech., 6(7), pp. 757-772.
184. Sleight, D. W., 1999, "Progressive Failure Analysis Methodology for Laminated Composite Structures," NASA/TP Report No. 1999-209107.
185. Sleight, D. W., Knight, N. F., Jr., and Wang, J. T., 1997, "Evaluation of a Progressive Damage Methodology for Laminated Composite Structures," Proceedings of the 38th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference, Kissimmee, FL, Apr. 7-10, pp. 2257-2272.
186. Sleight, D. W., and Lotts, C. G., 2002, "Application of Interface Technology in Progressive Failure Analysis of Composite Panels," Proceedings of the 43rd AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference, Denver, CO, Apr. 22-25, pp. 1915-1924.
187. Wang, J. T., Lotts, C. G., and Sleight, D. W., 1999, "Analysis of Discrete-Source Damage Progression in a Tensile Stiffened Composite Panel," Proceedings of the 40th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference, St. Louis, MO, Apr. 12-15, pp. 1174-1187.
188. Hyer, M. W., and Wolford, G. F., 2002, "Microcrack Progression in Internally Pressurized Elliptical Cylinders," Proceedings of the 17th Annual Technical Conference of the American Society for Composites, Boca Raton, FL.
189. Hyer, M. W., and Wolford, G. F., 2002, "Progressive Failure Analysis of Internally Pressurized Noncircular Composite Cylinders," Proceedings of the 43rd AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics and Materials Conference, Denver, CO, Apr. 22-25, pp. 1522-1532.
190. Knight, N. F., Jr., Rankin, C. C., and Brogan, F. A., 2002, "STAGS Computational Procedure for Progressive Failure Analysis of Laminated Composite Structures," Int. J. Non-Linear Mech., 37(4-5), pp. 833-849.
191. Mahadevan, S., Liu, X., and Xiao, Q., 1997, "A Probabilistic Progressive Failure Model of Composite Laminates," J. Reinf. Plast. Compos., 16(11), pp. 1020-1038.
192. Liu, X., and Mahadevan, S., 1997, "System Reliability of Composite Laminates," Proceedings of the 38th AIAA/ASME/ASCE/AHS Structures, Structural Dynamics, and Materials Conference, Kissimmee, FL, Apr. 7-10, pp. 2877-2884.
193. Chen, J., Wang, X., and Luo, C., 2002, "Reliability Analysis of FRP Laminates Plates With Consideration of Both Initial Imperfection and Failure Sequence," Acta. Mech. Solida. Sin., 15(3), pp. 227-235.
194. Mazzeranghi, A., and Vanghi, D., 1994, "A Post-Failure Model for Composite Laminates Based on Phenomenologic Aspects of Damage," Compos. Struct., 28, pp. 323-332.
195. Reddy, Y. S. N., Moorthy, C. M. D., and Reddy, J. N., 1995, "Non-Linear Progressive Failure Analysis of Laminated Composite Plates," Int. J. Non-Linear Mech., 30(5), pp. 629-649.
196. Chang, F. K., and Kutlu, Z., 1989, "Strength and Response of Cylindrical Composite Shells Subjected to Out-of-Plane Loadings," J. Compos. Mater., 23(1), pp. 11-31.
197. Chang, F. K., and Kutlu, Z., 1990, "Study on the Crushing Response of Cylindrical Composite Shells Subjected to Transverse Loading," J. Compos. Technol. Res., 12(4), pp. 239-244.
198. Tsai, S. W., and Hahn, H. T., 1980, Introduction to Composite Materials, Technomic, Westport, CT.
199. Chang, F. K., and Chang, K. Y., 1987, "Post-Failure Analysis of Bolted Composite Joints in Tension or Shear-Out Mode Failure," J. Compos. Mater., 21(9), pp. 809-833.
200. Joo, S. G., Hong, C. S., and Kim, C. G., 2001, "Free Edge Effect on the Post Failure Behavior of Composite Laminates Under Tensile Loading," J. Reinf. Plast. Compos., 20(3), pp. 191-221.
201. Joo, S. G., and Hong, C. S., 2000, "Progressive Failure Analysis of Composite Laminates Using 3-D Finite Element Method," Key Eng. Mater., 183-187, pp. 535-540.
202. Sun, H. T., Chang, F. K., and Qing, X., 2002, "The Response of Composite Joints With Bolt-Clamping Loads, Part I: Model Development," J. Compos. Mater., 36(1), pp. 47-67.
203. Sun, H. T., Chang, F. K., and Qing, X., 2002, "The Response of Composite Joints With Bolt-Clamping Loads, Part II: Model Verification," J. Compos. Mater., 36(1), pp. 69-92.
204. Qing, X., Sun, H. T., Dagba, L., and Chang, F. K., 2000, "Damage-Tolerance-Based Design of Bolted Composite Joints," Composite Structures: Theory and Practice, P. Grant and C. Q. Rousseau, eds., American Society for Testing and Materials, West Conshocken, PA, pp. 243-272.
205. Shahid, I., and Chang, F. K., 1995, "An Accumulative Damage Model for Tensile and Shear Failures of Laminated Composite Plates," J. Compos. Mater., 29(7), pp. 926-981.
206. Qing, X., Chang, F. K., and Starnes, J., 2003, "Damage Tolerance of Notched Composite Laminates With Reinforcing Strips," J. Compos. Mater., 37(2), pp. 111-128.
207. Idelsohn, S., Laschet, G., and Nyssen, C., 1982, "Pre- and Post- Degradation Analysis of Composite MaterialsWith Different Moduli in Tension and Compression," Comput. Methods Appl. Mech. Eng., 30(2), pp. 133-149.
208. Sandhu, R. S., Gallo, R. L., and Sendeckyj, G. P., 1982, "Initiation and Accumulation of Damage in Composite Laminates," Composite Materials: Testing and Design, I. M. Daniel, ed., American Society for Testing and Materials, Philadelphia, ASTM STP 787, pp. 163-182.
209. Lin, W. P., and Hu, H. T., 2002, "Nonlinear Analysis of Fiber-Reinforced Composite Laminates Subjected to Uniaxial Tensile Load," J. Compos. Mater., 36(12), pp. 1429-1450.
210. Lin, W. P., and Hu, H. T., 2002, "Parametric Study on the Failure of Fiber-Reinforced Composite Laminates Under Biaxial Tensile Load," J. Compos. Mater., 36(12), pp. 1481-1503.
211. Moas, E., and Griffin, O. H., Jr., 1997, "Progressive Failure Analysis of Laminated Composites Structures," Proceedings of the 38th AIAA/ASME/ASCE/AHS/ASC Structures, Structural Dynamics, and Materials Conference, Kissimmee, FL, Apr. 7-10, pp. 2246-2256.
212. Petit, P. H., and Waddoups, M. E., 1969, "A Method of Predicting the Nonlinear Behavior of Laminated Composites," J. Compos. Mater., 3(1), pp. 2-19.
213. Grimes, G. C., and Whitney, J. M., 1974, "Degradation of Graphite/Epoxy Composite Materials Because of Load Induced Micromechanical Damage," SAMPE Q., 5(4), pp. 1-13.
214. Craddock, J. N., 1985, "Behavior of Composite Laminates After First-Ply-Failure," Compos. Struct., 3(2), pp. 187-200.
215. Nahas, M. N., 1986, "Yield and Ultimate Strengths of Fibre Composite Laminates," Compos. Struct., 6(4), pp. 283-294.
216. Hahn, H. T., Kiusalaas, J., Burns, B. P., and Bogetti, T. A., 1992, "Constitutive Modeling of Composite Laminates With Progressive Ply Cracking," Proceedings of ASME International Computers in Engineering Conference and Exposition, San Francisco, CA, Aug. 2-6, pp. 185-193.
217. Lee, J. W., and Daniel, I. M., 1990, "Progressive Transverse Cracking of Crossply Composite Laminates," J. Compos. Mater., 24(11), pp. 1225-1243.
218. Zinoviev, P. A., Grigoriev, S. V., Lebedeva, O. V., and Tairova, L. P., 1998, "The Strength of Multilayered Composites Under a Plane-Stress State," Compos. Sci. Technol., 58(7), pp. 1209-1223.
219. Zinoviev, P. A., Lebedeva, O. V., and Tairova, L. P., 2002, "A Coupled Analysis of Experimental and Theoretical Results on the Deformation and Failure of Laminated Composites Under a State of Plane Stress," Compos. Sci. Technol., 62(12-13), pp. 1711-1723.
220. Kim, Y. W., and Hong, C. S., 1992, "Progressive Failure Model for the Analysis of Laminated Composites Based on Finite Element Approach," J. Reinf. Plast. Compos., 11(10), pp. 1078-1092.
221. Lim, S. G., and Hong, C. S., 1989, "Prediction of Transverse Cracking and Stiffness Reduction in Cross-Ply Laminated Composites," J. Compos. Mater., 23(7), pp. 695-713.
222. Chang, K. Y., Liu, S., and Chang, F. K., 1991, "Damage Tolerance of Laminated Composites Containing an Open Hole and Subjected to Tensile Loadings," J. Compos. Mater., 25(3), pp. 274-301.
223. Shahid, I., and Chang, F. K., 1992, "Modeling of Failure and Response to Laminated Composites Subjected to In-plane Loads," Workshop on Computational Methods for Failure Analysis and Life Prediction, Hampton, VA, Oct. 14-15, pp. 83-120.
224. Shahid, I., Sun, H. T., and Chang, F. K., 1995, "Predicting Scaling Effect on the Notched Strength of Prepreg and Fiber Tow-Placed Laminated Composites," J. Compos. Mater., 29(8), pp. 1063-1095.
225. Hung, C. L., and Chang, F. K., 1996, "Bearing Failure of Bolted Composite Joints. Part II: Model and Verification," J. Compos. Mater., 30(12), pp. 1359-1400.
226. Hung, C. L., and Chang, F. K., 1996, "Strength Envelope of Bolted Composite Joints Under Bypass Loads," J. Compos. Mater., 30(13), pp. 1402-1435.
227. Kwon, Y. W., and Berner, J. M., 1997, "Matrix Damage of Fibrous Composites: Effects of Thermal Residual Stresses and Layer Sequences," Comput. Struct., 64(1-4), pp. 375-382.
228. Kwon, Y. W., and Berner, J. M., 1994, "Analysis of Matrix Damage Evolution in Laminated Composite Plates," Eng. Fract. Mech., 48(6), pp. 811-817.
229. Swanson, S. R., and Christoforou, A. P., 1986, "Response of Quasi-Isotropic Carbon/Epoxy Laminates to Biaxial Stress," J. Compos. Mater., 20(5), pp. 457-471.
230. Swanson, S. R., and Christoforou, A. P., 1987, "Progressive Failure in Carbon/Epoxy Laminates Under Biaxial Stress," ASME J. Eng. Mater. Technol., 109(1), pp. 12-16.
231. Hwang, T. K., Hong, C. S., and Kim, C. G., 2003, "Probabilistic Deformation and Strength Prediction for a Filament Wound Pressure Vessel," Composites, Part B, 34(5), pp. 481-497.
232. Edge, E. C., 1998, "Stress-Based Grant-Sanders Method for Predicting Failure of Composite Laminates," Compos. Sci. Technol., 58(7), pp. 1033-1041.
233. Edge, E. C., 2002, "A Comparison of Theory and Experiment for Stress-Based Grant-Sanders Method," Compos. Sci. Technol., 62(12-13), pp. 1571-1589.
234. Rotem, A., 1998, "Prediction of Laminate Failure With Rotem Failure Criterion," Compos. Sci. Technol., 58(7), pp. 1083-1094.
235. Rotem, A., 2002, "The Rotem Failure Criterion: Theory and Practice," Compos. Sci. Technol., 62(12-13), pp. 1663-1671.
236. Sun, C. T., and Tao, J., 1998, "Prediction of Failure Envelopes and Stress/Strain Behavior of Composite Laminates," Compos. Sci. Technol., 58(7), pp. 1125-1136.
237. Sun, C. T., Tao, J., and Kaddour, A. S., 2002, "Prediction of Failure Envelopes and Stress-Strain Behavior of Composite Laminates: Comparison With Experimental Results," Compos. Sci. Technol., 62(12-13), pp. 1673-1682.
238. Tao, X. J., and Sun, C. T., 1996, "Effect of Matrix Cracking on Stiffness of Composite Laminates," Mech. Compos. Mater. Struct., 3(3), pp. 225-239.
239. Puck, A., and Schürmann, H., 1998, "Failure Analysis of FRP Laminates by Means of Physically Based Phenomenological Models," Compos. Sci. Technol., 58(7), pp. 1045-1067.
240. Puck, A., and Schürmann, H., 2002, "Failure Analysis of FRP Laminates by Means of Physically Based Phenomenological Models-Part B," Compos. Sci. Technol., 62(12-13), pp. 1633-1662.
241. Cuntze, R. G., and Freund, A., 2004, "The Predictive Capability of Failure Mode Concept-Based Strength Criteria for Multidirectional Laminates," Compos. Sci. Technol., 64(3-4), pp. 343-377.
242. Cuntze, R. G., 2004, "The Predictive Capability of Failure Mode Conceptbased Strength Criteria for Multi-Directional Laminates: Part B," Compos. Sci. Technol., 64(3-4), pp. 487-516.
243. Knops, M., and Bogle, C., 2006, "Gradual Failure in Fibre/Polymer Laminates," Compos. Sci. Technol., 66(5), pp. 616-625.
244. Puck, A., 1969, "Festigkeitsberechnung and Glasfaser/Kunststoff-Laminaten bei Zusannengesetzter Beanspruchung: Bruchhypothesen und Schichtweise Bruchanalyse," Kunststoffe, 55, pp. 18-19.
245. Hult, J., 1987, "Introduction and General Overview," Continuum Damage Mechanics: Theory and Applications, D. Krajcinovic and J. Lemaitre, eds., Springer-Verlag, New York, pp. 1-36.
246. Lemaitre, J., 1996, A Course on Damage Mechanics, 2nd ed., Springer-Verlag, Germany.
247. Voyiadjis, G. Z., and Kattan, P. I., 2005, Damage Mechanics, Taylor & Francis, New York.
248. Murakami, S., and Kamiya, K., 1997, "Constitutive and Damage Evolution Equations of Elastic-Brittle Materials Based on Irreversible Thermodynamics," Int. J. Mech. Sci., 39(4), pp. 473-486.
249. Germain, P., Nguyen, Q. S., and Suquet, P., 1983, "Continuum Thermodynamics," ASME J. Appl. Mech., 50, pp. 1010-1020.
250. Lemaitre, J., and Chaboche, J. L., 1990, Mechanics of Solid Materials, Cambridge University Press, Cambridge.
251. Lawrence, M. E., 1969, Introduction to the Mechanics of a Continuous Medium, Prentice-Hall, Englewood Cliffs, NJ.
252. Renard, J., Favre, J. P., and Jeggy, Th., 1993, "Influence of Transverse Cracking on Ply Behavior: Introduction of a Characteristic Damage Variable," Compos. Sci. Technol., 46(1), pp. 29-37.
253. Thionnet, A., Lesne, P.-M., and Renard, J., 1991, "Using Characteristic Damage Variables to Simulate Degradations and Their Evolutions in Composite Materials-Comparison Between Experimental and Numerical Simulations," 14th Annual Energy-Sources Technology Conference and Exhibition, Houston, TX, Jan. 20-23, pp. 105-111.
254. Renard, J., and Thionnet, A., 1992, "Meso-Macro Approach to Predict the Damage Evolution of Transverse Cracking in Laminated Composite," Winter Annual Meeting of the American Society of Mechanical Engineers, Anaheim, CA, Nov. 8-13, pp. 31-39.
255. Renard, J., and Thionnet, A., 2006, "Damage in Composites: From Physical Mechanisms to Modelling," Compos. Sci. Technol., 66(5), pp. 642-646.
256. Thionnet, A., and Renard, J., 1993, "Meso-Macro Approach to Transverse Cracking in Laminated Composites Using Talreja's Model," Composites Eng., 3(9), pp. 851-871.
257. Nguyen, B. N., 1997, "Three-Dimensional Modeling of Damage in Laminated Composites Containing a Central Hole," J. Compos. Mater., 31(17), pp. 1672-1693.
258. Nguyen, B. N., 1997, "A Three-Dimensional Modeling of Transverse Matrix Cracking in Laminated Composites," Key Eng. Mater., 127-131(2), pp. 1117-1126.
259. Nguyen, B. N., 1998, "Damage Modeling of Laminated Composites by the Use of Multilayer Volume Elements," Compos. Sci. Technol., 58(6), pp. 891-905.
260. Laws, N., Dvorak, G. J., and Hejazi, M., 1983, "Stiffness Changes in Unidirectional Composites Caused by Crack Systems," Mech. Mater., 2(2), pp. 123-137.
261. Dvorak, G. J., Laws, N., and Hejazi, M., 1985, "Analysis of Progressive Matrix Cracking in Composite Laminates I. Thermoelastic Properties of a Ply With Cracks," J. Compos. Mater., 19(3), pp. 216-234.
262. Phillips, E. A., Herakovich, C. T., and Graham, L. L., 2001, "Damage Development in Composites With Large Stress Gradients," Compos. Sci. Technol., 61(15), pp. 2169-2182.
263. Allix, O., Ladaveze, P., Gilletta, D., and Ohayon, R., 1989, "A Damage Prediction Method for Composite Structures," Int. J. Numer. Methods Eng., 27(2), pp. 271-283.
264. Herakovich, C. T., 1998, Mechanics of Fibrous Composites, Wiley, New York.
265. Flesher, N. D., and Herakovich, C. T., 2006, "Predicting Delamination in Composite Structures," Compos. Sci. Technol., 66(6), pp. 745-754.
266. Coats, T. W., and Harris, C. E., 1999, "A Progressive Damage Methodology for Residual Strength Predictions of Notched Composite Panels," J. Compos. Mater., 33(23), pp. 2193-2224.
267. Coats, T. W., and Harris, C. E., 1998, "A Damage-Dependent Finite Element Analysis for Fiber-Reinforced Composite Laminates," 1998 International Conference on Computational Engineering Sciences, Atlanta, GA, Oct. 6-9.
268. Allen, D. H., Harris, C. E., and Groves, S. E., 1987, "A Thermomechanical Constitutive Theory for Elastic Composites With Distributed Damage-I. Theoretical Development," Int. J. Solids Struct., 23(9), pp. 1301-1318.
269. Allen, D. H., Harris, C. E., and Groves, S. E., 1987, "Thermo-Mechanical Constitutive Theory for Elastic Composites With Distributed Damage-II. Application to Matrix Cracking in Laminated Composites," Int. J. Solids Struct., 23(9), pp. 1319-1338.
270. Allen, D. H., Harris, C. E., and Groves, S. E., 1987, "Damage Modelling in Laminated Composites," Proceedings of IUTAM/ICM Symposium on Yielding, Damage, and Failure of Anisotropic Solids, Villard-de-Lans, France, Aug. 24-28, p. 535.
271. Tay, T. E., Lam, K. Y., and Cen, Z., 1997, "Analysis of Composite Structures With Distributed and Localized Damage by the Finite-Element Method," Compos. Struct., 37(2), pp. 135-143.
272. Tay, T. E., and Lim, E. H., 1996, "Analysis of Composite Laminates With Transverse Cracks," Compos. Struct., 34(4), pp. 419-426.
273. Tay, T. E., Lim, E. H., and Tay, A. A. O., 1994, "Analysis of Stresses in Cross-Ply Laminates Containing Distributed Transverse Cracks," Finite Elem. Anal. Des., 18(1-3), pp. 301-308.
274. Lim, E. H., and Tay, T. E., 1996, "Stiffness Loss of Composite Laminates With Transverse Cracks Under Mode I and Mode III Loading," Int. J. Damage Mech., 5(2), pp. 190-215.
275. Tay, T. E., and Lim, E. H., 1993, "Analysis of Stiffness Loss in Cross-Ply Composite Laminates," Compos. Struct., 25(1-4), pp. 419-423.
276. Kennedy, T. C., and Nahan, M. F., 1996, "A Simple Nonlocal Damage Model for Predicting Failure of Notched Laminates," Compos. Struct., 35(2), pp. 229-236.
277. Kennedy, T. C., and Nahan, M. F., 1997, "A Simple Nonlocal Damage Model for Predicting Failure in a Composite Shell Containing a Crack," Compos. Struct., 39(1-2), pp. 85-91.
278. Nahan, M. F., and Kennedy, T. C., 2000, "A Nonlocal Damage Theory for Laminated Plate With Application to Aircraft Damage Tolerance," J. Reinf. Plast. Compos., 19(5), pp. 354-363.
279. Engblom, J. J., Yang, Q., Abdul-samad, N., and Havelka, J., 1993, "Residual Property Predictions for Laminated Composite Structures: FE Based Internal State Variable Approach," Proceedings of the 33rd Structures, Dynamics and Materials Conference, Dallas, TX, Apr. l 13-15, pp. 21-28.
280. Yang, Q., and Engblom, J. J., 1995, "Finite Element Based Sub-Laminate Damage Model for Intraply Cracking," J. Reinf. Plast. Compos., 14(3), pp. 233-254.
281. Engblom, J. J., 1987, "Modelling the Effects of Intraply Cracking in Composite Laminates at the Sublaminate Level," Proceedings of the ASME Pressure Vessels and Piping Conference, American Society of Mechanical Engineers, Pressure Vessels and Piping Division, New York, Vol. 121, pp. 105-110.
282. Talreja, R., 1985, "A Continuum Mechanics Characterization of Damage in Composite Materials," Proc. R. Soc. London, Ser. A, 399, pp. 195-216.
283. Talreja, R., 1985, "Transverse Cracking and Stiffness Reduction in Composite Laminates," J. Compos. Mater., 19(4), pp. 355-375.
284. Talreja, R., 1987, "Modeling of Damage Development in Composites Using Internal Variables Concepts," Winter Annual Meeting of the American Society of Mechanical Engineers, Boston, MA, Dec. 13-18, pp. 11-16.
285. Talreja, R., 1994, "Damage Characterization by Internal Variables," Damage Mechanics of Composite Materials (Composite Materials Series), R. Talreja, ed., Elsevier Science, Amsterdam, Vol. 9, pp. 53-78.
286. Talreja, R., 1987, "Internal Variable Damage Mechanics of Composite Materials," Proceedings of IUTAM/ICM Symposium on Yielding, Damage, and Failure of Anisotropic Solids, Villard-de-Lans, France, Aug. 24-28, pp. 509-533.
287. Talreja, R., Yalvac, S., Yats, L. D., and Wetters, D. G., 1992, "Transverse Cracking and Stiffness Reduction in Cross Ply Laminates of Different Matrix Toughness," J. Compos. Mater., 26(11), pp. 1644-1663.
288. Goyal, V. K., Jaunky, N. R., Johnson, E. R., and Ambur, D. R., 2004, "Intralaminar and Interlaminar Progressive Failure Analyses of Composite Panels With Circular Cutouts," Compos. Struct., 64(1), pp. 91-105.
289. Schipperen, J. H. A., 2001, "An Anisotropic Damage Model for the Description of Transverse Matrix Cracking in a Graphite-Epoxy Laminate," Compos. Struct., 53(3), pp. 295-299.
290. Isometsa, J., and Sjoling, S. G., 1999, "A Continuum Damage Mechanics Model for Fiber Reinforced Composites," Int. J. Damage Mech., 8(1), pp. 2-17.
291. Yang, F., and Chow, C. L., 1998, "Progressive Damage of Unidirectional Graphite/Epoxy Composites Containing a Circular Hole," J. Compos. Mater., 32(6), pp. 504-525.
292. Chow, C. L., and Yang, F., 1994, "Inelastic Finite Element Analysis of Fiber Reinforced Laminates Damage" , International Mechanical Engineering Congress and Exposition, Chicago IL, Nov. 6-11, pp. 111-135.
293. Chow, C. L., and Yang, F., 1992, "A Simple Model for Brittle Composite Lamina With Damage," J. Reinf. Plast. Compos., 11(3), pp. 222-242.
294. Chow, C. L., and Yang, F., 1991, "On One-Parameter Description of Damage State for Brittle Material," Eng. Fract. Mech., 40(2), pp. 335-343.
295. Chow, C. L., and Yang, F., 1997, "Three-Dimensional Inelastic Stress Analysis of Center Notched Composite Laminates With Damage," Int. J. Damage Mech., 6(1), pp. 23-50.
296. Chow, C. L., Yang, F., and Asundi, A., 1993, "A Three-Dimensional Analysis of Symmetric Composite Laminates With Damage," Int. J. Damage Mech., 2(3), pp. 229-245.
297. Chow, C. L., Yang, F., and Asundi, A., 1992, "A Method for Nonlinear Damage Analysis for Anisotropic Materials and Its Application to Thin Composite Materials," Int. J. Damage Mech., 1(3), pp. 347-366.
298. Chatterjee, S. N., 2000, "Damage, Stiffness Loss, and Failure in Composite Structures," Composite Structures: Theory and Practice, P. Grant and C. Q. Rousseau, eds., American Society for Testing and Materials, West Conshohocken, PA, ASTM STP 1383, pp. 452-469.
299. Turon, A., Costa, J., Maimi, P., Trias, D., and Mayugo, J. A., 2005, "A Progressive Damage Model for Unidirectional Fibre-Reinforced Composites Based on Fibre Fragmentation. Part I: Formulation," Compos. Sci. Technol., 65(13), pp. 2039-2048.
300. Barbero, E. J., and Lonetti, P., 2001, "Damage Model for Composites Defined in Terms of Available Data," Mech. Compos. Mater. Struct., 8(4), pp. 299-315.
301. Barbero, E. J., and Lonetti, P., 2002, "An Inelastic Damage Model for Fiber Reinforced Laminates," J. Compos. Mater., 36(8), pp. 941-962.
302. Barbero, E. J., and Vivo, L. D., 2001, "A Constitutive Model for Elastic Damage in Fiber-Reinforced PMC Laminae," Int. J. Damage Mech., 10(1), pp. 73-93.
303. Barbero, E. J., Abdelal, G. F., and Caceres, A., 2005, "A Micromechanics Approach for Damage Modeling of Polymer Matrix Composites," Compos. Struct., 67(4), pp. 427-436.
304. Ladeveze, P., and La Dantec, E., 1992, "Damage Modelling of the Elementary Ply for Laminated Composites," Compos. Sci. Technol., 43(3), pp. 257-267.
305. Ladeveze, P., 1992, "A Damage Computational Method for Composite Structures," Comput. Struct., 44(1-2), pp. 79-87.
306. Allix, O., Bahlouli, N., Cluzel, C., and Perret, L., 1996, "Modelling and Identification of Temperature Dependent Mechanical Behavior of the Elementary Ply in Carbon/Epoxy Laminates," Compos. Sci. Technol., 56(7), pp. 883-888.
307. Reid, S. R., and Soden, P. D., 1998, "A Continuum Damage Model for Transverse Matrix Cracking in Laminated Fibre-Reinforced Composites," Philos. Trans. R. Soc. London, Ser. A, 356, pp. 2379-2412.
308. Matzenmiller, A., Lubliner, J., and Taylor, R. L., 1995, "A Constitutive Model for Anisotropic Damage in Fiber-Composites," Mech. Mater., 20(2), pp. 125-152.
309. Hammer, V. B., 2000, "Optimization of Fibrous Laminates Undergoing Progressive Damage," Int. J. Numer. Methods Eng., 48(9), pp. 1265-1284.
310. Hammer, V. B., and Pedersen, P., 1999, "On an Orthotropic Model for Progressive Degradation," Compos. Struct., 46(3), pp. 217-228.