Gradual failure in fibre/polymer laminates

Composites Science and Technology

Volumn 66, Issue 5, 2006, Pages 616-625

  Knops, M ^a   Bogle C ^a  

^a RWTH AACHEN UNIVERSITY   (Germany)

Author keywords

Gradual failure; Inter fibre fracture; Non linear stress analysis

Indexed keywords

COMPUTER SIMULATION; FAILURE (MECHANICAL); FIBER REINFORCED PLASTICS; FRACTURE; MATHEMATICAL MODELS; STRESS ANALYSIS;

GRADUAL FAILURE; INTER FIBER FRACTURE; NONLINEAR STRESS ANALYSIS;

LAMINATED COMPOSITES;

DEFECT; FIBER REINFORCED COMPOSITE;

EID: 30344449184     PISSN: 02663538     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.compscitech.2005.07.044     Document Type: Article

References (44)

1. VDI 2014 Blatt 3. Entwicklung von Bauteilen aus Faser-Kunststof-Verbund (VDI Guideline 2014, part 3: Development of FRP components (fibre reinforced plastics) Analysis), Beuth-Verlag [in press].
2. J.A. Nairn S. Hu J.S. Bark A critical evaluation of theories for predicting microcracking in composite laminates J Mater Sci 28 1993 5099-5111
3. Nairn JA. Matrix microcracking in composites, polymer matrix composites. Comprehensive composite materials, vol. 2; 2000 [chapter 13].
4. R. Talreja Damage mechanics of composite materials 1994 Elsevier Verlag Amsterdam
5. P.D. Soden M.J. Hinton A.S. Kaddour Biaxial test results for strength and deformation of a range of E-glass and carbon fibre reinforced composite laminates: Failure exercise benchmark data Compos Sci Technol 62 2002 1489-1514
6. M.J. Hinton A.S. Kaddour P.D. Soden A comparison of the predictive capabilities of current failure theories for composite laminates, judged against experimental evidence Compos Sci Technol 62 2002 1725-1797
7. L.N. Mc Cartney Prediction transverse crack formation in cross-ply laminates Compos Sci Technol 58 1998 1069-1081
8. L.N. Mc Cartney Prediction of ply crack formation and failure in laminates Compos Sci Technol 62 2002 1619-1631
9. F.-K. Chang K.-Y. Chang A progressive damage model for laminated composites containing stress concentrations J Compos Mater 21 1987 834 ff
10. S. Li S.R. Reid P.D. Soden A finite strip analysis of cracked laminates Mech Mater 18 1994 289-311
11. S. Li S.R. Reid P.D. Soden A continuum damage model for transverse matrix cracking in laminated fibre-reinforced composites Phil Trans R Soc London A 356 1998 2379-2412
12. C.T. Sun J. Tao Prediction of failure envelopes and stress/strain behaviour of composite lamiantes Compos Sci Technol 58 1998 1125-1136
13. K.-S. Liu S.W. Tsai A progressive quadratic failure criterion for a laminate - Part A Compos Sci Technol 58 1998 1023-1032
14. P.K. Gotsis C.C. Chamis L. Minnetyan Prediction of composite laminate fracture: Micromechanics and progressive fracture Compos Sci Technol 58 1998 1137-1149
15. W.E. Wolf T.S. Butalia A strain-energy based failure criterion for non-linear analysis of composite laminates subjected to biaxial loading Compos Sci Technol 58 1998 1107-1124
16. M.N. Nahas Survey of failure and post-failure theories of laminated fiber-reinforced composites J Compos Technol Res 8 1986 138-153
17. A. Puck H. Schürmann Failure analysis of FRP laminates by means of physically based phenomenological models - Part A Compos Sci Technol 58 1998 1045-1067
18. A. Puck H. Schürmann Failure analysis of FRP laminates by means of physically based phenomenological models - Part B Compos Sci Technol 62 2002 1633-1662
19. Knops M. Sukzessives Bruchgeschehen in Faserverbundlaminaten (Gradual failure process in fibre/polymer laminates), technisch wissenschaftlicher Bericht, IKV Aachen, Band 140, Verlag Mainz, Aachen: 2003. ISBN 3-86130-480-5.
20. A. Thionnet J. Renard Meso-macro approach to transverse cracking in laminated composites using Talreja's model Compos Eng 3 1993 851-871
21. D.L. Flaggs M.H. Kural Experimental determination of the in situ transverse lamina strength in graphite epoxy laminates J Compos Mater 16 1982 103-116
22. K.W. Garrett J.E. Bailey Multiple transverse fracture in 90° cross ply laminates of a glass fibre-reinforced polyester J Mater Sci 12 1977 157-168
23. J.E. Bailey P.T. Curtis A. Parvizi On the transverse cracking and longitudinal splitting behaviour of glass and carbon fibre reinforced epoxy cross ply laminates and the effect of Poisson and thermally generated strain Proc R Soc Lond A 366 1979 599-623
24. J.A. Nairn S. Hu The formation and effect of outer-ply microcracks in cross-ply laminates: A variational approach Eng Fract Mech 41 1992 203-221
25. s laminates Appl Compos Mater 5 1998 11-23
26. A.L. Highsmith K.L. Reifsnider Stiffness-reduction mechanisms in composite laminates, Damage in composite materials ASTM-STP-775 Am Soc Testing Mater 1982 103-117
27. E.C. Edge Stress based grant-sanders method for predicting failure of composite laminates Compos Sci Technol 58 1998 1033-1044
28. S.E. Groves C.E. Harris A.L. Highsmith D.H. Allen R.G. Novell An experimental and analytical treatment of matrix cracking in cross-ply laminates Exp Mech 1987 73-79
29. s laminates: Experiments and predictions J Compos Technol Res 22 3 2000 153-160
30. L. Boniface P.A. Smith H.A. Rezaifard M.G. Bader Transversely ply cracking in composite laminates - initiation or propagation controlled? J Compos Mater 31 1997 1080-1112
31. M. Surgeon E. Vanswijgenhoven M. Wevers O. van der Biest Transverse cracking and Poison's ratio reduction in cross-ply carbon fibre-reinforced polymers J Mater Sci 21 1999 5513-5517
32. P.A. Smith J.R. Wood Poisson's ratio as a damage parameter in the static tensile loading of simple crossply laminates Compos Sci Technol 38 1990 85-93
33. C.L. Tsai I.M. Daniel The behavior of cracked cross-ply composite laminates under shear loading Int J Solids Struct 29 24 1992 3251-3267
34. HN.N.: URL: http://www.adhesives.vantico.com/frontPage.rhtm, 06.09.2004.
35. N.N. Betriebsanleitung für die SUTER Zug-Druck-Torsions-Prüfmaschine ZDT 18/5000, Suter + Co. Maschinenbau, Basel, 1995.
36. A. Puck Festigkeitsanalyse von Faser-Matrix-Laminaten - Modelle für die Praxis (Strength analysis of fibre-matrix laminates -models for practice) 1996 Carl Hanser Verlag München, Wien [in German]
37. J.M. Whitney Effective elastic constants of bidirectional laminates containing transverse ply cracks J Compos Mater 2000 955-978
38. Z. Hashin Analysis of cracked laminates: A variational approach Mech Mater 4 1985 S121-S136
39. Puck A. Festigkeitsberechnung an Glasfaser/Kunststoff-Laminaten bei zusammengesetzter Beanspruchung; Bruchhypothesen und schichtweise Bruchanalyse (Strength analysis on GRP-laminates under combined stresses; fracture hypotheses and layer-by-layer failure analysis), Kunststoffe, German Plastics 55 (bilinguar edition English + German), (1969), p. 18-9, German text 780-787.
40. Kopp J. Contribution to the stress and strength analysis of unidirectionally fibre reinforced plastics (German), Technical University of Aachen, Ph.D. thesis, 2000.
41. N.N. Roving for filament winding R099 1200 P139. Saint-Gobain Vetrotex Reinforcement GmbH, Herzogenrath. Available from: http://www.vetrotexeurope.com, 06.09.2004.
42. HN.N.: URL: http://www.sglcarbon.de/, 06.09.2004.
43. HN.N: URL: http://www.toray.com/, 06.09.2004.
44. N.N.: DELO-DUPOX 1785. Technical information of DELO Industrieklebstoffe HGmbH & Co. KG, Landsberg. Available from: URL: http://www.delo.de, 06.09.2004.