Bearing failure in bolted composite joints: Analytical tools development

Advanced Composite Materials: The Official Journal of the Japan Society of Composite Materials

Volumn 11, Issue 4, 2003, Pages 375-391

  Xiao, Yi ^a   Ishikawa, T ^a  

^a JAPAN AEROSPACE EXPLORATION AGENCY   (Japan)

Author keywords

Bearing failure; CFRP laminated composites; Continuum damage mechanics (CDM); Progressive damage

Indexed keywords

BEARING CAPACITY; COMPOSITE MATERIALS; CONTINUUM MECHANICS; DEFORMATION; ELASTICITY; FINITE ELEMENT METHOD; MATHEMATICAL MODELS;

CONTINUUM DAMAGE MECHANICS (CDM);

JOINTS (STRUCTURAL COMPONENTS);

EID: 0038475929     PISSN: 09243046     EISSN: None     Source Type: Journal    
DOI: 10.1163/156855102321669190     Document Type: Article

References (17)

1. J. L. Chaboche, Continuum damage mechanics: Part I - General concepts and Part II Damage growth, crack initiation and crack growth, J. Applied Mech. 55, 59-72 (1988).
2. F. K. Chang and K. Y. Chang, Post-failure analysis of bolted composite joints in tension or shear-out mode failure, J. Compos. Mater. 21, 809-833 (1987).
3. L. B. Lessard and M. M. Shokrieh, Two-dimensional modeling of comosite pinned-joint failure, J. Compos. Mater. 29, 671-697 (1995).
4. C. L. Hung and F. K. Chang, Bearing failure of bolted composite joints. Part II: model and verification, J. Compos. Mater. 30, 1359-1400 (1996).
5. S. J. Kim, J. S. Hwang and J. H. Kim, Progressive failure analysis of pin-loaded laminated composites using penalty finite element method, AIAA J. 36 (1), 75-80 (1998).
6. P. P. Camanho and F. L. Matthews, A progressive damage model for mechanically fastened joints in composite laminates, J. Compos. Mater. 33, 2248-2280 (1999).
7. Y. Xiao and T. Ishikawa, Relationship between bearing strength and damage progress behavior of mechanically fastened joints in CFRP composites, J. Japan Soc. Compos. Mater. 28 (2), 56-65 (2002) (in Japanese).
8. T. Ishikawa, M. Matsushima and Y. Hayashi, Hardening non-linear behavior in longitudinal tension of unidirectional carbon composite, J. Mater. Sci. 20, 4075-4083 (1985).
9. H. T. Hahn and S. W. Tsai, Nonlinear elastic behavior of unidirectional composite laminae, J. Compos. Mater. 7, 102-118 (1973).
10. F. K. Chang and L. B. Lessard, Damage tolerance of laminated composites containing an open hole and subjected to compressive loadings: Part I - analysis, J. Compos. Mater. 25, 2-43 (1991).
11. S. C. Tan and J. Perez, Progressive failure of laminated composites with a hole under compressive loading, J. Reinf. Plast. Compos. 12, 1043-1057 (1993).
12. Z. Hashin, Failure criteria for unidirectional fiber composites, J. Applied Mech. 47, 329-334 (1980).
13. S. E. Yamada and C. T. Sun, Analysis of laminate strength and its distribution, J. Compos. Mater. 12, 275-284 (1978).
14. Y. Xiao, W. X. Wang, Y. Takao and T. Ishikawa, The effective friction coefficient of a laminate composite, and analysis of pin-loaded plates, J. Compos. Mater. 34, 69-87 (2000).
15. ABAQUS/Standard version 5.8, User's Manual, HKS Inc., USA (1998).
16. ABAQUS/Standard version 5.8, Example Problem Manual, HKS Inc., USA I: 3.2.25 (1998).
17. Y. Xiao and T. Ishikawa, Non-contact measurement for bearing strength of mechanically fastened joints in CFRP composites, J. Japan Soc. Compos. Mater. 26 (6), 213-218 (2000) (in Japanese).