Three-dimensional inelastic stress analysis of center notched composite laminates with damage

International Journal of Damage Mechanics

Volumn 6, Issue 1, 1997, Pages 23-50

  Chow, C L ^a   Yang, Fan ^a  

^a University of Michigan Dearborn   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ENERGY DISSIPATION; FINITE ELEMENT METHOD; GRAPHITE FIBER REINFORCED PLASTICS; LAMINATED COMPOSITES; LOADS (FORCES); MATHEMATICAL MODELS; STIFFNESS; STRESS ANALYSIS; STRESS CONCENTRATION; STRESSES; THREE DIMENSIONAL;

CONSTITUTIVE MODEL; DAMAGE; HOLE; LOADING PATH; MECHANICAL RESPONSE; TENSION;

FRACTURE MECHANICS;

EID: 0030824480     PISSN: 10567895     EISSN: None     Source Type: Journal    
DOI: 10.1177/105678959700600104     Document Type: Article

References (18)

1. Tang, S. 1977. "Interlaminar Stresses around Circular Cutouts in Composite Plates under Tension," AIAA J., 15:1631-1637.
2. Rybicki, E. F. and D. W. Schmueser. 1978. "Effect of Stacking Sequence and Lay-Up Angle on Free Edge Stresses around a Hole in a Laminated Plate under Tension," J. of Composite Materials, 12:300-313.
3. Lee, J. D. 1982. "Three Dimensional Finite Element Analysis of Damage Accumulation in Composite Laminate," Computers & Structures, 15:335-350.
4. Carlsson, L. 1983. "Interlaminar Stresses at a Hole in a Composite Member Subjected to InPlane Loading," J. of Composite Materials, 17:238-249.
5. Klang, E. C. and M. W. Hyer. 1985. "Damage Initiation at Curved Free Edges: Application to Uniaxially Loaded Plates Containing Holes and Notches," Recent Advances in Composites in the United States and Japan, ASTM STP 864, J. R. Vinson and M. Taya, eds., pp. 62-90.
6. Nishioka, T. and S. N. Atluri. 1982. "Stress Analysis of Holes in Angle-Ply Laminates: An Efficient Assumed Stress 'Special-Hole-Element' Approach and a Simple Estimation Method," Computers & Structures, 15:135-147.
7. Chen, W. H. and T. F. Huang. 1989. "Three Dimensional Interlaminar Stress Analysis at Free Edges of Composite Laminate," Computers & Structures, 32:1275-1286.
8. Altus, E. and A. Dorogoy. 1989. "A Three-Dimensional Study of Delamination," Engg. Fract. Mech., 33:1-19.
9. Bar-Yoseph, P. and J. Avrashi. 1985. "Interlaminar Stress Analysis for Laminated Plates Containing a Curvilinear Hole," Computers & Structures, 21:917-932.
10. Shalev, D. and K. L. Reifsnider. 1989. "Influence of Relative Ply Orientations on the Nature of the Edge Effect Singularities for a Circular Hole in a Composite Laminate," Int. J. of Solids & Structures, 25:1115-1132.
11. Allix, O., P. Ladeveze, E. L. Dantec and E. Vittecoq. 1990. "Damage Mechanics for Composite Laminates under Complex Loading," Yielding, Damage, and Failure of Anisotropic Solids,EGFS, J. P. Boehler, ed., Mechanical Engineering Publications, London, pp. 551-569.
12. Kamimura, K. 1985. "Continuum Damage Approach to Mechanical Behavior of Damaged Laminate and a Modelling of Damage Parameter," Mechanical Characterization of Load Bearing Fiber Composite Laminates, A. H. Cardon and G. Verchery, ed., Elsevier Applied Science Publishers Ltd., pp. 115-126.
13. Talreja, R. 1990. "Internal Variable Damage Mechanics of Composite Materials," Yielding, Damage, and Failure of Anisotropic Solids, EGF5, J. P. Boehler, ed., Mechanical Engineering Publications, London, pp. 509-533.
14. Allen, D. H. and J. W. Lee. 1990. "Matrix Cracking in Laminated Composites under Monotonic and Cyclic Loadings," ASME-AD, 111:65-75.
15. Chang, F. K., K. Y. Chang and S. Liu. 1991. "Damage Tolerance of Laminated Composites Containing an Open Hole and Subjected to Tensile Loadings," Journal of Composite Materials, 25:274-301.
16. Chow, C. L. and F. Yang. 1992. "A Simple Model for Brittle Composite Lamina with Damage," J. of Reinforced Plastics & Composites, 11(3):222-242.
17. Chow, C. L., F. Yang and A. Asundi. 1992. "A Method of Nonlinear Damage Analysis for Brittle Materials and Its Application to Thin Composite Laminates," Int. J. of Damage Mechanics, 1(3):347-366.
18. Schapery, R. A. 1990. "A Theory of Mechanical Behavior of Elastic Media with Growing Damage and Other Changes in Structure," J. Mech. Phys. Solids, 38:215-253.