Corrosion-fatigue life prediction for 2024-t62 aluminum alloy using damage mechanics-based approach

International Journal of Damage Mechanics

Volumn 21, Issue 8, 2012, Pages 1245-1266

  Hu, W P ^a   Shen, Q A ^a   Zhang, M ^a   Meng, Q C ^a   Zhang, X ^a  

^a BEIHANG UNIVERSITY   (China)

Author keywords

corrosion fatigue; damage mechanics; fatigue; life prediction; pre corrosion fatigue

Indexed keywords

CORROSIVE ENVIRONMENT; CRACK INITIATION LIFE; DAMAGE EVOLUTION; DAMAGE MECHANICS; LIFE PREDICTIONS; PRE-CORROSION-FATIGUE; SALT SPRAY; STANDARD SPECIMENS;

FATIGUE DAMAGE; FATIGUE OF MATERIALS; FATIGUE TESTING; SODIUM CHLORIDE;

CORROSION;

EID: 84867630160     PISSN: 10567895     EISSN: 15307921     Source Type: Journal    
DOI: 10.1177/1056789511432791     Document Type: Conference Paper

References (24)

1. ASTM Standard E466-96. (2002). e1. Standard Practice for Conducting Force Controlled Constant Amplitude Axial Fatigue Tests of Metallic Material, West Conshohocken, PA, USA ASTM International.
2. ASTM Standard E8-04. (2004). Standard Test Methods for Tension Testing of Metallic Materials, West Conshohocken, PA, USA, ASTM International.
3. ASTM Standard B117-09. (2009). Standard Practice for Operating Salt Apray (fog) Apparatus, West Conshohocken, PA, USA, ASTM International.
4. Beretta S., Carboni M., Fiore G., Conte A.L.. Corrosion-fatigue of A1N Railway Axle Steel Exposed to Rainwater. International Journal of Fatigue. 2010 ; 32: 952-961
5. Bhuiyan M.S., Ostuka Y., Mutoh Y., Murai T., Iwakami S.. Corrosion Fatigue Behavior of Conversion Coated AZ61 Magnesium Alloy. Materials Science and Engineering A. 2010 ; 527: 4978-4984
6. Bolotin V.V., Shipkov A.A.. Mechanical Aspects of Corrosion Fatigue and Stress Corrosion Cracking. International Journal of Solids and Structures. 2001 ; 38: 7297-7318 (Pubitemid 32836318)
7. Burns J.T., Kim S., Gangloff R.P.. Effect of Corrosion Severity on Fatigue Evolution in Al-Zn-Mg-Cu. Corrosion Science. 2010 ; 52: 498-508
8. Chaboche J.L.. Continuum Damage Mechanics. Journal of Applied Mechanics. 1988 ; 55: 59-72
9. Dey S., Das S.K., Basumallick A., Chattoraj I.. The Effect of Pitting on Fatigue Lives of Peak-Aged and Overaged 7075 Aluminum Alloys. Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science. 2010 ; 41: 3297-3307
10. Ebara R.. Corrosion Fatigue Crack Initiation Behavior of Stainless Steels. Procedia Engineering. 2010 ; 2: 1297-1306
11. Harlow D.G., Wei R.P.. Probability Modeling and Material Microstructure Applied to Corrosion and Fatigue of Aluminum and Steel Alloys. Engineering Fracture Mechanics. 2009 ; 76: 695-708
12. He Y.D., Qi H.B. Introduction to Material Corrosion and Protection. 2005 ). Introduction to Material Corrosion and Protection, 1st edn. Beijing, China, Machinery Industry Press. 96-102, 130-133. Beijing, China: Machinery Industry Press ; 2005: - 96-102, 130-133.
13. Kachanov L.M. Introduction to Continuum Damage Mechanics. Dordrecht: The Netherlands, Martinus Nijhoff Publishers ; 1986 :
14. Lemaitre J. A Course on Damage Mechanics. 1992 ). A Course on Damage Mechanics, 1st edn. New York, NY, Springer-Verlag. New York, NY: Springer-Verlag ; 1992 :
15. Ma J., Zhang B., Wang J., Wang G.Z., Han E.H., Ke W.. Anisotropic 3D Growth of Corrosion Pits Initiated at MnS Inclusions for A537 Steel during Corrosion Fatigue. Corrosion Science. 2010 ; 52: 2867-2877
16. Palin-Luc T., Pérez-Mora R., Bathias C., Domínguez G., Paris P.C., Arana J.L.. Fatigue Crack Initiation and Growth on a Steel in the Very High Cycle Regime with Sea Water Corrosion. Engineering Fracture Mechanics. 2010 ; 77: 1866-1873
17. Pidaparti R.M., Koombua K., Abdelsayed I.. Degradation Experiments and Analysis of Corrosion Damage. International Journal of Damage Mechanics. 2010 ; 19: 197-210
18. Rezig E., Irving P.E., Robinson M.J.. Development and Early Growth of Fatigue Cracks from Corrosion Damage in High Strength Stainless Steel. Procedia Engineering. 2010 ; 2: 387-396
19. Rusk D.T., Hoppe W.. Fatigue Life Prediction of Corrosion-damaged High-strength Steel using an Equivalent Stress Riser (ESR) Model. Part I: Test Development and Results. International Journal of Fatigue. 2009 ; 31: 1454-1463
20. Rusk D.T., Hoppe W., Braisted W., Powar N.. Fatigue Life Prediction of Corrosion-damaged High-strength Steel using an Equivalent Stress Riser (ESR) Model. Part II: Model Development and Results. International Journal of Fatigue. 2009 ; 31: 1464-1475
21. Walde K., Hillderry B.M.. Characterization of Pitting Damage and Prediction of Remaining Fatigue Life. International Journal of Fatigue. 2008 ; 30: 106-118 (Pubitemid 350016285)
22. Wang Q.Y., Kawagoishi N., Chen Q., Pidaparti R.M.. Evaluation of the Probability Distribution of Pitting Corrosion Fatigue Life in Aircraft Materials. Acta Mechanica Sinica. 2003 ; 19 (3). 247-252
23. Zhang M., Meng Q., Hu W., Shi S., Hu M., Zhang X.. Damage Mechanics Method for Fatigue Life Prediction of Pitch-Change-Link. International Journal of Fatigue. 2010 ; 32 (10). 1683-1688
24. Zhao J., Zhang X.. The Asymptotic Study of Fatigue Crack Growth based on Damage Mechanics. Engineering Fracture Mechanics. 1995 ; 50 (1). 131-141