Anisotropic 3D growth of corrosion pits initiated at MnS inclusions for A537 steel during corrosion fatigue

Corrosion Science

Volumn 52, Issue 9, 2010, Pages 2867-2877

  Ma, Jin ^a   Zhang, Bo ^a   Wang, Jianqiu ^a   Wang, Guozhen ^b   Han, En Hou ^a   Ke, Wei ^a  

^a INSTITUTE OF METAL RESEARCH   (China)

^b EAST CHINA UNIVERSITY OF SCIENCE AND TECHNOLOGY   (China)

Author keywords

A. Steel; B. SEM; C. Corrosion fatigue; C. Pitting corrosion

Indexed keywords

3-D GROWTH; B. SEM; C. PITTING CORROSION; CONFOCAL SCANNING LASER MICROSCOPE; FINITE ELEMENT ANALYSIS; MNS INCLUSIONS; PIT GROWTH; PITTING CORROSION; PLASTIC STRAIN; SEM;

ANISOTROPY; FINITE ELEMENT METHOD; GROWTH KINETICS; METAL ANALYSIS; PITTING; PLASTIC DEFORMATION; THREE DIMENSIONAL;

CORROSION FATIGUE;

EID: 77953961241     PISSN: 0010938X     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.corsci.2010.04.036     Document Type: Article

References (30)

1. Gutman E.M. Mechanochemistry of Solid Surfaces (1994), World Scientific, Singapore
2. Despic A.R., Raicheff R.G., and Bockris J.O.M. Mechanism of the acceleration of the electrodic dissolution of metals during yielding under stress. The Journal of Chemical Physics 49 (1968) 926-938
3. 4. Journal of the Electrochemical Society 122 (1975) 1445-1453
4. Jivkov A.P. Strain-induced passivity breakdown in corrosion crack initiation. Theoretical and Applied Fracture Mechanics 42 (2004) 43-52
5. Gutman E.M., Solovioff G., and Eliezer D. The mechanochemical behavior of type 316L stainless steel. Corrosion Science 38 (1996) 1141-1145
6. Chen G.S., Wan K.-C., Gao M., Wei R.P., and Flournoy T.H. Transition from pitting to fatigue crack growth-modeling of corrosion fatigue crack nucleation in a 2024-T3 aluminum alloy. Materials Science and Engineering A 219 (1996) 126-132
7. Eliezer A., Gutman E.M., Abramov E., and Aghion E. Corrosion fatigue and mechanochemical behavior of magnesium alloys. Corrosion Reviews 16 (1998) 1-26
8. Muller M. Theoretical considerations on corrosion fatigue crack initiation. Metallurgical Transactions A-Physical Metallurgy and Materials Science 13 (1982) 649-655
9. Ebara R. Corrosion fatigue crack initiation in 12% chromium stainless steel. Materials Science and Engineering A 468-470 (2007) 109-113
10. Nan Z.Y., Ishihara S., and Goshima T. Corrosion fatigue behavior of extruded magnesium alloy AZ31 in sodium chloride solution. International Journal of Fatigue 30 (2008) 1181-1188
11. Murtaza G., and Akid R. Corrosion fatigue short crack growth behaviour in a high strength steel. International Journal of Fatigue 18 (1996) 557-566
12. Chlistovsky R.M., Heffernan P.J., and DuQuesnay D.L. Corrosion-fatigue behaviour of 7075-T651 aluminum alloy subjected to periodic overloads. International Journal of Fatigue 29 (2007) 1941-1949
13. Burstein G.T., Liu C., Souto R.M., and Vines S.P. Origins of pitting corrosion. Corrosion Engineering Science and Technology 39 (2004) 25-30
14. Shibata T., and Takeyama T. Pitting corrosion as a stochastic-process. Nature 260 (1976) 315-316
15. Shibata T., and Takeyama T. Stochastic theory of pitting corrosion. Corrosion 33 (1977) 243-251
16. Zhang W.L., and Frankel G.S. Localized corrosion growth kinetics in AA2024 alloys. Journal of the Electrochemical Society 149 (2002) B510-B519
17. Valor A., Caleyo F., Alfonso L., Rivas D., and Hallen J.M. Stochastic modeling of pitting corrosion: a new model for initiation and growth of multiple corrosion pits. Corrosion Science 49 (2007) 559-579
18. Zhang T., Yang Y.G., Shao Y.W., Meng G.Z., and Wang F.H. A stochastic analysis of the effect of hydrostatic pressure on the pit corrosion of Fe-20Cr alloy. Electrochimica Acta 54 (2009) 3915-3922
19. Suter T., Webb E.G., Bohni H., and Alkire R.C. Pit initiation on stainless steels in 1 M NaCl with and without mechanical stress. Journal of the Electrochemical Society 148 (2001) B174-B185
20. Wranglen G. Pitting and sulphide inclusions in steel. Corrosion Science 14 (1974) 331-349
21. Cerit M., Genel K., and Eksi S. Numerical investigation on stress concentration of corrosion pit. Engineering Failure Analysis 16 (2009) 2467-2472
22. Pidaparti R.M., and Rao A.S. Analysis of pits induced stresses due to metal corrosion. Corrosion Science 50 (2008) 1932-1938
23. Pidaparti R.M., and Patel R.R. Correlation between corrosion pits and stresses in Al alloys. Materials Letters 62 (2008) 4497-4499
24. Turnbull A., Horner D.A., and Connolly B.J. Challenges in modelling the evolution of stress corrosion cracks from pits. Engineering Fracture Mechanics 76 (2009) 633-640
25. Ma J., Zhang B., Xu D., Han E.H., and Ke W. Effects of inclusion and loading direction on the fatigue behavior of hot rolled low carbon steel. International Journal of Fatigue 32 (2010) 1116-1125
26. Rivas D., Caleyo F., Valor A., and Hallen J.M. Extreme value analysis applied to pitting corrosion experiments in low carbon steel: comparison of block maxima and peak over threshold approaches. Corrosion Science 50 (2008) 3193-3204
27. Turnbull A., Wright L., and Crocker L. New insight into the pit-to-crack transition from finite element analysis of the stress and strain distribution around a corrosion pit. Corrosion Science 52 (2010) 1492-1498
28. 4 solution. 1. The influence of mechanical strain on the transient dissolution behavior during corrosion fatigue. Acta Metallurgica et Materialia 41 (1993) 693-708
29. Sahal M., Creus J., Sabot R., and Feaugas X. The effects of dislocation patterns on the dissolution process of polycrystalline nickel. Acta Materialia 54 (2006) 2157-2167
30. Lu B.T., Luo J.L., Norton P.R., and Mac H.Y. Effects of dissolved hydrogen and elastic and plastic deformation on active dissolution of pipeline steel in anaerobic groundwater of near-neutral pH. Acta Materialia 57 (2009) 41-49