Characterization of pitting damage and prediction of remaining fatigue life

International Journal of Fatigue

Volumn 30, Issue 1, 2008, Pages 106-118

  van der Walde, K ^a   Hillberry, B M ^a  

^a Purdue University   (United States)

Author keywords

2024 T3 Aluminum; Corrosion fatigue; Life prediction; Pitting

Indexed keywords

ALUMINUM ALLOYS; COMPUTER SIMULATION; CORROSION FATIGUE; FATIGUE DAMAGE; PITTING; SENSITIVITY ANALYSIS;

CROSS SECTIONAL PLANE MICROGRAPHS; FATIGUE LIFE PREDICTION DISTRIBUTIONS; LIFE PREDICTION; MULTIPLE CRACK EVOLUTION SCENARIOS;

FATIGUE CRACK PROPAGATION;

EID: 35548990203     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2007.02.020     Document Type: Article

References (24)

1. Zamber JE. A probabilistic approach to predicting fatigue lives of corroded 2024-T3 aluminum, MS thesis, 1997, Purdue University.
2. Dolley E.J., Lee B., and Wei R.P. The effect of pitting corrosion on fatigue life. Fatigue Fract Eng Mater Struct 23 (2000) 555-560
3. Sankaran K.K., Perez R., and Jata K.V. Effects of pitting corrosion on the fatigue behavior of aluminum alloy 7075-T6: modeling and experimental studies. Mater Sci Eng A 297 (2001) 223-229
4. DuQuesnay D.L., Underhill P.R., and Britt H.J. Fatigue crack growth from corrosion damage in 7075-T6511 aluminum alloy under aircraft loading. Int J Fatigue 25 (2003) 371-377
5. Medved J.J., Breton M., and Irving P.E. Corrosion pit size distributions and fatigue lives - a study of the EIFS technique for fatigue design in the presence of corrosion. Int J Fatigue 26 (2004) 71-80
6. van der Walde K., Brockenbrough J.R., Craig B.A., and Hillberry B.M. Multiple fatigue crack growth in pre-corroded 2024-T3 aluminum. Int J Fatigue 27 (2005) 1509-1518
7. Perez R. Corrosion/Fatigue Metrics. In: Proc of ICAF97 Symp on Fatigue in New and Ageing Aircraft, Edinburgh, Scotland, 1996, p. 215-29.
8. Tuegel EJ. Investigation of the Effect of Corrosion Pitting on Fatigue Life of Aluminum Structure, Report AFRL-VA-WP-TR-2003-3088, Air Force Research Laboratory, Air Force Materiel Command, 2003, Wright-Patterson Air Force Base, Ohio.
9. Frantziskonis G.N., Simon L.B., Woo J., and Matikas T.E. Multiscale characterization of pitting corrosion and application to an aluminum alloy. Eur J Mech A - Solids 19 (2000) 309-318
10. Shell E. Prediction of residual fatigue life from NDE of corroded components, PhD dissertation, 2002, University of Dayton.
11. Fulton JP, Wincheski B, Nath S, and Namkung M. In: Proc of ASNT Conf, New Orleans, Louisiana, 1994, pp. 34-6.
12. Scheuring JN, Grandt AF. Quantification of corrosion damage utilizing a fracture mechanics based methodology. In: Proc of Third Joint FAA/DOD/NASA Conf on Aging Aircraft, Albuquerque, New Mexico, 1999.
13. Goldfine N, Grundy D, Zilberstein V, Schlicker D, LaCivita K, Champagne V. Corrosion detection and prioritization using scanning and permanently mounted MWM eddy-current arrays. In: Proc of Tri-Service Corrosion Conf, San Antonio, TX, 2002.
14. Rokhlin S.I., Kim J.Y., Nagy H., and Zoofan B. Effect of pitting corrosion on fatigue crack initiation and fatigue life. Eng Fract Mech 62 (1999) 425-444
15. Codaro E.N., Nakazato R.Z., Horovistiz A.L., Ribeiro L.M.F., Ribeiro R.B., and Hein L.R.O. An image processing method for morphology characterization and pitting corrosion evaluation. Mater Sci Eng A 334 (2002) 298-306
16. Gruenberg KM. A method for predicting the fatigue life of pre-corroded 2024-T3 aluminum from breaking load tests, PhD dissertation, 2001, Purdue University.
17. ASTM G110-92, 1997, Standard Practice for Evaluating Intergranular Corrosion Resistance of Heat Treatable Aluminum Alloys by Immersion in Sodium Chloride + Hydrogen Peroxide Solution.
18. Colvin E.L., Jones S.A., and Magnusen P.E. Effect of corrosion fatigue initiation and growth in damage tolerant aluminum sheet alloys 2024-T3 and 6013-T6. In: Van Der Sluys W.A., Piascik R.S., and Zawierucha R. (Eds). Effects of the Environment on the Initiation of Crack Growth, ASTM STP 1298 (1997), ASTM
19. ® Version 6.5.0.180913a Release 13, Copyright © 1984-2002 by The Mathworks, Inc., Natick, MA, USA, www.mathworks.com.
20. van der Walde K. Corrosion-nucleated fatigue crack growth, PhD dissertation, May 2005, Purdue University.
21. Montgomery D.C. Design and Analysis of Experiments. 5th ed. (2001), John Wiley and Sons, New York
22. Atluri S.N. Computational Methods in the Mechanics of Fracture Vol. 2 (1986), Elsevier Science Pub. Co., New York Chapter 9
23. Newman Jr. J.C., Phillips E.P., and Swain M.H. Fatigue-life prediction methodology using small-crack theory. Int J Fatigue 21 2 (1999) 109-119
24. Newman JC, Jr, Edwards PR. Short Crack Growth Behaviour in an Aluminum Alloy - An AGARD Cooperative Test Programme. AGARD-R-732, Advisory Group for Aerospace Research and Development. 1988.