Volumn 32, Issue 6, 2010, Pages 952-961

Corrosion-fatigue of A1N railway axle steel exposed to rainwater

Author keywords

A1N steel; Corrosion pits; Corrosion fatigue; Railway axles; Rainwater

Indexed keywords

A1N STEEL; ARTIFICIAL RAINWATER; AXLE FAILURES; COMBINED EFFECT; CORROSION PITS; CORROSIVE ENVIRONMENT; CRACK GROWTH MEASUREMENT; FATIGUE BEHAVIOR; FATIGUE CRACK GROWTH; FATIGUE LIMIT; FATIGUE PROPERTIES; HIGH-CYCLE FATIGUES; PIT-TO-CRACK TRANSITIONS; RAILWAY AXLES; S-N DIAGRAM; SURFACE CRACKS;

EID: 76949104425     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2009.08.003     Document Type: Article
Times cited : (94)

References (28)
  • 1
    • 4644268770 scopus 로고    scopus 로고
    • The development of a damage tolerance concept for railway components and its demonstration for a railway axle
    • Zerbst U., Vormwald M., Andersch C., Mädler K., and Pfuff M. The development of a damage tolerance concept for railway components and its demonstration for a railway axle. Eng Fract Mech 72 (2005) 209-239
    • (2005) Eng Fract Mech , vol.72 , pp. 209-239
    • Zerbst, U.1    Vormwald, M.2    Andersch, C.3    Mädler, K.4    Pfuff, M.5
  • 2
    • 14744300912 scopus 로고    scopus 로고
    • Application of fatigue crack growth algorithms to railway axles and comparison of two steel grades
    • Beretta S., Carboni M., Cantini S., and Ghidini A. Application of fatigue crack growth algorithms to railway axles and comparison of two steel grades. J Rail Rapid Transit 218 (2004) 317-326
    • (2004) J Rail Rapid Transit , vol.218 , pp. 317-326
    • Beretta, S.1    Carboni, M.2    Cantini, S.3    Ghidini, A.4
  • 3
    • 33748052659 scopus 로고    scopus 로고
    • Experiments and stochastic model for propagation lifetime of railway axles
    • Beretta S., and Carboni M. Experiments and stochastic model for propagation lifetime of railway axles. Eng Fract Mech 73 (2006) 2627-2641
    • (2006) Eng Fract Mech , vol.73 , pp. 2627-2641
    • Beretta, S.1    Carboni, M.2
  • 4
    • 39149110291 scopus 로고    scopus 로고
    • An investigation on the influence of rotary bending and press fitting on stress intensity factors and fatigue crack growth in railway axles
    • Madia M., Beretta S., and Zerbst U. An investigation on the influence of rotary bending and press fitting on stress intensity factors and fatigue crack growth in railway axles. Eng Fract Mech 75 (2008) 1906-1920
    • (2008) Eng Fract Mech , vol.75 , pp. 1906-1920
    • Madia, M.1    Beretta, S.2    Zerbst, U.3
  • 5
    • 38149011307 scopus 로고    scopus 로고
    • Effect of probability of detection upon the definition of inspection intervals of railway axles
    • Carboni M., and Beretta S. Effect of probability of detection upon the definition of inspection intervals of railway axles. J Rail Rapid Transit 221 (2007) 409-417
    • (2007) J Rail Rapid Transit , vol.221 , pp. 409-417
    • Carboni, M.1    Beretta, S.2
  • 6
    • 14744304622 scopus 로고    scopus 로고
    • Railway axle failure investigations and fatigue crack growth monitoring of an axle
    • Hoddinot D.S. Railway axle failure investigations and fatigue crack growth monitoring of an axle. J Rail Rapid Transit 218 (2004) 283-292
    • (2004) J Rail Rapid Transit , vol.218 , pp. 283-292
    • Hoddinot, D.S.1
  • 7
    • 46749125008 scopus 로고    scopus 로고
    • Main track derailment: Canadian national train No. G-894-31-14
    • Transportation Safety Board of Canada, R01Q0010; 2001
    • Transportation Safety Board of Canada. Main track derailment: Canadian national train No. G-894-31-14. Railway Investigation Report R01Q0010; 2001.
    • Railway Investigation Report
  • 9
    • 0025889592 scopus 로고
    • Short fatigue crack growth behavior of a low carbon steel under corrosion fatigue conditions
    • Akid R., and Miller K.J. Short fatigue crack growth behavior of a low carbon steel under corrosion fatigue conditions. Fatigue Fract Eng Mater Struct 14 (1991) 637-649
    • (1991) Fatigue Fract Eng Mater Struct , vol.14 , pp. 637-649
    • Akid, R.1    Miller, K.J.2
  • 10
    • 0024907288 scopus 로고
    • Corrosion fatigue of steel in various aqueous environments
    • Ragab A., Alawi H., and Sorein K. Corrosion fatigue of steel in various aqueous environments. Fatigue Fract Eng Mater Struct 12 (1989) 469-479
    • (1989) Fatigue Fract Eng Mater Struct , vol.12 , pp. 469-479
    • Ragab, A.1    Alawi, H.2    Sorein, K.3
  • 11
    • 46749144983 scopus 로고    scopus 로고
    • An investigation of the effects of corrosion on the fatigue strength of A1N steel railway axles
    • Beretta S., Carboni M., Lo Conte A., and Palermo E. An investigation of the effects of corrosion on the fatigue strength of A1N steel railway axles. J Rail Rapid Transit 222 (2008) 129-143
    • (2008) J Rail Rapid Transit , vol.222 , pp. 129-143
    • Beretta, S.1    Carboni, M.2    Lo Conte, A.3    Palermo, E.4
  • 12
    • 76949083706 scopus 로고    scopus 로고
    • BS EN13261. Railway applications - wheelsets and bogies - axles - product requirements. CEN; 2003.
    • BS EN13261. Railway applications - wheelsets and bogies - axles - product requirements. CEN; 2003.
  • 15
    • 19544390143 scopus 로고    scopus 로고
    • Propagation of short cracks in a high strength steel for railway axles
    • Krakow, Poland;
    • Beretta S. Propagation of short cracks in a high strength steel for railway axles. In: Proceedings of the 14th European conference on fracture, Krakow, Poland; 2002.
    • (2002) Proceedings of the 14th European conference on fracture
    • Beretta, S.1
  • 16
    • 0021869835 scopus 로고
    • Analysis of stress intensity factors of modes I, II and III for inclined surface cracks of arbitrary shape
    • Murakami Y. Analysis of stress intensity factors of modes I, II and III for inclined surface cracks of arbitrary shape. Eng Fract Mech 22 1 (1985) 101-114
    • (1985) Eng Fract Mech , vol.22 , Issue.1 , pp. 101-114
    • Murakami, Y.1
  • 17
    • 27144434031 scopus 로고    scopus 로고
    • Compression pre-cracking to generate near threshold fatigue-crack-growth rates in two aluminum alloys
    • Newman Jr. J.C., Schneider J., Daniel A., and McKnight D. Compression pre-cracking to generate near threshold fatigue-crack-growth rates in two aluminum alloys. Int J Fatigue 27 (2005) 1432-1440
    • (2005) Int J Fatigue , vol.27 , pp. 1432-1440
    • Newman Jr., J.C.1    Schneider, J.2    Daniel, A.3    McKnight, D.4
  • 18
    • 0043068061 scopus 로고    scopus 로고
    • Organic films for protection of copper and bronze against acid rain corrosion
    • Brunoro G., Frignani A., Colledan A., and Chiavari C. Organic films for protection of copper and bronze against acid rain corrosion. Corros Sci 45 (2003) 2219-2231
    • (2003) Corros Sci , vol.45 , pp. 2219-2231
    • Brunoro, G.1    Frignani, A.2    Colledan, A.3    Chiavari, C.4
  • 19
    • 2342636364 scopus 로고    scopus 로고
    • The cyclic deformation behavior and fatigue induced damage of the implant alloy TiAl6Nb7 in simulated physiological media
    • Leinenbach C., Fleck C., and Eifler D. The cyclic deformation behavior and fatigue induced damage of the implant alloy TiAl6Nb7 in simulated physiological media. Int J Fatigue 26 (2004) 857-864
    • (2004) Int J Fatigue , vol.26 , pp. 857-864
    • Leinenbach, C.1    Fleck, C.2    Eifler, D.3
  • 20
    • 33745832684 scopus 로고    scopus 로고
    • Prediction of corrosion fatigue lives of aluminium alloy on the basis of corrosion pit growth law
    • Ishihara S., Saka S., Nan Z.Y., Goshima T., and Sunada S. Prediction of corrosion fatigue lives of aluminium alloy on the basis of corrosion pit growth law. Fatigue Fract Eng Mater Struct 29 (2006) 472-480
    • (2006) Fatigue Fract Eng Mater Struct , vol.29 , pp. 472-480
    • Ishihara, S.1    Saka, S.2    Nan, Z.Y.3    Goshima, T.4    Sunada, S.5
  • 21
    • 0025746418 scopus 로고
    • Statistical investigations of the behavior of micro-cracks in carbon steels
    • Goto M. Statistical investigations of the behavior of micro-cracks in carbon steels. Fatigue Fract Eng Mater Struct 14 (1991) 833-845
    • (1991) Fatigue Fract Eng Mater Struct , vol.14 , pp. 833-845
    • Goto, M.1
  • 22
    • 0030233634 scopus 로고    scopus 로고
    • Micro-crack propagation and micro-structural parameters of fatigue damage
    • Beretta S. Micro-crack propagation and micro-structural parameters of fatigue damage. Fatigue Fract Eng Mater Struct 19 (1996) 1107-1115
    • (1996) Fatigue Fract Eng Mater Struct , vol.19 , pp. 1107-1115
    • Beretta, S.1
  • 23
    • 0019658622 scopus 로고
    • An empirical stress intensity factor equation for the surface crack
    • Newman Jr. J.C., and Raju I.S. An empirical stress intensity factor equation for the surface crack. Eng Fract Mech 15 (1981) 185-192
    • (1981) Eng Fract Mech , vol.15 , pp. 185-192
    • Newman Jr., J.C.1    Raju, I.S.2
  • 24
    • 67349237451 scopus 로고    scopus 로고
    • Modelling of fatigue thresholds for small cracks in a mild steel by "Strip-Yield" model
    • Beretta S., Carboni M., and Madia M. Modelling of fatigue thresholds for small cracks in a mild steel by "Strip-Yield" model. Eng Fract Mech 76 (2009) 1548-1561
    • (2009) Eng Fract Mech , vol.76 , pp. 1548-1561
    • Beretta, S.1    Carboni, M.2    Madia, M.3
  • 25
    • 0033340446 scopus 로고    scopus 로고
    • Influence of pitting on the fatigue life of a turbine blade steel
    • Zhou S., and Turnbull A. Influence of pitting on the fatigue life of a turbine blade steel. Fatigue Fract Eng Mater Struct 22 (1999) 1083-1093
    • (1999) Fatigue Fract Eng Mater Struct , vol.22 , pp. 1083-1093
    • Zhou, S.1    Turnbull, A.2
  • 26
    • 0034327888 scopus 로고    scopus 로고
    • Empirical corrosion fatigue life prediction models of a high strength steel
    • Murtaza G., and Akid R. Empirical corrosion fatigue life prediction models of a high strength steel. Eng Fract Mech 67 (2000) 461-474
    • (2000) Eng Fract Mech , vol.67 , pp. 461-474
    • Murtaza, G.1    Akid, R.2
  • 27
    • 0001030370 scopus 로고
    • Material science perspective of metal fatigue resistance
    • Miller K.J. Material science perspective of metal fatigue resistance. Mater Sci Technol 9 (1993) 453-462
    • (1993) Mater Sci Technol , vol.9 , pp. 453-462
    • Miller, K.J.1


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.