Effect of sandblasting on the long-term performance of dental ceramics

Journal of Biomedical Materials Research - Part B Applied Biomaterials

Volumn 71, Issue 2, 2004, Pages 381-386

  Zhang, Yu ^a   Lawn, Brian R ^a   Rekow, E Dianne ^b   Thompson, Van P ^b  

^a NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

^b NEW YORK UNIVERSITY   (United States)

Author keywords

Crowns; Dental ceramics; Fatigue; Radial cracks; Sandblasting

Indexed keywords

CERAMIC MATERIALS; COMPUTER SIMULATION; DENTISTRY; FRACTURE; POLYMERS; SUBSTRATES;

CERAMIC CROWNS; DENTAL CERAMICS; SANDBLASTING;

DENTAL MATERIALS;

ALUMINUM OXIDE; TOOTH CEMENT;

ARTICLE; CEMENTATION; CERAMICS; COMPARATIVE STUDY; DENTISTRY; FATIGUE; TOOTH CROWN; TOOTH FILLING; TOOTH FRACTURE;

ALGORITHMS; ALUMINUM OXIDE; BIOMECHANICS; CERAMICS; DENTAL MATERIALS; MATERIALS TESTING; MICROSCOPY, ELECTRON, SCANNING; SURFACE PROPERTIES; TENSILE STRENGTH;

EID: 7744239922     PISSN: 00219304     EISSN: None     Source Type: Journal    
DOI: 10.1002/jbm.b.30097     Document Type: Article

References (49)

1. Kelly JR. Ceramics in restorative and prosthetic dentistry. Annu Rev Mater Sci 1997;27:443-468.
2. Kelly JR. Clinically relevant approach to failure testing of all-ceramic restorations. J Prosthet Dent 1999;81:652-661.
3. Lawn BR, Deng Y, Thompson VP. Use of contact testing in the characterization and design of all-ceramic crown-like layer structures: A review. J Prosthet Dent 2001;86:495-510.
4. Lawn BR. Ceramic-based layer structures for biomechanical applications. Curr Opin Solid State Mater Sci 2002;6:229-235.
5. Lawn BR, Deng Y, Miranda P, Pajares A, Chai H, Kim DK. Overview: Damage in brittle layer structures from concentrated loads. J Mater Res 2002;17:3019-3036.
6. Willmann G. Ceramics for total hip replacement - What a surgeon should know. Orthopedics 1998;21:173-177.
7. Willmann G. Ceramic femoral heads for total hip arthroplasty. Adv Eng Mater 2000;2:114-122.
8. Lee C-S, Kim DK, Sanchez J, Miranda P, Pajares A, Lawn BR. Rate effects in critical loads for radial cracking in ceramic coatings. J Am Ceram Soc 2002;85:2019-2024.
9. Zhang Y, Lawn BR. Long-term strength of clinically relevant ceramics. J Biomed Mater Res 2004;69B:166-172.
10. Zhang Y, Pajares A, Lawn B. Fatigue and damage tolerance of Y-TZP ceramics in layered biomechanical systems. J Biomed Mater Res B, in press.
11. Kim H-W, Deng Y, Miranda P, Pajares A, Kim DK, Kim H-E, et al. Effect of flaw state on the strength of brittle coatings on soft substrates. J Am Ceram Soc 2001;84:2377-2384.
12. Suliman AH, Swift EJ, Perdigao J. Effects of surface treatment and bonding agents on bond strength of composite resin to porcelain. J Prosthet Dent 1993;70:118-120.
13. Kern M, Thompson VP. Bonding to glass infiltrated alumina ceramic: Adhesive methods and their durability. J Prosthet Dent 1995;73:240-249.
14. Kern M, Wegner SM. Bonding to zirconia ceramic: Adhesion methods and their durability. Dent Mater 1998;14:64-71.
15. Blixt M, Adamczak E, Linden LA, Oden A, Arvidson K. Bonding to densely sintered alumina surfaces: Effect of sandblasting and silica coating on shear bond strength of luting cements. Int J Prosthodont 2000;13:221-226.
16. Derand P, Derand T. Bond strength of luting cements to zirconium oxide ceramics. Int J Prosthodont 2000;13:131-135.
17. Ozcan M, Alkumru HN, Gemalmaz D. The Effect of surface treatment on the shear bond strength of luting cement to a glass-infiltrated alumina ceramic. Int J Prosthodont 2001;14:335-339.
18. Lu YC, Tseng H, Shih YH, Lee SY. Effects of surface treatments on bond strength of glass-infiltrated ceramic. J Oral Rehabil 2001;28:805-813.
19. Friederich R, Kern M. Resin Bond strength to densely sintered alumina ceramic. Int J Prosthodont 2002;15:333-338.
20. Wegner SM, Gerdes W, Kern M. Effect of different artificial aging conditions on ceramic-composite bond strength. Int J Prosthodont 2002;15:267-272.
21. Spohr AM, Sobrinho LC, Consani S, Sinhoreti MA, Knowles JC. Influence of surface conditions and silane agent on the bond of resin to IPS empress 2 ceramic. Int J Prosthodont 2003;16:277-282.
22. Oh WS, Shen C. Effect of surface topography on the bond strength of a composite to three different types of ceramic. J Prosthet Dent 2003;90:241-245.
23. Saygili G, Sahmali S. Effect of ceramic surface treatment on the shear bond strengths of two resin luting agents to all-ceramic materials. J Oral Rehabil 2003;30:758-764.
24. Cook RF, Lawn BR, Dabbs TP, Chantikul P. Effect of machining damage on the strength of a glass ceramic. J Am Ceram Soc 1981;64:C121-C122.
25. Marshall DB, Evans AG, Yakub BTK, Tien JW, Kino GS. The nature of machining damage in brittle materials. Proc R Soc Lond 1983;A385:461-475.
26. Green DJ, Hannink RHJ, Swain MV. Transformation toughening of ceramics. Boca Raton, FL: CRC Press; 1989.
27. Kosmac T, Oblak C, Jevnikar P, Funduk N, Marion L. The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic. Dent Mater 1999;15:426-433.
28. Kosmac T, Oblak C, Jevnikar P, Funduk N, Marion L. Strength and reliability of surface treated Y-TZP dental ceramics. J Biomed Mater Res 2000;53:304-313.
29. Deng Y, Miranda P, Pajares A, Lawn BR. Fracture of ceramic/ ceramic/polymer trilayers for biomechanical applications. J Biomed Mater Res 2003; 67A:828-833.
30. Oliver WC, Pharr GM. An improved technique for determining hardness and elastic-modulus using load and displacement sensing indentation experiments. J Mater Res 1992;7:1564-1583.
31. Guiberteau F, Padture NP, Lawn BR. Effect of grain size on hertzian contact in alumina. J Am Ceram Soc 1994;77:1825-1831.
32. Chai H, Lawn BR, Wuttiphan S. Fracture modes in brittle coatings with large interlayer modulus mismatch. J Mater Res 1999;14:3805-3817.
33. Miranda P, Pajares A, Guiberteau F, Deng Y, Lawn BR. Designing damage-resistant brittle-coating structures: I. Bilayers. Acta Mater 2003;51:4347-4356.
34. Xu HHK, Jahanmir S, Ives LK. Effect of grinding and strength of tetragonal zirconia and zirconia-toughened alumina. Mach Sci Technol 1997;1:49-66.
35. Smith DT, Wei L, Quantifying local microcrack density in ceramics: A comparison of instrumented indentation and thermal wave techniques. J Am Ceram Soc 1995;78:1301-1304.
36. Kim JH, Miranda P, Kim DK, Lawn BR. Effect of an adhesive interlayer on the fracture of a brittle coating on a supporting substrate. J Mater Res 2003;18:222-227.
37. Rodel J, Kelly J, Lawn BR. In situ measurements of bridged crack interfaces in the SEM. J Am Ceram Soc 1990;73:3313-3318.
38. Lawn BR, Marshall DB. Nonlinear stress-strain curves for solids containing closed cracks with friction. J Mech Phys Solids 1998;46:85-113.
39. Padture NP, Lawn BR. Contact fatigue of a silicon carbide with a heterogeneous grain structure. J Am Ceram Soc 1995;78:1431-1438.
40. Pajares A, Guiberteau F, Lawn BR, Lathabai S. Hertzian contact damage in magnesia-partially-stabilized zirconia. J Am Ceram Soc 1995;78:1083-1086.
41. Lawn BR, Kim DK, Lee SK, Jung Y-G, Peterson IM. Cyclic contact fatigue of brittle ceramics. In: Wu XR and Wang ZG, editors. The seventh international fatigue conference, Fatigue 99. Beijing, China: Higher Education Press; 1999. p 69-80.
42. Lee SK, Lawn BR. Contact fatigue in silicon nitride. J Am Ceram Soc 1999;82:1281-1288.
43. Kim DK, Jung Y-G, Peterson IM, Lawn BR. Cyclic fatigue of intrinsically brittle ceramics in contact with spheres. Acta Mater 1999;47:4711-4725.
44. Jung Y-G, Peterson IM, Kim DK, Lawn BR. Lifetime-limiting strength degradation from contact fatigue in dental ceramics. J Dent Res 2000;79:722-731.
45. 3 solid electrolyte after ageing. Solid State Ionics 1981;3:489-493.
46. Hirano M. Inhibition of low temperature degradation of tetragonal zirconia ceramics - A review. Br Ceram Transact J 1992;91:139-147.
47. Piconi C, Burger W, Richter HG, Cittadini A, Maccauro G, Covacci V, et al. Y-TZP ceramics for artificial joint replacements. Biomaterials 1998;19:1489-1494.
48. Piconi C, Maccauro G. Zirconia as a ceramic biomaterial. Biomaterials 1999;20:1-25.
49. Chevalier J, Cales B, Drouin JM. Low-temperature aging of Y-YZP ceramics. J Am Ceram Soc 1999;82:2150-2154.