Rate effects in critical loads for radial cracking in ceramic coatings

Journal of the American Ceramic Society

Volumn 85, Issue 8, 2002, Pages 2019-2024

  Lee, Chul Seung ^a   Kim, Do Kyung ^a,d   Sánchez, Jose ^b   Miranda, Pedro ^b   Pajares, Antonia ^b   Lawn, Brian R ^c,d  

^a Korea Advanced Institute of Science and Technology (KAIST)   (South Korea)

^b UNIVERSITY OF EXTREMADURA   (Spain)

^c NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

^d AMERICAN CERAMIC SOCIETY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

ADHESIVES; BENDING STRENGTH; BONDING; CRACK INITIATION; CRACK PROPAGATION; GLASS; LOADS (FORCES); POLYCARBONATES; RATE CONSTANTS; STRESSES; SUBSTRATES; VISCOELASTICITY;

GLASS-COATING BILAYERS; RADIAL CRACKING;

CERAMIC COATINGS;

EID: 0036686031     PISSN: 00027820     EISSN: None     Source Type: Journal    
DOI: 10.1111/j.1151-2916.2002.tb00398.x     Document Type: Article

References (33)

1. Damage-resistant alumina-based layer composites
2. Fracture modes in brittle coatings with large interlayer modulus mismatch
3. Damage-resistant brittle coatings
4. Contact-induced damage in ceramic coatings on compliant substrates: Fracture mechanics and design
5. Effect of Flaw state on the strength of brittle coatings on soft substrates
6. Cracking of porcelain coatings bonded to metal substrates of different modulus and hardness
7. Role of flaw statistics in contact fracture of brittle coatings
8. Making ceramics 'Ductile'
9. Brittle fracture versus quasi-plasticity in ceramics: A simple predictive index
10. Clinically relevant approach to failure testing of all-ceramic restorations
11. Damage modes in dental layer structures
12. Use of contact testing in the characterization and design of all-ceramic crown-like layer stractures: A review
13. Influence of water vapor on crack propagation in soda-lime glass
14. Stress corrosion and static fatigue of glass
15. Cyclic fatigue of intrinsically brittle ceramics in contact with spheres
16. Role of microstructure in dynamic fatigue of glass-ceramics after contact with spheres
17. Model for cyclic fatigue of quasi-plastic ceramics in contact with spheres
18. Fracture of glass/poly(vinyl butyral) (butacite™) laminates in biaxial flexure
19. Mechanics of strength degrading flaws in silicon
20. Contact fracture of brittle bilayer coatings on soft substrates
21. Subcritical crack growth in ceramics
22. Residual stress effects in sharp-contact cracking: I, indentation fracture mechanics
23. Residual stress effects in sharp-contact cracking: II, strength degradation
24. Flaw characteristics in dynamic fatigue: The influence of residual contact stresses
25. Elastic/plastic indentation damage in ceramics: The median/radial crack system
26. Theory of fatigue for brittle flaws originating from residual stress concentrations
27. Residual stresses in dynamic fatigue of abraded glass
28. Role of adhesive interlayer in transverse fracture of brittle layer structures
29. A dynamic fatigue study of soda-lime and borosilicate glasses using small-scale indentation flaws
30. Hertzian fracture in single crystals with the diamond structure
31. Effect of polymer coatings on the strength and fatigue behavior of indented soda-lime glass