Long-Term Strength of Ceramics for Biomedical Applications

Journal of Biomedical Materials Research - Part B Applied Biomaterials

Volumn 69, Issue 2, 2004, Pages 166-172

  Zhang, Yu ^a   Lawn, Brian ^a  

^a NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

Author keywords

Bilayers; Brittle coatings; Crack velocity; Critical loads; Dental crowns; Fracture; Lifetime

Indexed keywords

BIOMATERIALS; BIOMECHANICS; CERAMIC MATERIALS; CRACK INITIATION; CRACK PROPAGATION; CYCLIC LOADS; DENTAL PROSTHESES; HIP PROSTHESES;

BIOMECHANICAL SYSTEMS; DENTAL CROWNS;

BIOMEDICAL ENGINEERING;

ALUMINUM OXIDE; EPOXY RESIN; GLASS; POLYCARBONATE; POLYETHYLENE; ZIRCONIUM OXIDE;

ARTICLE; BIOMECHANICS; CERAMICS; LOADING TEST; MACHINE; TENSILE STRENGTH; TOOTH CROWN; TOTAL HIP PROSTHESIS; YOUNG MODULUS;

EID: 2442530603     PISSN: 00219304     EISSN: None     Source Type: Journal    
DOI: 10.1002/jbm.b.20039     Document Type: Article

References (26)

1. Jung YG, Wuttiphan S, Peterson IM, Lawn BR. Damage modes in dental layer structures. J Dent Res 1999;78:887-897.
2. Lawn BR et al. Damage-resistant brittle coatings. Adv Eng Mater 2000;2:745-748.
3. Lawn BR. Ceramic-based layer structures for biomechanical applications. Current Opinion Solid State Mater Sci 2002;6: 229-235.
4. Lawn BR, Deng Y, Miranda P, Pajares A, Chai H, Kim DK. Overview: Damage in brittle layer structures from concentrated loads. J Mater Res 2002;17:3019-3036.
5. Kelly JR. Ceramics in restorative and prosthetic dentistry. Annu Rev Mater Sci 1997;27:443-468.
6. Kelly JR. Clinically relevant approach to failure testing of all-ceramic restorations. J Prosthet Dent 1999;81:652-661.
7. Lawn BR, Deng Y, Thompson VP. Use of contact testing in the characterization and design of all-ceramic crown-like layer structures: A review. J Prosthet Dent 2001;86:495-510.
8. Lee CS, Kim DK, Sanchez J, Miranda P, Pajares A, Lawn BR. Rate effects in critical loads for radial cracking in ceramic coatings. J Am Ceram Soc 2002;85:2019-2024.
9. Wiederhorn SM, Bolz LH. Stress corrosion and static fatigue of glass. J Am Ceram Soc 1970;53:543-548.
10. Wiederhorn SM. A chemical interpretation of static fatigue. J Am Ceram Soc 1972;55:81-85.
11. Willmann G. Improving bearing surfaces of artificial joints. Adv Eng Mater 2001;3:135-141.
12. Lohbauer U, Petschelt A, Greil P. Lifetime prediction of CAD/CAM dental ceramics. J Biomed Mater Res 2002;63:780-785.
13. Lawn BR. Indentation of ceramics with spheres: A century after Hertz. J Am Ceram Soc 1998;81:1977-1994.
14. Rhee YW, Kim HW, Deng Y, Lawn BR. Contact-induced damage in ceramic coatings on compliant substrates: Fracture mechanics and design. J Am Ceram Soc 2001;84:1066-1072.
15. Deng Y, Lawn BR, Lloyd IK. Characterization of damage modes in dental ceramic bilayer structures. J Biomed Mater Res Appl Biomater 2002;63:137-145.
16. Höland W, Schweiger M, Frank M, Rheinberger V. A comparison of the microstructure and properties of the IPS Empress®2 and the IPS Empress® glass-ceramics. J Biomed Mater Res 2000;53:297-303.
17. Chai H, Lawn BR, Wuttiphan S. Fracture modes in brittle coatings with large interlayer modulus mismatch. J Mater Res 1999;14:3805-3817.
18. Kim HW et al. Effect of flaw state on the strength of brittle coatings on soft substrates. J Am Ceram Soc 2001;84:2377-2384.
19. Miranda P, Pajares A, Guiberteau F, Deng Y, Lawn BR. Designing damage-resistant brittle-coating structures: I. Bilayers. Acta Mater 2003;51:4347-4356.
20. Wiederhorn SM. Subcritical crack growth in ceramics. In: Bradt RC, Lange FF, Hasselman DPH, editors. Fracture mechanics of ceramics. New York: Plenum. p. 613.
21. Lawn BR. Fracture of brittle solids. Cambridge: Cambridge University Press; 1993.
22. Lawn BR, Padture NP, Cai H, Guiberteau F. Making ceramics "ductile." Science 1994;263:1114-1116.
23. Kim DK, Jung YG, Peterson IM, Lawn BR. Cyclic fatigue of intrinsically brittle ceramics in contact with spheres. Acta Mater 1999;47:4711-4725.
24. Jung YG, Peterson IM, Kim DK, Lawn BR. Lifetime-limiting strength degradation from contact fatigue in dental ceramics. J Dent Res 2000;79:722-731.
25. Miranda P, Pajares A, Guiberteau F, Cumbrera FL, Lawn BR. Role of flaw statistics in contact fracture of brittle coatings. Acta Mater 2001;49:3719-3726.
26. Lakshminarayanan R, Shetty DK, Cutler RA. Toughening of layered ceramic composites with residual surface compression. J Am Ceram Soc 1996;79:79-87.