Mechanical and environmental influences on stress corrosion cracking of an x-70 pipeline steel in dilute near-neutral ph solutions

Corrosion

Volumn 63, Issue 5, 2007, Pages 419-432

  Fang, B ^a   Han, E H ^a   Wang, J ^a   Ke, W ^a  

^a INSTITUTE OF METAL RESEARCH   (China)

Author keywords

Near neutral Ph; Pipeline steel; Potential; Slow strain rate test; Strain rate; Stress corrosion cracking

Indexed keywords

CARBON DIOXIDE; CATHODIC PROTECTION; CRACK INITIATION; ELECTROCHEMISTRY; PIPELINES; STRAIN RATE; STRESS CORROSION CRACKING;

ELECTROCHEMICAL POTENTIAL; SLOW STRAIN RATE TEST; TRANSGRANULAR;

STEEL PIPE;

CARBON DIOXIDE; CATHODIC PROTECTION; CRACK INITIATION; ELECTROCHEMISTRY; PIPELINES; STEEL PIPE; STRAIN RATE; STRESS CORROSION CRACKING;

EID: 34249326924     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3278395     Document Type: Article

References (55)

1. N. Sridhar, P.C. Lichtner, D.S. Dunn, "Evolution of Environment Under Disbonded Coating on Cathodically Protected Pipeline - Preliminary Modeling and Experimental Studies," CORROSION/98, paper no. 680 (Houston, TX: NACE International, 1998).
2. B.A. Harle, J.A. Beavers, Corrosion 49 (1993): p. 861-863.
3. Z. Szklarska-Smialowska, Z. Xia, R.B. Rebak, Corrosion 50 (1994): p. 334-338.
4. R.B. Parkins, W.K. Blanchard, Jr., B.S. Delanty, Corrosion 50 (1994): p. 394-408.
5. R.B. Rebak, Z. Xia. R. Safruddin, Z. Szklarska-Smialowska, "Electrochemical Processes Controlling SCC of Underground Pipelines," CORROSION/1995, paper no. 184 (Houston, TX: NACE, 1995).
6. B.A. Harle, J.A. Beavers, C.W. Jaske, "Mechanical and Metallurgical Effects on Low-pH Stress Corrosion Cracking of Natural Gas Pipelines," CORROSION/1995, paper no. 646 (Houston, TX: NACE, 1995).
7. R.B. Rebak, Z. Xia, R. Safruddin, Z. Szklarska-Smialowska, Corrosion 52 (1996): p. 396-404.
8. B.Y. Fang, A. Atrens, J.Q. Wang, E.H. Han, Z.Y. Zhu, W. Ke, J. Mater. Sci. 38 (2003): p. 127-132.
9. F. King, T. Jack, W.X. Chen, M. Wilmott, R.R. Fessler, K. Krist, "Mechanistic Studies of Initiation and Early Stage Crack Growth for Near-Neutral pH SCC on Pipelines," CORROSION/2000, paper no. 361 (Houston, TX: NACE, 2000).
10. J.A. Beavers, C.L. Durr, B.S. Delanty, D.M. Owen, R.L. Sutherby, "Near-Neutral pH SCC: Crack Propagation in Susceptible Soil Environments," CORROSION/2001, paper no. 01217 (Houston, TX: NACE, 2001).
11. M. Meyer, L. Scoppio, B. Rudd, E. Lo Piccolo, S. Mattews, J.P. Jansen, "Near-Neutral pH SCC Resistance of Pipeline Steels: Effect of Some Material and Mechanical Parameters (EPRG-Report)," in Proc. Int. Pipeline Technology Conf., ed. R. Denys held May 9-13 (Beaconsfield, U.K.: Pipeline World and the Journal of Pipeline Integrity, 2004), p. 1, 789.
12. Z. Qin, B. Demko, J. Noel, D. Shoesmith, F. Fing, R. Worthingham, K. Keith, Corrosion 60 (2004): p. 906-914.
13. R.L. Eadie, K.E. Szklarz, R.L. Sutherby, Corrosion 61 (2005): p. 167-173.
14. B.W. Williams, S.B. Lambert, R. Sutherby, A. Plumtree, Corrosion 60 (2004): p. 95-103.
15. J.G. Gonzalez-Rodrguez, M. Casales, V.M. Salinas-Bravo, J.L. Albarran, L. Martinez, Corrosion 58 (2002): p. 584-590.
16. B.A. Kim, N. Oguchi, Y. Hosokawa, W. Zheng, G. Williams, M. Laronde, J.A. Gianetto, G. Shen, W.R. Tyson, "Experimental Study on SCC Susceptibility of X60 Steel Using Full Pipe Sections in Near-Neutral pH Environment," Int. Pipeline Conf. (New York, NY: ASME International, 2004), p. 133-141.
17. J. Been, H. Lu, R. Eadie, G. Shen, R. Sutherby, "The Role of Stress Intensifiers in Near-Neutral pH Corrosion Fatigue of Line Pipe," CORROSION/2004, paper no. 04552 (Houston, TX: NACE, 2000).
18. National Energy Board of Canada, "Report of Public Inquiry Concerning Stress Corrosion Cracking on Canadian Oil and Gas Pipelines," MH-2-95, November 1996.
19. R.N. Parkins, J.A. Beavers, Corrosion 59 (2003): p. 258-273.
20. 2 on Near-Neutral pH Stress Corrosion Crack Propagation," CORROSION/2000, paper no. 356 (Houston, TX: NACE, 2000).
21. G. Gabetta, S. Diliberto, A. Bennardo, N. Mancini, Br. Corros. J. 36 (2001): p. 24-28.
22. F.P. Ford, "The Crack-Tip System and Its Relevance to the Prediction of Cracking in Aqueous Environments," eds. R.P. Gangloff, M.B. Ives, Proc. 1st Int. Conf. on Environment-Induced Cracking of Metals (Houston, TX: NACE, 1988), p. 139-165.
23. J.T. Evans, R.N. Parkins, Acta Metall. 24 (1976): p. 511-515.
24. T. Shoji, S. Suzuki, T. G. Ballinger, "Theoretical Prediction of SCC Growth Behavior-Threshold and Plateau Growth Rate," Proc. 7th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, held August 7-10 (Houston, TX: NACE, 1995), p. 881-892.
25. S. Suzuki, T. Shoji, Y.S. Yi, J. Kim, "Theoretical SCC Crack Growth Prediction Under Various Loading Modes in High Temperature Water," Proc. 8th Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems - Water Reactors, held August 10- 14 (LaGrange Park, IL: American Nuclear Society [ANSI, 1997), p. 695-703.
26. Q.J. Peng, J. Kwon, T. Shoji, J. Nucl. Mater. 324 (2004): p. 52-61.
27. R.N. Parkins, "Constant Strain Rate Stress Corrosion Testing," in NATO Advanced Study Institute on Stress Corrosion Cracking (Brussels, Begium: North Atlantic Treaty Organization [NATO], 1975), p. 28.
28. R.N. Parkins, "Development of Strain-Rate Testing and Its Implications," Proc. Stress Corrosion Cracking - The Slow Strain-Rate Technique, held May 2-4, 1977 (West Conshohocken, PA: ASTM International, 1979), p. 5-25.
29. J.H. Payer, W.E. Berry, R.N. Parkins, "Application of Slow Strain-Rate Technique to Stress Corrosion Cracking of Pipeline Steel," Proc. Stress Corrosion Cracking - The Slow Strain-Rate Technique, held May 2-4, 1977 (West Conshohocken, PA: ASTM International, 1979), p. 222-234.
30. R.N. Parkins, G.P. Marsh, J.T. Evans, "Strain Rate Effects in Environment Sensitive Fracture," in Proc. Predictive Methods for Assessing Corrosion Damage to BWR Piping and PWR Steam Generators, held May 28-June 2 (Houston, TX: NACE, 1978), p. 249-260.
31. ASTM Standard G129-00, "Standard Practice for Slow Strain Rate Testing to Evaluate the Susceptibility of Metallic Materials to Environmentally Assisted Cracking," in Annual Book of ASTM Standards (West Conshohocken, PA: ASTM International, 2000).
32. R.N. Parkins, "A Review of Stress Corrosion Cracking of High-Pressure Gas Pipelines," CORROSION/2000, paper no. 363 (Houston, TX: NACE, 2000).
33. R.R. Fessler, K. Krist, "Research Challenges Regarding Stress Corrosion Cracking of Pipelines," CORROSION/2000, paper no. 370 (Houston, TX: NACE, 2000).
34. M. Elboujdaini, Y.Z. Wang, R.W. Revie, "Initiation of Stress Corrosion Cracking on X-65 Linepipe Steels in Near-Neutral pH Environment," Int. Pipeline Conf. 2000 (New York, NY: ASME International, 2000), p. 967-978.
35. S.H. Wang, W. Chen, T. Jack, F. King, R.R. Fessler, K. Krist, "Role of Prior Cyclic Loading in the Initiation of Stress-Corrosion Cracks in Pipeline Steels Exposed to Near-Neutral pH Environment," Int. Pipeline Conf. 2000 (New York, NY: ASME International, 2000), p. 1,005-1,009.
36. R. King, R. Jack, W. Chen, S.H. Wang, M. Elboujdaini, W. Revie, R. Worthingham, P. Dusek, "Development of Predictive Model for the Initiation and Early-Stage Growth of Near-Neutral pH SCC of Pipeline Steels," CORROSION/2001, paper no. 01214 (Houston, TX: NACE, 2001).
37. T. Boellinghaus, E. Viyanit, H. Hoffmeister, "Numerical Modeling of Hydrogen-Assisted Cracking," CORROSION/2001, paper no. 01226 (Houston, TX: NACE, 2001).
38. NACE Publication 35103, "External Stress Corrosion Cracking of Underground Pipelines" (Houston, TX: NACE, 2003).
39. Department of Transportation, Research and Special Programs Administration, Office of Pipeline Safety, "Stress Corrosion Cracking Study (Final Report)," TTO number 8, Integrity Management Program, Delivery Order DTRS56-02-D-70036, January 2005.
40. M. Touzet, N. Lopez, M. Puiggali, "Effect of Applied Potential on Cracking of Low-Alloyed Pipeline Steel in Low pH Soil Environment," in Advances in Corrosion Control and Materials in Oil and Gas Production, EUROCORR'97 Corrosion Congress, held Sept. 22-25, 1997 (London, U.K.: Intstitute of Metals, 1999), p. 198-209.
41. D.W. Hoeppner, "Model for Prediction of Fatigue Lives Based Upon a Pitting Corrosion Fatigue Process," in Fatigue Mechanisms, ASTM STP 675, ed. J.T. Fong (West Conshohocken, PA: ASTM International, 1979), p. 841-870.
42. M. Muller, Metall. Trans. 13A (1982): p. 649-655.
43. Y. Kondo, Corrosion 45 (1989): p. 7-11.
44. G.S. Chen, K.C. Wan, M. Gao, R.P. Wei, T.H. Flournoy, Mater. Sci. Eng. A219 (1996): p. 126-132.
45. A. Turnbull, "Issues In Modeling of Environmentally Assisted Cracking," in Environmentally Assisted Cracking: Predictive Methods for Risk Assessment and Evaluation of Materials, Equipment, and Structures, ASTM STP 1401, ed. R.D. Kane (West Conshohocken, PA: ASTM International, 2000), p. 23-39.
46. R.N. Parkins, "Stress Corrosion Cracking," Proc. 1st Int. Conf. on Environment-Induced Cracking of Metals, eds. R.P. Gangloff, M.B. Ives, held Sept. (Houston, TX: NACE, 1998), p. 1-17.
47. J. Congleton, T. Shoji, R.N. Parkins, Corros. Sci. 25 (1985): p. 633-650.
48. Y.C. Gao, K.C. Hwang, "Elastic-Plastic Fields in Steady Crack Growth in a Strain Hardening Material," in Advances in Fracture Research, 5th Int. Conf. on Fracture, ed. D. Francois, Cannes, France, vol. 2 (Oxford, U.K.: Pergamon Press, 1981), p. 669-682.
49. W.W. Gerberich, D.L. Davidson, M. Kaczorowski, J. Mech. Phys. Solids 38 (1990): p. 87-113.
50. B. Fang, E.-H. Han, J. Wang, W. Ke, Acta Metall. Sinica 41 (2005): p. 1,173-1,182.
51. B. Fang, "Stress Corrosion Cracking of High-Strength Pipeline Steels in Near-Neutral pH Environments" (Ph.D. thesis, Institute of Metal Research, Chinese Academy of Sciences, May 2005).
52. R.H. Jones, Stress-Corrosion Cracking: Materials Performance and Evaluation (Materials Park, OH: ASM International, 1992), p. 1-61.
53. B. Gu, W.Z. Yu, J.L. Luo, X. Mao, Corrosion 55 (1999): p. 312-318.
54. T.R. Jack, B. Erno, K. Krist, R.R. Fessler, "Generation of Near-Neutral pH and High pH SCC Environments on Buried Pipelines," CORROSION/2000, paper no. 362 (Houston, TX: NACE, 2000).
55. W. Chen, F. King, T. Jack, M.L. Wilmott, Metall. Mater. Trans. 33A (2002): p. 1,429-1,437.