Effects of O2 and CO2 on near-neutral-ph stress corrosion crack propagation

NACE - International Corrosion Conference Series

Volumn 2000-March, Issue , 2000, Pages

  Johnson, J T ^a   Durr, C L ^a   Beavers, J A ^a   Delanty, B S ^b  

^a CC Technologies USA   (United States)

^b TRANSCANADA PIPELINES LIMITED   (Canada)

Author keywords

Crack growth; Hydrogen permeation; Pipelines; Potentiodynamic polarization; Stress corrosion cracking

Indexed keywords

CARBON DIOXIDE; CORROSION RATE; CRACK PROPAGATION; CRACKS; CYCLIC LOADS; ELECTROCHEMICAL CORROSION; ELECTROLYTES; GROWTH KINETICS; HYDROGEN; PERMEATION; PIPELINE CORROSION; PIPELINES; POLARIZATION; POTENTIODYNAMIC POLARIZATION; RESIDUAL STRESSES; STEEL CORROSION;

CORROSION POTENTIALS; CRACK GROWTH BEHAVIOR; CRACK GROWTH TESTS; CYCLIC GROWTH; CYCLIC LOADING TEST; HYDROGEN PERMEATION; LINEPIPE STEEL; NEAR-NEUTRAL PH;

STRESS CORROSION CRACKING;

EID: 84882767872     PISSN: 03614409     EISSN: None     Source Type: Book Series    
DOI: None     Document Type: Conference Paper

References (12)

1. R. L. Wenk, "Field Investigation of Stress Corrosion Cracking", 5th Symposium on Line Pipe Research, American Gas Association. Inc., Catalog No. L30174, p. T-1. 1974.
2. J. M. Sutcliffe, R. R. Fessier, W. K. Boyd, and R. N. Parkins. "Stress Corrosion Cracking of Carbon Steel in Carbonate Solutions", Corrosion. Vol 28, p. 313, 1972.
3. J. T. Justice and J. D. Mackenzie. "Progress in the Control of Stress Corrosion Cracking in a 914 mm O. D. Gas Transmission Pipeline", Proceedings of the NG-18/EPRG Seventh Biennial Joint Technical Meeting on Line Pipe Research, Pipeline Research Committee of the American Gas Association, Paper No. 28, 1988.
4. B. S. Delanty and J. E. Marr. "Stress Corrosion Cracking Severity Rating Model", International Conference on Pipeline Reliability, Calgary, Alberta, CANMET, June 1992.
5. M. Urednicek, S. Lambert. and O. Vosikovski. "Stress Corrosion Cracking - Monitoring and Control", International Conference on Pipeline Reliability, Calgary, Alberta, CANMET, June 1992.
6. ASTM Standard G 61-86, Standard Practice for Conducting Potentiodynamic Polarization Measurements for Localized Corrosion, American Society for Testing and Materials, Philadelphia. 1995.
7. ASTM Standard G 5-94. Standard Reference Test Method for Making Potentiostatic and Potentiodynamic Anodic Polarization Measurements, American Society for Testing and Materials, Philadelphia. 1995.
8. M. A. V. Devanathan and L. Stachurski, Proc. Roy. Soc. (London), A270, 90, 1962.
9. J. A. Beavers. and E. L. Hagerdorn. "Low-pH SCC: Mechanical Effects On Cracking Propagation", PRCI Project 186-9402, September 1996.
10. ASTM Standard E 647-88a, Standard Test Method of Fatigue Crack Growth Rates, American Society for Testing and Materials, Philadelphia, 1991.
11. Beavers. J. A. and Harle. B. A., "Mechanisms of High-pH and Near-Neutral-pH SCC of Underground Pipelines." ASME B International Pipeline Conference; Calgary, Alberta Canada, June 1996. Paper No. IPC 96408.
12. Beavers. J. A. and C. E. Jaske. "Near-Neutral pH SCC In Pipelines: Effects Of Pressure Fluctuations On Crack Propagation. " Corrosion NACExpo 98, NACE International. San Diego, CA. Paper No. 257, March 1998.