Localized dissolution of millscale-covered pipeline steel surfaces

Corrosion

Volumn 60, Issue 10, 2004, Pages 906-914

  Qin, Z ^a   Demko, B ^a   Noel J ^a   Shoesmith, D ^a   King, F ^b   Worthingham, R ^c   Keith, K ^c  

^a UNIVERSITY OF WESTERN ONTARIO   (Canada)

^b NOVA CHEMICALS CORPORATION   (Canada)

^c TRANSCANADA PIPELINES LIMITED   (Canada)

Author keywords

Localized corrosion; Millscale; Pipeline steel; Pores; Stress corrosion cracking

Indexed keywords

CORROSION; DISSOLUTION; ENERGY DISPERSIVE SPECTROSCOPY; POLARIZATION; RAMAN SPECTROSCOPY; SCANNING ELECTRON MICROSCOPY; STEEL; STRESS CORROSION CRACKING;

CORROSION POTENTIALS; POLARIZATION RESISTANCE; SOLUTION RESISTANCE; SURFACE ANALYSIS;

PIPELINES;

ELECTROCHEMICAL CORROSION; PIPELINE; STEEL; STRESS CORROSION CRACKING;

EID: 7244243961     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3287824     Document Type: Article

References (20)

1. R.N. Parkins, "The Controlling Parameters in Stress Corrosion Cracking," Proc. of 5th Symp. on Line Pipe Research, paper no. 5 (Arlington, VA: American Gas Association Inc., 1974), p. U1.
2. P.J. Kentish, Br. Corros. J. 20 (1985): p. 139.
3. B. Delanty, J. O'Beirne, Oil Gas J. 6, 15 (1992): p. 39.
4. F. King, W. Chen, "Surface Characteristics of Pipeline Steel under Non-Disbonded Polyethylene Tape Coating," Nova Research & Technology Corporation Report 01359 (2000).
5. X. Liu, X. Mao, Scr. Metall. Mater. 33 (1995): p. 145.
6. J.J. Perdomo, I. Song, Corros. Sci. 42 (2000): p. 1,389.
7. J.J. Perdomo, M.E. Chabica, I, Song, Corros. Sci. 43 (2001): p. 515.
8. M. Pourbaix, Atlas of Electrochemical Equilibria in Aqueous Solution (Oxford, U.K.: Pergamon Press, 1966), p. 308.
9. U.R. Evans, Proc. R. Soc. A 107 (1925): p. 228.
10. M.J. Pryor, U.R. Evans, J. Chem. Soc. (1950): p. 1,259.
11. D.S. Mancey, "The Dissolution of Magnetite Films from Carbon Steel Surfaces" (Ph.D. thesis, Univ. of Manitoba, Canada, 1985).
12. D.W. Shoesmith, W. Lee, D.S. Owen, Power Industry Res. 1 (1981): p. 253.
13. T.R. Jack, F. King, L. Yang, R. Sutherby, "Kinetic Isotope Effects in the Corrosion and Hydrogen Loading of Line Pipe Steel: Implications for Stress Corrosion Cracking," Proc. Environmental Degradation of Materials and Corrosion Control in Metals, eds. J. Luo, M. Elboujdaini, D. Shoesmith, P.C. Patnaik (Montreal, PQ: Canadian Inst. of Mining, Metallurgy, and Petroleum, 2003), p. 205.
14. G.J. Brug, A.L.G. Van Den Eeden, M. Sluyters-Rehbach, J.H. Sluyters, J. Electroanal. Chem. 176 (1984): p. 275.
15. I. Frateur, C. Deslouis, M.E. Orazem, B. Tribollet, Electrochim. Acta 44 (1999): p. 4,345.
16. M. Sfaira, A. Srhiri, H. Takenouti, M. Marie de Ficquelmont-Loizos, A. Ben Bachir, M. Khlakhil, J. Appl. Electrochem. 31 (2001): p. 537.
17. B.R. Linder, G.T. Burstein, Corros. Sci. 41 (1999): p. 117.
18. E.B. Castro, J.R. Vilche, A.J. Arvia, Corros. Sci. 32 (1991): p. 37.
19. R.N. Parkins, E. Belhimer, W.K. Blanchard, Corrosion 49 (1993): p. 951.
20. H. Asahi, T. Kushida, M. Kimura, H. Fukai, S. Okano, Corrosion 55 (1999): p. 644.