Effect of Microstructure on the stress corrosion cracking of X-80 pipeline steel in diluted sodium bicarbonate solutions

Corrosion

Volumn 58, Issue 7, 2002, Pages 584-590

  Gonzalez Rodriguez, J G ^a   Casales, M ^a   Salinas Bravo, V M ^a   Albarran, J L ^a   Martinez, L ^a  

^a UNIVERSIDAD AUTÓNOMA DEL ESTADO DE MORELOS   (Mexico)

Author keywords

Anodic dissolution; Bicarbonate; Stress corrosion cracking; X 80 pipeline steel

Indexed keywords

CORROSION RESISTANCE; CRACK INITIATION; DISSOLUTION; HEAT TREATMENT; MICROSTRUCTURE; QUENCHING; SODIUM COMPOUNDS; STEEL; STRAIN RATE; STRESS CORROSION CRACKING;

STRAIN RATE TESTING;

PIPELINES;

AQUEOUS SOLUTION; MICROSTRUCTURE; SODIUM CARBONATE; STEEL PIPE; STRESS CORROSION CRACKING;

EID: 0036629311     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3277649     Document Type: Article

References (17)

1. Progress in the control of stress corrosion cracking in a 914-mm OD gas transmission pipeline
2. Mechanism of high-pH and near-neutral-pH SCC of underground pipelines
3. The controlling parameters in stress corrosion cracking
4. ISCC values influenced SSC susceptibility of materials