Effect of Solution Composition and Electrochemical Potential on Stress Corrosion Cracking of X-52 Pipeline Steel

Corrosion (Houston)

Volumn 52, Issue 5, 1996, Pages 396-405

  Rebak, R B ^a,b   Xia, Z ^c   Safruddin, R ^c   Szklarska Smialowska, Z ^a  

^a Ohio State University   (United States)

^b HAYNES INTERNATIONAL INC   (United States)

^c NONE

Author keywords

Bending; Bicarbonate; Carbon steel; Cold work; Electrochemical potential; Gas pipelines; Hydrogen embrittlement; pH; Soil; Stress corrosion cracking; Sulfate

Indexed keywords

BENDING (DEFORMATION); CARBON STEEL; CARBONATES; COLD WORKING; COMPOSITION EFFECTS; ELECTROCHEMISTRY; GAS PIPELINES; HYDROGEN EMBRITTLEMENT; PH; SOILS; SOLUTIONS; STEEL PIPE;

ANODIC POTENTIAL; AQUEOUS SULFATE; BICARBONATE; CATHODIC POTENTIAL; CONSTANT EXTENSION RATE TESTS; CORROSION POTENTIAL; ELECTROCHEMICAL POTENTIAL; METAL DISSOLUTION; TRANSGRANULAR CRACKING;

STRESS CORROSION CRACKING;

EID: 0000312637     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3292126     Document Type: Article

References (27)

1. H.E. Townsend Jr., MP 11, 10 (1972): p. 33.
2. R.L. Wenk, "Field Investigation of Stress Corrosion Cracking," 5th Symp. Line Pipe Research 2 (Arlington, VA: American Gas Association, 1974), p. T-1.
3. P.J. Kentish, Brit. Corros. J. 20 (1985): p. 139.
4. B. Delanty, J. O'Beirne, Oil Gas J. June 15 (1992): p. 39.
5. R.N. Parkins, "Conceptual Understanding and Life Prediction for SCC of Pipelines," In Research Topical Symposia (Houston, TX: NACE, 1996), p. 1.
6. J.M. Sutcliffe, R.R. Fessier, W.K. Boyd, R.N. Parkins, Corrosion 28 (1972): p. 313.
7. R.N. Parkins, B.S. Greenwell, Met. Sci. 11 (1977): p. 405.
8. T.J. Barlo "Stress Corrosion Cracking Steel Susceptibility," 6th Symp. Line Pipe Research (Arlington, VA: American Gas Association, 1979).
9. R.R. Fessler "Stress Corrosion Cracking Temperature Effects," 6th Symp. Une Pipe Research (Arlington, VA: American Gas Association, 1979), p. R-1 to R-10.
10. J.A. Beavers, W.E. Berry, R.N. Parkins, MP 25, 6 (1986): p. 9.
11. J.A. Beavers, R.N. Parkins, "Recent Advances in Understanding Factors Affecting Stress Corrosion Cracking of Line Pipe Steels," 7th Symp. Line Pipe Research (Arlington, VA: American Gas Association, 1986), p. 25-1 to 25-13.
12. J.A. Beavers, T.K. Christman, R.N. Parkins, MP 27, 4 (1988): p. 22.
13. R.N. Parkins, A.J. Markworth, J.H. Holbrook, Corrosion 44 (1988): p. 572.
14. T.K. Christman, Corrosion 46 (1990): p. 450.
15. R.N. Parkins, P.M. Singh, Corrosion 46 (1990): p. 485.
16. R.N. Parkins, E. Belhimer, W.K. Blanchard Jr., Corrosion 49 (1993): p. 951.
17. B.A. Harle, J.A Beavers, Corrosion 49 (1993): p. 861.
18. Z. Szklarska-Smialowska, Z. Xia, R.B. Rebak, Corrosion 50 (1994): p. 334.
19. R.N. Parkins, W.K. Blanchard Jr., B.S. Delanty, Corrosion 50 (1994): p. 394.
20. M. Urednicek, S. Lambert O. Vosikovsky, "Stress Corrosion Cracking Monitoring and Control," paper no. 7-2, Et. Conf. Pipeline Reliability, Calgary, Canada, June 1992 (Houston, TX: GALS Publishing Co., 1992).
21. R.B. Rebak, Z. Xia, R Safruddin, Z. Szklarska-Smialowska, "Electrochemical Processes Controlling SCC of Underground Pipelines," CORROSION/95, paper no. 184 (Houston, TX: NACE, 1995).
22. W. Zheng, R.W. Revie, F.A. MacLeod, D. Kiff, S. Rajan, "Testing Methods for Low-pH Pipeline SCC: A Comparison of SSRT and Full-Scale Testing," CORROSION/95, paper no. 187 (Houston, TX: NACE, 1995).
23. B.A. Harle, J.A. Beavers, C.E. Jaske, "Mechanical and Metallurgical Effects on Low-pH Stress Corrosion Cracking of Natural Gas Pipelines," CORROSION/95, paper no. 646 (Houston, TX: NACE, 1995).
24. N. Totsuka, E. Lunarska, G. Cragnolino, Z. Szklarska-Smialowska, Scrip. Metal. 20 (1986): p. 1,035.
25. X. Liu, X. Mao, R.W. Revie, "Pitting Corrosion Behavior of Pipeline Steel in Solutions with Coating Disbonded Area Chemistry and in Bicarbonate Solutions. Proc. 12th Int. Corros. Cong., Sept. 19-24, 1993, vol. 4 (Houston TX: NACE, 1993), p. 2,831.
26. R.S. Treseder, T.M. Swanson, Corrosion 24 (1968): p. 31.
27. R.N. Tutfle, MP 9, 9 (1970): p. 11.