Some effects of strain rate on the transgranular stress corrosion cracking of ferritic steels in dilute near-neutral-pH solutions

Corrosion

Volumn 59, Issue 3, 2003, Pages 258-273

  Parkins, R N ^a   Beavers, J A ^b  

^a NEWCASTLE UNIVERSITY   (United Kingdom)

^b CC Technologies USA   (United States)

Author keywords

Near neutral pH solutions; Pipeline steels; Strain rate effects; Stress corrosion cracking

Indexed keywords

CRACK PROPAGATION; CYCLIC LOADS; DISSOLUTION; FERRITE; HYDROGEN; PH EFFECTS; SOLUTIONS; STEEL METALLOGRAPHY; STRAIN RATE;

OPEN-CIRCUIT VALUES;

STRESS CORROSION CRACKING;

CORROSION INHIBITOR; CRACKING; PH; PIPELINE; STEEL; STRESS;

EID: 0037354962     PISSN: 00109312     EISSN: None     Source Type: Journal    
DOI: 10.5006/1.3277559     Document Type: Article

References (39)

1. R.D. Kane, ed., ASTM STP 1210. "Slow Strain Rate Testing for the Evaluation of Environmentally Induced Cracking: Research and Engineering Applications" (West Conshohocken. PA: ASTM International, 1993).
2. R.N. Parkins, W.K. Blanchard, Jr., B.S. Delanty, Corrosion 50 (1994): p. 394.
3. R.C. Newman, Corrosion Chemistry Within Pits. Crevices, and Cracks, ed. A. Turnbull (London, England: HMSO, 1987), p. 317.
4. M.A.V. Devanathan, Z. Stachurski. Proc. Roy. Soc. London A270 (1962): p. 90.
5. E.A. Charles, R.N. Parkins, Corrosion 51 (1995): p. 518.
6. R.A. Oriani, Acta Metall. 18 (1970): p. 147.
7. P.L. Andresen, F.P. Ford, Proc. CORROSION/96. Research Topical Symposia, Part 1. Life Prediction of Structures Subject to Environmental Degradation (Houston, TX: NACE International. 1996), p. 51.
8. B.R. Linter, G.T. Burstein, Corros. Sci. 41 (1999): p. 117.
9. T. Boellinghaus, E. Viyanit, H. Hoffmeister, "Numerical Modelling of Hydrogen-Assisted Cracking." CORROSION/2001. paper no. 226 (Houston, TX: NACE, 2001).
10. R.W.K. Honeycombe, The Plastic Deformation of Metals (London. England: Ed. Arnold, 1968), p. 152.
11. J.P. Hirth, "The Role of Hydrogen in Enhancing Plastic Instability and Degrading Fracture Toughness in Steels," Hydrogen Effects in Metals, eds. A.W. Thompson, N.R. Moody (Warrendale, PA: The Minerals, Metals and Materials Society, 1994), p. 507.
12. R.W. Revie, private communication. Natural Resources Canada. Materials Technology Laboratory, Ottawa (1999).
13. M. Elboujdaini, Y.-Z. Wang, R.W. Revie, R.N. Parkins, M.T. Shehata. "Stress Corrosion Crack Initiation Processes: Pitting and Microcrack Coalescence." CORROSION/2000. paper no. 379 (Houston, TX: NACE, 2000).
14. R.N. Parkins, B.S. Delanty, "The Initiation and Early Stages of Growth of Stress Corrosion Cracks in Pipeline Steel Exposed to a Dilute. Near-Neutral-pH Solution," 9th Symp. Pipeline Research of PRCI, catalog no. L51746, paper no. 19 (Arlington, VA: American Gas Association, 1996), p. 19-1.
15. S. Zhou, A. Turnbull, Fatigue Fract. Eng. Mater. Struct. 22 (1999): p. 1,083.
16. J. Congleton, T. Shoji, R.N. Parkins, Corros. Sci. 25 (1985): p. 633.
17. L.L. Shreir, R.A. Jarman, G.T. Burstein. Corrosion, 3rd ed., vol. 1 (Oxford, U.K.: Butterworth-Heinemann, Ltd., 1994), p. 1:179.
18. R.B. Diegle, D.A. Vermilyea, J. Electrochem. Soc. 122 (1975): p. 180.
19. G.M. Pressouyre, I.M. Bernstein, Metall. Trans. A 9A (1978): p. 1,571.
20. B.G. Pound, R.M. Sharp, G.A. Wright. Acta Metall. 35 (1987): p. 263.
21. Z. Szklarska-Smialowska, Z. Xia, Corros. Sci. 39 (1997): p. 2,171.
22. A. Turnbull, M.W. Carroll. Corros. Sci. 30 (1990): p. 667.
23. R.C. Frank, in Internal Stresses and Fatigue in Metals, eds. G.M. Rassweiler, W.L. Grube (New York, NY: Elsevier, 1959). p. 411.
24. J.A. Donovan. Metall. Trans. A 7A (1976): p. 145.
25. J.P. Hirth, Metall. Trans. 11A (1980): p. 861.
26. J.A. Beavers, C.L. Durr, S.S. Shademan. "Mechanistic Studies of Near-Neutral-pH SCC on Underground Pipelines." in Materials for Resource Recovery and Transport, ed. L. Collins (Quebec, Canada: Canadian Institute of Mining, Metallurgy, and Petroleum, 1998), p. 51.
27. R.P. Gangloff, B.P. Somerday, D. Cooke, "Understanding Crack Tip Strain Rate Effects in Hydrogen Embrittlement for Improved Fitness-for-Service Modeling." Proc. CORROSION/96. Research Topical Symposia (Houston, TX: NACE, 1996). p. 161.
28. T. Shoji, S. Suzuki, R.G. Ballinger, "Theoretical Prediction of SCC Growth Behavior·: Proc. 7th Int. Symp. Environmental Degradation of Materials in Nuclear Power Plants (Houston, TX: NACE, 1995). p. 881.
29. P.M. Scott, A.E. Truswell, "Corrosion Fatigue Crack Growth in Reactor Pressure Vessel Steels-Measurement and Application." in Structural Integrity of Light Water Reactor Components, ed. L.E. Steels (London, England: Applied Science Publications, 1982), p. 287.
30. W. Zheng, R.W. Revie, O. Dinardo, F.A. MacLeod, W.R. Tyson, R.D. Kiff, "Pipeline SCC in Near-Neutral-pH Environment: Effects of Environmental and Metallurgical Variables." 9th Symp. Pipeline Research of PRCI, catalog no. L51746, paper no. 22 (Arlington, VA: American Gas Association, 1996), p. 22-1.
31. J.A. Beavers, E.L. Hagerdorn, "Near-Neutral-pH SCC: Mechanical Effects on Crack Propagation." 9th Symp. Pipeline Research of PRCI, catalog no. 151746. paper no. 24 (Arlington, VA: American Gas Association, 1996), p. 24-1.
32. X.-Y. Zhang, S.B. Lambert, R. Sutherby, A. Plumtree, Corrosion 55 (1999): p. 297.
33. E. Senigallia, M. Pontremoll, "Test Methodologies for the Study of Near-Neutral Stress Corrosion Cracking in Pipeline Steels (EPRG)." 12th Biennial Joint Technical Meeting on Pipeline Research, paper no. (European Pipeline Research Group. Corrosion Subcommittee, EPRG/PRCI, 1999), p. 9-1.
34. J.A. Beavers, C.E. Jaske, "Effects of Pressure Fluctuations on SCC Propagation." paper no. PR-186-9706, report to Pipeline Research Council International, Inc., Arlington, VA (December 2000).
35. P. Andrews, M. McQueen, N. Millwood, Corrosion 57 (2001): p. 721.
36. "Public Inquiry Concerning Stress Corrosion Cracking on Canadian Oil and Gas Pipelines." National Energy Board, MH-2-95 (Alberta, Canada: National Energy Board, November, 1996). p. 85.
37. B.N. Leis, R.N. Parkins, Fatigue Fract. Eng. Mater. Struct. 21 (1998): p. 583.
38. G. Gabetta, S. Di Liberto, A. Bennardo, N. Mancini, Br. Corros. J. 36 (2001): p. 24.
39. B.A. Harle, J.A. Beavers, C.E. Jaske, "Low-pH Stress Corrosion Cracking of Natural Gas Pipelines." Canadian Western Region Conference (Houston, TX: NACE, 1994), p. 473.