Contact damage in brittle coating layers: Influence of surface curvature

Journal of Biomedical Materials Research - Part B Applied Biomaterials

Volumn 73, Issue 1, 2005, Pages 179-185

  Qasim, Tarek ^a   Bush, Mark B ^a   Hu, Xiaozhi ^a   Lawn, Brian R ^b  

^a UNIVERSITY OF WESTERN AUSTRALIA   (Australia)

^b NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

Author keywords

Brittle layers; Contact damage; Crown failure; Curved surfaces; Radial cracks

Indexed keywords

BRITTLENESS; COMPUTER SIMULATION; CRACKS; DENTAL MATERIALS; DIES; FILLERS; FRACTURE; POLYMERS; STEEL; STRESS ANALYSIS; SUBSTRATES;

BRITTLE COATING LAYERS; DENTAL CROWN STRUCTURES; EPOXY FILLERS; POLYMERIC SUBSTRATES;

COATINGS;

GLASS; POLYMER;

ARTICLE; CALCULATION; CERAMICS; DENTIN; ENAMEL; EVALUATION; FINITE ELEMENT ANALYSIS; MATERIAL COATING; SIMULATION; STRENGTH; SURFACE PROPERTY; THICKNESS; TOOTH CROWN;

BIOCOMPATIBLE MATERIALS; CERAMICS; CROWNS; DENTAL MATERIALS; DENTAL PORCELAIN; DENTAL PROSTHESIS DESIGN; DENTAL RESTORATION FAILURE; DENTAL RESTORATION WEAR; DENTAL VENEERS; DENTIN; EPOXY RESINS; GLASS; MATERIALS TESTING; MICROSCOPY, VIDEO; SURFACE PROPERTIES;

EID: 16444364441     PISSN: 00219304     EISSN: None     Source Type: Journal    
DOI: 10.1002/jbm.b.30188     Document Type: Article

References (30)

1. Peterson IM, Pajares A, Lawn BR, Thompson VP, Rekow ED. Mechanical characterization of dental ceramics using hertzian contacts. J Dent Res 1998;77:589-602.
2. Jung YG, Wuttiphan S, Peterson IM, Lawn BR. Damage modes in dental layer structures. J Dent Res 1999;78:887-897.
3. Lawn BR, Lee KS, Chai H, Pajares A, Kim DK, Wuttiphan S, Peterson IM, Hu X. Damage-resistant brittle coatings. Adv Eng Mater 2000;2:745-748.
4. Lawn BR. Ceramic-based layer structures for biomechanical applications. Curr Opin Solid State Mater Sci 2002;6:229-235.
5. Lawn BR, Deng Y, Miranda P, Pajares A, Chai H, Kim DK. Overview: Damage in brittle layer structures from concentrated loads. J Mater Res 2002;17:3019-3036.
6. Deng Y, Lawn BR, Lloyd IK. Characterization of damage modes in dental ceramic bilayer structures. J Biomed Mater Res 2002;63B:137-145.
7. Shrotriya P, Wang R, Katsube N, Seghi R, Soboyejo WO. Contact damage in model dental multilayers: An investigation of the influence of indenter size. J Mater Sci Mater Med 2003;14:17-26.
8. Lawn BR, Pajares A, Zhang Y, Deng Y, Polack M, Lloyd IK, et al. Materials design in the performance of all-ceramic crowns. Biomaterials 2004;25:2885-2892.
9. Kelly JR. Ceramics in restorative and prosthetic dentistry. Annu Rev Mater Sci 1997;27:443-468.
10. Kelly JR. Clinically relevant approach to failure testing of all-ceramic restorations. J Prosthet Dent 1999;81:652-661.
11. Malament KA, Socransky SS. Survival of dicor glass-ceramic dental restorations over 14 years: I. Survival of dicor complete coverage restorations and effect of internal surface acid etching, tooth position, gender and age. J Prosthet Dent 1999;81:23-32.
12. Malament KA, Socransky SS. Survival of dicor glass-ceramic dental restorations over 14 years: II. Effect of thickness of dicor material and design of tooth preparation. J Prosthet Dent 1999;81:662-667.
13. Malament KA, Socransky SS. Survival of dicor glass-ceramic dental restorations over 16 years: Part III: Effect of luting agent and tooth or tooth-substitute core structure. J Prosthet Dent 2001;86:511-519.
14. Wuttiphan S. Contact damage and fracture of ceramic layer structures. PhD thesis Dissertation, University of Maryland, 1997.
15. Chai H, Lawn BR, Wuttiphan S. Fracture modes in brittle coatings with large interlayer modulus mismatch. J Mater Res 1999;14:3805-3817.
16. Zhao H, Hu XZ, Bush MB, Lawn BR. Contact damage in porcelain/Pd-alloy bilayers. J Mater Res 2000;15:676-682.
17. Zhao H, Hu X, Bush MB, Lawn BR. Cracking of porcelain coatings bonded to metal substrates of different modulus and hardness. J Mater Res 2001;16:1471-1478.
18. Lee C-S, Lawn BR, Kim DK. Effect of tangential loading on critical conditions for radial cracking in brittle coatings. J Am Ceram Soc 2001;84:2719-2721.
19. Miranda P, Pajares A, Guiberteau F, Cumbrera FL, Lawn BR. Contact fracture of brittle bilayer coatings on soft substrates. J Mater Res 2001;16:115-126.
20. Zhao H, Miranda P, Lawn BR, Hu X. Cracking in ceramic/ metal/polymer trilayer systems. J Mater Res 2002;17:1102-1111.
21. Lee C-S, Kim DK, Sanchez J, Miranda P, Pajares A, Lawn BR. Rate effects in critical loads for radial cracking in ceramic coatings. J Am Ceram Soc 2002;85:2019-2024.
22. Ford C, Bush MB, Hu XZ, Zhao H. A Numerical study of fracture modes in contact damage in porcelain/Pd-alloy bilayers. Mater Sci Eng 2004;A364:202-206.
23. Lawn BR, Deng Y, Thompson VP. Use of contact testing in the characterization and design of all-ceramic crown-like layer structures: A review. J Prosthet Dent 2001;86:495-510.
24. Rhee Y-W, Kim H-W, Deng Y, Lawn BR. Contact-induced damage in ceramic coatings on compliant substrates: fracture mechanics and design. J Am Ceram Soc 2001;84:1066-1072.
25. Zhang Y, Lawn BR, Rekow ED, Thompson VP. Effect of sandblasting on the long-term strength of dental ceramics. J Biomed Mater Res 2004;71B:381-386.
26. Fischer-Cripps AC, Lawn BR, Pajares A, Wei L. Stress analysis of elastic-plastic contact damage in ceramic coatings on metal substrates. J Am Ceram Soc 1996;79:2619-2625.
27. Kim H-W, Deng Y, Miranda P, Pajares A, Kim DK, Kim H-E, et al. Effect of flaw state on the strength of brittle coatings on soft substrates. J Am Ceram Soc 2001;84:2377-2384.
28. Zhang Y, Lawn BR. Long-term strength of ceramics for biomedical applications. J Biomed Mater Res 2004;69B: 166-172.
29. Zhang Y, Pajares A, Lawn BR. Fatigue and damage tolerance of Y-TZP ceramics in layered biomechanical systems. J Biomed Mater Res 2004;71B:166-171.
30. Willmann G. Ceramic femoral heads for total hip arthroplasty. Adv Eng Mater 2000;2:114-122.