Synthesis of Porous Emulsion-Templated Polymers Using High Internal Phase CO2-in-Water Emulsions

Journal of the American Chemical Society

Volumn 125, Issue 47, 2003, Pages 14473-14481

  Butler, R ^a   Hopkinson, I ^b   Cooper, A I ^a  

^a UNIVERSITY OF LIVERPOOL   (United Kingdom)

^b UNIVERSITY OF MANCHESTER   (United Kingdom)

Author keywords

[No Author keywords available]

Indexed keywords

BIOMATERIALS; MONOMERS; ORGANIC SOLVENTS; POLYAMIDES; POROSITY; REDOX REACTIONS; SURFACE ACTIVE AGENTS; VISCOSITY;

EMULSION STABILITY; PORE DIAMETER;

EMULSIONS;

CARBON DIOXIDE; POLYACRYLIC ACID; POLYMER; WATER;

AQUEOUS SOLUTION; ARTICLE; EMULSION; MOLECULAR STABILITY; OXIDATION REDUCTION REACTION; PHASE TRANSITION; POLYMERIZATION; POROSITY; PURIFICATION; SYNTHESIS; TEMPERATURE; VISCOSITY;

EID: 0345306278     PISSN: 00027863     EISSN: None     Source Type: Journal    
DOI: 10.1021/ja037570u     Document Type: Article

References (47)

1. Cameron. N. R.; Sherrington, D. C. Adv. Polym. Sci. 1996, 126, 163-214.
2. Ruckenstein, E. Adv. Polym. Sci. 1997, 127, 1-58.
3. Cameron, N. R.; Sherrington, D. C.; Albiston, L.; Gregory, D. P. Colloid Polym. Sci. 1996, 274, 592-595.
4. Barbetta, A.; Cameron, N. R.; Cooper, S. J. Chem. Commun. 2000, 221-222.
5. Imhof, A.; Pine, D. J. Nature 1997, 389, 948-951.
6. Imhof, A.; Pine, D. J. Adv. Mater. 1999, 11, 311-314.
7. Schmidt-Winkel, P.; Lukens, W. W.; Yang, P. D.; Margolese, D. I.; Lettow, J. S.; Ying, J. Y.; Stucky, G. D. Chem. Mater. 2000, 12, 686-696.
8. Manoharan, V. N.; Imhof, A.; Thorne, J. D.; Pine, D. J. Adv. Mater. 2001, 13, 447-450.
9. Yu, C. Z.; Tian, B. H.; Fan, J.; Stucky, G. D.; Zhao, D. Y. Chem. Lett. 2002, 62-63.
10. Tai, H,; Sergienko, A.; Silverstein, M. S. Polymer 2001, 42, 4473-4482.
11. Zhang, H.; Cooper, A. I. Chem. Mater. 2002, 14, 4017-4020.
12. Zhang, H.; Hardy, G.; Rosseinsky, M. J.; Cooper, A. I. Adv. Mater. 2003, 15, 78-81.
13. DeSimone, J. M. Science 2002, 297, 799-803.
14. DeSimone, J. M.; Guan, Z.; Elsbemd, C. S. Science 1992, 257, 945-947.
15. DeSimone, J. M.; Maury, E. E.; Menceloglu, Y. Z.; McClain, J. B.; Romack, T. J.; Combes, J. R. Science 1994, 265, 356-359.
16. (a) Cooper, A. I. J. Mater. Chem. 2000, 10, 207-234.
17. (b) Cooper, A. I. Adv. Mater. 2001, 13, 1111-1114.
18. Cooper, A. I. Adv. Mater. 2003, 15, 1049-1059.
19. Parks, K. L.; Beckman, E. J. Polym. Eng. Sci. 1996, 36, 2404-2416.
20. Parks, K. L.; Beckman, E. J. Polym. Eng. Sci. 1996, 36, 2417-2431.
21. Howdle, S. M.; Watson, M. S.; Whitaker, M. J.; Popov, V. K.; Davies, M. C.; Mandel, F. S.; Wang, J. D.; Shakesheff, K. M. Chem. Commun. 2001, 109-110.
22. (a) Cooper, A. I.; Holmes, A. B. Adv. Mater. 1999, 11, 1270-1274.
23. (b) Cooper, A. I.; Wood, C. D., Holmes, A. B. Ind. Eng. Chem. Res. 2000, 39, 4741-4744.
24. Wood, C. D.; Cooper, A. I. Macromolecules 2001, 34, 5-8.
25. Hebb, A. K.; Senoo, K.; Bhat, R.; Cooper, A. I. Chem. Mater. 2003, 15, 2061-2069.
26. Shi, C.; Huang, Z.; Kilic, S.; Xu, J.; Enick, R. M.; Beckman, E. J.; Carr, A. J.; Melendez, R. E.; Hamilton, A. D. Science 1999, 286, 1540-1543.
27. Butler, R.; Davies, C. M.; Cooper, A. I. Adv. Mater. 2001, 13, 1459-1463.
28. Lee, C. T.; Psathas, P. A.; Johnston, K. P.; deGrazia, J.; Randolph, T. W. Langmuir 1999, 15, 6781-6791.
29. Johnston, K. P.; Harrison, K. L.; Clarke, M. J.; Howdle, S. M.; Heitz, M. P.; Bright, F. V.; Carlier, C.; Randolph, T. W. Science 1996, 271, 624-626.
30. Lee, C. T.; Ryoo, W.; Smith, P. G.; Arellano, J.; Mitchell, D. R.; Lagow, R. J.; Webber, S. E.; Johnston, K. P. J. Chem. Am. Soc. 2003, 125, 3181-3189.
31. Psathas, P. A.; da Rocha, S. R. P.; Lee, C. T.; Johnston, K. P.; Lim, K. T.; Webber, S. Ind. Eng. Chem. Res. 2000, 39, 2655-2664.
32. Not allowing for any shrinkage in the materials during drying.
33. The scatter in these data might be explained in part by the fact that these PVA samples had differing degrees of hydrolysis (see Supporting Information).
34. Cameron, N. R.; Barbetta, A. J. Mater. Chem. 2000, 10, 2466-2472.
35. da Rocha, S. R. P.; Psathas, P. A.; Klein, E.; Johnston, K. P. J. Colloid Interface Sci. 2001, 239, 241-253.
36. Lange, K. R. Surfactants: A Practical Handbook; Hanser Gardner Publications: Cincinnati, OH, 1999.
37. da Rocha, S. R. P.; Harrison, K. L.; Johnston, K. P. Langmuir 1999, 15, 419-428.
38. Zhou, W. J.; Yao, K. J.; Kurth, M. J. J. Appl. Polym. Sci. 1997, 64, 1001-1007.
39. See Supporting Information for electron micrographs.
40. Note that the salt concentration (arising from added initiator) was approximately 1.3 M, assuming complete dissociation-somewhat lower than the 2 M KBr concentration used in Johnston's studies.
41. Retama. J. R.; Lopez-Ruiz, B.; Lopez-Cabarcos, E. Biomaterials 2003, 24, 2965-2973.
42. Song, J.; Saiz, E.; Bertozzi, C. R. J. Am. Chem. Soc. 2003, 125, 1236-1243.
43. Luo, Y.; Dalton, P. D.; Shoichet, M. S. Chem. Mater. 2001, 13, 4087-4093.
44. Chiellini, F.; Bizzarri, R.; Ober, C. K.; Schmaljohann, D.; Yu, T. Y.; Solaro, R.; Chiellini, E. Macromol. Rapid Commun. 2001, 22, 1284-1287.
45. Husing, N.; Schubert, U. Angew. Chem. Int. Ed. 1998, 37, 23-45.
46. Cruise, G. M.; Scharp, D. S.; Hubbell, J. A. Biomaterials 1998, 19, 1287-1294.
47. Shin, H.; Temenoff, J. S.; Mikos, A. G. Biomacromolecules 2003, 4, 552-560.