Fatigue behavior in water of Y-TZP zirconia ceramics after abrasion with 30 μm silica-coated alumina particles

Dental Materials

Volumn 27, Issue 2, 2011, Pages

  Scherrer, Susanne S ^a   Cattani Lorente, Maria ^a   Vittecoq, Eric ^b   De Mestral, François ^b   Griggs, Jason A ^c   Wiskott, H W Anselm ^a  

^a UNIVERSITY OF GENEVA   (Switzerland)

^b UNIVERSITY OF APPLIED SCIENCES WESTERN SWITZERLAND   (Switzerland)

^c UNIVERSITY OF MISSISSIPPI MEDICAL CENTER   (United States)

Author keywords

Ceramics; Dental; Fatigue testing; Zirconia

Indexed keywords

ALUMINA PARTICLES; ALUMINA-SILICA; BEFORE AND AFTER; CERAMICS; CRITICAL FLAW; CYCLIC FATIGUE; DENTAL; FAILURE STRESS; FATIGUE BEHAVIOR; FATIGUE LIMIT; KAPLAN-MEIER; MEDIAN SURVIVAL; RANK TEST; RESIN CEMENT; S-N CURVE; SEM; SILICA-COATED; STATIC VALUES; STATISTICAL ANALYSIS; STRESS LEVELS; SURVIVAL ANALYSIS; ZIRCONIA CERAMIC; ZIRCONIA MATERIALS;

CEMENTS; CERAMIC MATERIALS; CRACK INITIATION; QUALITY ASSURANCE; RESINS; SILICA; STEEL BRIDGES; WATER TANKS; YTTRIUM ALLOYS; ZIRCONIA;

FATIGUE TESTING;

ALUMINUM OXIDE; SILICATE; SILICON DIOXIDE; WATER; YTTRIA STABILIZED TETRAGONAL ZIRCONIA; YTTRIUM; ZIRCONIUM; ZIRCONIUM OXIDE;

ARTICLE; CHEMISTRY; DENTAL CARE; DENTAL ETCHING; HUMAN; INSTRUMENTATION; MATERIALS TESTING; MECHANICAL STRESS; METHODOLOGY; PARTICLE SIZE; PHYSICAL CHEMISTRY; PLIABILITY; SCANNING ELECTRON MICROSCOPY; SURFACE PROPERTY; TOOTH PROSTHESIS; X RAY DIFFRACTION; YOUNG MODULUS;

ALUMINUM OXIDE; DENTAL ETCHING; DENTAL PORCELAIN; DENTAL STRESS ANALYSIS; ELASTIC MODULUS; HUMANS; MATERIALS TESTING; MICROSCOPY, ELECTRON, SCANNING; PARTICLE SIZE; PHYSICOCHEMICAL PHENOMENA; PLIABILITY; SILICATES; SILICON DIOXIDE; STRESS, MECHANICAL; SURFACE PROPERTIES; WATER; X-RAY DIFFRACTION; YTTRIUM; ZIRCONIUM;

EID: 78651261376     PISSN: 01095641     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.dental.2010.10.003     Document Type: Article

References (53)

1. J. Tinschert, D. Zwez, R. Marx, and K.J. Anusavice Structural reliability of alumina-, feldspar-, leucite-, mica- and zirconia-based ceramics J Dent 28 2000 529 535
2. J. Tinschert, G. Natt, W. Mautsch, M. Augthun, and H. Spiekermann Fracture resistance of lithium disilicate-, alumina-, and zirconia-based three-unit fixed partial dentures: a laboratory study Int J Prosthodont 14 2001 231 238
3. M. Guazzato, K. Proos, L. Quach, and M.V. Swain Strength, reliability and mode of fracture of bilayered porcelain/zirconia (Y-TZP) dental ceramics Biomaterials 25 2004 5045 5052
4. M. Guazzato, M. Albakry, S.P. Ringer, and M.V. Swain Strength, fracture toughness and microstructure of a selection of all-ceramic materials. Part II. Zirconia-based dental ceramics Dent Mater 20 2004 449 456
5. J.R. Kelly, and I. Denry Stabilized zirconia as a structural ceramic: an overview Dent Mater 24 2008 289 298
6. I. Denry, and J.R. Kelly State of the art of zirconia for dental applications Dent Mater 24 2008 299 307
7. R.C. Garvie, R.H. Hannink, and R.T. Pascoe Ceramic steel? Nature 258 1975 703 704
8. E.C. Subbarao Zirconia - an overview Adv Ceram 3 1981 1 13
9. C. Piconi, and G. Maccauro Zirconia as a ceramic biomaterial Biomaterials 20 1999 1 25
10. P.M. Kelly, and C.J. Ball Crystallography of stress-induced martensitic transformation in partially stabilized zirconia J Am Ceram Soc 65 1986 242 246
11. T. Kosmac, C. Oblak, P. Jevnikar, N. Funduk, and L. Marion The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic Dent Mater 15 1999 426 433
12. M. Guazzato, L. Quach, M. Albakry, and M.V. Swain Influence of surface and heat treatments on the flexural strength of Y-TZP dental ceramic J Dent 33 2005 9 18
13. T. Kosmac, C. Oblak, P. Jevnikar, N. Funduk, and L. Marion Strength and reliability of surface treated Y-TZP dental ceramics J Biomed Mater Res 53 2000 304 313
14. R.G. Luthardt, M. Holzhuter, O. Sandkuhl, V. Herold, J.D. Schnapp, and E. Kuhlisch Reliability and properties of ground Y-TZP-zirconia ceramics J Dent Res 81 2002 487 491
15. R.G. Luthardt, M.S. Holzhuter, H. Rudolph, V. Herold, and M.H. Walter CAD/CAM-machining effects on Y-TZP zirconia Dent Mater 20 2004 655 662
16. M. Kern, and S.M. Wegner Bonding to zirconia ceramic: adhesion methods and their durability Dent Mater 14 1998 64 71
17. M. Wolfart, F. Lehmann, S. Wolfart, and M. Kern Durability of the resin bond strength to zirconia ceramic after using different surface conditioning methods Dent Mater 23 2007 45 50
18. M.B. Blatz, G. Chiche, S. Holst, and A. Sadan Influence of surface treatment and simulated aging on bond strengths of luting agents to zirconia Quintessence Int 38 2007 745 753
19. M.B. Blatz, A. Sadan, J. Martin, and B. Lang In vitro evaluation of shear bond strengths of resin to densely-sintered high-purity zirconium-oxide ceramic after long-term storage and thermal cycling J Prosthet Dent 91 2004 356 362
20. B.K. Kim, H.E. Bae, J.S. Shim, and K.W. Lee The influence of ceramic surface treatments on the tensile bond strength of composite resin to all-ceramic coping materials J Prosthet Dent 94 2005 357 362
21. S.S. Atsu, M.A. Kilicarslan, H.C. Kucukesmen, and P.S. Aka Effect of zirconium-oxide ceramic surface treatments on the bond strength to adhesive resin J Prosthet Dent 95 2006 430 436
22. G. Akgungor, D. Sen, and M. Aydin Influence of different surface treatments on the short-term bond strength and durability between a zirconia post and a composite resin core material J Prosthet Dent 99 2008 388 399
23. Y. Zhang, B.R. Lawn, K.A. Malament, P. Van Thompson, and E.D. Rekow Damage accumulation and fatigue life of particle-abraded ceramics Int J Prosthodont 19 2006 442 448
24. Y. Zhang, A. Pajares, and B.R. Lawn Fatigue and damage tolerance of Y-TZP ceramics in layered biomechanical systems J Biomed Mater Res B: Appl Biomater 71 2004 166 171
25. Y. Zhang, B.R. Lawn, E.D. Rekow, and V.P. Thompson Effect of sandblasting on the long-term performance of dental ceramics J Biomed Mater Res B: Appl Biomater 71 2004 381 386
26. A.R. Curtis, A.J. Wright, and G.J. Fleming The influence of surface modification techniques on the performance of a Y-TZP dental ceramic J Dent 34 2006 195 206
27. H. Wang, M.N. Aboushelib, and A.J. Feilzer Strength influencing variables on CAD/CAM zirconia frameworks Dent Mater 24 2008 633 638
28. J. Chevalier, B. Cales, and J.M. Drouin Low-temperature aging of Y-TZP ceramics J Am Ceram Soc 82 1999 2150 2154
29. J. Chevalier What future for zirconia as a biomaterial? Biomaterials 27 2006 535 543
30. J. Chevalier, L. Gremillard, and S. Deville Low-temperature degradation of zirconia and implications for biomedical implants Annu Rev Mater Res 37 2007 1 32
31. A.R. Curtis, A.J. Wright, and G.J. Fleming The influence of simulated masticatory loading regimes on the bi-axial flexure strength and reliability of a Y-TZP dental ceramic J Dent 34 2006 317 325
32. A.R. Studart, F. Filser, P. Kocher, and L.J. Gauckler Fatigue of zirconia under cyclic loading in water and its implications for the design of dental bridges Dent Mater 23 2007 106 114
33. A.R. Studart, F. Filser, P. Kocher, and L.J. Gauckler In vitro lifetime of dental ceramics under cyclic loading in water Biomaterials 28 2007 2695 2705
34. E.C. Teixeira, J.R. Piascik, B.R. Stoner, and J.Y. Thompson Dynamic fatigue and strength characterization of three ceramic materials J Mater Sci Mater Med 18 2007 1219 1224
35. J. Tinschert, G. Natt, N. Mohrbotter, H. Spiekermann, and K.A. Schulze Lifetime of alumina- and zirconia ceramics used for crown and bridge restorations J Biomed Mater Res B: Appl Biomater 80 2007 317 321
36. E. Kaplan, and P. Meier Nonparametric estimation from incomplete observations J Am Stat Assoc 53 1958 457 481
37. J.R. Kelly Dental ceramics: current thinking and trends Dent Clin North Am 48 2004 513 530
38. G.D. Quinn Fractography of ceramics and glasses. A NIST recommended practice guide. Special Publication 960-16 May 2007 National Institute of Standards and Technology Washington, DC http://www.ceramics.nist.gov/pubs/ practice.htm
39. S.S. Scherrer, J.R. Kelly, G.D. Quinn, and K. Xu Fracture toughness (KIc) of a dental porcelain determined by fractographic analysis Dent Mater 15 1999 342 348
40. F.F. Lange Powder processing science and technology for increased reliability J Am Ceram Soc 72 1989 3 15
41. F.F. Lange, and M. Metcalf Processing-related fracture origins: II. Agglomerate motion and cracklike internal surfaces caused by differential sintering J Am Ceram Soc 66 1983 398 406
42. D.W. Richerson Modern ceramic engineering. properties, processing, and use in design 1992 Marcel Dekker, Inc. New York
43. G.D. Quinn, and L.K. Ives On the nature of machining cracks in ground ceramics: Part I. SRBSN strengths and fractographic analysis Machining Sci Technol 9 2005 169 210
44. J.J. Mecholsky Jr., S.W. Freiman, and R.W. Rice Effect of grinding on flaw geometry and fracture of glass J Am Ceram Soc 60 1977 114 117
45. S.Y. Liu, and I.W. Chen Fatigue of yttria-stabilized zirconia: I. Fatigue damage, fracture origins, and lifetime prediction J Am Ceram Soc 74 1991 1197 1205
46. J. Chevalier, S. Deville, E. Munch, R. Jullian, and F. Lair Critical effect of cubic phase on aging in 3 mol% yttria-stabilized zirconia ceramics for hip replacement prosthesis Biomaterials 25 2004 5539 5545
47. K. Matsui, H. Horikoshi, N. Ohmichi, and M. Ohgai Cubic-formation and grain-growth mechanisms in tetragonal zirconia polycrystal J Am Ceram Soc 86 2003 1401 1408
48. K. Matsui, H. Yoshida, and Y. Ikuhara Isothermal sintering effects on phase separation and grain growth in yttria-stabilized zirconia tetragonal polycrystal J Am Ceram Soc 92 2009 467 475
49. A. Virkar, and R.L.K. Matsumoto Ferroelastic domain switching as a toughening mechanism in tetragonal zirconia J Am Ceram Soc 69 1986 224 226
50. P. Pittayachawan, A. McDonald, A. Petrie, and J.C. Knowles The biaxial flexural strength and fatigue property of Lava Y-TZP dental ceramic Dent Mater 23 2007 1018 1029
51. P. Pittayachawan, A. McDonald, A. Young, and J.C. Knowles Flexural strength, fatigue life, and stress-induced phase transformation study of Y-TZP dental ceramic J Biomed Mater Res B: Appl Biomater 88 2009 366 377
52. M. Cattani Lorente, S.S. Scherrer, J. Richard, R. Demellayer, M. Amez-Droz, and H. W.A. Wiskott Surface roughness and EDS characterization of a Y-TZP dental ceramic treated with the CoJet™ Sand Dent Mater 26 2010 1035 1042
53. M. Kern, A. Barloi, and B. Yang Surface conditioning influences zirconia ceramic bonding J Dent Res 88 2009 817 822