On the formation of GBF of high-strength steels in the very high cycle fatigue regime

Materials Science and Engineering: A

Volumn 497, Issue 1-2, 2008, Pages 408-415

  Liu, Y B ^a   Yang, Z G ^a   Li, Y D ^a   Chen, S M ^a   Li, S X ^a   Hui, W J ^b   Weng, Y Q ^b  

^a INSTITUTE OF METAL RESEARCH   (China)

^b CENTRAL IRON AND STEEL RESEARCH INSTITUTE   (China)

Author keywords

GBF; High strength steels; Hydrogen; Stress intensity factor; Very high cycle fatigue

Indexed keywords

CRACKS; FATIGUE TESTING; FRACTURE; HIGH-CYCLE FATIGUE; HYDROGEN; HYDROGEN EMBRITTLEMENT; STRESS ANALYSIS; STRESS INTENSITY FACTORS; TENSILE STRENGTH; ULTRASONIC TESTING;

FRACTURE SURFACES; GRANULAR BRIGHT FACETS; HIGH CYCLE FATIGUE TEST; HIGH-STRENGTH STEELS; STRESS AMPLITUDES; STRESS-INTENSITY FACTORS; THRESHOLD-VALUE; TWO-STEP LOADINGS; ULTRASONIC FATIGUE TESTING MACHINE; VERY-HIGH-CYCLE FATIGUE;

HIGH STRENGTH STEEL;

EID: 53349163287     PISSN: 09215093     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.msea.2008.08.011     Document Type: Article

References (31)

1. Murakami Y., Nomoto T., and Ueda T. Fatigue Fract. Eng. Mater. Struct. 22 (1999) 581-590
2. Bathias C. Fatigue Fract. Eng. Mater. Struct. 22 (1999) 559-565
3. Shiozawa K., Morii Y., Nishino S., and Lu L. Int. J. Fatigue 28 (2006) 1521-1532
4. Yang Z.G., Li S.X., Zhang J.M., Li G.Y., Li Z.B., Hui W.J., and Weng Y.Q. Acta Mater. 52 (2004) 5235-5241
5. Yang Z.G., Zhang J.M., Li S.X., Li G.Y., Hui W.J., and Weng Y.Q. Mater. Sci. Eng. A 427 (2006) 167-174
6. Yang Z.G., Li S.X., Liu Y.B., Li Y.D., Li G.Y., Hui W.J., and Weng Y.Q. Int. J. Fatigue 30 (2008) 1016-1023
7. Zhang J.M., Li S.X., Yang Z.G., Li G.Y., Hui W.J., and Weng Y.Q. Int. J. Fatigue 29 (2007) 765-771
8. Li Y.D., Yang Z.G., Liu Y.B., Li S.X., Li G.Y., Hui W.J., and Weng Y.Q. Mater. Sci. Eng. A 489 (2008) 373-379
9. Chapetti M.D., Tagawa T., and Miyata T. Mater. Sci. Eng. A 356 (2003) 227-235
10. Chapetti M.D., Tagawa T., and Miyata T. Mater. Sci. Eng. A 356 (2003) 236-244
11. Sakai T., Sato Y., and Oguma N. Fatigue Fract. Eng. Mater. Struct. 25 (2002) 765-773
12. Wang Q.Y., Berard J.Y., Rathery S., and Bathias C. Fatigue Fract. Eng. Mater. Struct. 22 (1999) 673-677
13. Sakai T., Sato Y., Nagano Y., Takeda M., and Oguma N. Int. J. Fatigue 28 (2006) 1547-1554
14. Akiniwa Y., Miyamoto N., Tsuru H., and Tanaka K. Int. J. Fatigue 28 (2006) 1555-1565
15. Ochi Y., Matsumura T., Masaki K., and Yoshida S. Fatigue Fract. Eng. Mater. Struct. 25 (2002) 823-830
16. Murakami Y., and Matsunaga H. Int. J. Fatigue 28 (2006) 1509-1520
17. Shiozawa K., and Lu L. Fatigue Fract. Eng. Mater. Struct. 25 (2002) 813-822
18. Nakajima M., Kamiya N., Itoga H., Tokaji K., and Ko H.N. Int. J. Fatigue 28 (2006) 1540-1546
19. Itoga H., Tokaji K., Nakajima M., and Ko H.N. Int. J. Fatigue 25 (2003) 379-385
20. Murakami Y. Metal Fatigue: Effect of Small Defects and Non-metallic Inclusions (2002), Elsevier, Amsterdam & Boston p. 17
21. Tanaka K., Nakai Y., and Yamashita M. Int. J. Fracture 17 (1981) 519-533
22. Murakami Y., and Endo M. Int. J. Fatigue 16 (1994) 163-182
23. Harrison J.D. Metal Construct. Br. Weld. J. 17 (1970) 93-98
24. Makino T. Int. J. Fatigue 30 (2008) 1409-1418
25. Marines-Garcia I., Paris P.C., Tada H., Bathias C., and Lados D. Eng. Fract. Mech. 75 (2008) 1657-1665
26. Brinbaum H.K., and Sofronis P. Mater. Sci. Eng. A 176 (1994) 191-202
27. Oriani R.A., Hirth J.P., and Smialowski M. Hydrogen Degradation of Ferrous Alloys (1985), Noyes Publ. Park, Ridge, USA pp. 763-792
28. Narita N., Shiga T., and Higashida K. Mater. Sci. Eng. A 176 (1994) 203-209
29. Nakasa K., Takei H., and Kajiwara K. Eng. Fract. Mech. 14 (1981) 507-517
30. Tien J.K., Richards R.J., Buck O., and Marcus H.L. Scripta Metal. 9 (1975) 1097-1101
31. Gerberich W.W., Livne T., Chen X.F., and Kaczorowski M. Metall. Trans. A 19 (1988) 1319-1334