Fatigue and Fracture of Engineering Materials and Structures

Volumn 25, Issue 8-9, 2002, Pages 813-822

Very high-cycle fatigue behaviour of shot-peened high-carbon-chromium bearing steel

(2) Shiozawa, K a Lu, L a

a UNIVERSITY OF TOYAMA (Japan)

Author keywords

Fish eye; High cycle fatigue; Internal crack; Shot peening; Surface crack; Surface treatment

Indexed keywords

ASPECT RATIO; COMPRESSIVE STRESS; CRACK INITIATION; CRACK PROPAGATION; CRACKS; FATIGUE OF MATERIALS; FATIGUE TESTING; FRACTURE; RESIDUAL STRESSES; SHOT PEENING; STRESS INTENSITY FACTORS; SURFACE TREATMENT;

FISH-EYE; GRANULAR-BRIGHT-FACET;

STEEL;

EID: 0036674602 PISSN: 8756758X EISSN: None Source Type: Journal
DOI: 10.1046/j.1460-2695.2002.00567.x Document Type: Article

Times cited : (204)

References (29)

1
- 0033177737
- Gigacycle fatigue of ferrous alloys
- (1999) Fatigue Fract. Engng. Mater. Struct. , vol.22 , pp. 667-672
- Wang, Q.Y.¹ Berard, Y.² Dubarre, A.³ Baudry, G.⁴ Rathery, S.⁵ Bathias, C.⁶

2
- 0032664906
- Factors influencing the mechanism of superlong fatigue failure in steels
- (1999) Fatigue Fract. Engng. Mater. Struct. , vol.22 , pp. 581-590
- Murakami, Y.¹ Nomoto, T.² Ueda, T.³

3
- 0000849719
- Analysis of the mechanism of superlong fatigue failure by optical microscope and SEM/AFM observations
- (1999) J. Soc. Mater. Sci. Jpn. , vol.48 , pp. 1112-1117
- Murakami, Y.¹ Nomoto, T.² Ueda, T.³ Murakami, Y.⁴ Ohori, M.⁵

4
- 0032187756
- Super-long life tension-compression fatigue properties of quenched and tempered 0.46% carbon steel
- (1998) Int. J. Fatigue , vol.20 , pp. 661-667
- Murakami, Y.¹ Takada, M.² Toriyama, T.³

5
- 0032639632
- Stepwise S-N curve and fish-eye failure in gigacycle fatigue
- (1999) Fatigue Fract. Engng. Mater. Struct. , vol.22 , pp. 601-607
- Nishijima, S.¹ Kanazawa, K.²

6
- 0031368488
- Fatigue fracture of low alloy steel at ultra-high-cycle region under elevated temperature condition
- (1997) J. Soc. Mater. Sci. Jpn. , vol.46 , pp. 1396-1401
- Kanazawa, K.¹ Nishijima, S.²

7
- 0000439083
- Experimental evidence of duplex S-N characteristics in wide life region for high strength steels
- (Edited by X. R. Wu and Z. G. Wang); Higher Education Press
- (1999) Fatigue '99 , vol.1 , pp. 573-578
- Sakai, T.M.¹ Takeda, K.² Shiozawa, Y.³ Ochi, M.⁴ Nakajima, T.⁵ Nakamura⁶ Oguma⁷

8
- 0034226327
- Experimental reconfirmation of characteristic S-N property for high carbon chromium bearing steel in wide life region in rotating bending
- (2000) J. Soc. Mater. Sci. Jpn. , vol.49 , pp. 779-785
- Sakai, T.¹ Takeda, M.² Shiozawa, K.³ Ochi, Y.⁴ Nakajima, M.⁵ Nakamura, T.⁶ Oguma, N.⁷

9
- 0000542598
- An observation of fish-eye fracture process in high strength steel SUJ2
- (1999) J. Jpn. Soc. Mech. Engng. , vol.65 A , pp. 2504-2510
- Nakajima, M.¹ Sakai, T.² Shimizu, T.³

10
- 0005453102
- Characteristic S-N property of high carbon chromium bearing steel in ultra-wide life region under rotating bending
- (2001) Mat. Sci. Res. Inst. , vol.STP-1 , pp. 41-46
- Sakai, T.¹ Takeda, M.² Tanaka, N.³ Kanemitsu, M.⁴ Oguma, N.⁵ Shiozawa, K.⁶

11
- 0024305258
- Fatigue strength characteristics of high strength steel
- (1989) J. Jpn. Soc. Mech. Engng. , vol.55 , pp. 45-50
- Emura, H.¹ Asami, K.²

12
- 0022701265
- Relationship between fatigue strength and hardness for high strength steels
- (1986) J. Jpn. Soc. Mech. Engng. , vol.52 A , pp. 847-852
- Masuda, C.¹ Nishijima, S.² Tanaka, Y.³

13
- 85004504504
- Relationship between fatigue properties and hardness for high hardness steels tempered at several temperatures
- (1989) J. Mater. Sci. Jpn. , vol.38 , pp. 1128-1132
- Konuma, S.¹ Furukawa, T.²

14
- 0002781645
- Subsurface fatigue-crack initiation and growth of plasma-assisted duplex surface-treated tool steel
- (Edited by K. S. Ravichandran, R. O. Ritchie and Y.Murakami). Elsevier, Amsterdam
- (1999) Small Fatigue Cracks, Mechanics, Mechanisms and Applications , pp. 39-47
- Shiozawa, K.¹ Nishino, S.² Ohtani, T.³ Mizuno, S.⁴

15
- 0027576876
- Fracture mode transition in high cycle fatigue of high strength steel
- (1993) J. Jpn. Soc. Mech. Engng. , vol.59 , pp. 1001-1006
- Kuroshima, Y.¹ Shimizu, M.² Kawasaki, K.³

16
- 0032256678
- A study of method utilizing fatigue life data on two competing fracture mode
- (1998) J. Soc. Mater. Sci. Jpn. , vol.47 , pp. 1216-1220
- Kaneko, M.¹ Nakamura, T.² Noguchi, T.³

17
- 0001203568
- Crack initiation and small fatigue crack growth behaviour of beta Ti-15V-3Cr-3Al-3Sn alloy
- (1996) Fatigue , vol.96 , pp. 301-306
- Shiozawa, K.¹ Matsushita, H.²

18
- 0002065578
- Effect of stress ratio on subsurface fatigue crack initiation behavior of beta-type titanium alloy
- (1998) J. Jpn. Soc. Mech. Engng. , vol.64 A , pp. 2528-2535
- Shiozawa, K.¹ Kuroda, Y.² Nishino, S.³

19
- 0001860710
- On the process of subsurface fatigue crack initiation in Ti-6Al-4V
- ASTM STP 675 (Edited by J. T. Fong)
- (1979) , pp. 47-68
- Ruppen, J.¹ Bhowal, P.² Eylon, D.³ McEvily, J.⁴

20
- 0020751081
- Subsurface crack initiation in high cycle fatigue in Ti-6Al-4V and in a typical martensic stainless steel
- (1983) Scripta Metall. , vol.17 , pp. 601-606
- Atrens, A.¹ Hoffelner, W.² Duering, T.W.³ Allison, J.E.⁴

21
- 0001142289
- Influence of microstructure and mean stress on fatigue strength of Ti-6Al-4V
- (1985) Proceedings of the 5th International Conference on Titanium Science and Technology , vol.4 , pp. 2139-2146
- Adachi, S.¹ Wagner, L.² Lutjering, G.³

22
- 0029344408
- Effect of microstructure on fatigue behaviour of Ti-15Mo-5Zr-3Al alloy
- (1995) J. Soc. Mater. Sci. Jpn. , vol.44 , pp. 933-938
- Bian, J.¹ Tokaji, K.² Nakajima, M.³ Ogawa, T.⁴

23
- 0033208078
- Subsurface fatigue crack initiation behavior and S-N curve characteristics in high carbon-chromium bearing steel
- (1999) J. Soc. Mater. Sci. Jpn. , vol.48 , pp. 1095-1100
- Shiozawa, K.¹ Lu, L.² Ishihara, S.³

24
- 0005441144
- Duplex S-N curve characteristics and subsurface fatigue crack initiation behaviour in high carbon-chromium bearing steel
- ECF-13, CD-ROM. Elsevier, Amsterdam
- (2000) Fracture Mechanic: Applications and Challenges
- Shiozawa, K.¹ Lu, L.² Ishihara, S.³

25
- 0005390059
- Characteristics of S-N curve and subsurface crack initiation behavior of high strength bearing steel in gigacycle fatigue
- (2001) Mater. Sci. Res. Int. , vol.STP-1 , pp. 35-40
- Lu, L.¹ Shiozawa, K.² Ishihara, S.³

26
- 0035657940
- S-N curve characteristics and subsurface crack initiation behaviour in ultra-long life fatigue of a high carbon-chromium bearing steel
- (2001) Fatigue Fract. Engng. Mater. Struct. , vol.24 , pp. 781-790
- Shiozawa, K.¹ Lu, L.² Ishihara, S.³

27
- 0003406844
- Yokendo, Tokyo (in Japanese)
- (1993) Metal Fatigue: Effect of Small Defects and Nonmetallic Inclusions
- Murakami, Y.¹

28
- 0023999231
- Quantitative evaluation of effects of nonmetallic inclusions on fatigue strength of high strength steel
- (1988) J. Jpn. Soc. Mech. Engng. , vol.54 , pp. 688-695
- Murakami, Y.¹ Kodama, S.² Konuma, S.³

29
- 0003395797
- Pergamon Press
- (1992) Stress Intensity Factor Handbook , pp. 734-741
- Murakami, Y.¹

* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.