Effect of stress ratio on long life fatigue behavior of high carbon chromium bearing steel under axial loading

International Journal of Fatigue

Volumn 28, Issue 11, 2006, Pages 1547-1554

  Sakai, Tatsuo ^a   Sato, Yosuke ^b   Nagano, Yoshiyuki ^c   Takeda, Mitsuhiro ^d   Oguma, Noriyasu ^e  

^a RITSUMEIKAN UNIVERSITY   (Japan)

^b EMIC Corporation Ltd   (Japan)

^c Japan Airlines   (Japan)

^d TORAY INDUSTRIES INC   (Japan)

^e JTEKT CORPORATION   (Japan)

Author keywords

Duplex S N property; Fatigue crack initiation; Fatigue threshold; Long life fatigue; Stress ratio

Indexed keywords

CARBON; CHROMIUM ALLOYS; CRACK PROPAGATION; FRACTURE; LOADING; STEEL;

DUPLEX S-N PROPERTY; FATIGUE THRESHOLD; LONG LIFE FATIGUE; STRESS RATIO;

FATIGUE OF MATERIALS;

EID: 33746379584     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2005.04.018     Document Type: Article

References (33)

1. Sakai T, Takeda M, Shiozawa K, Ochi Y, Nakajima M, Nakamura T, et al. Experimental evidence of duplex S-N characteristics in wide life region for high strength steels. In: Proceedings of the seventh international fatigue congress, vol. 1; 1999. p. 573-8.
2. Ochi Y., and Sakai T. Fatigue of metallic materials in the very high cycle regime. J Soc Mat Sci Jpn (2003) 433-439
3. Sakai T., Hirano H., Nishida T., and Tomoto T. A study on ultra long life fatigue characteristics in rotating bending for aluminum alloy with some surface treatments. Proc VHCF-3 (2004) 585-592
4. Bathias C. There is no infinite fatigue life in metallic materials. Fatigue Fract Eng Mater Struct 22 (1999) 559-565
5. 2 + γ) TiAl alloy. Int J Fatigue 26 (2004) 1263-1275
6. Stanzl-Tschegg S.E. Fracture mechanisms and fracture mechanics at ultrasonic frequencies. Fatigue Fract Eng Mater Struct 22 (1999) 567-579
7. Berger C., and Kaiser B. Results of long-term fatigue tests on helical compression springs. Proc VHCF-3 (2004) 342-349
8. Bathias C., and Paris P.C. Gigacycle fatigue in mechanical practice (2005), Marcel Dekker Inc.
9. Masuda C., Nishijima S., and Tanaka Y. Relationship between fatigue strength and hardness for high strength steels. Trans JSME 52A (1986) 847-852
10. Sakai T., Takeda M., Tanaka N., Kanemitsu M., Oguma N., and Shiozawa K. S-N property and fractography of high carbon chromium bearing steel over ultra wide life region under rotating bending. Trans JSME 67A (2001) 1805-1812
11. Nishijima S., and Kanazawa K. Stepwise S-N curve and fish-eye failure in gigacycle fatigue. Fatigue Fract Eng Mater Struct 22 (1999) 601-607
12. Asami K. Long-life fatigue strength of tufftrided and carburized steels. J Heat Treatment Technol Assoc 25 (1985) 123-128
13. Asami K., and Sugiyama Y. Fatigue strength of various surface hardened steels. J Heat Treatment Technol Assoc 25 (1985) 147-150
14. Naito T., Ueda H., and Kikuchi M. Fatigue behavior of carburized steel with internal oxides and non-martensitic microstructure near the surface. Metal Trans 15A (1984) 1431-1436
15. Asami K., and Hironaga M. Effect of shot-peening on suppression of scatter of fatigue strength in Ti-6Al-4V alloy. J Soc Mat Sci Jpn 43 (1994) 12-17
16. Sakai T., Takeda M., Shiozawa K., Ochi Y., Nakajima M., Nakamura T., et al. Experimental reconfirmation of characteristic S-N property for high carbon-chromium bearing steel in wide life region in rotating bending. J Soc Mat Sci Jpn 49 (2000) 779-785
17. Shiozawa K., Lu L., and Ishihara S. Subsurface fatigue crack initiation behavior and S-N curve characteristics in high carbon-chromium bearing steel. J Soc Mat Sci Jpn 48 (1999) 1095-1100
18. Marines I., Rubio C., Dominguez G., and Bathias C. Carburized steel S-N curves in the gigacycle regime. Proc VHCF-3 (2004) 116-123
19. Ritchie R.O., Alsem D.H., Muhlstein C.L., and Stach E.A. Very high-cycle fatigue of micron-scale polysilicon films for MEMS. Proc VHCF-3 (2004) 68-76
20. Baudry G., Daquier P., Marines I., Bathias C., Doucet J.P., Vittori J.F., et al. Very high cycle (gigacyclic) fatigue of a wide range of alternative engineering materials used automotive industry. Proc VHCF-3 (2004) 298-305
21. Sakai T., Sato Y., and Oguma N. Characteristic S-N property of high carbon chromium bearing steel under axial loading in long life fatigue. Fatigue Fract Eng Mater Struct 25 (2002) 765-773
22. Peterson R.E. Stress concentration design factors (1953), Wiley
23. Sakai T, Okada K, Oguma N, Mori K. A study on distribution characteristics of static mechanical properties for high carbon and high strength steels. In: Proceedings of the sixth Japan international SAMPE symposium; 1999. p. 361-4.
24. Oguma N., and Sakai T. Fatigue life prediction for bearing steel failed with fish-eye at subsurface in rotating bending. J Soc Mat Sci Jpn 50 (2001) 516-523
25. Oguma N., Harada H., and Sakai T. Strength level dependence of long-life fatigue behavior for bearing steel in rotating bending. Proc VHCF-3 (2004) 617-624
26. Harada H., Oguma N., and Sakai T. Formation mechanism of fine granular area around inclusion for bearing steel in rotating bending. Proc VHCF-3 (2004) 101-107
27. Murakami Y., and Matsunaga H. Effect of hydrogen on high cycle fatigue properties of stainless steels and other steels used for fuel cell system. Proc VHCF-3 (2004) 322-333
28. Murakami Y., Nomoto T., Ueda T., Murakami Y., and Ohori M. Analysis of the mechanism of super long fatigue failure by optical microscope and SEM/AFM observations. J Soc Mat Sci Jpn 48 (1999) 1112-1117
29. Shiozawa K., Morii Y., Nishino S., and Lu L. A study of subsurface crack initiation and propagation mechanism of high-strength steel by fracture surface topographic analysis. J Soc Mat Sci Jpn 52 (2003) 1311-1317
30. Beswick J.M. Fracture and fatigue crack propagation properties of hardened 52100 steel. Metal Trans 20A (1989) 1961-1973
31. Paris P.C., and Erdogan F. A critical analysis of crack propagation laws. Trans ASME D85-4 (1963) 528-534
32. Murakami Y., et al. Stress intensity factors handbook vol. 2 (1987), Pergamon Press
33. Murakami Y., Kodama S., and Konuma S. Quantitative evaluation of effects of non-metallic inclusions on fatigue strength of high strength steel. Trans JSME 54A (1988) 688-695