Volumn 28, Issue 11, 2006, Pages 1540-1546

Experimental estimation of crack initiation lives and fatigue limit in subsurface fracture of a high carbon chromium steel

Author keywords

Fatigue limit; Fish eye; Giga cycle fatigue; Granular area; Subsurface crack initiation; Two step variable amplitude loading tests

Indexed keywords

CARBON; CHROMIUM; FATIGUE OF MATERIALS; FRACTURE; NUCLEATION; STEEL;

EID: 33746344981     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2005.05.017     Document Type: Article
Times cited : (55)

References (15)
  • 1
    • 0024305258 scopus 로고
    • Fatigue strength characteristics of high strength steel
    • Emura H., and Asami K. Fatigue strength characteristics of high strength steel. Trans Jpn Soc Mech Eng A55 (1989) 45-50
    • (1989) Trans Jpn Soc Mech Eng , vol.A55 , pp. 45-50
    • Emura, H.1    Asami, K.2
  • 2
    • 85004271419 scopus 로고
    • Relationship between fatigue crack propagation originating at inclusion and fracture-mode transition of high strength steel
    • Kuroshima Y., Saito Y., Shimizu M., and Kawasaki K. Relationship between fatigue crack propagation originating at inclusion and fracture-mode transition of high strength steel. Trans Jpn Soc Mech Eng A60 (1994) 2710-2715
    • (1994) Trans Jpn Soc Mech Eng , vol.A60 , pp. 2710-2715
    • Kuroshima, Y.1    Saito, Y.2    Shimizu, M.3    Kawasaki, K.4
  • 3
    • 0029699994 scopus 로고    scopus 로고
    • Influences of non-metallic inclusion and carbide on high-cycle fatigue strength of tool steels
    • Abe T., and Kanazawa K. Influences of non-metallic inclusion and carbide on high-cycle fatigue strength of tool steels. J Soc Mater Sci 45 (1996) 9-15
    • (1996) J Soc Mater Sci , vol.45 , pp. 9-15
    • Abe, T.1    Kanazawa, K.2
  • 4
    • 0005529316 scopus 로고    scopus 로고
    • Relation between high cycle fatigue characteristics and fracture origins in low-temperature-tempered Cr-Mo steel
    • Nakamura T., Kaneko M., Noguchi T., and Jinbo K. Relation between high cycle fatigue characteristics and fracture origins in low-temperature-tempered Cr-Mo steel. Trans Jpn Soc Mech Eng A64 (1998) 1820-1825
    • (1998) Trans Jpn Soc Mech Eng , vol.A64 , pp. 1820-1825
    • Nakamura, T.1    Kaneko, M.2    Noguchi, T.3    Jinbo, K.4
  • 5
    • 0032626508 scopus 로고    scopus 로고
    • There is no infinite fatigue life in metallic materials
    • Bathias C. There is no infinite fatigue life in metallic materials. Fatigue Fract Eng Mater Struct 22 (1999) 559-565
    • (1999) Fatigue Fract Eng Mater Struct , vol.22 , pp. 559-565
    • Bathias, C.1
  • 6
    • 0032664906 scopus 로고    scopus 로고
    • Factors influencing the mechanism of superlong fatigue failure in steels
    • Murakami Y., Nomoto T., and Ueda T. Factors influencing the mechanism of superlong fatigue failure in steels. Fatigue Fract Eng Mater Struct 22 (1999) 581-590
    • (1999) Fatigue Fract Eng Mater Struct , vol.22 , pp. 581-590
    • Murakami, Y.1    Nomoto, T.2    Ueda, T.3
  • 7
    • 0000542598 scopus 로고    scopus 로고
    • An observation of fish-eye fracture process in high strength steel SUJ2
    • Nakajima M., Sakai T., and Shimizu T. An observation of fish-eye fracture process in high strength steel SUJ2. Trans Jpn Soc Mech Eng A65 (1999) 2504-2510
    • (1999) Trans Jpn Soc Mech Eng , vol.A65 , pp. 2504-2510
    • Nakajima, M.1    Sakai, T.2    Shimizu, T.3
  • 8
    • 0035657940 scopus 로고    scopus 로고
    • S-N curve characteristics and subsurface crack initiation behaviour in ultra-long life fatigue of a high carbon-chromium bearing steel
    • Shiozawa K., Lu L.T., and Ishihara S. S-N curve characteristics and subsurface crack initiation behaviour in ultra-long life fatigue of a high carbon-chromium bearing steel. Fatigue Fract Eng Mater Struct 24 (2001) 781-790
    • (2001) Fatigue Fract Eng Mater Struct , vol.24 , pp. 781-790
    • Shiozawa, K.1    Lu, L.T.2    Ishihara, S.3
  • 9
    • 2942685637 scopus 로고    scopus 로고
    • Effect of fine particle bombarding on fatigue strength of high strength steel
    • Brebbia C.A. (Ed), WIT Press
    • Ko H.N., Kagaya C., Itoga H., Tokaji K., and Nakajima M. Effect of fine particle bombarding on fatigue strength of high strength steel. In: Brebbia C.A. (Ed). Surface treatment V (2001), WIT Press 313-322
    • (2001) Surface treatment V , pp. 313-322
    • Ko, H.N.1    Kagaya, C.2    Itoga, H.3    Tokaji, K.4    Nakajima, M.5
  • 10
    • 0036873972 scopus 로고    scopus 로고
    • Effect of two-step load variation on super-long life fatigue and internal crack growth behavior of high carbon-chromium bearing steel
    • Lu L.T., and Shiozawa K. Effect of two-step load variation on super-long life fatigue and internal crack growth behavior of high carbon-chromium bearing steel. Trans Jpn Soc Mech Eng 68 (2002) 1666-1673
    • (2002) Trans Jpn Soc Mech Eng , vol.68 , pp. 1666-1673
    • Lu, L.T.1    Shiozawa, K.2
  • 11
    • 0023999231 scopus 로고
    • Quantitative evaluation of effects of nonmetallic inclusions on fatigue strength of high strength steel
    • Murakami Y., Kodama S., and Konuma S. Quantitative evaluation of effects of nonmetallic inclusions on fatigue strength of high strength steel. Trans Jpn Soc Mech Eng A54 (1988) 688-696
    • (1988) Trans Jpn Soc Mech Eng , vol.A54 , pp. 688-696
    • Murakami, Y.1    Kodama, S.2    Konuma, S.3
  • 12
    • 33746375389 scopus 로고    scopus 로고
    • -8 m/cycle. ASTM standard E647-00; 2002.
  • 13
    • 0000504982 scopus 로고
    • Effects of defects, inclusions and inhomogeneities on fatigue strength
    • Murakami Y., and Endo M. Effects of defects, inclusions and inhomogeneities on fatigue strength. Int J Fatigue 16 (1994) 163-182
    • (1994) Int J Fatigue , vol.16 , pp. 163-182
    • Murakami, Y.1    Endo, M.2
  • 14
    • 0141894939 scopus 로고    scopus 로고
    • Factors influencing the formation of ODA in ultralong fatigue regime
    • Nagata J., and Murakami Y. Factors influencing the formation of ODA in ultralong fatigue regime. J Soc Mater Sci 52 (2003) 966-973
    • (2003) J Soc Mater Sci , vol.52 , pp. 966-973
    • Nagata, J.1    Murakami, Y.2


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.