Notch effect on fatigue strength reduction of bearing steel in the very high cycle regime

International Journal of Fatigue

Volumn 28, Issue 11, 2006, Pages 1555-1565

  Akiniwa, Yoshiaki ^a   Miyamoto, Nobuyuki ^b   Tsuru, Hirotaka ^a   Tanaka, Keisuke ^a  

^a NAGOYA UNIVERSITY   (Japan)

^b DENSO CORPORATION   (Japan)

Author keywords

Bearing steel; Fatigue crack propagation; Fish eye; Fractography; Inclusion; Notch effect; S N curve; Ultrasonic fatigue; Very high cycle fatigue

Indexed keywords

CRACK PROPAGATION; DEFORMATION; FATIGUE OF MATERIALS; FRACTOGRAPHY; INCLUSIONS; STRESS INTENSITY FACTORS;

FATIGUE CRACK PROPAGATION; NOTCH EFFECT; S-N CURVE; ULTRASONIC FATIGUE; VERY HIGH CYCLE FATIGUE;

STRENGTH OF MATERIALS;

EID: 33746382566     PISSN: 01421123     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.ijfatigue.2005.04.017     Document Type: Article

References (21)

1. Sakai T., Takeda M., Shiozawa K., Ochi Y., Nakajima M., Nakamura T., et al. Experimental reconfirmation of characteristic S-N property for high carbon chromium bearing steel in wide life region in rotating bending. J Soc Mater Sci Japan 49 7 (2000) 779-785
2. Goto M., Yamamoto T., Nisitani H., Sakai T., and Gawagoishi N. Effect of removing surface hardened layer on the fatigue strength of bearing steel SUJ2 ground specimen in the long life field. J Soc Mater Sci Japan 49 7 (2000) 786-792
3. 7 cycles). Part 1: influence of hydrogen trapped by inclusions. Fatigue Fract Eng Mater Struct 23 11 (2000) 893-902
4. 7 cycles). Part II: influence of hydrogen trapped by inclusions. Fatigue Fract Eng Mater Struct 23 11 (2000) 903-910
5. Murakami Y., Yokoyama N.N., and Nagata J. Mechanism of fatigue failure in ultralong life regime. Fatigue Fract Eng Mater Struct 25 8/9 (2002) 735-746
6. Shiozawa K., and Lu L. Very high-cycle fatigue behaviour of shot-peened high-carbon-chromium bearing steel. Fatigue Fract Eng Mater Struct 25 8/9 (2002) 813-822
7. Ochi Y., Matsumura T., Masaki K., and Yoshida S. High-cycle rotating bending fatigue property in very long-life regime of high-strength steels. Fatigue Fract Eng Mater Struct 25 8/9 (2002) 822-823
8. Sakai T., Sato Y., and Oguma N. Characteristic S-N properties of high-carbon-chromium-bearing steel under axial loading in long-life fatigue. Fatigue Fract Eng Mater Struct 25 8/9 (2002) 765-773
9. Akiniwa Y., Tanaka K., and Kimura H. Microstructural effects on crack closure and propagation thresholds of small fatigue cracks. Fatigue Fract Eng Mater Struct 24 12 (2001) 817-830
10. Tanaka K., and Akiniwa Y. Fatigue crack propagation behaviour derived from S-N data in very high cycle regime. Fatigue Fract Eng Mater Struct 25 8/9 (2002) 775-784
11. Marines I., Dominguez G., Baudry G., Vittori J.-F., Rathery S., Doucet J.-P., et al. Ultrasonic fatigue tests on bearing steel AISI-SAE 52100 at frequency of 20 and 30 kHz. Int J Fatigue 25 9/11 (2003) 1037-1046
12. Stanzl-Tschegg S.E. Ultrasonic fatigue. In: Lutjering G., and Nowack H. (Eds). Fatigue 96: proceedings of the 6th international fatigue congress vol. III (1996), Pergamon, Oxford 1887-1898
13. Ishii H., Yamanaka K., and Tohgo K. Giga-cycle fatigue strengths in some high strength steels by ultrasonic fatigue testing. Mater Sci Res Int STP 1 (2001) 59-63
14. Furuya Y., Matsuoka S., Abe T., and Yamaguchi K. Gigacycle fatigue properties for high-strength low-alloy steel at 100 Hz, 600 Hz, and 20 kHz. Scripta Mater 46 2 (2002) 157-162
15. Murakami Y. Analysis of stress intensity factors of modes I, II and III for inclined surface cracks of arbitrary shape. Eng Fract Mech 22 1 (1985) 101-114
16. Kuroshima Y., Ikeda T., Harada M., and Harada S. Subsurface crack growth behavior on high cycle fatigue of high strength steel. Trans Jpn Soc Mech Eng A 64 626 (1998) 2536-2541
17. Omata S. Evaluation of fatigue properties in the ultra-high-cycle regime of steels for crackshafts based on crack propagation characteristics. In: Sakai T, Ochi Y, editors. VHCF3: proceedings of the 3rd international conference on very high cycle fatigue. The Soc Mater Sci Japan; 2004. p. 306-12.
18. Lu L.T., and Shiozawa K. Effect of two-step load variation on super-long fatigue and internal crack growth behavior of high carbon-chromium bearing steel. Trans Jpn Soc Mech Eng A 68 675 (2002) 1666-1673
19. Nakajima M., Ito K., Kamiya N., Tokaji K., and Kou I. Estimation of subsurface crack initiation lives for a high strength steel under variable amplitude loading test. Proceedings of the meeting of Japan Society of Mechanical Engineers vol. I. 03-1 (2003), Japan Society of Mechanical Engineer 169-170
20. Tanaka K., and Akiniwa Y. Modeling of fatigue crack growth: mechanistic models. In: Ritchie R.O., and Murakami Y. (Eds). Comprehensive structural integarity vol. 4 (2003), Elsevier 165-190
21. Mayer H., Papakyriacou M., Zettl B., and Stanzl-Tschegg S.E. Influence of porosity on the fatigue limit of die cast magnesium and aluminium alloys. Int J Fatigue 25 3 (2002) 245-256