Crack healing in alumina bioceramics

Dental Materials

Volumn 24, Issue 3, 2008, Pages 328-332

  Fischer, H ^a   Weiss R ^a   Telle, R ^a  

^a RWTH AACHEN UNIVERSITY   (Germany)

Author keywords

Alumina; Crack healing; Glass; Infiltration; Surface flaws

Indexed keywords

ALUMINA; DENTAL COMPOSITES; GLASS; INFILTRATION; MICROSTRUCTURE; SCANNING ELECTRON MICROSCOPY; SPECIMEN PREPARATION; VICKERS HARDNESS TESTING;

CERAMIC RESTORATIONS; CRACK HEALING; SURFACE FLAWS;

BIOCERAMICS;

ALLOY; ALUMINUM OXIDE; GLASS; LANTHANUM; LANTHANUM OXIDE; OXIDE;

ARTICLE; DENTAL CARE; ELASTICITY; MATERIALS TESTING; PLIABILITY; QUALITY CONTROL; TOOTH PROSTHESIS;

ALUMINUM OXIDE; DENTAL PORCELAIN; DENTAL PROSTHESIS REPAIR; DENTAL STRESS ANALYSIS; ELASTICITY; GLASS; LANTHANUM; MATERIALS TESTING; METAL CERAMIC ALLOYS; OXIDES; PLIABILITY; QUALITY CONTROL;

EID: 38349091960     PISSN: 01095641     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.dental.2007.06.001     Document Type: Article

References (30)

1. Andersson M., and Odén A. A new all-ceramic crown: a densesintered, high purity aluminia coping with porcelain. Acta Odontol Scand 51 (1993) 59-64
2. Sundh A., Molin M., and Sjögren G. Fracture resistance of yttrium oxide partially-stabilized zirconia all-ceramic bridges after veneering and mechanical fatigue testing. Dent Mater 21 (2005) 476-482
3. Hager B., Oden A., Andersson B., and Andersson L. Procera AllCeram laminates: a clinical report. J Prosthet Dent 85 (2001) 231-232
4. Meyenberg K.H., Lüthy H., and Schärer P. Zirconia posts: a new all-ceramic concept for nonvital abutment teeth. J Esthet Dent 7 (1995) 73-80
5. Ardlin B.I. Transformation-toughened zirconia for dental inlays, crowns and bridges: chemical stability and effect of low-temperature aging on flexural strength and surface structure. Dent Mater 18 (2002) 590-595
6. Zinelis S., Eliades T., Eliades G., Makou M., and Silikas N. Comparative assessment of the roughness, hardness, and wear resistance of aesthetic bracket materials. Dent Mater 21 (2005) 890-894
7. Heydecke G., Sieraalta M., and Razzoog M.F. Evolution and use of aluminium oxide single-tooth implant abutments: a short review and presentation of two cases. Int J Prosthodont 15 (2002) 488-493
8. Kohal R.J., and Klaus G. A zirconia implant-crown system: a case report. Int J Periodontics Restorative Dent 24 (2004) 147-153
9. Ritter J.E. Predicting lifetimes of materials and material structures. Dent Mater 11 (1995) 142-146
10. Green D.J. An introduction to the mechanical properties of ceramics (1998), Cambridge University Press, Cambridge
11. Munz D., and Fett T. Ceramics: mechanical properties, failure behaviour, materials selection (1999), Springer-Verlag, Berlin
12. Rice R.W., and Mecholsky Jr. J.I. The nature of strength-controlling machining flaws in ceramics. In: Hockey B., and Rice R. (Eds). The science of ceramic machining and surface finishing. National Bureau of Standards, Special Publication 562 (1979), U.S. Government Printing Office, Washington, DC 351-378
13. Sindel J., Petschelt A., Grellner F., Dierken C., and Greil P. Evaluation of subsurface damage in CAD/CAM machined dental ceramics. J Mater Sci-Mater M 9 (1998) 291-295
14. Fischer H., Weinzierl P., Weber M., and Marx R. Processing related damage of dental ceramic. Dtsch Zahnärztl Z 54 (1999) 484-488
15. Luthardt R.G., Holzhüter M.S., Rudolph H., Herold V., and Walter M.H. CAD/CAM-machining effects on Y-TZP zirconia. Dent Mater 20 (2004) 655-662
16. Khuri-Yakub B.T., Kino G.S., and Evans A.G. Acoustic surface wave measurements of surface cracks in ceramics. J Am Ceram Soc 63 (1980) 65-71
17. Bashkansky M., Battle P.R., Duncan M.D., Kahn M., and Reintjes J. Subsurface defect detection in ceramics using an optical gated scatter reflectometer. J Am Ceram Soc 79 (1996) 1397-1400
18. Hockin H.K.X., and Jahanmir S. Simple technique for observing subsurface damage in machining of ceramics. J Am Ceram Soc 77 (1994) 1388-1390
19. Fischer H., Karaca F., and Marx R. Detection of microscopic cracks in dental ceramic materials by fluorescent penetrant method. J Biomed Mater Res 61 (2002) 153-158
20. Chu M.C., Cho S.J., Lee Y.C., Park H.M., and Yoon D.Y. Crack healing in silicon carbide. J Am Ceram Soc 87 (2004) 490-492
21. Chu M.C., Cho S.J., Park H.M., Ryu H., and Yoon K.J. Crack healing in reaction-bonded silicon carbide. Mater Lett 58 (2004) 1313-1316
22. Chu M.C., Cho S.J., Yoon D.Y., and Park H.M. Crack repairing in alumina by penetrating glass. J Am Ceram Soc 88 (2005) 491-493
23. Ray A.K. A new technique for precracking ceramic specimens in fatigue and fracture. J Eur Ceram Soc 18 (1998) 1655-1662
24. Schmid M., Fischer J., Hoffmann C., and Strub J.R. Chemical and thermal compatibility of all-ceramic systems. Dtsch Zahnärztl Z 45 (1990) 505-508
25. Kübler J. Fracture toughness of ceramics using the SEVNB method; round robin. VAMAS-Report No. 37. Dübendorf: EMPA; 1999.
26. N.N. Processing Instructions. Fabrication of the substructure vita In-Ceram alumina. Vita Zahnfabrik, Bad Säckingen; 2005. p. 15.
27. Bao Y., and Zhou Y. A new method for precracking beam for fracture toughness experiments. J Am Ceram Soc 89 (2006) 1118-1121
28. Fischer J., Schmid M., Kappert H.F., and Strub J.R. Texture formation of the dental ceramic core material In-Ceram and thermal expansion of its individual components. Dtsch Zahnärztl Z 46 (1991) 461-463
29. 4. Mater Sci Eng A-Struct 302 (2001) 83-91
30. Fischer H., Rentzsch W., and Marx R. A modified size effect model for brittle nonmetallic materials. Eng Fract Mech 69 (2002) 781-791