Role of substrate material in failure of crown-like layer structures

Journal of Biomedical Materials Research - Part B Applied Biomaterials

Volumn 81, Issue 2, 2007, Pages 305-311

  Kim, Jae Won ^a,b   Bhowmick, Sanjit ^a   Chai, Herzl ^a   Lawn, Brian R ^a  

^a NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

^b NEW YORK UNIVERSITY   (United States)

Author keywords

Brittle shells; Contact damage; Curved surfaces; Dental crowns; Radial cracks

Indexed keywords

ALUMINA; CRACKS; EPOXY RESINS; FAILURE ANALYSIS; FRACTURE MECHANICS; POLYMERIC GLASS;

BRITTLE GLASS; GLASS DISKS; RADIAL CRACKS; SUBSTRATE MODULUS;

SUBSTRATES;

ALUMINUM OXIDE; EPOXY RESIN; GLASS;

ARTICLE; DENTIN; FINITE ELEMENT ANALYSIS; TOOTH CROWN; TOOTH FRACTURE;

CERAMICS; CROWNS; DENTAL MATERIALS; DENTAL MODELS; DENTAL RESTORATION FAILURE; GLASS; HUMANS; MATERIALS TESTING; STRESS, MECHANICAL; SURFACE PROPERTIES;

EID: 34247594208     PISSN: 15524973     EISSN: 15524981     Source Type: Journal    
DOI: 10.1002/jbm.b.30666     Document Type: Article

References (35)

1. Lawn BR. Ceramic-based layer structures for biomechanical applications. Curr Opin Solid State Mater Sci 2002;6:229-235.
2. Lawn BR, Deng Y, Miranda P, Pajares A, Chai H, Kim DK. Overview: Damage in brittle layer structures from concentrated loads. J Mater Res 2002;17:3019-3036.
3. Deng Y, Lawn BR, Lloyd IK. Characterization of damage modes in dental ceramic bilayer structures. J Biomed Mater Res 2002;63:137-145.
4. Chai H, Lawn BR, Wuttiphan S. Fracture modes in brittle coatings with large interlayer modulus mismatch. J Mater Res 1999;14:3805-3817.
5. McLean JW. The Science and Art of Dental Ceramics, Vol. 1: The Nature of Dental Ceramics and Their Clinical Use. Chicago: Quintessence; 1979.
6. Kelly JR. Ceramics in restorative and prosthetic dentistry. Annu Rev Mater Sci 1997;27:443-468.
7. Kelly JR. Clinically relevant approach to failure testing of all-ceramic restorations. J Prosthet Dent 1999;81:652-661.
8. Malament KA, Socransky SS. Survival of dicor glass-ceramic dental restorations over 14 years. I. Survival of dicor complete coverage restorations and effect of internal surface acid etching, tooth position, gender and age. J Prosthet Dent 1999;81:23-32.
9. Malament KA, Socransky SS. Survival of dicor glass-ceramic dental restorations over 14 years. II. Effect of thickness of dicor material and design of tooth preparation. J Prosthet Dent 1999;81:662-667.
10. Malament KA, Socransky SS. Survival of dicor glass-ceramic dental restorations over 16 years, Part III: Effect of luting agent and tooth or tooth-substitute core structure. J Prosthet Dent 2001;86:511-519.
11. Lawn BR, Deng Y, Thompson VP. Use of contact testing in the characterization and design of all-ceramic crown-like layer structures: A review. J Prosthet Dent 2001;86:495-510.
12. Qasim T, Bush MB, Hu X, Lawn BR. Contact damage in brittle coating layers: Influence of surface curvature. J Biomed Mater Res B 2005;73:179-185.
13. Qasim T, Ford C, Bush MB, Hu X, Lawn BR. Effect of off-axis concentrated loading on failure of curved brittle layer structures. J Biomed Mater Res B 2006;76:334-339.
14. Rudas M, Qasim T, Bush MB, Lawn BR. Failure of curved brittle layer systems from radial cracking in concentrated loading. J Mater Res 2005;20:2812-2819.
15. Scherrer SS, deRijk WG. The fracture resistance of all-ceramic crowns on supporting structures with different elastic moduli. Int J Prosthodont 1993;6:462-467.
16. Lee KS, Rhee Y-W, Blackburn DH, Lawn BR, Chai H. Cracking of brittle coatings adhesively bonded to substrates of unlike modulus. J Mater Res 2000;15:1653-1656.
17. Zhang Y, Lawn BR, Rekow ED, Thompson VP. Effect of sandblasting on the long-term strength of dental ceramics. J Biomed Mater Res B 2004;71:381-386.
18. Oliver WC, Pharr GM. An improved technique for determining hardness and elastic-modulus using load and displacement sensing indentation experiments. J Mater Res 1992;7:1564-1583.
19. Mikosza AG, Lawn BR. Section-and-etch study of hertzian fracture mechanics. J Appl Phys 1971;42:5540-5545.
20. Timoshenko S, Woinowsky-Krieger S. Theory of Plates and Shells. New York: McGraw-Hill; 1959.
21. Rhee Y-W, Kim H-W, Deng Y, Lawn BR. Contact-induced damage in ceramic coatings on compliant substrates: Fracture mechanics and design. J Am Ceram Soc 2001;84:1066-1072.
22. Cao YQ. Three-dimensional finite element modeling of subsurface median crack in trilayer sandwiches due to contact loading. Eng Fract Mech 1996;69:729-743.
23. Chai H. Crack propagation in glass coatings under expanding spherical contact. J Mech Phys Solids 2006;54:447-466.
24. Wiederhorn SM. Fracture surface energy of glass. J Am Ceram Soc 1969;52:99-105.
25. Chai H, Lawn BR. Cracking in brittle laminates from concentrated loads. Acta Mater 2002;50:2613-2625.
26. Chai H, Lawn BR. Fracture mode transitions in brittle coating layers on compliant substrates as a function of thickness. J Mater Res 2004;19:1752-1761.
27. Kim H-W, Deng Y, Miranda P, Pajares A, Kim DK, Kim H-E, Lawn BR. Effect of flaw state on the strength of brittle coatings on soft substrates. J Am Ceram Soc 2001;84:2377-2384.
28. Chai H. Transverse fracture in thin-film coatings under spherical indentation. Acta Mater 2005;53:487-498.
29. Kim DK, Jung Y-G, Peterson IM, Lawn BR. Cyclic fatigue of intrinsically brittle ceramics in contact with spheres. Acta Mater 1999;47:4711-4725.
30. Zhang Y, Kwang J-K, Lawn BR. Deep penetrating conical cracks in brittle layers from hydraulic cyclic contact. J Biomed Mater Res B 2005;73:186-193.
31. Rhee Y-W, Kim H-W, Deng Y, Lawn BR. Brittle fracture versus quasiplasticity in ceramics: A simple predictive index. J Am Ceram Soc 2001;84:561-565.
32. Rudas M, Bush MB, Reimanis IE. The kinking behaviour of a bimaterial interface crack under indentation loading. Eng Anal Bound Elem 2004;28:1455-1462.
33. Qasim T, Bush MB, Hu X, Malament KA, Lawn BR. Margin cracks in brittle dome structures. J Biomed Mater Res B, in press.
34. Tabor D. Hardness of Metals. Oxford: Clarendon; 1951.
35. Zhao H, Hu X, Bush MB, Lawn BR. Cracking of porcelain coatings bonded to metal substrates of different modulus and hardness. J Mater Res 2001;16:1471-1478.