Hertzian fatigue in alumina/zirconia laminated composites;Fatiga por contacto esférico en materiales multicapa de alúmina circona

Boletin de la Sociedad Espanola de Ceramica y Vidrio

Volumn 44, Issue 5, 2005, Pages 307-312

  Jimenez Pique E ^a   Ceseracciu, L ^a   Anglada, M ^a   Chalvet, F ^b   De Portu, G ^b  

^a UNIVERSITAT POLITÈCNICA DE CATALUNYA   (Spain)

^b CNR   (Italy)

Author keywords

Alumina; Fatigue; Hertzian contact; Laminated composites; Stress corrosion cracking; Zirconia

Indexed keywords

ALUMINA; ALUMINUM OXIDE; CERAMIC MATERIALS; CRACKS; CYCLIC LOADS; LAMINATED COMPOSITES; LAMINATING; RESIDUAL STRESSES; STRESS ANALYSIS; STRESS CORROSION CRACKING; ZIRCONIA;

ALUMINA-ZIRCONIA; CERAMIC LAMINATES; CONTACT FATIGUES; ENGINEERING APPLICATIONS; HERTZIAN CONTACTS; HERTZIAN FATIGUE; LAMINATE COMPOSITES; MONOLITHIC ALUMINA;

FATIGUE OF MATERIALS;

EID: 33744823577     PISSN: 03663175     EISSN: None     Source Type: Journal    
DOI: 10.3989/cyv.2005.v44.i5.358     Document Type: Article

References (54)

1. Moya, J.S. "Layered Ceramics." Adv. Mater. 7.2 (1995): 185-189.
2. Chan, H. M. "Layered Ceramics: proceesing and mechanical behaviour." Annu. Rev. Mater. Sci..27 (1997):249-282.
3. Harner, M.P., Chan, H.M., and Miller, G. A. "Unique opportunities for microstructural engineering with duplex and laminar ceramic composites." J. Am. Ceram. Soc. 75.7 (1992): 1715-1728.
4. Lakshminarayanan, R., Shetty, D. K., and Cutler, R. A. "Toughening of layered ceramic composites with residual surface compression." J. Am. Ceram. Soc. 79.11 (1996): 79-87.
5. Tomanszewski, H., Strezeszewski, J., and Gebicki, W. "The role of residual stress in layered composites of Y-ZrO2 and Al203." J. Eur. Ceram. Soc. 19 (1999): 255-262.
6. Blattner, A.J., Lakshminarayanan, R., and Shetty, D.K. "Toughening of layered ceramic composites with residual surface compression: effect of layer thickness." Eng. Fract. Mech. 68 (2001): 1-7.
7. Sánchez-Herencia, A.J., Pascual, C., He, J., and Lange, F.F. "ZrO2/ZrO2 layered composites for crack bifurcation." J. Am. Ceram. Soc. 82.6 (1999): 1512-1518.
8. Sánchez-Herencia, A. J., James, L., and Lange, F.F. "Bifurcaion in alumina plates produced by a phase transformation in central alumina/zirconia thin layers." J. Eur. Ceram. Soc. 20.9 (2000): 1297-1300.
9. Moon, R.J., Hoffman, M., Hilden, J., Bouwman, K., Trumble, K., and Rödel, J. "Weigth function analysis on the R-curve behaviour of multilayered alumina-zirconia composites." J. Am. Ceram. Soc. 85.6 (2002): 1505-1511.
10. Moon, R., Bowman, K., Trumble, K., and Rödel, J. "Comparison of R-curves from single-edge V-notched-beam (SEVNB) and Surface-Crackin-Flexure (SCF) Fracture-Toughenss test methods on Multilayer alumina-zirconia composites." J. Am. Ceram. Soc. 83.2 (2000): 445-447.
11. Hutchinson, J.W., and Suo, Z. "Mixed mode cracking in layered materials." Adv. Appl. Mech. 29 (1992): 63-191.
12. He, M.-Y., and Hutchinson, J.W. "Crack deflection at an interface between dissimilar materials." Int. J. Solids. Struct. 25 (1989): 1053-1067.
13. He, M.-Y., Evans, A.G., and Hutchinson, J.W. "Crack deflection at an interface between dissimilar elastic materials: role of residual stresses." Int. J. Solids Structures 31.24 (1994): 3443-3455.
14. Rao, M.P., Sánchez-Herencia, A.J., Beltz, G.E., McMeeking, R.M., and Lange, F.F. "Laminar Ceramics that exhibit a threshold strength." Science 286 (1999): 102-105.
15. Rao, M.P., Rödel, J., and Lange, F.F., "Residual Stress Induced R-curve in Laminar Ceramics that exhibit a threshold strength." J. Am. Ceram. Soc. 84.11 (2001): 2722-2724.
16. Rao, M.P., and Lange, F.F. "Factors affecting threshold strength in laminar ceramics containing thin compressive layers." J. Am. Ceram. Soc. 85.5 (2002): 1222-1228.
17. Ho, S., Hillman, C., Lange, EE, and Sue, Z. "Surface cracking in layers under biaxial, residual compressive stress." J. Am. Ceram. Soc. 78.9 (1995): 2353-2359.
18. Lugovy, M, Orlovskaya, N., Slyunyayev, V., Gogotsi, G., Kübler, J., and Sanchez-Herencia, A.J. "Crack bifurcation features in laminar specimens with fixed total thickness." Comp. Sci. Tech. 62 (2002): 819-830.
19. Oechsner, M., Hillman, C., and Lange, RE "Crack bifurcation in laminar ceramic composites." J. Am. Ceram. Soc. 79.7 (1996): 1834-1838.
20. Russo C.J, Harmer M.P., Chan H.M, Miller G.A. "Design of a laminated ceramic composite for improved strength and toughness" J. Am. Ceram. Soc. 75.12 (1992): 3396-3400
21. 3 laminated composites" Wear 224 (1999): 255-262
22. Toschi, E, Melandri, C., Pinasco, R, Roncari, E., Guicciardi, S., and de Portu, G. "Influence of Residual Stresses on the wear behavior of alumina/alumina-zirconia laminated composites." J. Am. Ceram. Soc. 86.9 (2003): 1547-1553.
23. Lawn, B.R. "Indentation of ceramics with spheres: a century after Hertz." J. Am. Ceram. Soc. 81.8 (1998): 1977-1994.
24. Rhee, Y.-W, Kim, H.-W, Deng, Y., and Lawn, B.R. "Brittle fracture versus quasi plasticity in ceramics: a simple predictive index." J. Am. Ceram. Soc. 48.3 (2001): 561-565.
25. Lawn, B.R., Padture, N.P., Cai, H., and Giberteau, F. "Making ceramics "ductile"." Science 263 (1994): 1114-1116.
26. Lawn BR, Deng Y, Miranda P, Pajares A, Chai H, Kim DK "Overview: Damage in brittle layer structures from concentrated loads" J. Mater. Res. 17.12 (2002): 3019-3036
27. Miranda P, Pajares A, Guiberteau F, Deng Y, Lawn BR "Designing damage-resistant brittle-coating structures: I. Trilayers" Acta Mater. 51.14 (2003): 4347-4356
28. Miranda P, Pajares A, Guiberteau F, Deng Y, Zhao H, Lawn BR "Designing damage-resistant brittle-coating structures: II. Trilayers" Acta Mater. 51.14 (2003): 4357-4365
29. Pajares A, Miranda P, Guiberteau F, Cumbrera FI "Mechanical characterization of materials for dental applications" Revista de Metalurgia 37.2 (2001): 316-329
30. Miranda P, Pajares A, Guiberteau P. Cumbrera FL, Lawn BR "Role of flaw statistics in contact fracture of brittle coatings" Acta Mater. 49.18 (2001): 3719-3726
31. An, L., Ha, H.-C., and Chan, H. M. "High-strength alumina/alumina: calcium-Hexaluminate layer composites." J. Am. Ceram. Soc. 81.12 (1998): 3321-3324.
32. Jitcharoen J, Paciture NP, Giannakopoulos AE, Suresh S "Hertzian-crack suppression in ceramics with elastic-modulus-graded surfaces" J. Am. Ceram. Soc. 81.9 (2001): 2301-2308
33. An, L. "Indentation fatigue in random and textured alumina composites" J. Am. Ceram. Soc. 82.1(1999): 178-182
34. Kim, D.K., Jung, Y.-G., Peterson, I.M., and Lawn, B.R. "Cyclic fatigue of intrinsically brittle ceramics in contact with spheres." Acta mater. 47.18 (1999): 4711-4725.
35. Lee, K.S., Jung, Y.-G., Peterson, I.M., Lawn, B.R., Kim, D.K., and Lee, S.K. "Model for cyclic fatigue of quasi-plastic ceramics in contact with spheres." J. Am. Ceram. Soc. 83.9 (2000): 2255-7262.
36. Lee, S.K., and Lawn, B.R. "Contact fatigue in Silicon Nitride." J. Am. Ceram. Soc. 82.5 (1999): 1281-1288.
37. Fett, T., Keller, R., Munz. D., Ernst, E., and Thun, G. Fatigue of alumina under contact loading." Eng. Fract. Mech. 70 (2003): 1143-1152.
38. Fett, T., Creek, D., Badenheim, D., and Oberacker, R. "Crack growth data from dynamic tests under contact loading?." J. Eur. Ceram. Soc. 24 (2004): 2049-2034.
39. Legin Eyzop, B., and Karlsson, S. "Cyclic contact fatigue of silicon nitride." Wear 225-229 (1999): 1303-1308.
40. Legin Ezyop, B., and Karlsson, S. "Contact fatigue of silicon nitride." Wear 249 (2001): 208-213.
41. Chen, Z., Cuneo, J.C., Mecholosky, J.J., and Hu, S. "Damage processes in S13N4 bearing material under contact loading." Wear 198 (1996): 197-207.
42. Langitan, F.B., and Lawn, B.R. "Effect of reactive enviroment on the Hertzian strength of brittle solids." J. Appl. Phys. 41.8 (1970): 3357-3365.
43. Pavón, J.J., Jiménez-Piqué, E., Anglada, M., Saiz, E., Tornsia, A. "Stress corrosion cracking of a glass coating on Ti6Al4V for biomedical applications" J. Eur. Ceram. Soc.(2005) en prensa
44. Fiori, C., de Portu, G. "Tape Casting: a technique for preparing and studying new materials" pp. 213-25 en Proceedings of the British Ceramic Society No. 38,1986, Novel Ceramic Fabrication Processes and Applications. Editado por R.W. Davidge, Shelton, Stroke-on-Trent, Reino Unido, 1986.
45. Anstis, G.R., Chantikul, P. and Lawn, B.R. "A critical evaluation of indentation techniques for measuring fracture toughness: I, direct crack measurements". J. Am. Ceram. Soc. 64 (1981): 533-538
46. Roebben, G., Steen, M., Bressers, J., and van der Biest, O. "Mechanical fatigue in monolithic non-transforming ceramics." Prog. Mat. Sci. 40 (1996): 265-331.
47. Li, M., and Guiu, F.;. "Subcritical crack growth in alumina- I. Effects of grain size, specimen size and loading mode." Acta metall. mater. 43.5 (1995): 1859-1869.
48. Li, M., and Guiu, F. "Subcritical crack growth in alumina- II. Crack bridging and cyclic fatigue mechanisms." Acta metall. mater. 43.5 (1995): 1871-1884.
49. Kruzic, J.J., Cannon, R.M., and Ritchie, R.O. "Crack-size effects on cyclic and monotonic crack growth in polycristaline alumina: quantification of the role of grain bridging." J. Am. Ceram. Soc. 87.1 (2004): 93-103
50. Licht, V., Hilselmeier, R, and Fett, T. "Probability of cone crack initation due to spherical indentation due to spherical contact loading." J. Eur. Ceram. Soc. 24 (2004): 2907-2915.
51. Warren, P.D. "Determining the Fracture Toughness of Brittle Materials by Hertzian Indentation." J. Eur. Ceram. Soc. 15 (1995): 201-207.
52. Barinov, S.M., Ivanov, N.V, Orlov, S.V, and Shevchenko, V.J. "Influence of Enviroment on delayed failure of alumina ceramics." J. Eur. Ceram. Soc. 18 (1998): 2057-2063.
53. Guiu, F., Reece, M.J., and Vaughan, D.A.J. "Cyclic fatigue of ceramics." J. Mater. Sci. 26 (1991): 3275-3286.
54. Nagl, M.M.; Llanes, L.; Fernández, R. y Anglada, M. "The fatigue behaviour of Mg-PSZ and ZTA Ceramics". En Fracture Mechanics of Ceramics Vol 12, editado por Bradt R.C., Plenum Press, Nueva York (EEUU), 1996