Crack growth data from dynamic tests under contact loading?

Journal of the European Ceramic Society

Volumn 24, Issue 7, 2004, Pages 2049-2054

  Fett, T ^a   Creek, D ^b   Badenheim, D ^b   Oberacker, R ^b  

^a KARLSRUHE INSTITUTE OF TECHNOLOGY   (Germany)

^b UNIVERSITY OF KARLSRUHE   (Germany)

Author keywords

A12O3; Crack growth; Test methods

Indexed keywords

ALUMINA; CRACK PROPAGATION; STRENGTH OF MATERIALS;

BENDING TESTS; CONTACT LOADING;

CERAMIC MATERIALS;

CERAMICS; CRACK PROPAGATION;

EID: 1042266975     PISSN: 09552219     EISSN: None     Source Type: Journal    
DOI: 10.1016/S0955-2219(03)00626-5     Document Type: Article

References (8)

1. Fett T. Munz D. Thun G. Test devices for strength measurements of bars under contact loading Journal of Testing and Evaluation 29 2001 1-10
2. Fett T. Munz D. Influence of stress gradients on failure in contact strength tests with cylinder loading Engng. Fract. Mech. 69 2002 1353-1361
3. Fett T. Ernst E. Munz D. Badenheim D. Oberacker R. Effect of multiaxiality and stress gradients on failure in cylinder contact strength tests J. Eur. Ceram. Soc. 23 2003 2031-2037
4. Richard, H. A., Prediction of Fracture of Cracks Subjected to Combined Tensile and Shear Loads (in German), VDI Research Report 631/85. 1985, Düsseldorf, Germany.
5. Fett T. Munz D. Kinked cracks and Richard fracture criterion Int. J. Fracture 115 2002 L69-L73
6. Cotterell B. Rice J.R. Slightly curved or kinked cracks Int. J. Fracture 16 1980 155-169
7. Thoman D.R. Bain L.J. Antle C.E. Inferences on the parameters of the Weibull distribution Technometrics 11 1969 445
8. 3, determined by different methods J. Mater. Sci. Lett. 22 2003 363-365