Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: Bilayer structures

Journal of Materials Research

Volumn 20, Issue 10, 2005, Pages 2792-2800

  Bhowmick, Sanjit ^a   Zhang, Yu ^b   Lawn, Brian R ^a  

^a NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

^b NEW YORK UNIVERSITY COLLEGE OF DENTISTRY   (United States)

Author keywords

[No Author keywords available]

Indexed keywords

BRITTLE FRACTURE; BRITTLENESS; COMPRESSIVE STRESS; CRACK PROPAGATION; CRACKS; INDENTATION; PLASTICITY; POLYCARBONATES; SOLIDS; SUBSTRATES; TENSILE STRESS;

BILAYER STRUCTURES; FRACTURE MODES; QUASIPLASTICITY ZONES; SODA LIME GLASS;

GLASS;

EID: 29144439840     PISSN: 08842914     EISSN: None     Source Type: Journal    
DOI: 10.1557/JMR.2005.0335     Document Type: Article

References (16)

1. Y. Zhang, S. Bhowmick, and B.R. Lawn: Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: Monoliths. J. Mater. Res. 20, 2021 (2005).
2. B.R. Lawn, Y. Deng, P. Miranda, A. Pajares, H. Chai, and D.K. Kim: Overview: Damage in brittle layer structures from concentrated loads. J. Mater. Res. 17, 3019 (2002).
3. Y. Zhang, J-K. Kwang, and B.R. Lawn: Deep penetrating conical cracks in brittle layers from hydraulic cyclic contact. J. Biomed. Mater. Res. B 73B, 186 (2005).
4. D.K. Kim, Y-G. Jung, I.M. Peterson, and B.R. Lawn: Cyclic fatigue of intrinsically brittle ceramics in contact with spheres. Acta Mater. 47, 4711 (1999).
5. H. Chai, B.R. Lawn, and S. Wuttiphan: Fracture modes in brittle coatings with large interlayer modulus mismatch. J. Mater. Res. 14, 3805 (1999).
6. Y-W. Rhee, H-W. Kim, Y. Deng, and B.R. Lawn: Contact-induced damage in ceramic coatings on compliant substrates: Fracture mechanics and design. J. Am. Ceram. Soc. 84, 1066 (2001).
7. Y. Deng, B.R. Lawn, and I.K. Lloyd: Characterization of damage modes in dental ceramic bilayer structures. J. Biomed. Mater. Res. 63B, 137 (2002).
8. B.R. Lawn, Y. Deng, and V.P. Thompson: Use of contact testing in the characterization and design of all-ceramic crown-like layer structures: A review. J. Prosthet. Dent. 86, 495 (2001).
9. B.R. Lawn, S.K. Lee, I.M. Peterson, and S. Wuttiphan: Model of strength degradation from Hertzian contact damage in tough ceramics. J. Am. Ceram. Soc. 81, 1509 (1998).
10. H. Chai and B.R. Lawn: Hydraulically pumped cone fractures in brittle solids. (in press).
11. B.R. Lawn, K.S. Lee, H. Chai, A. Pajares, D.K. Kim, S. Wuttiphan, I.M. Peterson, and X. Hu: Damage-resistant brittle coatings. Adv. Eng. Mater. 2, 745 (2000).
12. T. Qasim, M.B. Bush, X. Hu and B.R. Lawn: Contact damage in brittle coating layers: Influence of surface curvature. J. Biomed. Mater. Res. 73B 179, (2005).
13. Y. Deng, P. Miranda, A. Pajares, and B.R. Lawn: Fracture of ceramic/ ceramic/polymer trilayers for biomechanical applications. J. Biomed. Mater. Res. 67A, 828 (2003).
14. S. Timoshenko and S. Woinowsky-Krieger: Theory of Plates and Shells (McGraw-Hill, New York, 1959).
15. S.M. Wiederhorn and L.H. Bolz: Stress corrosion and static fatigue of glass. J. Am. Ceram. Soc. 53, 543 (1970).
16. S.M. Wiederhorn: A chemical interpretation of static fatigue. J. Am. Ceram. Soc. 55, 81 (1972).