Fatigue sensitivity of Y-TZP to microscale sharp-contact flaws

Journal of Biomedical Materials Research - Part B Applied Biomaterials

Volumn 72, Issue 2, 2005, Pages 388-392

  Zhang, Yu ^a   Lawn, Brian R ^b  

^a NEW YORK UNIVERSITY COLLEGE OF DENTISTRY   (United States)

^b NATIONAL INSTITUTE OF STANDARDS AND TECHNOLOGY   (United States)

Author keywords

Biomechanical ceramics; Cyclic fatigue; Microcracks; Sharp contacts

Indexed keywords

DIAMONDS; ELASTIC MODULI; FATIGUE TESTING; INDENTATION; PLASTICS; SUBSTRATES;

CERAMIC PLATES; FATIGUE SENSITIVITY; PLASTIC SUBSTRATES; SHARP-CONTACT DAMAGE;

CERAMIC MATERIALS;

TOOTH CEMENT;

ARTICLE; BIOMECHANICS; CERAMIC PROSTHESIS; COMPRESSIVE STRENGTH; DENTAL BONDING; FATIGUE; TENSILE STRENGTH; WEIGHT BEARING;

EQUIPMENT FAILURE ANALYSIS; MECHANICS; MICROSCOPY, ATOMIC FORCE; PROSTHESIS FAILURE; SURFACE PROPERTIES; YTTRIUM; ZIRCONIUM;

EID: 12744254880     PISSN: 00219304     EISSN: None     Source Type: Journal    
DOI: 10.1002/jbm.b.30174     Document Type: Article

References (40)

1. Lawn, BR, Evans AG, Marshall DB. Elastic/plastic indentation damage in ceramics: the median/radial crack system. J Am Ceram Soc 1980;63:574-581.
2. Reece M, Guiu F, Sammur MFR. Cyclic fatigue crack propagation in alumina under direct tension-compression loading of high-purity alumina in fluid environments. J Am Ceram Soc 1989;72:348-352.
3. Guiu F, Reece M, Vaughan DAJ. Cyclic fatigue of ceramics. J Mater Sci 1991;26:3275-3286.
4. Reece M, Guiu F. Indentation fatigue of high-purity alumina in fluid environments. J Am Ceram Soc 1991;74:148-154.
5. Guiberteau F, Padture NP, Cai H, Lawn BR. Indentation fatigue: a simple cyclic Hertzian test for measuring damage accumulation in polycrystalline ceramics. Philos Mag 1993;A68:1003-1016.
6. Cai H, Kalceff MAS, Hooks BM, Lawn BR, Chyung K. Cyclic fatigue of a mica-containing glass-ceramic at Hertzian contacts. J Mater Res 1994;9:2654-2661.
7. Lawn BR, Padture NP, Cai H, Guiberteau F. Making ceramics ductile. Science 1994;263:1114-1116.
8. Padture NP, Lawn BR. Contact fatigue of a silicon carbide with a heterogeneous grain structure. J Am Ceram Soc 1995;78:1431-1438.
9. Padture NP, Lawn BR. Fatigue in ceramics with interconnecting weak interfaces: a study using cyclic Hertzian contacts. Acta Metall 1995;43:1609-1617.
10. Pajares A, Wei L, Lawn BR, Marshall DB. Damage accumulation and cyclic fatigue in Mg-PSZ at Hertzian contacts. J Mater Res 1995;10:2613-2625.
11. Peterson IM, Pajares A, Lawn BR, Thompson VP, Rekow ED. Mechanical characterization of dental ceramics using Hertzian contacts. J Dent Res 1998;77:589-602.
12. Lee SK, Lawn BR. Contact fatigue in silicon nitride. J Am Ceram Soc 1999;82:1281-1288.
13. Jung Y-G, Peterson IM, Kim DK, Lawn BR. Lifetime-limiting strength degradation from contact fatigue in dental ceramics. J Dent Res 2000;79:722-731.
14. Lee KS, Jung Y-G, Peterson IM, Lawn BR, Kim DK, Lee SK. Model for cyclic fatigue of quasiplastic ceramics in contact with spheres. J Am Ceram Soc 2000;83:2255-2262.
15. Lawn BR, Deng Y, Miranda P, Pajares A, Chai H, Kim DK. Overview: damage in brittle layer structures from concentrated loads. J Mater Res 2002;17:3019-3036.
16. Lawn BR, Pajares A, Zhang Y, Deng Y, Polack M, Lloyd IK, et al. Materials design in the performance of all-cCeramic crowns. Biomaterials 2004;25:2885-2892.
17. Zhang Y, Pajares A, Lawn BR. Fatigue and damage tolerance of Y-TZP ceramics in layered biomechanical systems. J Biomed Mater Res 2004;71B:166-171.
18. Zhang Y, Lawn BR, Rekow ED, Thompson VP. Effect of sandblasting on the long-term strength of dental ceramics. J Biomed Mater Res 2004;71B:381-386.
19. Willmann G. Ceramic femoral heads for total hip arthroplasty. Adv Eng Mater 2000;2:114-122.
20. Willmann G. Improving bearing surfaces of artificial joints. Adv Eng Mater 2001;3:135-141.
21. Ritchie RO. Mechanisms of fatigue crack propagation in ductile and brittle solids. Int J Fract 1998;100:55-83.
22. Kelly JR. Ceramics in restorative and prosthetic dentistry. Ann Rev Mater Sci 1997;27:443-468.
23. Kelly JR. Clinically relevant approach to failure testing of all-ceramic restorations. J Prosthet Dent 1999;81:652-661.
24. Lawn BR, Deng Y, Thompson VP. Use of contact testing in the characterization and design of all-ceramic crown-like layer structures: a review. J Prosthet Dent 2001;86:495-510.
25. Zhang Y, Lawn BR. Long-term strength of ceramics for biomedical Applications. J Biomed Mater Res 2004;69B:166-172.
26. Lawn BR, Marshall DB. Hardness, toughness, and brittleness: an indentation analysis. J Am Ceram Soc 1979;62:347-350.
27. Deng Y, Lawn BR, Lloyd IK. Characterization of damage modes in dental ceramic bilayer structures. J Biomed Mater Res 2002;63B:137-145.
28. Deng Y, Miranda P, Pajares A, Lawn BR. Fracture of ceramic/ceramic/ polymer trilayers for biomechanical applications. J Biomed Mater Res 2003;67A:828-833.
29. Chai H, Lawn BR, Wuttiphan S. Fracture modes in brittle coatings with large interlayer modulus mismatch. J Mater Res 1999;14:3805-3817.
30. Miranda P, Pajares A, Guiberteau F, Deng Y, Lawn BR. Designing damage-resistant brittle-coating structures: I. Bilayers. Acta Mater 2003;51:4347-4356.
31. Readey MJ, McCallen CL, McNamara P, Lawn BR. Correlations between flaw tolerance and reliability in zirconia. J Mater Sci 1993;28:6748-6752.
32. Cook RF, Braun LM, Cannon WR. Trapped cracks at indentations: I. Experiments on yttria-tetragonal zirconia polycrystals. J Mater Sci 1994;29:2133-2142.
33. Marshall DB, Lawn BR, Chantikul P. Residual stress effects in sharp-contact cracking: II. Strength degradation. J Mater Sci 1979;14:2225-2235.
34. Lathabai S, Mai Y-W, Lawn BR. Cyclic fatigue behavior of an alumina ceramic with crack-resistance curves. J Am Ceram Soc 1989;72:1760-1763.
35. Lee SK, Tandon R, Readey MJ, Lawn BR. Scratch damage in zirconia ceramics. J Am Ceram Soc 2000;83:1428-1432.
36. Kosmac T, Oblak C, Jevnikar P, Funduk N, Marion L. The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic. Dent Mater 1999;15: 426-433.
37. Kosmac T, Oblak C, Jevnikar P, Funduk N, Marion L. Strength and reliability of surface treated Y-TZP dental ceramics. J Biomed Mater Res 2000;53:304-313.
38. Pajares A, Guiberteau F, Lawn BR, Lathabai S. Hertzian contact damage in magnesia-partially-stabilized zirconia. J Am Ceram Soc 1995;78:1083-1086.
39. Lawn BR, Kim DK, Lee SK, Jung Y-G, Peterson IM. Cyclic contact fatigue of brittle ceramics. In: Wu XR, Wang ZG, editors. The Seventh International Fatigue Conference, Fatigue 99. Beijing; Higher Education Press: 1999. p 69-80.
40. Kim DK, Jung Y-G, Peterson IM, Lawn BR. Cyclic fatigue of intrinsically brittle ceramics in contact with spheres. Acta Mater 1999;47:4711 Wu XR and Wang ZG, editor. 4725.