Evaluation of air-particle abrasion of Y-TZP with different particles using microstructural analysis

Australian Dental Journal

Volumn 58, Issue 2, 2013, Pages 183-191

  Turp, V ^a   Sen, D ^a   Tuncelli, B ^a   Goller, G ^b   Ozcan M ^c  

^a ISTANBUL UNIVERSITY   (Turkey)

^b ISTANBUL TECHNICAL UNIVERSITY   (Turkey)

^c UNIVERSITY OF ZURICH   (Switzerland)

Author keywords

Air particle abrasion; profilometry; surface roughness; XRD analysis; Y TZP

Indexed keywords

ALUMINUM OXIDE; SILICON DIOXIDE; YTTRIA STABILIZED TETRAGONAL ZIRCONIA; YTTRIUM; ZIRCONIUM;

ARTICLE; CERAMICS; CHEMISTRY; DENTAL PROCEDURE; MATERIALS TESTING; METHODOLOGY; PARTICLE SIZE; SURFACE PROPERTY;

ALUMINUM OXIDE; CERAMICS; DENTAL STRESS ANALYSIS; MATERIALS TESTING; PARTICLE SIZE; SILICON DIOXIDE; SURFACE PROPERTIES; YTTRIUM; ZIRCONIUM;

EID: 84878405299     PISSN: 00450421     EISSN: 18347819     Source Type: Journal    
DOI: 10.1111/adj.12065     Document Type: Article

References (27)

1. Filser F, Kocher P, Weibel F, Lüthy H, Schärer P, Gauckler LJ,. Reliability and strength of all-ceramic dental restorations fabricated by direct ceramic machining (DCM). Int J Compt Dent 2001; 4: 89-106.
2. Miyazaki T, Hotta Y, Kunii J, Fujiwara T,. Current status and future prospects of a dental CAD/CAM system used in crown-bridge restorations. Dent Jpn 2007; 43: 189-194.
3. Chevalier J,. What future for zirconia as a biomaterial? Biomaterials 2006; 27: 535-543.
4. Piconi C, Maccauro G,. Zirconia as a ceramic biomaterial. Biomaterials 1999; 20: 1-25.
5. Blatz MB, Sadan A, Kern M,. Resin-ceramic bonding: a review of the literature. J Prosthet Dent 2003; 89: 268-274.
6. Özcan M, Vallittu PK,. Effect of surface conditioning methods on the bond strength of luting cement to ceramics. Dent Mater 2003; 19: 725-731.
7. Edelhoff D, Özcan M,. To what extent does the longevity of fixed dental prostheses depend on the function of the cement? Clin Oral Implants Res 2007; 18: 193-204.
8. Özcan M, Kerkdijk S, Valandro LF,. Comparison of resin cement adhesion to Y-TZP ceramic following manufacturers' instructions of the cements only. Clin Oral Investig 2008; 12: 279-282.
9. Özcan M, Pfeiffer P, Nergiz I,. A brief history and current status of metal/ceramic surface conditioning concepts for resin bonding in dentistry. Quintessence Int 1998; 29: 713-724.
10. Özcan M,. Evaluation of alternative intraoral repair techniques for fractured ceramic-fused-to-metal restorations. J Oral Rehabil 2003; 30: 194-203.
11. Guazzato M, Quach L, Albakry M, Swain MV,. Influence of surface and heat treatments on the flexural strength of Y-TZP dental ceramics. J Dent 2005; 33: 9-18.
12. Deville S, Chevalier J, Gremillard L,. Influence of surface finish and residual stresses on the ageing sensitivity of biomedical grade zirconia. Biomaterials 2006; 27: 2186-2192.
13. Garvie RC, Nicholson PS,. Phase analysis in zirconia systems. J Am Ceram Soc 1972; 55: 303-330.
14. 2 system by X-ray diffraction. J Am Ceram Soc 1984; 67: 119-121.
15. Koutayas O, Vagkopoulou T, Pelekanos S, Koidis P, Strub JR,. Zirconia in dentistry. Part 2. Evidence-based clinical breakthrough. Eur J Esthet Dent 2009; 4: 348-380.
16. Aboushelib MN, Feilzer AJ, Kleverlaan CJ,. Bonding to zirconia using a new surface treatment. J Prosthodont 2010; 19: 340-346.
17. Bachhav VC, Aras MA,. Zirconia-based fixed partial dentures: a clinical review. Quintessence Int 2011; 42: 173-182.
18. Cavalcanti AN, Foxton RM, Watson TF, Oliveira MT, Giannini M, Marchi GM,. Y-TZP ceramics: key concepts for clinical application. Oper Dent 2009; 34: 344-351.
19. Mizrahi B,. The anterior all-ceramic crown: a rationale for the choice of ceramic and cement. Br Dent J 2008; 205: 251-255.
20. Kosmac T, Oblak C, Jevnikar P, Funduk N, Marion L,. The effect of surface grinding and sandblasting on flexural strength and reliability of Y-TZP zirconia ceramic. Dent Mater 1999; 15: 426-433.
21. Amaral R, Özcan M, Bottino MA, Valandro LF,. Microtensile bond strength of a resin cement to glass infiltrated zirconia-reinforced ceramic: the effect of surface conditioning. Dent Mater 2006; 22: 283-290.
22. Denry IL, Holloway JA,. Microstructural and crystallographic surface changes after grinding zirconia-based dental ceramics. J Biomed Mater Res Part B: Appl Biomater 2006; 76: 440-448.
23. Kosmac T, Oblac C, Jevnikar P, Funduk N, Marion L,. Strength and reliability of surface treated Y-TZP dental ceramics. J Biomed Mater Res 2000; 53: 304-313.
24. ISO Standard 13356: 2008. Implants for surgery-Ceramic materials based on yttria-stabilized tetragonal zirconia (Y-TZP).
25. Lughi V, Sergo V,. Low temperature degradation -aging- of zirconia: a critical review of the relevant aspects in dentistry. Dent Mater 2010; 26: 807-820.
26. Wang H, Aboushelib MN, Feilzer AJ,. Strength influencing variables on CAD/CAM zirconia frameworks. Dent Mater 2008; 24: 633-638.
27. Sato H, Yamada K, Pezzotti G, Nawa M, Ban S,. Mechanical properties of dental zirconia ceramics changed with sandblasting and heat treatment. Dent Mater J 2008; 27: 408-414.