Influence of surface treatment of yttria-stabilized tetragonal zirconia polycrystal with hot isostatic pressing on cyclic fatigue strength

Dental Materials Journal

Volumn 32, Issue 2, 2013, Pages 274-280

  Toshihiko, Iijima ^a   Shinya, Homma ^a   Hideshi, Sekine ^a   Hodaka, Sasaki ^a   Yasutomo, Yajima ^a   Masao, Yoshinari ^a  

^a TOKYO DENTAL COLLEGE   (Japan)

Author keywords

Fatigue strength; Hot isostatic pressing; Surface topography; Y tzp

Indexed keywords

BI-AXIAL FLEXURAL STRENGTH; CYCLIC FATIGUE; CYCLIC FATIGUE TESTS; DISTILLED WATER; FATIGUE STRENGTH; MECHANICAL PERFORMANCE; Y-TZP; YTTRIA-STABILIZED TETRAGONAL ZIRCONIA POLYCRYSTALS;

FATIGUE TESTING; HOT ISOSTATIC PRESSING; POLYCRYSTALS; SURFACE TOPOGRAPHY; SURFACE TREATMENT; YTTRIUM ALLOYS; ZIRCONIA;

YTTRIA STABILIZED ZIRCONIA;

ALUMINUM OXIDE; DENTAL MATERIAL; HYDROFLUORIC ACID; WATER; YTTRIA STABILIZED TETRAGONAL ZIRCONIA; YTTRIUM; ZIRCONIUM;

ARTICLE; CHEMISTRY; COMPARATIVE STUDY; CONTROLLED CLINICAL TRIAL; CONTROLLED STUDY; CRYSTALLOGRAPHY; DENTAL ACID ETCHING; DENTAL ETCHING; DENTAL PROCEDURE; EQUIPMENT; HEAT; HUMAN; MATERIALS TESTING; MECHANICAL STRESS; METHODOLOGY; PHASE TRANSITION; PLIABILITY; PRESSURE; RANDOMIZED CONTROLLED TRIAL; SCANNING ELECTRON MICROSCOPY; SURFACE PROPERTY; TEMPERATURE; TIME; TOOTH BRUSHING; DEVICES; PROCEDURES; TIME FACTOR;

ACID ETCHING, DENTAL; ALUMINUM OXIDE; CRYSTALLOGRAPHY; DENTAL ETCHING; DENTAL MATERIALS; DENTAL POLISHING; DENTAL STRESS ANALYSIS; HOT TEMPERATURE; HUMANS; HYDROFLUORIC ACID; MATERIALS TESTING; MICROSCOPY, ELECTRON, SCANNING; PHASE TRANSITION; PLIABILITY; PRESSURE; STRESS, MECHANICAL; SURFACE PROPERTIES; TEMPERATURE; TIME FACTORS; WATER; YTTRIUM; ZIRCONIUM;

EID: 84875893636     PISSN: 02874547     EISSN: 18811361     Source Type: Journal    
DOI: 10.4012/dmj.2012-247     Document Type: Article

References (34)

1. Pittayachawan P, McDonald A, Young A, Knowles JC. Flexural strength, fatigue life, and stress-induced phase transformation study of Y-TZP dental ceramic. J Biomed Mater Res B Appl Biomater 2009; 88: 366-377.
2. Sevilla P, Sandino C, Arciniegas M, Martínez-Gomis J, Peraire M, Gil FJ. Evaluating mechanical properties and degradation of YTZP dental implants. Mater Sci Eng C 2010; 30: 14-19.
3. Oliva J, Oliva X, Oliva JD. One-year follow-up of first consecutive 100 zirconia dental implants in humans: a comparison of 2 different rough surfaces. Int J Oral Maxillofac Implants 2007; 22: 430-435.
4. Lalor PA, Revell PA, Gray AB, Wright S, Railton GT, Freeman MAR. Sensitivity to titanium. A cause of implant failure? J Bone Joint Surg 1991; 73-B: 25-28.
5. Olmedo DG, Paparella ML, Brandizzi D, Cabrini RL. Reactive lesions of peri-implant mucosa associated with titanium dental implants:a report of 2 cases. Int J Oral Maxillofac Surg 2010; 39: 503-507
6. Gahlert M, Gudehus T, Eichhorn S, Steinhauser E, Kniha H, Erhardt W. Biomechanical and histomorphometric comparison between zirconia implants with varying surface textures and a titanium implant in the maxilla of miniature pigs.Clin Oral Implants Res 2007;18: 662-668.
7. Akagawa Y, Ichikawa Y, Nikai H, Tsuru H. Interface histology of unloaded and early loaded partially stabilized zirconia endosseous implant in initial bone healing. J Prosthet Dent 1993; 69: 599-604.
8. Scarano A, Di Carlo F, Quaranta M, Piattelli A. Bone response to zirconia ceramic implants: an experimental study in rabbits. J Oral Implantol 2003; 29: 8-12.
9. Sennerby L, Dasmah A, Larsson B, Iverhed M. Bone tissue responses to surface-modified zirconia implants: A histomorphometric and removal torque study in the rabbit. Clin Implant Dent Relat Res 2005; 7 suppl 1: S13-S20.
10. Chevalier J, Gremillard L, Deville S. Low-temperature degradation of zirconia and implications for biomedical implants. Annu Rev Mater Res 2007; 37: 1-32.
11. Chevalier J, Cales B, Drouin JM. Low-temperature aging of Y-TZP ceramics. J Am Ceram Soc 1999; 82: 2150-2154.
12. Guo X. Property degradation of tetragonal zirconia induced by low-temperature defect reaction with water molecules. Chem Mater 2004; 16: 3988-3994.
13. Piconi C, Maccauro G. Zirconia as a ceramic biomaterial. Biomaterials 1999; 20: 1-25.
14. Studart AR, Filser F, Kocher P, Gauckler LJ. In vitro lifetime of dental ceramics under cyclic loading in water. Biomaterials 2007; 28: 2695-2705.
15. 3 Ceramics. J Am Ceram Soc 1986; 69: 638-640.
16. Druschitz AP, Schroth JG. Hot isostatic pressing of a presintered yttria-stabilized zirconia ceramic. J Am Ceram Soc 1989; 72: 1591-1597.
17. Khraisat A, Stegaroiu R, Nomura S, Miyakawa O. Fatigue resistance of two implant/abutment joint designs. J Prosthet Dent 2002; 88: 604-610.
18. Norton MR. An in vitro evaluation of the strength of an internal conical interface compared to a butt joint interface in implants design. Clin Oral Implants Res 1997; 8: 290-298.
19. Möllersten L, Lockowandt P, Lindén LA. Comparison of strength and failure mode of seven implant systems: an in vitro test. J Prosthet Dent 1997; 78: 582-591.
20. Kosmac T, Oblak C, Jevnikar P, Funduk N, Marion L. Strength and reliability of surface treated Y-TZP dental ceramics. J Biomed Mater Res 2000; 53: 304-313.
21. Pittayachawan P, McDonald A, Petrie A, Knowles JC. The biaxial flexural strength and fatigue property of Lava Y-TZP dental ceramic. Dent Mater 2007; 23: 1018-1029.
22. Zhang Y, Pajares A, Lawn BR. Fatigue and damage tolerance of Y-TZP ceramics in layered biomechanical systems. J Biomed Mater Res B Appl Biomater 2004; 71: 166-171.
23. 3 nanocomposite with different surfaces. J Dent Res 2012; 91: 800-804.
24. Koch FP, Weng D, Kramer S, Biesterfeld S, Jahn-Eimermacher A, Wagner W. Osseointegration of one-piece zirconia implants compared with a titanium implant of identical design: a histomorphometric study in the dog. Clin Oral Implants Res 2010; 21: 350-356.
25. Teixeira EC, Piascik JR, Stoner BR, Thompson JY. Dynamic fatigue and strength characterization of three ceramic materials. J Mater Sci Mater Med 2007; 18: 1219-1224.
26. Collins JA. Failure of materials in mechanical design: Analysis, prediction, prevention. New York: John Wiley & Sons; 1981. p. 360-378.
27. Garvie RC, Nicholson PS. Phase analysis in zirconia systems. J Am Ceram Soc 1972; 55: 303-305.
28. Ban S, Anusavice KJ. Influence of test method on failure stress of brittle dental materials. J Dent Res 1990; 69: 1791-1799.
29. Little RE, Jebe EH. Fitting the P-S curve: Statistical design of fatigue experiments. New York-Toronto: A halsted press book, A division of John Wiley & Sons 1975. p. 168-197. 30) Yamamoto M, Takahashi H. Tensile fatigue strength of light cure composite resins for posterior teeth. Dent Mater J 1995; 14: 175-184.
30. Kim JY, Uchida N, Uematsu K. Effect of hiping defect and strength characteristics in y-tzp. J Ceram Soc Jpn 1992; 100: 311-314 (in Japanese).
31. Hirano M. Inhibition of Low temperature degradation of tetragonal zirconia ceramics a review. Br Ceram Trans J 1992; 91: 139-147.
32. Zinelis S, Thomas A, Syres K, Silikas N, Eliades G. Surface characterization of zirconia dental implants. Dent Mater 2010; 26: 295-305.
33. Benzaid R, Chevalier J, Saadaoui M, Fantozzi G, Nawa M, Diaz LA, Torrecilla R. Fracture toughness, strength and slow crack growth in a ceria stabilized zirconia-alumina nanocomposite for medical applications. Biomaterials 2008; 29: 3636-3641.
34. Shojai F, Mäntylä TA. Structuralstability of yttria doped zirconia membranes in acid and basic aqueous solutions. J Eur Ceram Soc 2001; 21: 37-44.