Identification of oxygen vacancy types from Raman spectra of SnO 2 nanocrystals

Journal of Raman Spectroscopy

Volumn 43, Issue 10, 2012, Pages 1423-1426

  Liu, L Z ^a   Li, T H ^a,b   Wu, X L ^a   Shen, J C ^a   Chu, P K ^c  

^a NANJING UNIVERSITY   (China)

^b GUANGXI NORMAL UNIVERSITY   (China)

^c CITY UNIVERSITY OF HONG KONG   (Hong Kong)

Author keywords

annealing processing; density functional calculation; oxygen vacancies; Raman spectroscopy

Indexed keywords

HYDROTHERMAL SYNTHESIS; LASER ABLATION; NANOCRYSTALS; OXYGEN VACANCIES; RAMAN SCATTERING;

ANNEALING PROCESSING; ANNEALING TEMPERATURES; BRIDGING OXYGEN; BULK MATERIALS; DENSITY-FUNCTIONAL CALCULATIONS; PULSED LASER ABLATION; RAMAN MODES; SNO 2;

DENSITY FUNCTIONAL THEORY;

EID: 84867579937     PISSN: 03770486     EISSN: 10974555     Source Type: Journal    
DOI: 10.1002/jrs.4078     Document Type: Article

References (24)

1. S. Brovelli, A. Chiodini, A. Lauria, F. Meinardi, A. Paleari, Phys. Rev. B 2006, 73, 073406.
2. C. Killic, A. Zunger, Phys. Rev. Lett. 2002, 88, 095501.
3. S. O. Kucheyev, T. F. Baumann, P. A. Sterne, Y. M. Wang, T. Buuren, A. V. Hamza, L. J. Terminello, T. M. Willey, Phys. Rev. B 2005, 72, 035404.
4. Y. Idota, T. Kubota, A. Matsufuji, Y. Maekawa, T. Miyasaka, Science 1997, 276, 1395.
5. R. Asahi, T. Morijawa, T. Ohwaki, K. Aoki, Y. Taga, Science, 2001, 293, 269.
6. Y. J. Chen, L. Nie, X. Y. Xue, Y. G. Wang, T. H. Wang, Appl. Phys. Lett. 2006, 88, 083105.
7. L. Z. Liu, X. X. Li, X. L. Wu, X. T. Chen, P. K. Chu, Appl. Phys. Lett. 2011, 98, 133102.
8. J. Q. Hu, Y. Bando, Q. L. Liu, D. Golberg, Adv. Funct. Mater. 2003, 13, 493.
9. H. T. Chen, S. J. Xiong, X. L. Wu, J. Zhu, J. C. Shen, P. K. Chu, Nano Lett. 2009, 1926.
10. E. J. H. Lee, C. Ribeiro, T. R. Giraldi, E. Longo, E. R. Leite, J. A. Varela, Appl. Phys. Lett. 2004, 84, 1745.
11. L. H. Jiang, G. Q. Sun, Z. H. Zhou, S. G. Sun, Q. Wang, S. Y. Yan, H. Q. Li, J. Tian, J. S. Guo, B. Zhou, Q. Xin, J. Phys. Chem. B 2005, 109, 8774.
12. M. A. Mäki-Jaskari, T. T. Rantal, Phys. Rev. B 2002, 65, 245428.
13. L. Z. Liu, X. L. Wu, F. Gao, J. C. Shen, T. H. Li, P. K. Chu, Solid State Commun. 2011, 151, 811.
14. T. Hirata, K. Ishioka, M. Kitajima, H. Doi, Phys. Rev. B 1996, 53, 8442.
15. T. H. Li, L. Z. Liu, X. L. Wu, J. C. Shen, F. Gao, P. K. Chu, Appl. Phys. Lett. 2010, 97, 121901.
16. J. Zou, C. Y. Xu, X. M. Liu, C. S. Wang, C. Y. Wang, Y. Hu, Y. T. Qian, J. Appl. Phys. 1994, 75, 1835.
17. L. Abello, B. Bochu, A. Gaskov, S. Koudryavtseva, G. Lucazeau, M. Roumyantseva, J. Solid State Chem. 1998, 135, 78.
18. A. Diéguez, A. Romano-Rodríguez, A. Vilö, J. R. Morante, J. Appl. Phys. 2001, 90, 1550.
19. L. Z. Liu, X. L. Wu, Z. Y. Zhang, T. H. Li, P. K. Chu, Appl. Phys. Lett. 2009, 95, 093109.
20. I. H. Campbell, P. M. Fauchtet, Solid State Commun. 1986, 58, 739.
21. T. H. Li, L. Z. Liu, X. X. Li, X. L. Wu, H. T. Chen, P. K. Chu, Opt. Lett. 2011, 36 4296.
22. K. N. Yu, Y. H. Xiong, Y. L. Liu, C. S. Xiong, Phys. Rev. B 1997, 55, 2666.
23. L. Z. Liu, X. L. Wu, J. C. Shen, T. H. Li, F. Gao, P. K. Chu, Chem. Comm. 2010, 46, 5539.
24. B. G. Pfrommer, M. Cote, S. G. Louie, M. L. J. Cohen, J. Comput. Phys. 1997, 131, 233.