One-pot hydrothermal synthesis of heterostructured ZnO/ZnS nanorod arrays with high ethanol-sensing properties

Chemistry - A European Journal

Volumn 18, Issue 15, 2012, Pages 4681-4686

  Gao, Peng ^a   Wang, Longqiang ^a   Wang, Ying ^a   Chen, Yujin ^a   Wang, Xiaona ^a   Zhang, Guoli ^a  

^a HARBIN ENGINEERING UNIVERSITY   (China)

Author keywords

hydrothermal synthesis; nanorods; nanostructures; photoluminescence; zinc

Indexed keywords

AXIAL DIRECTION; EPITAXIAL RELATIONSHIPS; GREEN EMISSIONS; HIGH SENSITIVITY; HYDROTHERMAL METHODS; LOW TEMPERATURES; NANOROD ARRAYS; ONE POT; ONE-POT PROCEDURES; STRUCTURAL CHARACTERIZATION; UNIFORM DIAMETER; ZINC-BLENDE; ZNO;

ETHANOL; HYDROTHERMAL SYNTHESIS; NANOSTRUCTURES; PHOTOLUMINESCENCE; ZINC; ZINC OXIDE; ZINC SULFIDE;

NANORODS;

EID: 84859245833     PISSN: 09476539     EISSN: 15213765     Source Type: Journal    
DOI: 10.1002/chem.201102927     Document Type: Article

References (43)

1. J. T. Hu, T. W. Odom, C. M. Lieber, Acc. Chem. Res. 1999, 32, 435-445
2. X. S. Fang, T. Y. Zhai, U. K. Gautam, L. Li, L. M. Wu, Y. Bando, D. Golberg, Prog. Mater. Sci. 2011, 56, 175-287
3. X. S. Fang, Y. Bando, M. Y. Liao, U. K. Gautam, C. Y. Zhi, B. Dierre, B. D. Liu, T. Y. Zhai, T. Sekiguchi, Y. Koide, D. Golberg, Adv. Mater. 2009, 21, 2034-2039
4. J. Q. Sun, X. P. Shen, K. M. Chen, Q. Liu, W. Liu, Solid State Commun. 2008, 147, 501-504
5. X. S. Fang, Y. Bando, G. Z. Shen, C. H. Ye, U. K. Gautam, P. M. F. J. Costa, C. Y. Zhi, C. C. Tang, D. Golberg, Adv. Mater. 2007, 19, 2593-2596
6. X. S. Fang, U. K. Gautam, Y. Bando, B. Dierre, T. Sekiguchi, D. Golberg, J. Phys. Chem. C. 2008, 112, 4735-4742
7. L. F. Hu, J. Yan, M. Y. Liao, L. M. Wu, X. S. Fang, Small 2011, 7, 1012-1017
8. G. C. Xi, Y. T. He, C. Wang, Chem. Eur. J. 2010, 16, 5184-5190
9. X. S. Fang, L. F. Hu, K. F. Huo, B. Gao, L. J. Zhao, M. Y. Liao, P. K. Chu, Y. Bando, D. Golberg, Adv. Funct. Mater. 2011, 21, 3907-3915
10. C. C. Li, X. M. Yin, L. B. Chen, Q. H. Li, T. H. Wang, Chem. Eur. J. 2010, 16, 5215-5221.
11. M. S. Gudiksen, L. J. Lauhon, J. Wang, D. C. Smith, C. M. Lieber, Nature 2002, 415, 617-620.
12. W. I. Park, G. C. Yi, M. Y. Kim, S. J. Pennycook, Adv. Mater. 2003, 15, 526-529.
13. J. Q. Hu, Y. Bando, Z. W. Liu, T. Sekiguchi, D. Golberg, J. H. Zhan, J. Am. Chem. Soc. 2003, 125, 11306-11313.
14. Q. Li, C. R. Wang, J. Am. Chem. Soc. 2003, 125, 9892-9893.
15. Y. J. Hsu, S. Y. Lu, Chem. Commun. 2004, 2102-2103.
16. L. Fu, Z. M. Liu, Y. Q. Liu, B. X. Han, J. Q. Wang, P. J. Hu, L. C. Cao; D. B. Zhu, J. Phys. Chem. B 2004, 108, 13074-13078
17. D. B. Zhu, J. Phys. Chem. B 2004, 108, 13074-13078.
18. X. C. Jiang, Q. H. Xiong, S. W. Nam, F. Qian, Y. Li, C. M. Lieber, Nano Lett. 2007, 7, 3214-3218.
19. J. H. Li, D. X. Zhao, X. Q. Meng, Z. Z. Zhang, J. Y. Zhang, D. Z. Shen, Y. M. Lu, X. W. Fan, J. Phys. Chem. B. 2006, 110, 14685-14687.
20. M. W. Murphy, P. S. GraceKim, Z X. T. Hou, J. G. Zhou, M. Coulliard, G. A. Botton, T. K. Shamm, J. Phys. Chem. C. 2009, 113, 4755-4757.
21. J. Yan, X. S. Fang, L. Zhang, Y. Bando, U. K. Gautam, B. Dierre, T. Sekiguchi, D. Golberg, Nano Lett. 2008, 8, 2794-2799.
22. M. Y. Lu, J. H. Song, M. P. Lu, C. Y. Lee, L. J. Chen, Z. L. Wang, ACS Nano 2009, 3, 357-362.
23. P. Gao, Y. J. Chen, Y. Wang, Q. Zhang, X. F. Li, M. Hu, Chem. Commun. 2009, 2762-2764.
24. R. Yi, G. Z. Qiu, X. H. Liu, J. Solid State Chem. 2009, 182, 27912795.
25. J. Liang, J. Liu, Q. Xie, S. Bai, W. Yu, Y. Qian, J. Phys. Chem. B. 2005, 109, 9463-9467.
26. F. Li, Y. Jiang, L. Hua, L. Y. Liu, Z. Li, X. T. Huang, J. Alloys Compd. 2009, 474, 531-535.
27. S. Kar, B. N. Pal, S. Chaudhuri, D. Chakravorty, J. Phys. Chem. B. 2006, 110, 4605-4611.
28. J. Schrier, D. O. Demchenko, L. W. Wang, Nano Lett. 2007, 7, 2377-2382.
29. G. Z. Shen, Y. Bando, D. Golberg, Appl. Phys. Lett. 2006, 88, 123107.
30. J. F. Gong, S. G. Yang, J. H. Duan, R. Zhang, Y. W. Du, Chem. Commun. 2005, 351-353.
31. B. D. Yao, Y. F. Chan, N. Wang, Appl. Phys. Lett. 2002, 81, 757-760.
32. I. Shalish, H. Temkin, V. Narayanamurti, Phys. Rev. B 2004, 69, 245401-2454405.
33. M. Zhang, E. Ciocan, Y. Bando, K. Wada, L. L. Cheng, P. Pirouz, Appl. Phys. Lett. 2002, 80, 491-493.
34. T. Mitsui, N. Yamamoto, T. Tadokoro, S. Ohta, J. Appl. Phys. 1996, 80, 6972-6979.
35. S. Wagh, G. H. Jain, D. R. Patil, S. A. Patil, L. A. Patil, Sens. Actuators B 2006, 115, 128-133.
36. J. Wöllenstein, J. A. Plaza, C. Cane, Y. Min, H. Bottner, H. L. Tuller, Sens. Actuators B 2003, 93, 350-355.
37. S. Mridha, D. Basak, Semicond. Sci. Technol. 2006, 21, 928-932.
38. G. G. Huang, C. T. Wang, H. T. Tang, Y. S. Huang, J. Yang, Anal. Chem. 2006, 78, 2397-2404.
39. Y. Sun, N. G. Ndifor-Angwafor, D. J. Riley, M. N. R. Ashfold, Chem. Phys. Lett. 2006, 431, 352-357.
40. T. Jen. Hsueh, S. J. Chang, C. L. Hsu, Y. R. Lin, I. C. Chen, J. Electrochem. Soc. 2008, 155, 152-155.
41. R. W. J. Scott, S. M. Yang, G. Chabanis, N. Coombs, D. E. Williams, G. A. Ozin, Adv. Mater. 2001, 13, 1468-1472.
42. C. L. Zhu, Y. J. Chen, R. X. Wang, L. J. Wang, M. S. Cao, X. L. Shi, Sens. Actuators B 2009, 140, 185-189.
43. X. L. Yu, H. M. Ji, H. L. Wang, J. Sun, X. W. Du, Nanoscale Res. Lett. 2010, 5, 644-648.