Environmentally assisted "in-bulk" steel degradation of long term service gas trunkline

Author keywords

Fracture mechanics; Hydrogen damage; Mechanical testing; Pipeline failures; Stress corrosion cracking

Indexed keywords

GRAIN BOUNDARY RELAXATION; HYDROGEN EXTRACTION; HYDROGEN PERMEATION; LONG TERM; LONG TERM SERVICE; MATERIAL DEGRADATION; MICRO-DEFECTS; PIPELINE FAILURES; REDUCTION OF AREAS; TRUNK PIPELINES; TWO STAGE;

EID: 76049124928     PISSN: 13506307     EISSN: None     Source Type: Journal    
DOI: 10.1016/j.engfailanal.2009.04.007     Document Type: Article
Times cited : (81)

References (20)
  • 1
    • 1842778889 scopus 로고    scopus 로고
    • Corrosion resistance of pipe steel in oil-water media
    • Slobodyan Z.V., Nykyforchyn H.M., and Petrushchak O.I. Corrosion resistance of pipe steel in oil-water media. Mater Sci 38 3 (2002) 424-429
    • (2002) Mater Sci , vol.38 , Issue.3 , pp. 424-429
    • Slobodyan, Z.V.1    Nykyforchyn, H.M.2    Petrushchak, O.I.3
  • 2
    • 69349084035 scopus 로고    scopus 로고
    • Corrosion and flow models predictions compared using case histories
    • Expo paper 07522, Nashville, USA;
    • Gabetta G, Margarone M. Corrosion and flow models predictions compared using case histories. In: Proceedings of NACE corrosion conference, Expo paper 07522, Nashville, USA; 2007. p. 13-9.
    • (2007) Proceedings of NACE corrosion conference , pp. 13-19
    • Gabetta, G.1    Margarone, M.2
  • 3
    • 0023536496 scopus 로고
    • The hydrogen degradation and hydrogen induced cracking behaviour of linepipe in dynamic full scale tests
    • Hyodo T., Iino M., Ikeda A., et al. The hydrogen degradation and hydrogen induced cracking behaviour of linepipe in dynamic full scale tests. Corros Sci 27 (1987) 1077-1089
    • (1987) Corros Sci , vol.27 , pp. 1077-1089
    • Hyodo, T.1    Iino, M.2    Ikeda, A.3
  • 5
    • 49349106769 scopus 로고    scopus 로고
    • Hydrogen degradation of steels in gas mains after long term periods of operation
    • Tsyrulnyk O.T., Nykyforchyn H.M., Petryna D., Hredil M.I., and Dzioba I.M. Hydrogen degradation of steels in gas mains after long term periods of operation. Mater Sci 43 5 (2007) 708-717
    • (2007) Mater Sci , vol.43 , Issue.5 , pp. 708-717
    • Tsyrulnyk, O.T.1    Nykyforchyn, H.M.2    Petryna, D.3    Hredil, M.I.4    Dzioba, I.M.5
  • 6
    • 76049104781 scopus 로고    scopus 로고
    • SEP 1315. Stahl-Eisen-Prufballater des vereins Deutscher Eisengutteneute. Kerbschlagbiegeversuch mit Ermittlung von Kraft und Weg; 1987.
    • SEP 1315. Stahl-Eisen-Prufballater des vereins Deutscher Eisengutteneute. Kerbschlagbiegeversuch mit Ermittlung von Kraft und Weg; 1987.
  • 7
    • 76049117817 scopus 로고    scopus 로고
    • Standard test method for J-integral characterization of fracture toughness, 03.01. ASTM E 813. Annual Book of ASTM Standards; 1995. p. 713-27.
    • Standard test method for J-integral characterization of fracture toughness, vol. 03.01. ASTM E 813. Annual Book of ASTM Standards; 1995. p. 713-27.
  • 8
    • 76049089535 scopus 로고    scopus 로고
    • ESIS P4-92 D. ESIS recommendations for stress corrosion testing using pre-cracked specimens (1st draft). Delft: European Structural Integrity Society; 1992.
    • ESIS P4-92 D. ESIS recommendations for stress corrosion testing using pre-cracked specimens (1st draft). Delft: European Structural Integrity Society; 1992.
  • 10
    • 84975363070 scopus 로고
    • The mechanism of hydrogen evolution on iron in acid solutions by determination of permeation rates
    • Devanathan M.A.V., and Stachurski Z. The mechanism of hydrogen evolution on iron in acid solutions by determination of permeation rates. J Electrochem Soc 111 (1964) 619-623
    • (1964) J Electrochem Soc , vol.111 , pp. 619-623
    • Devanathan, M.A.V.1    Stachurski, Z.2
  • 11
    • 0029540244 scopus 로고
    • Factor affecting the reliability of hydrogen permeation measurement
    • Turnbull A. Factor affecting the reliability of hydrogen permeation measurement. Mater Sci Forum 192-194 (1995) 63-75
    • (1995) Mater Sci Forum , vol.192-194 , pp. 63-75
    • Turnbull, A.1
  • 12
    • 0000093508 scopus 로고
    • Hydrogen embrittlement and hydrogen traps
    • Bockris J.O.M., and Subramanyan P.K. Hydrogen embrittlement and hydrogen traps. J Electrochem Soc 118 (1971) 1114-1121
    • (1971) J Electrochem Soc , vol.118 , pp. 1114-1121
    • Bockris, J.O.M.1    Subramanyan, P.K.2
  • 13
    • 70349097223 scopus 로고    scopus 로고
    • Application of hydrogen permeation technique for estimation of gradual hydrogen induced degradation of steel
    • Proceedings of the international conference on environmental degradation of engineering materials, Gdańsk-Jurata, Poland, 1999
    • Lunarska E. Application of hydrogen permeation technique for estimation of gradual hydrogen induced degradation of steel. Proceedings of the international conference on environmental degradation of engineering materials, Gdańsk-Jurata, Poland, 1999. Gdańskie Towarzystwo Naukowe 1 (1999) 32-37
    • (1999) Gdańskie Towarzystwo Naukowe , vol.1 , pp. 32-37
    • Lunarska, E.1
  • 15
    • 70349086632 scopus 로고    scopus 로고
    • Effect of the long term service of the gas pipeline on the properties of the ferrite-pearlite steel
    • doi:10.1002/maco.200805158
    • Nykyforchyn H, Lunarska E, Tsyrulnik O, Nikiforov K, Gabetta G. Effect of the long term service of the gas pipeline on the properties of the ferrite-pearlite steel. Werkstoffe & Korrosion 2009;60. doi:10.1002/maco.200805158.
    • (2009) Werkstoffe & Korrosion , pp. 60
    • Nykyforchyn, H.1    Lunarska, E.2    Tsyrulnik, O.3    Nikiforov, K.4    Gabetta, G.5
  • 16
    • 0031070409 scopus 로고    scopus 로고
    • Grain boundary internal friction of hydrogen precharged 13CrMo44 steel
    • Lunarska E., Ososkov Y., and Jagodzinski Y. Grain boundary internal friction of hydrogen precharged 13CrMo44 steel. Phys Status Solidi (a) 159 2 (1997) 335-341
    • (1997) Phys Status Solidi (a) , vol.159 , Issue.2 , pp. 335-341
    • Lunarska, E.1    Ososkov, Y.2    Jagodzinski, Y.3
  • 17
    • 4143128264 scopus 로고
    • Grain boundary relaxation under irradiation
    • Tolsky A. Grain boundary relaxation under irradiation. Mater Sci Forum 119-121 (1993) 291-296
    • (1993) Mater Sci Forum , vol.119-121 , pp. 291-296
    • Tolsky, A.1
  • 18
    • 55849100382 scopus 로고    scopus 로고
    • Metallic materials for the hydrogen energy industry and main gas pipelines: complex physical problems of aging, embrittlement, and failure
    • Nechaev Yu.S. Metallic materials for the hydrogen energy industry and main gas pipelines: complex physical problems of aging, embrittlement, and failure. Phys Usp 51 (2008) 681-697
    • (2008) Phys Usp , vol.51 , pp. 681-697
    • Nechaev, Yu.S.1
  • 19
    • 14944362589 scopus 로고    scopus 로고
    • Rola wodoru w korozyjnym niszczeniu wewne{ogonek}trznych powierzchni rurocia{ogonek}gu naftowego
    • [in Polish]
    • Nykyforchyn H., Slobodyan Z., Petrushchak O., and Lunarska E. Rola wodoru w korozyjnym niszczeniu wewne{ogonek}trznych powierzchni rurocia{ogonek}gu naftowego. Ochrona przed Korozja{ogonek} 45 (2002) 445-449 [in Polish]
    • (2002) Ochrona przed Korozja{ogonek} , vol.45 , pp. 445-449
    • Nykyforchyn, H.1    Slobodyan, Z.2    Petrushchak, O.3    Lunarska, E.4
  • 20
    • 67349265619 scopus 로고    scopus 로고
    • The influence of X52 steel exploitation on corrosion processes in model solution of gas condensate
    • Tsyrulnyk O.T., Slobodyan Z.V., Zvirko O.I., Hredil M.I., and Nykyforchyn H.M. The influence of X52 steel exploitation on corrosion processes in model solution of gas condensate. Mater Sci 44 5 (2008) 619-629
    • (2008) Mater Sci , vol.44 , Issue.5 , pp. 619-629
    • Tsyrulnyk, O.T.1    Slobodyan, Z.V.2    Zvirko, O.I.3    Hredil, M.I.4    Nykyforchyn, H.M.5


* 이 정보는 Elsevier사의 SCOPUS DB에서 KISTI가 분석하여 추출한 것입니다.