Hydrogen degradation of steels in gas mains after long periods of operation

Materials Science

Volumn 43, Issue 5, 2007, Pages 708-717

  Tsyrul'nyk, O T ^a   Nykyforchyn, H M ^a   Petryna, D Yu ^b   Hredil', M I ^a   Dz'oba, I M ^c  

^a KARPENKO PHYSICOMECHANICAL INSTITUTE   (Ukraine)

^b IVANO FRANKIVSK NATIONAL TECHNICAL UNIVERSITY OF OIL AND GAS   (Ukraine)

^c KIELCE UNIVERSITY OF TECHNOLOGY   (Poland)

Author keywords

[No Author keywords available]

Indexed keywords

CORROSION; CORROSION RESISTANCE; DEGRADATION; HYDROGEN; IMPACT RESISTANCE; IMPACT STRENGTH; MECHANICAL PROPERTIES; METALS; NONMETALS; PIPELINES; PROCESS ENGINEERING; SENSITIVITY ANALYSIS; STEEL; STEEL RESEARCH; STRESS-STRAIN CURVES; STRESSES; SULFATE MINERALS;

CORROSION PROPERTIES; CRACK RESISTANCE; GAS MAINS; HYDROGEN DEGRADATION; IMPACT TOUGHNESS; POLARIZATION RESISTANCE; SERVICE DEGRADATION; STRAIN AGEING; STRAIN-HARDENING; STRESS-STRAIN DIAGRAMS;

HYDROGEN EMBRITTLEMENT;

EID: 49349106769     PISSN: 1068820X     EISSN: None     Source Type: Journal    
DOI: 10.1007/s11003-008-9010-5     Document Type: Article

References (30)

1. M. I. Honcharuk, "Corrosion and depressurization of gas pipelines," Naft. Haz. Prom., No. 2, 56-57 (2003).
2. O. I. Radkevych and H. V. Chumalo, "Damage to the metal of industrial pipelines in hydrogen-sulfide environments," Mater. Sci., 39, No. 4, 596-600 (2003).
3. B. S. Covino, Jr., S. J. Bullard, S. D. Cramer, et al., "Detecting internal corrosion of natural gas transmission pipelines: field tests of probes and systems for real-time corrosion measurement," in: Proc. of the Europ. Corrosion Congr. "Eurocorr 2005", Lisbon, Portugal (2005), Paper No. 396.
4. S. Polyakov, L. Nyrkova, A. Klymenko, et al., "Corrosion of the inner surfaces of gas mains," Fiz.-Khim. Mekh. Mater., Special Issue, No. 5, Vol. 1, 300-304 (2006).
5. A. Y. Krasowky, A. A. Dolgiy, and V. M. Torop, "Charpy testing to estimate pipeline steel degradation after 30 years of operation," in: Proc. of the "Charpy Centenary Conference," Vol. 1, Poitiers (2001), pp. 489-495.
6. Z. V. Slobodyan, H. M. Nykyforchyn, and O. I. Petrushchak, "Corrosion resistance of pipe steel in petroleum-water media," Mater. Sci., 38, No. 3, 424-429 (2002).
7. O. T. Tsyrul'nyk, H. M. Nykyforchyn, O. I. Zvirko, and D. Yu. Petryna, "In-service embrittlement of steels of petroleum mains," Mater. Sci., 40, No. 2, 302-304 (2004).
8. A. Zagórski, H. Matysiak, O. Tsyrulnyk, O. Zvirko, H. Nykyforchyn, and K. Kurzydlowski, "Corrosion and stress-corrosion cracking of exploited storage tank steel," Mater. Sci., 40, No. 3, 421-427 (2004).
9. Strength Analysis of Acting Main Pipelines with Defects. Departmental Building Code of the Ukraine [in Ukrainian], Derzhnaftohazprom, Kyiv (2000).
10. Standard Test Method for J-Integral Characterization of Fracture Toughness, ASTM. E 1737.
11. M. Stern, "A method for determining corrosion rates from linear polarization data," Corrosion, 14, No. 9, 440t-444t (1958).
12. N. G. Krapivnyi, V. I. Sobornitskii, and G. V. Radkovskaya, "Kinetic features of the absorption of hydrogen by the substrate in the process of electrodeposittion of metals," Fiz.-Khim. Mekh. Mater., 24, No. 5, 58-63 (1988).
13. K. M. Yamaleev, Aging of the Metal of Pipes in the Process of Operation of Pipelines [in Russian], VNIIOÉNG, Moscow (1994).
14. G. A. Lanchakov, A. I. Stepanenko, and Yu. I. Pashkov, "Influence of the period of operation on the residual life of pipelines," Gaz. Promyshl., No. 3, 11-12 (1994).
15. V. D. Tarlinskii, "Experimental evaluation of the properties of the metal of gas pipelines after long-term operation," Stroit. Trubopr., No. 1, 29-32 (1997).
16. G. A. Lanchakov, E. E. Zorin, Yu. I. Pashkov, and A. I. Stepanenko, Serviceability of Pipelines. Fracture Resistance [in Russian], Part 2, Nedra, Moscow (2001).
17. V. F. Dmitriev, G. Kh. Murzakhanov, and G. A. Filippov, "Evaluation of the residual service life of the oil pipeline and planning of its major overhaul," Stroit. Trubopr., No. 3, 29-32 (1997).
18. G. A. Filippov and O. V. Livanova, "Interaction of structural defects and degradation of the properties of structural materials," Materialovedenie, No. 10, 17-21 (2002).
19. A. G. Pirogov, "Dynamics of changes in the properties of the metal of pipes in operating pipelines," in: Proc. of the Fourth Congr. of the Oil Workers of Russia "Problems and Methods Aimed at Guaranteeing the Reliability and Safety of the Objects of Pipeline Transport of Hydrocarbon Raw Materials" [in Russian], Ufa (2004), pp. 41-49.
20. A. G. Penkin, V. F. Terent'ev, and L. G. Maslov, "Evaluation of the degree of degradation of the mechanical properties and the residual service life of pipe steels by the methods of acoustic emission and kinetic hardness," www.sds.ru/articles/degradation/index.html (2004).
21. V. A. Sandakov, Evaluation of the Susceptibility of Objects of Gas Distribution to Delayed Fracture [in Russian], Author's Abstract of the Candidate-Degree Thesis (Engineering), Rotaprint GUP IPTÉR, Ufa (2005).
22. S. I. Il'in, M. A. Smirnov, Yu. I. Pashkov, et al., "Changes in the structure and properties of pipe steel in the process of long-term holding under loading," Izv. Chelyabinsk Nauchn. Tsentr, Ser. Fiz. Khim. Tekhnol. Neorg. Mater., Issue 4 (17), 42-46 (2002).
23. N. P. Lyakishev, M. M. Kantor, and V. N. Voronin, "Investigation of the structure of the metal of gas pipelines after long-term operation," Metally, No. 1, 3-16 (2005).
24. V. K. Babich, Yu. P. Gul', and I. E. Dolzhenkov, Strain Aging of Steels [in Russian], Metallurgiya, Moscow (1972).
25. M. N. Zakharov, Methodology of Evaluation of the Load-Carrying Capacity of Main Pipelines with Local Defects [in Russian], Author's Abstract of the Doctoral-Degree Thesis (Engineering), Gubkin Ross. State Oil-and-Gas University, Moscow (2002).
26. O. N. Romaniv, Fracture Toughness of Structural Steels [in Russian], Metallurgiya, Moscow (1979).
27. H. M. Nykyforchyn and O. Z. Student, "Assessment of high-temperature hydrogen degradation of power-equipment steels," in: Proc. of the 16th Europ. Conf. of Fracture "ECF16", Alexandroupolis, Greece (2006), Paper No 749.
28. M. M. Shved, "Role of hydrogen in the embrittlement of iron and steel," Fiz.-Khim. Mekh. Mater., 17, No. 1, 11-16 (1981).
29. N. R. Moody, S. L. Robinson, and W. M. Garrison, "Hydrogen effects on the properties and fracture modes of iron-based alloys," Res. Mech., 30, No. 2, 143-206 (1990).
30. M. L. Bershtein, Strength of Steel [in Russian], Metallurgiya, Moscow (1974).