Effect of the long-term service of the gas pipeline on the properties of the ferrite-pearlite steel

Materials and Corrosion

Volumn 60, Issue 9, 2009, Pages 716-725

  Nykyforchyn, H ^a   Lunarska, E ^b   Tsyrulnyk, O ^a   Nikiforov, K ^b   Gabetta, G ^c  

^a KARPENKO PHYSICOMECHANICAL INSTITUTE   (Ukraine)

^b INSTITUTE OF PHYSICAL CHEMISTRY   (Poland)

^c ENI S P A   (Italy)

Author keywords

[No Author keywords available]

Indexed keywords

BULK METALS; CORROSION PROCESS; FERRITE-PEARLITE STEEL; HYDROGEN PERMEATION STUDIES; LIFE-TIMES; MECHANICAL BEHAVIOUR; METAL DEGRADATION; MICRO-DEFECTS; MICROSTRUCTURE OBSERVATION; STRUCTURE DEGRADATION;

BRITTLE FRACTURE; CORROSION RESISTANCE; DEGRADATION; GAS PIPELINES; HYDROGEN; NATURAL GAS PIPELINES; NATURAL GAS TRANSPORTATION; PIPE; PIPELINES; STEEL; STRESS CORROSION CRACKING;

MECHANICAL PROPERTIES;

EID: 70349086632     PISSN: 09475117     EISSN: 15214176     Source Type: Journal    
DOI: 10.1002/maco.200805158     Document Type: Article

References (26)

1. A. Krasowsky, A. Dolgiy, V. Torop, Eds, D. Francois, A. Pineau, Proc. of the Charpy Centenary Conference, Poitiers, 2001, Vol.1, pp. 489-495.
2. Z. Slobodyan, H. Nykyforchyn, O. Petrushchak, Mater. Sci. 2002, 38, 424.
3. Z. Slobodyan, O. Petrushchak, H. Nykyforchyn, E. Lunarska, Int. J. Physicochem. Mech. Mater. 2002, 3, 782.
4. H. Nykyforchyn, K. Kurzydlowsk, E. Lunarska, in: Environment-induced cracking of materials vol.2 "Prediction, industrial developments and evaluations" S. Ed. Elsevier, 2007, pp. 349-361.
5. Swieczko-Zurek, B. Shipilov, A. Zielinski, E. Lunarska, Mater. Corr. 2008, 59, 289.
6. G. Gabetta, M. Margaron, NACE Corrosion 2007 Conference Expo, Nashville, USA, April 2007, Paper 07522,13.
7. T. Hyodo, M. Iino, A. Ikeda, M. Kimura, M. Shimizu, Corrosion Sci. 1987, 27, 1077.
8. A. Penkin, V. Terentiev, L. Maslov, L. G. Evaluation of the degradation level of mechanical properties and residual workability of pipe steels by the methods of acoustic emission and kinetic hardness (Rus.) www.sds.ru/articles/ degradation/index.html, 2004.
9. E. Lunarska, Proc. Int. Conf. Environmental. Degradation of Engineering. Materiale-EDEM-99, Vol. 1, A. Zielńsi, D. Desjar- dins, Eds., Gdańskie Towarzystwo Naukowe, Gdásk-Jurata 1999, pp. 32-37.
10. E. Lunarska, K. Nikiforov, H. Nykyforchyn, Proc. 2th Intern. Conf. Environmental Degradation of Engineering Materials-EDEM-2, 264 Event of EFC, Bordeaux, 2003, CD PH3.
11. E. Lunarska, Y. Ososkov, Y. Jagodzinski, Phys. Stat. Sol. (a) 1997, 150, 335.
12. I. Bernstein, G. Pressouyre, in: Hydrogen Degradation of Ferrous Alloys, R. A. Oriani, J. P. Hirth, M. Smialowski, Eds., Noyes Publ., Park Ridge 1985, pp. 641-685.
13. A. Turnbull, Mater. Sci. Forum 1995, 192-194, 63.
14. A. Nowick, S. Berry, Inelastic relaxation in crystalline solids, Academic Press, New York 1972.
15. Standard Test Method for J-Integral Characterization of Fracture Toughness. ASTM. E 813, in: Annual Book ofASTM Standards, Vol. 03.01, 2006, pp. 713-727.
16. ESIS P 4-92 D, ESIS Recommendations for Stress Corrosion Testing Using Pre-Cracked Specimens (1st Draft), European Structural Integrity Society, Delft, 1992.
17. SEP 1315. Stahl-Eisen-Prüfblätter des Vereins Deutscher Eisenhuttenleute. Kerbschlagbiegeversuch mit Ermittlung von Kraft und Weg, Diüsseldorf 1987.
18. V. Devanathan, Z. Stachurski, J. Electrochem. Soc. 1964, 111, 619.
19. R. Zachariasz, PhD. Thesis, Silesiak Unoversity, Sosnowiec, 2004.
20. F. Sanchez, B. Mishra, D. Olson, Scripta Mater. 2005, 53, 1443.
21. Sl. Jonsta, J. Sojka, P. Vanova, Acta Metallurgica Slovaca 2007, 13, 489.
22. A. Fragiel, S. Sertna, B. Campillo, L. Cota, Mater. Sci. Eng. 2007, 467,1.
23. R. Requez, S. Camero, A. L. Rivas, Microsc. Microanal. 2005, 11, 1992.
24. V. Babich, Y. Gul, I. Dovzhenko, Deformation ageing of steels (Russ.), Metallurgia, Moscow 1972, pp. 320.
25. A. Tolsky, Mater. Sci. Forum 1993, 119-121, 291.
26. J. Bockris, P. Subramanyan, J. Electrochem. Soc. 1971, 118, 1114.