Volumn 204, Issue 8, 2010, Pages 1158-1162
|
CrN/NbN coatings deposited by HIPIMS: A preliminary study of erosion-corrosion performance
|
Author keywords
CrN NbN; Erosion corrosion; HIPIMS; Ionisation; Nanoscale; Slurry impingement
|
Indexed keywords
BUFFER SOLUTIONS;
CATHODIC ARC TECHNIQUE;
CHARACTERISATION;
CRN/NBN MULTILAYER;
DC SPUTTERING;
DEFECT FREE COATINGS;
DENSE STRUCTURES;
DEPOSITION CONDITIONS;
DEPOSITION TECHNIQUE;
DEPOSITION TECHNOLOGY;
DROPLET DEFECTS;
DRY SLIDING WEAR;
EROSION-CORROSION;
EROSION-CORROSION RESISTANCE;
GAS RATIO;
GROWTH DEFECTS;
HIGH HARDNESS;
HIGH-ADHESION;
HIGH-POWER;
HIPIMS;
IMPACT ANGLES;
INTERGRANULAR;
IONISATION;
LOW FRICTION COEFFICIENTS;
NANO SCALE;
PRETREATMENT CONDITIONS;
PVD COATINGS;
VOID-FREE;
YOUNG'S MODULUS;
CHROMIUM;
COATINGS;
DEFECTS;
DEPOSITS;
DROP FORMATION;
EROSION;
FRICTION;
IONIZATION;
METAL IONS;
NANOSTRUCTURED MATERIALS;
PLASMA DIAGNOSTICS;
CORROSION RESISTANCE;
|
EID: 70849091190
PISSN: 02578972
EISSN: None
Source Type: Journal
DOI: 10.1016/j.surfcoat.2009.11.006 Document Type: Article |
Times cited : (36)
|
References (29)
|