Optical properties of Ce-doped ZnO nanowires directionally grown by hydrothermal method

Journal of Nanoscience and Nanotechnology

Volumn 8, Issue 9, 2008, Pages 4514-4519

  Chen, Y S ^a   Tseng, T Y ^a,b  

^a NATIONAL TAIPEI UNIVERSITY OF TECHNOLOGY   (Taiwan)

^b NATIONAL CHIAO TUNG UNIVERSITY   (Taiwan)

Author keywords

Cathodoluminescence; Ce dopant; Hydrothermal method

Indexed keywords

CATHODOLUMINESCENCE SPECTRUMS; CE DOPANT; CE DOPANTS; CRYSTALLINE SIZES; EMISSION PEAKS; GREEN EMISSION PEAKS; HYDROTHERMAL METHOD; HYDROTHERMAL METHODS; ZNO NANOWIRES;

CATHODOLUMINESCENCE; CERIUM COMPOUNDS; DOPING (ADDITIVES); ELECTRIC WIRE; EMISSION SPECTROSCOPY; LIGHT EMISSION; LUMINESCENCE; NANOSTRUCTURED MATERIALS; NANOSTRUCTURES; NANOWIRES; OPTICAL PROPERTIES; SEMICONDUCTING ZINC COMPOUNDS; ZINC ALLOYS; ZINC OXIDE;

CERIUM;

EID: 55849134476     PISSN: 15334880     EISSN: None     Source Type: Journal    
DOI: 10.1166/jnn.2008.680     Document Type: Article

References (29)

1. J. C. Johnson, K. P. Knutsen, H. Yan, M. Law, Y. Zhang, P. Yang, and R. J. Saykally, Nano Lett. 4, 197 (2004).
2. N. G. Shang, F. Y. Meng, R C. K. Au, Q. Li, C. S. Lee, I. Bello, and S. T. Lee, Adv. Mater. 14, 1308 (2002).
3. M. H. Zhao, Z. L. Wang, and S. X. Mao, Nano Lett. 4, 587 (2004).
4. R. Abramson, W. C. Kim, S. T. Huxtable, H. Yan, Y. Wu, A. Majumdar, C. L. Tien, and P. Yang, J. Microelectromech. Syst. 13, 505 (2004).
5. T. E. Huber, A. Nikolaeva, D. Gitsu, L. Konopko, C. A. Foss, Jr., and M. J. Graf, Appl. Phys. Lett. 84, 1326 (2004).
6. T. S. Xia, L. F. Register, and S. K. Banerjee, J. Appl. Phys. 95, 1597 (2004).
7. X. D. Bai, P. X. Gao, Z. L. Wang, and E. G. Wang, Appl. Phys. Lett. 82, 4806 (2003).
8. C. Y. Lee, T. Y. Tseng, S. Y. Li, and P. Lin, NanoTech. 17, 83 (2006).
9. S. Bachir, K. Azuma, J. Kossanyi, P. Valat, and J. C. Ronfard-Haret, J. Lumin. 75, 35 (1997).
10. K. J. Kim and Y. R. Park, Appl. Phys. Leu. 78, 475 (2001).
11. A. Kaschner, U. Haboeck, M. Strassburg, G. Kaczmarczyk, A. Hoffmann, C. Thomsen, A. Zeuner, H. R. Alves, D. M. Hofmann, and B. K. Meyer, Appl. Phys. Lett. 80, 1909 (2002).
12. M. Ishii, S. Komuro, T. Morikawa, and Y. Aoyagi, J. Appl. Phys. 89, 3679 (2001).
13. M. Abdullah, T. Morinoto, and K. Okuyama, Adv. Fund. Mater. 13, 800 (2003).
14. B. C. Chen, Y. H. Xiao, G. S. Wu, and L. D. Zhang, Adv. Funct. Mater. 14, 913 (2004).
15. C. Y. Lee, T. Y. Tseng, S. Y. Li, and P. Lin, NanoTech. 16, 1105 (2005).
16. E. R. Leite, A. P. Maciel, I. T. Weber, P. N. Lisboa-Filho, E. Longo, C. O. Paiva-Santos, A. V. C. Andrade, C. A. Pakoscimas, Y. Maniette, and W. H. Schreiner, Adv. Mater. (Weinhelm, Ger.) 14, 905 (2002).
17. B. C. Cheng, Y. H. Xiao, G. S. Wu, and L. D. Zhang, Appl. Phys. Lett. 84, 3 (2004).
18. C. Sudhakar and M. Vannice, Appl. Catal. A 14, 47 (1985).
19. G. Praline, B. E. Koel, R. L. Hance, H. I. Lee, and J. M. White, J. Electron. Spectrosc. Relat. Phenom. 21, 17 (1978).
20. H. J. Fan, R. Scholz, M. Zacharias, and U. Gösele, Appl. Phys. Lett. 86, 023113 (2005).
21. X. Zhang, Y. Zhang, J. Xu, Z. Wang, X. Chen, and D. Yua, Appl. Phys. Lett. 87, 123111 (2005).
22. S. Y. Bae, H. W. Seo, and J. Park, J. Phys. Chem. B 108, 5206 (2004).
23. H. J. Fan, F. Bertram, A. Dadgar, J. Christen, A. Krost, and M. Zacharias, NanoTech. 15, 1401 (2004).
24. Y. C. Kong, D. P. Yu, B. Zhang, W. Fang, and S. Q. Feng, Appl. Phys. Lett. 78, 407 (2001).
25. K. Vanheusden, W. L. Warren, C. H. Seager, D. R. Tallant, J. A. Voigt, and B. E. Gnade, J. Appl. Phys. 79, 7983 (1996).
26. T. Gao, Q. H. Li, and T. H. Wang, Chem. Mater. 17, 887 (2005).
27. K. J. Kim and Y. R. Park, Appl. Phys. Lett. 78, 475 (2001).
28. B. Y. Geng, G. Z. Wang, Z. Jiang, T. Xie, S. H. Sun, G. W. Meng, and L. D. Zhang, Appl. Phys. Lett. 82, 4791 (2003).
29. G. Shen, J. H. Cho, J. K. Yoo, G. C. Yi, and C. J. Lee, J. Phys. Chem. B 109, 5491 (2005).