Damage maps for layered ceramics under simulated mastication

Journal of Dental Research

Volumn 87, Issue 7, 2008, Pages 671-675

  Kim, J H ^a   Kim, J W ^a   Myoung, S W ^b   Pines, M ^a   Zhang, Y ^a  

^a NEW YORK UNIVERSITY COLLEGE OF DENTISTRY   (United States)

^b Changwon National University   (South Korea)

Author keywords

Cementation radial fracture; Fatigue; Layered ceramic structures; Occlusal partial cone fracture; Off axis loading

Indexed keywords

ANALYSIS OF VARIANCE; ARTICLE; CERAMICS; CHEMISTRY; DENTAL CARE; DENTAL SURGERY; DENTURE; EQUIPMENT; MASTICATION; MATERIALS TESTING; MOLAR TOOTH; SHEAR STRENGTH; TOOTH CROWN; TOOTH PROSTHESIS;

ANALYSIS OF VARIANCE; CERAMICS; CROWNS; DENTAL PORCELAIN; DENTAL RESTORATION WEAR; DENTAL RESTORATION, PERMANENT; DENTAL STRESS ANALYSIS; DENTAL VENEERS; EQUIPMENT FAILURE ANALYSIS; MASTICATION; MATERIALS TESTING; MOLAR; SHEAR STRENGTH;

EID: 47649088646     PISSN: 00220345     EISSN: None     Source Type: Journal    
DOI: 10.1177/154405910808700706     Document Type: Article

References (19)

1. Bhowmick S, Zhang Y, Lawn BR (2005). Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: bilayer structures. J Mater Res 20:2792-2800.
2. DeLong R, Douglas WH (1983). Development of an artificial oral environment for the testing of dental restoratives: bi-axial force and movement control. J Dent Res 62:32-36.
3. Kelly JR (1999). Clinically relevant approach to failure testing of all-ceramic restorations. J Prosthet Dent 81:652-661.
4. Kelly JR, Tesk JA, Sorensen JA (1995). Failure of all-ceramic fixed partial dentures in vitro and in vivo: analysis and modeling. J Dent Res 74:1253-1258.
5. Kim JW, Kim JH, Thompson VP, Zhang Y (2007). Sliding contact fatigue damage in layered ceramic structures. J Dent Res 86:1046-1050.
6. Kocer C, Collins RE (1998). The angle of Hertzian cone cracks. J Am Ceram Soc 81:1736-1742.
7. Lawn BR, Wiederhorn SM, Roberts DE (1984). Effect of sliding friction forces on the strength of brittle materials. J Mater Sci 19:2561-2569.
8. Lee C-S, Lawn BR, Kim DK (2001). Effect of tangential loading on critical conditions for radial cracking in brittle coatings. J Am Ceram Soc 84:2719-2721.
9. Qasim T, Bush MB, Hu X, Lawn BR (2005). Contact damage in brittle coating layers: influence of surface curvature. J Biomed Mater Res B Appl Biomater 73:179-185.
10. Qasim T, Ford C, Bush MB, Hu X, Malament KA, Lawn BR (2007). Margin failures in brittle dome structures: relevance to failure of dental crowns. J Biomed Mater Res B Appl Biomater 80:78-85.
11. Rekow D, Zhang Y, Thompson V (2007). Can material properties predict survival of all-ceramic posterior crowns? Compend Contin Educ Dent 28:362-368.
12. Sailer I, Fehér A, Lüthy H, Filser F, Gauckler LJ, Hämmerle CHF, et al. (2006). Prospective clinical study of zirconia posterior fixed partial dentures: 3-year follow-up. Quintessence Int 37:685-693.
13. Scherrer SS, De Rijk WG, Wiskott HW, Belser UC (2001). Incidence of fractures and lifetime predictions of all-ceramic crown systems using censored data. Am J Dent 14:72-80.
14. Silva NR, de Souza GM, Coelho PG, Stappert CF, Clark EA, Rekow ED, et al. (2008). Effect of water storage time and composite cement thickness on fatigue of a glass-ceramic trilayer system. J Biomed Mater Res B Appl Biomater 84:117-123.
15. Zhang Y, Lawn BR, Rekow ED, Thompson VP (2004). Effect of sandblasting on the long-term performance of dental ceramics. J Biomed Mater Res 71(B):381-386.
16. Zhang Y, Bhowmick S, Lawn BR (2005a). Competing fracture modes in brittle materials subject to concentrated cyclic loading in liquid environments: monoliths. J Mater Res 20:2021-2029.
17. Zhang Y, Song JK, Lawn BR (2005b). Deep penetrating conical cracks in brittle layers from hydraulic cyclic contact. J Biomed Mater Res 73(B):186-193.
18. Zhang Y, Lawn BR, Malament KA, Thompson VP, Rekow ED (2006). Damage accumulation and fatigue life of sandblasted dental ceramics. Int J Prosthodont 19:442-448.
19. Zhang Y, Kim JW, Kim JH, Lawn BR (2008). Fatigue damage in ceramic coatings from cyclic contact loading with a tangential component. J Am Ceram Soc 91:198-202.