A literature survey on the stability and significance of residual stresses during fatigue

Fatigue and Fracture of Engineering Materials and Structures

Volumn 30, Issue 3, 2007, Pages 173-205

  McClung, R Craig ^a  

^a SOUTHWEST RESEARCH INSTITUTE   (United States)

Author keywords

Cold expansion; Crack growth; Fatigue; Machining; Peening; Relaxation; Residual stress; Welding

Indexed keywords

CRACK PROPAGATION; CYCLIC LOADS; FATIGUE OF MATERIALS; MANUFACTURE; RESIDUAL STRESSES; STRUCTURAL RELAXATION; THERMAL EFFECTS; WELDING;

CRACK EXTENSION; STATIC MECHANICAL LOAD; THERMAL EXPOSURE;

FRACTURE;

EID: 33947242948     PISSN: 8756758X     EISSN: 14602695     Source Type: Journal    
DOI: 10.1111/j.1460-2695.2007.01102.x     Document Type: Article

References (239)

1. Totten, G., Howes, M. and Inoue, T., Editors (2002) Handbook of Residual Stress and Deformation of Steel. ASM International, Materials Park, Ohio.
2. Anonymous (2002) Handbook for Damage Tolerant Design, Air Force Research Laboratory, published on the Internet at http://www.siresearch.info/ projects/dtdh/index.php.
3. Rosenthal, D. (1959) Influence of residual stress on fatigue. In: Metal Fatigue (Edited by G. Sines and J. L. Waisman). McGraw-Hill, pp. 170-196.
4. Vöhringer, O. (1983) Relaxation of residual stresses. In: Proceedings of European Conference on Residual Stresses (Edited by E. Karlsruhe, W. Macherauch and V. Hauk). DGM Informationsgesellschaft, pp. 47-80.
5. Vöhringer, O. (1987) Relaxation of residual stresses by annealing or mechanical treatment. In: Advances in Surface Treatments, Technology - Applications - Effects: Residual Stresses, Vol. 4. Pergamon Press, pp. 367-396.
6. Löhe, D. and Vöhringer, O. (2002) Stability of residual stresses. In: Handbook of Residual Stress and Deformation of Steel (Edited by G. Totten, M. Howes and T. Inoue). ASM International, Materials Park, Ohio, pp. 54-69.
7. Löhe, D., Lang, K.-H. and Vöhringer, O. (2002) Residual stress and fatigue behavior. In: Handbook of Residual Stress and Deformation of Steel (Edited by G. Totten, M. Howes and T. Inoue). ASM International, Materials Park, Ohio, pp. 27-53.
8. Lu, J. (2002) Prestress engineering of structural material: A global design approach to the residual stress problem. In: Handbook of Residual Stress and Deformation of Steel (Edited by G. Totten, M. Howes and T. Inoue), ASM International, Materials Park, Ohio, pp. 11-26.
9. Fitzpatrick, M. E. and Edwards, L. (1998) Fatigue crack/residual stress field interactions and their implications for damage-tolerant design. J. Mater. 7, 190-198.
10. Webster, G. A. and Ezeilo, A. N. (2001) Residual stress distribution and their influence on fatigue lifetimes. Int. J. Fatigue, 23, S375-S383.
11. Schulze, V. (2005) Modern Mechanical Surface Treatment: States, Stability, Effects. Wiley-VCH, Weinheim, Germany.
12. Lu, J., Editor (2005) Handbook on Residual Stress, 2nd Edition, Society for Experimental Mechanics.
13. Vöhringer, O. (1987) Changes in the state of the material by shot peening. In: Proceedings of the 3rd International Conference on Shot Peening (ICSP3), Garmisch-Partenkirchen, Germany (Edited by H. Wohlfahrt, R. Kopp and O. Vöhringer). DGM Informationsgesellschaft Verlag, Oberursel, pp. 185-204.
14. Zhuang, W. and Wicks, B. (2003) Mechanical surface treatment technologies for gas turbine engine components. J. Engng. Gas Turb. Power, 125, 1021-1025.
15. Ezeilo, A., Webster, G., Webster, P. J. and Webster, P. S. (1993) Comparison of shot peening residual stress distributions in a selection of materials. In: Proceedings of the 5th International Conference on Shot Peening (ICSP5), Oxford, UK (Edited by D. Kirk), pp. 275-282.
16. Meister, T. J. (1996) Overcoming detrimental residual stress in titanium by the shot peening process. In: Surface Performance of Titanium: Proceedings of Symposium on Surface Performance of Titanium, TMS, Cincinnati, Ohio, pp. 253-263.
17. Cao, W., Khadhraoui, M., Brenier, B., Guedou, J. Y. and Castex, L. (1994) Thermomechanical relaxation of residual stress in shot peened nickel base superalloy. Mater. Sci. Technol. 10, 947-954.
18. Tufft, M. (2002) Modeling of fatigue behavior due to shot peening conditions. In: Proceedings of the 8th International Conference on Shot Peening (ICSP-8), Garmisch-Partenkirchen, Germany (Edited by L. Wagner). Wiley-VCH GmbH. KGaA, pp. 530-539.
19. Robertson, G. T. (1971) The effects of shot size on the residual stresses resulting from shot peening. In: SAE Technical Paper 710284, Reprinted in Shot Peener 11, 1987, pp. 46-48.
20. Reed, E. C. and Viens, J. A. (1960) The influence of surface residual stress on fatigue limit of titanium. J. Engng. Ind., pp. 76-78.
21. Dorr, T. and Wagner, L. (1999) Fatigue response of various titanium alloys to shot peening. In: Surface Treatment IV: Computer Methods and Experimental Measurements, Proceedings of the 4th International Conference on Computer Methods and Experimental Measurements for Surface Treatment Effects, Assisi, Italy, pp. 349-357.
22. Lautridou, J. C. and DuQuenne, C. (1996) Effect of shot-peening on the fatigue strength of nickel-based super-alloys produced by powder metallurgy. Bulletin du Cercle d'âetudes des Mâetaux, 16, 21.1-21.10.
23. Happ, M. B., Mourer, D. P. and Schmidt, R. L. (1987) Residual stress analysis and LCF test results for peened bolt hole and dovetail configurations. In: Proceedings of the ASM Conference on Residual Stress in Design, Process and Materials Selection. ASM International, Cincinnati, Ohio, pp. 127-136.
24. Lee, H. and Mall, S. (2004) Stress relaxation behavior of shot-peened Ti-6Al-4V under fretting fatigue at elevated temperature. Mater. Sci. Engng. A366, 412-420.
25. Lee, H. and Mall, S. (2005) Fretting fatigue and stress relaxation behaviors of shot-peened Ti-6Al-4V. J. ASTM Int. 2, Paper ID JAI12031.
26. Everett, Jr., R. A., Matthews, W. T., Prabhakaran Newman, Jr., J. C. and Dubberly, M. J. (2000) The effects of shot and laser peening on crack growth and fatigue life in 2024 aluminum alloy and 4340 steel. In: USAF Structural Integrity Program Conference, San Antonio, Texas.
27. Nikitin, I., Scholtes, B., Maier, H. and Altenberger, I. (2004) High temperature fatigue behavior and residual stress stability of laser-shock peened and deep rolled austenitic steel AISI 304. Scripta Materialia, 50, 1345-1350.
28. Nalla, R. K., Altenberger, I., Noster, U., Liu, G. Y., Scholtes, B. and Ritchie, R. O. (2003) On the influence of mechanical surface treatments-deep rolling and laser shock peening-on the fatigue behavior of TI-6AL-4V at ambient and elevated temperatures. Mater. Sci. Engng. A355, 216-230.
29. Prevéy, P. S., Hornbach, D., Ravindranath, R. and Cammett, J. T. (2003a) Application of low plasticity burnishing to improve damage tolerance of a Ti-6Al-4V first stage fan blade. In: Proceedings of the 44th AIAA/ASME/ASCE/AHS Structures, Structural Dynamics & Materials Conference. Norfolk, Virginia.
30. Prevéy, P. S., Jayaraman, N. and Ravindranath, R. A. (2003b) Effect of surface treatments on HCF performance and FOD tolerance of a Ti-6Al-4V vane. In: Proceedings of the 8th National Turbine Engine High Cycle Fatigue (HCF) Conference. Monterey, California.
31. Prevéy, P. S., Jayaraman, N. and Shepard, M. J. (2004) Improved HCF performance and FOD tolerance of surface treated Ti-6-2-4-6 compressor blades. In: Proceedings of the 9th National Turbine Engine High Cycle Fatigue Conference. Pinehurst, North Carolina.
32. Wagner, L. (1999) Effect of mechanical surface treatments on fatigue performance of titanium alloys. In: Fatigue Behavior of Titanium Alloys. TMS, pp. 253-265.
33. Sridhar, B. R., Ramachandra, K. and Padmanabhan, K. A. (1996) Effect of shot peening on the fatigue and fracture behaviour of two titanium alloys. J. Mater. Sci. 31, 5953-5960.
34. Burck, L. H., Sullivan, C. P. and Wells, C. H. (1970) Fatigue of a glass bead blasted nickel-base superalloy. Metall. Trans. 1, 1595-1600.
35. Elber, W. (1974) Effects of shot-peening residual stresses on the fracture and crack-growth properties of D6AC steel. In: Fracture Toughness and Slow-Stable Cracking, ASTM STP 559, American Society for Testing and Materials, pp. 45-58.
36. Hack, J. E. and Leverant, G. R. (1982) Influence of compressive residual stress on the crack-opening behavior of part-through fatigue cracks. In: Residual Stress Effects in Fatigue, ASTM STP 776, American Society for Testing and Materials, pp. 204-223.
37. Misumi, M. and Ohkubo, M. (1987) Deceleration of small crack growth by shot-peening. Int. J. Mater. Product Technol. 2, 36-47.
38. De Los Rios, E. R., Mercier, P. and El-Sehily, B. M. (1996) Short crack growth behaviour under variable amplitude loading of shot peened surfaces. Fatigue Fract. Engng. Mater. Struct. 19, 175-184.
39. Natkaniec-Kocanda, D., Kocanda, S. and Miller, K. J. (1996) Influence of shot-peening on short crack behavior in a medium carbon steel. Fatigue Fract. Engng. Mater. Struct. 19, 911-917.
40. Turnbull, A., De Los Rios, E. R., Tait, R. B., Laurant, C. and Boabaid, J. S. (1998) Improving the fatigue crack resistance of Waspaloy by shot peening. Fatigue Fract. Engng. Mater. Struct. 21, 1513-1524.
41. Ruschau, J. J., John, R., Thompson, S. R. and Nicholas, T. (1999) Fatigue crack growth rate characteristics of laser shock peened Ti-6Al-4V. J. Engng. Mater. Technol. 121, 321-329.
42. Mutoh, Y., Fair, G. H., Noble, B. and Waterhouse, R. B. (1987) The effect of residual stresses induced by shot-peening on fatigue crack propagation in two high strength aluminium alloys. Fatigue Fract. Engng. Mater. Struct. 10, 261-272.
43. De Los Rios, E. R., Walley, A., Milan, M. T. and Hammersley, G. (1995) Fatigue crack initiation and propagation on shot-peened surfaces in A316 stainless steel. Int. J. Fatigue, 17, 493-499.
44. Honda, T., Ramulu, M. and Kobayashi, A. (2005) Effect of shot peening on fatigue crack growth in 7075-T7351. J. ASTM Int. 2, Paper ID JAI12569.
45. Berns, H. and Weber, L. (1986) Influence of residual stresses on crack growth. In: Impact Surface Treatment (Edited by S. A. Meguid), Elsevier, pp. 31-44.
46. De Los Rios, E. R., Trull, M. and Levers, A. (2000) Modelling fatigue crack growth in shot-peened components of Al 2024-T351. Fatigue Fract. Engng. Mater. Struct. 23, 709-716.
47. Zhu, X. Y. and Shaw, W. J. D. (1995) Correlation of fatigue crack growth behaviour with crack closure in peened specimens. Fatigue Fract. Engng. Mater. Struct. 18, 811-820.
48. Prevéy, P. S., Telesman, J., Gabb, T. and Kantzos, P. (2000) FOD resistance and fatigue crack arrest in low plasticity burnished IN718. In: Proceedings of the 5th National Turbine Engine High Cycle Fatigue Conference, Chandler, Arizona.
49. Wilks, M. D. B., Nowell, D. and Hills, D. A. (1994) The influence of residual stress on crack growth rate. In: Proceedings of the 4th International Conference on Residual Stresses, Baltimore, Maryland, pp. 1238-1245.
50. Leverant, G. R., Langer, B. S., Yuen, A. and Hopkins, S. W. (1979) Surface residual stresses, surface topography and the fatigue behavior of Ti-6Al-4V. Metall. Trans. 10A, 251-257.
51. Vöhringer, O., Hirsch, Th. and Macherauch, E. (1984) Relaxation of shot peening induced residual stresses of TiAl6V4 by annealing or mechanical treatment. In: Proceedings of the 5th International Conference on Titanium, Munich, FRG, Vol. 4, pp. 2203-2210.
52. Gray, H., Wagner, L. and Lutjering, G. (1987) Influence of shot peening induced surface roughness, residual macrostresses and dislocation density on the elevated temperature HCF-properties of Ti alloys. In: Proceedings of the 3rd International Conference on Shot Peening (ICSP3), Garmisch-Partenkirchen, Germany (Edited by H. Wohlfahrt, R. Kopp and O. Vöhringer), DGM Informationsgesellschaft Verlag, Oberursel, pp. 447-457.
53. Wagner, L. (1997) Mechanical surface treatments on titanium alloys: fundamental mechanisms. In: Surface Performance of Titanium, TMS, pp. 199-215.
54. Prevéy, P. S., Hornbach, D. J. and Mason, P. W. (1997) Thermal residual stress relaxation and distortion in surface enhanced gas turbine engine components. In: Proceedings of the 17th Heat Treating Society Conference and Exposition and the 1st International Induction Heat Treating Symposium, Indianapolis, Indiana, ASM, pp. 3-12.
55. Berger, M.-C. and Gregory, J. K. (1999) Residual stress relaxation in shot peened Timetal 21s. Mater. Sci. Engng. A, A263, 200-204.
56. Khadhraoui, M., Cao, W., Castex, L. and Guedou, J. Y. (1997) Experimental investigations and modelling of relaxation behaviour of shot peening residual stresses at high temperature for nickel base superalloys. Mater. Sci. Technol. 13, 360-367.
57. Prevéy, P. S. (2000) The effect of cold work on the thermal stability of residual compression in surface enhanced IN718. In: Proceedings of the 20th ASM Materials Solutions Conference & Exposition, St. Louis, Missouri, pp. 426-434.
58. Cammett, J. T., Prevéy, P. S. and Jayaraman, N. (2005) The effect of shot peening coverage on residual stress, cold work, and fatigue in a nickel-based superalloy. In: Proceedings of the 9th International Conference on Shot Peening (ICSP-9), Paris, Marne la Vallée, France, Paper 261.
59. Masmoudi, N. and Castex, L. (1988) The effect of temperature and time on the stress relaxation of shot peened nickel based superalloy IN100. In: International Conference on Residual Stresses, Nancy, France (Edited by G. Beck, S. Denis and A. Simon), pp. 710-715.
60. Buchanan, D. J., John, R. and Ashbaugh, N. E. (2006) Thermal residual stress relaxation in powder metal IN100 superalloy. J. ASTM Int. 3, Paper ID JAI12552.
61. Gabb, T. P., Telesman, J., Kantzos, P. T., Bonacuse, P. J., Barrie, R. L. and Hornbach, D. J. (2004) Stress relaxation in powder metallurgy superalloy disks. TMS Letters, 1, 115-116.
62. Hoffmann, J., Scholtes, B., Vöhringer, O. and Macherauch, E. (1987) Thermal relaxation of shot peening residual stresses in the differently heat treated plain carbon steel Ck 45. In: Proceedings of the 3rd International Conference on Shot Peening (ICSP3), Garmisch-Partenkirchen, Germany (Edited by H. Wohlfahrt, R. Kopp and O. Vöhringer), DGM Informationsgesellschaft Verlag, Oberursel, pp. 239-246.
63. Schulze, V., Vöhringer, O. and Macherauch, E. (1993) Thermal relaxation of shot peening induced residual stresses in a quenched and tempered steel 42 Cr Mo 4. In: Proceedings of the 5th International Conference on Shot Peening (ICSP5), Oxford, UK (Edited by D. Kirk), pp. 265-274.
64. Menig, R., Schulze, V. and Vöhringer, O. (2002) Comparison of surface characteristics and thermal residual stress relaxation of laser peened and shot peened AISI 4140. In: Proceedings of the 8th International Conference on Shot Peening (ICSP-8), Garmisch-Partenkirchen, Germany (Edited by L. Wagner), Wiley-VCH GmbH & Co. KGaA, pp. 498-504.
65. Prevéy, P. and Cammett, J. (2002) The effect of shot peening coverage on residual stress, cold work and fatigue in a Ni-Cr-Mo low alloy steel. In: Proceedings of the 8th International Conference on Shot Peening (ICSP-8), Garmisch-Partenkirchen, Germany (Edited by L. Wagner), Wiley-VCH GmbH & Co. KGaA, pp. 293-304.
66. Krull, P., Nitschke-Pagel, T. and Wohlfahrt, H. (1999) Stability of residual stresses in shot peened and high pressure water peened stainless steels at elevated temperatures. In: Proceedings of the 7th International Conference on Shot Peening (ICSP7), Warsaw, Poland (Edited by A. Nakonieczny), Institute of Precision Mechanics.
67. Childs, W. H. (1988) The effect of elevated temperature on shot peened 403 stainless steel. In: Analytical and Experimental Methods for Residual Stress Effects in Fatigue, ASTM STP 1004 (Edited by Champoux, Underwood and Kapp), American Society for Testing and Materials, pp. 21-24.
68. Roth, M. and Wortman, C. (2002) Relaxation of shot peening residual stresses in the 7050-T7451 aluminium alloy after heat cycles for adhesive bonding. In: Proceedings of the 8th International Conference on Shot Peening (ICSP-8), Garmisch-Partenkirchen, Germany (Edited by L. Wagner), Wiley-VCH GmbH & Co. KGaA, pp. 208-214.
69. Potter, J. M. and Millard, R. A. (1976) The effect of temperature and load cycling on the relaxation of residual stresses. In: Proceedings of the 25th Conference on Application of X-Ray Analysis (Edited by H. F. McMurdie, C. S. Barrett, J. B. Newkirk and C. O. Ruud), pp. 309-319.
70. Eigenmann, B., Schulze, V. and Vöhringer, O. (1994) Surface residual stress relaxation in steels by thermal or mechanical treatment. In: Proceedings of the 4th International Conference on Residual Stresses, Baltimore, Maryland, pp. 598-607.
71. Hanagarth, H., Vöhringer, O. and Macherauch, E. (1990) Relaxation of shot peening residual stresses of the steel 42 CrMo 4 by tensile or compressive deformation. In: Proceedings of the 4th International Conference on Shot Peening (ICSP4), Tokyo (Edited by K. Iida), Japan Society of Precision Engineering, pp. 337-345.
72. Eigenmann, B. (1995) Residual stresses due to thermal, thermo-chemical, and mechanical surface treatments: Generation, determination, evaluation. In: Computer Methods and Experimental Measurements for Surface Treatment Effects II, Proceedings of the International Conference on Computer Methods and Experimental Measurements for Surface Treat, pp. 17-25.
73. Holzapfel, H., Schulze, V., Vöhringer, O. and Macherauch, E. (1996) Relaxation behaviour of shot peening induced residual stresses in AISI 4140 due to quasistatic uniaxial loading at elevated temperatures. In: Proceedings of the 6th International Conference on Shot Peening (ICSP6), San Francisco (Edited by J. Champaigne), pp. 385-396.
74. Holzapfel, H., Schulze, V., Vöhringer, O. and Macherauch, E. (1996) Stability and relaxation behaviour of shot peening induced residual stresses in AISI 4140 during bending fatigue. In: Proceedings of the 6th International Conference on Shot Peening (ICSP6), San Francisco (Edited by J. Champaigne), pp. 413-423.
75. Holzapfel, H., Schulze, V., Vöhringer, O. and Macherauch, E. (1998) Residual stress relaxation in an AISI 4140 steel due to quasistatic and cyclic loading at higher temperatures. Mater. Sci. Engng. A, A248, 9-18.
76. Kirk, D. (1987) Effects of plastic straining on residual stresses induced by shot peening. In: Proceedings of the 3rd International Conference on Shot Peening (ICSP3), Garmisch-Partenkirchen, Germany (Edited by H. Wohlfahrt, R. Kopp and O. Vöhringer), DGM Informationsgesellschaft Verlag, Oberursel, pp. 213-220.
77. Cammett, J. T., Sauer, C. A. and Arnold, T. E. (1993) Observations on shot peening residual stresses in 17Cr-7Ni austenitic stainless steel and their redistribution via mechanical loading. In: Proceedings of the 5th International Conference on Shot Peening (ICSP5), Oxford, UK (Edited by D. Kirk), pp. 283-290.
78. Prevéy, P. S., Shepard, M. J. and Smith, P. R. (2001) The effect of low plasticity burnishing on the HCF performance and FOD resistance of Ti-6Al-4V. In: Proceedings of the 6th National Turbine Engine High Cycle Fatigue (HCF) Conference, Jacksonville, Florida.
79. Smith, D. J., Farrahi, G. H., Zhu, W. X. and McMahon, C. A. (2001) Experimental measurement and finite element simulation of the interaction between residual stresses and mechanical loading. Int. J. Fatigue, 23, 293-302.
80. Altenberger, I., Noster, U., Boyce, B. L., Peters, J. O., Scholtes, B. and Ritchie, R. O. (2002) Effects of mechanical surface treatment on fatigue failure in Ti-6Al-4V: Role of residual stresses and foreign-object damage. In: ECRS 6, Proceedings of the of the 6th European Conference on Residual Stresses Materials Science Forum, Coimbra, Portugal, Mater. Sci. Forum, 404, 457-462.
81. Altenberger, I., Noster, U., Scholtes, B. and Ritchie, R. (2002) High temperature fatigue of mechanically surface treated materials. In: Proceedings of the 8th International Conference on Shot Peening (ICSP-8), Garmisch-Partenkirchen, Germany (Edited by L. Wagner), Wiley-VCH GmbH & Co. KGaA, pp. 483-489.
82. Noster, U., Altenberger, I., Ritchie, R. and Scholtes, B. (2002) Isothermal fatigue behavior and residual stress states of mechanically surface treated Ti-6Al-4V: Laser shock peening vs. deep rolling. In: Proceedings of the 8th International Conference on Shot Peening (ICSP-8), Garmisch-Partenkirchen, Germany (Edited by L. Wagner), Wiley-VCH GmbH & Co. KGaA, pp. 447-453.
83. Cheong, W., Zhuang, W. and Zhang, L. (2004) Study of residual stress relaxation using x-ray diffraction. Key Engng. Mater. 274-276, 871-876.
84. Zhuang, W. Z. and Halford, G. R. (2001) Investigation of residual stress relaxation under cyclic load. Int. J. Fatigue, 23, S31-S37.
85. Boggs, B. D. and Byrne, J. G. (1973) Fatigue stability of residual stress in shot peened alloys. Metall. Trans. 4, 2153-2157.
86. Berkley, S. G., Bradley, E. F. and Thomas, M. C. (1997) A new approach to tracking turbine engine low cycle fatigue disk life (Phase IIB). In: 41st Annual Air Transport Association Non-Destructive Testing Forum, Indianapolis, Indiana.
87. Berkley, S. G., Bradley, E. F. and Thomas, M. C. (1999) Residual stress in new, in-service and retired disks. In: 1999 USAF ASIP Conference, San Antonio, Texas.
88. Vukelich, S., Russ, S., Berkley, S. and Bradley, E. F. (2002) Residual stress measurement and its application to achieve predicted full life potential of low cycle fatigue (LCF) limited engine disks. In: Proceedings of the 9th International Symposium on Transport Phenomena and Dynamics of Rotating Machinery, Honolulu, Hawaii.
89. Belassel, M., Brauss, M. and Berkley, S. G. (2000) Residual stress relaxation in nickel base alloys subjected to low cycle fatigue. In: Proceedings of the 6th International Conference on Residual Stresses: ICRS-6, Oxford, UK, pp. 144-151.
90. Belassel, M., Brauss, M., Pineault, J. and Berkley, S. G. (2002) Fatigue damage mechanism and stress relaxation in shot peened and polished nickel Base materials. In: ECRS 6, Proceedings of the of the 6th European Conference on Residual Stresses, Coimbra, Portugal, Mater. Sci. Forum, 404, 451-455.
91. Seppi, F. L. (1975) Relief of shot-peened compressive layer by fatigue loading. In: Proceedings of the of a Workshop on Nondestructive Evaluation of Residual Stress, San Antonio, Texas, NTIAC-76-2, pp. 73-74.
92. Hammond, D. W. and Meguid, S. A. (1990) Crack propagation in the presence of shot-peening residual stresses. Engng. Fract. Mech. 37, 373-387.
93. Meguid, S. A. and Hammond, D. W. (1989) Fatigue fracture and residual stress relaxation in shot-peened components. In: Proceedings of the 2nd International Conference on Residual Stresses, ICRS 2, Nancy, France, pp. 797-802.
94. Rasouli Yazdi, S. and Lu, J. (1999) Prediction of relaxation of residual stress induced by shot peening in aluminum alloys. In: Proceedings of the SEM Annual Conference on Theoretical, Experimental, and Computational Mechanics, pp. 880-883.
95. Bonnafé, J. P., Maeder, G. and Bathias, C. (1987) Study of fatigue damage in shot peened aluminium alloys using acoustic emission and macro/microscopic x-ray diffraction investigations. In: Proceedings of the 3rd International Conference on Shot Peening (ICSP3), Garmisch-Partenkirchen, Germany (Edited by H. Wohlfahrt, R. Kopp and O. Vöhringer), DGM Informationsgesellschaft Verlag, Oberursel, pp. 485-497.
96. Fontanari, V., Frendo, F., Rosellini, W. and Scardi, P. (2001) Analysis of residual stress distribution in shot peened Al 6082 T5 alloy subjected to fatigue loading. In: Surface Treatment V, Proceedings of the 5th International Conference on Computer Methods and Experimental Measurements for Surface Treatment Effects, pp. 333-342.
97. Zinn, W. and Scholtes, B. (1999) Mechanical surface treatments of lightweight materials-effects on fatigue strength and near-surface microstructures. J. Mater. 8, 145-151.
98. Bathias, C., Bonnafe, J. P., Lebrun, J. L. and Maeder, G. (1988) X-ray diffraction and acoustic emission study of fatigue damage in aluminum alloys. In: Analytical and Experimental Methods for Residual Stress Effects in Fatigue, ASTM STP 1004 (Edited by Champoux, Underwood and Kapp), American Society for Testing and Materials, pp. 25-36.
99. Taira, S. and Murakami, Y. (1960) On the changes in residual stresses due to repeated stressing. In: Proceedings of the 3rd Japan Congress on Testing Materials, Kyoto, Japan, pp. 52-55.
100. Esquivel, A. L. and Evans, K. R. (1968) X-ray diffraction study of residual macrostresses in shot-peened and fatigued 4130 steel. In: Exp. Mech., 8, 496-503.
101. Kodama, S. (1972) The behaviour of residual stress during fatigue stress cycles. In: Proceedings of the International Conference of Mechanical Behavior of Materials, Vol. II, pp. 111-118.
102. Schulze, V., Lang, K.-H., Vöhringer, O. and Macherauch, E. (1996) Relaxation of shot peening induced residual stresses in quenched and tempered steel AISI 4140 due to uniaxial cyclic deformation. In: Proceedings of the 6th International Conference on Shot Peening (ICSP6), San Francisco, California (Edited by J. Champaigne), pp. 403-412.
103. Wick, A., Schulze, V. and Vöhringer, O. (1999) Influence of the shot peening temperature on the relaxation behaviour of residual stresses during cyclic bending. In: Proceedings of the 7th International Conference on Shot Peening, Warsaw, Poland, pp. 102-109.
104. Wick, A., Schulze, V. and Vöhringer, O. (1999) Shot peening and stress peening of AISI 4140 at increased temperatures. In: Proceedings of the 7th International Conference on Shot Peening, Warsaw, Poland, pp. 110-116.
105. Wick, A., Schulze, V. and Vöhringer, O. (2000) Effects of warm peening on fatigue life and relaxation behaviour of residual stresses in AISI 4140 steel. Mater. Sci. Engng. A, A293, 191-197.
106. Menig, R., Schulze, V. and Vöhringer, O. (2002) Residual stress relaxation and fatigue strength of AISI 4140 under torsional loading after conventional shot peening, stress peening, and warm peening. In: Proceedings of the 8th International Conference on Shot Peening (ICSP-8), Garmisch-Partenkirchen, Germany (Edited by L. Wagner), Wiley-VCH GmbH & Co. KGaA, pp. 311-316.
107. Menig, R., Schulze, V. and Vöhringer, O. (2002) Influence of optimized warm peening on residual stress stability and fatigue strength of AISI 4140 in different material states. In: Proceedings of the 8th International Conference on Shot Peening (ICSP-8), Garmisch-Partenkirchen, Germany (Edited by L. Wagner), Wiley-VCH GmbH & Co. KGaA, pp. 317-323.
108. Bergström, J. and Ericsson, T. (1986) Relaxation of shot peening induced compressive stress during fatigue of notched steel samples. Surface Engng. 2, 115-120.
109. Iida, K. and Hirose, Y. (1999) The residual stress distribution in shot peened carburized steel under fatigue. In: Proceedings of the 7th International Conference on Shot Peening, Warsaw, Poland, pp. 96-101.
110. Zeller, R. (1993) Influence of stress peening on residual stresses and fatigue limit. In: Residual Stresses, DGM Informationsgesesellschaft Verlag, pp. 907-917.
111. McClinton, M. and Cohen, J. B. (1982) Changes in residual stress during the tension fatigue of normalized and peened SAE 1040 steel. Mater. Sci. Engng. 56, 259-263.
112. Teodosio, J. R., Cindra, F. M. and Pedrosa, P. D. (2003) Relaxation of residual stresses during fatigue cycles in steels. In: THERMEC′2003, Parts 1-5, International Conference on Processing & Manufacturing of Advanced Materials, Madrid, Spain, Mater. Sci. Forum, 426, 3981-3986.
113. Qui, Q. and Wang, R. (1987) Changes in the state of the material by shot peening. In: Proceedings of the 3rd International Conference on Shot Peening (ICSP3), Garmisch-Partenkirchen, Germany (Edited by H. Wohlfahrt, R. Kopp and O. Vöhringer), DGM Informationsgesellschaft Verlag, Oberursel, pp. 231-238.
114. Torres, M. A. S. and Voorwald, H. J. C. (2002) An evaluation of shot peening, residual stress and stress relaxation on the fatigue life of AISI 4340 steel. Int. J. Fatigue, 24, 877-886.
115. Torres, M., Pereira do Nascimento, M. and Voorwald, H. (2002) Consideration of shot peening treatment applied to a high strength aeronautical steel with different hardnesses. In: Proceedings of the 8th International Conference on Shot Peening (ICSP-8), Garmisch-Partenkirchen, Germany (Edited by L. Wagner), Wiley-VCH GmbH & Co. KGaA, pp. 37-43.
116. Bignonnet, A. (1987) Fatigue strength of shot-peened grade 35 NCD 16 Steel-variation of residual stresses introduced by shot peening according to type of loading. In: Proceedings of the 3rd International Conference on Shot Peening (ICSP3), Garmisch-Partenkirchen, Germany (Edited by H. Wohlfahrt, R. Kopp and O. Vöhringer), DGM Informationsgesellschaft Verlag, Oberursel, pp. 659-666.
117. Neff, P. J. (1981) A quantitative evaluation of surface residual stress and its relation to fatigue performance. In: Residual Stress for Designers and Metallurgists, (Edited by L. J. VandeWalle), ASM, pp. 119-135.
118. Bergström, J. and Ericsson, T. (1984) Relaxation of shot peening induced compressive stress during fatigue of notched steel samples. In: Proceedings of the 2nd International Conference on Shot Peening, ICSP-2, Chicago, Illinois, pp. 241-248.
119. Bergström, J. and Ericsson, T. (1987) X-ray microstructure and residual stress analysis of shot peened surface layers during fatigue loading. In: Proceedings of the 3rd International Conference on Shot Peening (ICSP3), Garmisch-Partenkirchen, Germany (Edited by H. Wohlfahrt, R. Kopp and O. Vöhringer), DGM Informationsgesellschaft Verlag, Oberursel, pp. 221-230.
120. Bignonnet, A., Lieurade, H. P., Picouet, L. and Castex, L. (1987) Shot peening of welded joints and residual stress relaxation during fatigue. In: Proceedings of the 3rd International Conference on Shot Peening (ICSP3), Garmisch-Partenkirchen, Germany (Edited by H. Wohlfahrt, R. Kopp and O. Vöhringer), DGM Informationsgesellschaft Verlag, Oberursel, pp. 585-593.
121. Cao, W. and Castex, L. (1988) Modelling of the shot peening residual stress relaxation in steel structure under cyclic loading. In: International Conference on Residual Stresses, Nancy, France, (Edited by G. Beck, S. Denis and A. Simon), pp. 631-637.
122. Farrahi, G. H., LeBrun, J. L. and Couratin, D. (1995) Effect of shot peening on residual stress and fatigue life of a spring steel. Fatigue Fract. Engng. Mater. Struct. 18, 211-220.
123. Iida, K. and Taniguchi, K. (1996) Relaxation of residual stress distribution produced by shot peening under fatigue test. In: Proceedings of the 6th International Conference on Shot Peening (ICSP6), San Francisco (Edited by J. Champaigne), pp. 397-402.
124. Batista, A. C., Dias, A. M., Lebrun, J. L., LeFlour, J. C. and Inglebert, G. (2000) Contact fatigue of automotive gears: Evolution and effects of residual stresses introduced by surface treatments. Fatigue Fract. Engng. Mater. Struct. 23, 217-228.
125. Capello, E., Davoli, P., Filippini, M. and Foletti, S. (2004) Relaxation of residual stresses induced by turning and shot peening on steels. J. Strain Anal. 39, 285-290.
126. Lu, J. and Flavenot, J. F. (1987) Use of a finite element method for the prediction of the shot-peened residual stress relaxation during fatigue. In: Proceedings of the 3rd International Conference on Shot Peening (ICSP3), Garmisch-Partenkirchen, Germany (Edited by H. Wohlfahrt, R. Kopp and O. Vöhringer), DGM Informationsgesellschaft Verlag, Oberursel, pp. 391-398.
127. Lu, J. and Flavenot, J. F. (1988) Prediction of residual stress relaxation during fatigue loading and taking residual stresses in a multiaxial fatigue criteria into account. In: International Conference on Residual Stresses, Nancy, France (Edited by G. Beck, S. Denis and A. Simon), pp. 784-790.
128. Lu, J., Flavenot, J. F. and Turbat, A. (1988) Prediction of residual stress relaxation during fatigue. In: Mechanical Relaxation of Residual Stresses, ASTM STP 993 (Edited by L. Mordfin). American Society for Testing and Materials, pp. 75-90.
129. Meguid, S., Shagal, G., Stranart, J., Liew, K. and Ong, L. (2005) Relaxation of peening residual stresses due to cyclic thermo-mechanical overload. J. Engng. Mater. Technol. 127, 170-178.
130. Phillips, J. L. (1974) Sleeve Coldworking Fastener Holes. Vol. 1, AFML-TR-74-10, Air Force Materials Laboratory, Wright-Patterson AFB, Ohio.
131. Rufin, A. C. (1993) Extending the fatigue life of aircraft engine components by hole cold expansion technology. J. Engng. Gas Turb. Power, 115, 165-171.
132. Sha, G. T., Cowles, B. A. and Fowler, R. L. (1980) Fatigue Life of a coldworked hole. In: Emerging Technologies in Aerospace Structures, Design, Structural Dynamics and Materials Proceedings. The Aerospace Conference - Century 2 - Emerging Technology Conferences, San Francisco, California, pp. 125-140.
133. Ezelio, A. N., Webster, P. S., Webster, G. A. and Webster, P. J. (1994) Influence of cyclic loading on residual stress distribution caused by cold hole expansion. In: Proceedings of the 4th International Conference on Residual Stresses, Baltimore, Maryland, pp. 1275-1284.
134. Rich, D. L. and Impellizzeri, L. F. (1977) Fatigue analysis of cold-worked and interference fit fastener holes. In: Cyclic Stress-Strain and Plastic Deformation Aspects of Fatigue Crack Growth, ASTM STP 637, pp. 153-175.
135. Almer, J. D., Cohen, J. B. and Winholtz, R. A. (1998) The effects of residual macrostresses and microstresses on fatigue crack propagation. Metall. Mater. Trans. A 29A, 2127-2136.
136. Almer, J. D., Cohen, J. B. and Moran, B. (2000) The effects of residual macrostresses and microstresses on fatigue crack initiation. Mater. Sci. Engng. A, A284, 268-279.
137. Prawoto, Y. and Winholtz, R. A. (2001) Fatigue crack growth with tensile residual stresses. In: Advances in Fracture Research, ICF10, Proceedings of the 10th International Conference on Fracture, Honolulu, Hawaii, December 2001, Paper 983.
138. Su, X., Gu, M. and Yan, M. (1986) A simplified residual stress model for predicting fatigue crack growth behavior at coldworked fastener holes. Fatigue Fract. Engng. Mater. Struct. 9, 57-64.
139. Toparli, M., Ozel, A. and Aksoy, T. (1997) Effect of the residual stresses on the fatigue crack growth behavior at fastener holes. Mater. Sci. Engng. A225, 196-203.
140. Cannon, D. F., Sinclair, J. and Sharpe, K. A. (1985) Improving the fatigue performance of bolt holes in railway rails by cold expansion. In: Proceedings of the International Conference and Exposition on Fatigue, Corrosion Cracking, Fracture Mechanics, and Failure Analysis, Salt Lake City, Utah, pp. 353-369.
141. Clark, G. (1984) Fatigue crack growth through residual stress fields-theoretical and experimental studies on thick-walled cylinders. Theor. Appl. Fract. Mech. 2, 111-125.
142. Underwood, J. H., Parker, A. P., Troiano, E., Vigilante, G. N. and Whitherell, M. D. (2001) Fatigue and hydrogen cracking in cannons with mechanical and thermal residual stresses. In: Advances in Fracture Research, ICF10, Proceedings of the 10th International Conference on Fracture, Honolulu, Hawaii, December 2001, Paper 986.
143. Stacey, A. and Webster, G. A. (1988) Stress intensity factors caused by residual stress fields in autofrettaged tubing. In: Analytical and Experimental Methods for Residual Stress Effects in Fatigue, ASTM STP 1004, American Society for Testing and Materials, pp. 37-53.
144. Stacey, A. and Webster, G. A. (1988) Influence of residual stress on fatigue crack growth in thick-walled cylinders. In: Analytical and Experimental Methods for Residual Stress Effects in Fatigue, ASTM STP 1004, American Society for Testing and Materials, pp. 107-121.
145. Hsu, Y. C. and Forman, R. G. (1975) Elastic-plastic analysis of an infinite sheet having a circular hole under pressure. J. Appl. Mech. 42, 347-352.
146. Chang, J. B. (1977) Prediction of fatigue crack growth at cold-worked fastener holes. J. Aircraft, 14, 903-908.
147. Wang, G. S. (1988) An elastic-plastic solution for a normally loaded center hole in a finite circular body. Int. J. Press. Vessels Pip. 33, 269-284.
148. Clark, G. (1991) Modelling residual stresses and fatigue crack growth at cold-expanded fastener holes. Fatigue Fract. Engng. Mater. Struct. 14, 579-589.
149. Guo, W. (1993) Elastic-plastic analysis of a finite sheet with a cold-worked hole. Engng. Fract. Mech. 46, 465-472.
150. Ball, D. L. (1995) Elastic-plastic stress analysis of cold expanded fastener holes. Fatigue Fract. Engng. Mater. Struct. 18, 47-63.
151. Armen, H., Levy, A. and Eidinoff, H. L. (1984) Elastic-plastic behavior of coldworked holes. J. Aircraft, 21, 193-201.
152. Heller, M., Jones, R. and Williams, J. F. (1991) Analysis of cold-expansion for cracked and uncracked fastener holes. Engng. Fract. Mech. 39, 195-212.
153. Ball, D. L. and Lowry, D. R. (1998) Experimental investigation on the effects of cold expansion of fastener holes. Fatigue Fract. Engng. Mater. Struct. 21, 17-34.
154. Moreira, P., De Matos, P., Pinho, S., Pastramǎ, S. and Camanho, P. (2004) The residual stress intensity factors for cold-worked crack holes: A technical note. Fatigue Fract. Engng. Mater. Struct. 27, 879-886.
155. Poussard, C., Pavier, M. J. and Smith, D. J. (1995) Analytical and finite element predictions of residual stresses in cold worked fastener holes. J. Strain Anal. 30, 291-304.
156. Pavier, M. J., Poussard, C. G. C. and Smith, D. J. (1997) A finite element simulation of the cold working process for fastener holes. J. Strain Anal. 32, 287-300.
157. Pavier, M. J., Poussard, C. G. C. and Smith, D. J. (1998) Finite element modelling of the interaction of residual stress with mechanical load for a crack emanating from a cold worked fastener hole. J. Strain Anal. 33, 275-289.
158. Papanikos, P. and Meguid, S. A. (1998) Three-dimensional finite element analysis of cold expansion of adjacent holes. Int. J. Mech. Sci. 40, 1019-1028.
159. Chakherlou, T. N. and Vogwell, J. (2003) The effect of cold expansion on improving the fatigue life of fastener holes. Engng. Failure Anal. 10, 13-24.
160. Kang, J., Johnson, W. S. and Clark, D. A. (2002) Three-dimensional finite element analysis of the cold expansion of fastener holes in two aluminum alloys. J. Engng. Mater. Technol. 124, 140-145.
161. Zhang, Y., Edwards, L. and Fitzpatrick, M. E. (2002) Finite element simulation of hole cold expansion process in EN8 steel plates. In: UK ABAQUS User Group Conference, November 2002.
162. Özdemir, A. T. and Edwards, L. (1996) Measurement of the three-dimensional residual stress distribution around split-sleeve cold-expanded holes. J. Strain Anal. 31, 413-421.
163. Wang, D. Q. and Edwards, L. (1998) Neutron diffraction determination of the complete 3D residual stress distribution surrounding a cold expanded hole. In: Proceedings of the 4th European Conference on Residual Stresses, pp. 619-626.
164. Stefanescu, D., Bouzina, A., Dutta, M., Wang, D. Q., Fitzpatrick, M. E. and Edwards, L. (2002) Comparison of residual stress measurements using neutron and x-ray diffraction around cold expanded holes. J. Neutron Res. 9, 399-405.
165. Zhang, Y., Fitzpatrick, M. E. and Edwards, L. (2002) Measurement of the residual stresses around a cold expanded hole in an EN8 steel plate using the contour method. Mater. Sci. Forum, 404-407, 527-532.
166. Chandawanich, N. and Sharpe, Jr., W. N. (1979) An experimental study of fatigue crack initiation and growth from coldworked holes. Engng. Fract. Mech. 11, 609-620.
167. Grandt, Jr., A. F. (1975) Stress intensity factors for some through-cracked fastener holes. Int. J. Fract. 11, 283-294.
168. Grandt, Jr., A. F. (1978) Stress intensity factors for cracked holes and rings loaded with polynomial crack face pressure distributions. Int. J. Fract. 14, R221-R229.
169. Cathey, W. H. and Grandt, Jr., A. F. (1980) Fracture mechanics consideration of residual stresses introduced by coldworking fastener holes. J. Engng. Mater. Technol. 102, 85-91.
170. Pavier, M. J., Poussard, C. G. C. and Smith, D. J. (1999) Effect of residual stress around cold worked holes on fracture under superimposed mechanical load. Engng. Fract. Mech. 63, 751-773.
171. Pell, R. A., Beaver, P. W., Mann, J. Y. and Sparrow, J. G. (1989) Fatigue of thick-section cold-expanded holes with and without cracks. Fatigue Fract. Engng. Mater. Struct. 12, 553-567.
172. Kokaly, M. T., Ransom, J. S., Restis, J. H. and Reid, L. (2005) Observations and analysis of fatigue crack growth from cold expanded holes. In: Proceedings of the 8th Joint NASA/FAA/DoD Conference on Aging Aircraft, Palm Springs, California.
173. Saunder, T. J. and Grandt, Jr., A. F. (2000) The effect of edge distance on coldworking fastener holes. In: Proceedings of the 4th Joint DoD/FAA/ NASA Conference on Aging Aircraft, St. Louis, Missouri.
174. Mann, J. Y. and Jost, G. S. (1983) Stress fields associated with interference fitted and cold-expanded holes. Metals Forum, 6, 43-53.
175. Stefanescu, D., Dutta, M., Wang, D. Q., Edwards, L. and Fitzpatrick, M. E. (2003) The effect of high compressive loading on residual stresses and fatigue crack growth at cold expanded holes. J. Strain Anal. 38, 419-427.
176. Hermann, R. and Moffatt, J. (1991) Experiments and analysis of the fatigue life improvements in fastener holes of aluminium-lithium alloy 2091. In: Proc eedings of the International Aluminum-Lithium Conference, Garmisch-Partenkirchen, Germany, pp. 621-626.
177. Özdemir, A. T. and Edwards, L. (1997) Relaxation of residual stresses at cold-worked fastener holes due to fatigue loading. Fatigue Fract. Engng. Mater. Struct. 20, 1443-1451.
178. Clark, D. A. and Johnson, W. S. (2003) Temperature effects on fatigue performance of cold expanded holes in 7050-T7451 aluminum alloy. Int. J. Fatigue, 25, 159-165.
179. Lacarac, V. D., Smith, D. J. and Pavier, M. J. (2001) The effect of cold expansion on fatigue crack growth from open holes at room and high temperature. Int. J. Fatigue, 23, S161-S170.
180. Garcia-Granada, A. A., Lacarac, V. D., Holdway, P., Smith, D. J. and Pavier, M. J. (2001) Creep relaxation of residual stresses around cold expanded holes. J. Engng. Mater. Technol. 23, 125-131.
181. Stefanescu, D. (2004a) Measurement and prediction of fatigue crack growth from cold expanded holes part 1: The effect of fatigue crack growth on cold expansion residual stresses. J. Strain Anal. 39, 25-39.
182. Stefanescu, D. (2004b) Measurement and prediction of fatigue crack growth from cold expanded holes part 2: Prediction of fatigue crack growth from cold expanded holes. J. Strain Anal. 39, 41-53.
183. Adams, N. J. I. (1973) Crack growth in the vicinity of welds. Welding Research Supplement 508-s-513-s.
184. Berkovits, A., Kelly, D. W. and Di, S., (1998) Considerations of the effect of residual stresses on fatigue of welded aluminium alloy structures. Fatigue Fract. Engng. Mater. Struct. 21, 159-170.
185. Dalle Donne, C. and Raimbeaux, G. (2001) Residual stress effects on fatigue crack propagation in friction stir welds. In: Advances in Fracture Research, ICF10, Proceedings of the 10th International Conference on Fracture, Honolulu, Hawaii, December 2001, Paper 125.
186. James, M. N., Hattingh, D. G., Hughes, D. J., Wei, L.-W., Patterson, E. A. and Quintana Da Fonseca, J. (2004) Synchrotron diffraction investigation of the distribution and influence of residual stresses in fatigue. Fatigue Fract. Engng. Mater. Struct. 27, 609-622.
187. Terada, H. (1976) An analysis of the stress intensity factor of a crack perpendicular to the welding bead. Engng. Fract. Mech. 8, 441-444.
188. Tada, H. and Paris, P. C. (1983) The stress intensity factor for a crack perpendicular to the welding bead. Int. J. Fract. 21, 279-284.
189. Smith, E. (1985) The stress intensity factor for a crack perpendicular to a longitudinal weld in a large plate. Int. J. Fract. 27, 75-79.
190. Terada, H. and Nakajima, T. (1985) Analysis of stress intensity factor of a crack approaching welding bead. Int. J. Fract. 27, 83-90.
191. Rybicki, E. F., Stonesifer, R. B. and Olson, R. J. (1981) Stress intensity factors due to residual stresses in thin-walled girth-welded pipes. J. Pressure Vessel Technol. 103, 66-75.
192. Glinka, G. (1979) Effect of residual stresses on fatigue crack growth in steel weldments under constant and variable amplitude loads. In: Fracture Mechanics, ASTM STP 677 (Edited by C. W. Smith), American Society for Testing and Materials, pp. 198-214.
193. Glinka, G. (1987) Residual stresses in fatigue and fracture: Theoretical analyses and experiments. In: Advances in Surface Treatment and Residual Stresses (Edited by A. Niku-Lari), Pergamon Press, pp. 413-454.
194. Parker, A. P. (1982) Stress intensity factors, crack profiles, and fatigue crack growth rates in residual stress fields. In: Residual Stress Effects in Fatigue, ASTM STP 776, American Society for Testing and Materials, pp. 13-31.
195. Nelson, D. V. (1982) Effects of residual stress on fatigue crack propagation. In: Residual Stress Effects in Fatigue, ASTM STP 776, American Society for Testing and Materials, pp. 172-194.
196. Miyazaki, K., Mochizuki, M., Kanno, S., Hayashi, M., Shiratori, M. and Yu, Q. (2002) Analysis of stress intensity factor due to surface crack propagation in residual stress fields caused by welding. JSME Int. J., Series A, 45, 199-207.
197. Miyamoto, H., Miyoshi, T. and Fukuda, S. (1973) An analysis of crack propagation in welded structures. In: Significance of Defects in Welded Structures, Proceedings of the Japan-U. S. Seminar, Tokyo, pp. 189-202.
198. Fukuda, S. and Sugino, M. (1980) A numerical study of the effect of welding residual stress upon fatigue crack propagation with attention paid to the phenomenon of crack opening and closure. In: Numerical Methods in Fracture Mechanics, pp. 615-629.
199. Fukuda, S. Watari, S. and Horikawa, K. (1979) An experimental study of effect of welding residual stress upon fatigue crack propagation based on observation of crack opening and closure. Transact. Japan Welding Res. Inst. 8, 265-271.
200. Itoh, Y. Z., Suruga, S. and Kashiwaya, H. (1989) Prediction of fatigue crack growth rate in welding residual stress field. Engng. Fract. Mech. 33, 397-407.
201. Kang, K. J., Song, J. H. and Earmme, Y. Y. (1989) Fatigue crack growth and closure through a tensile residual stress field under compressive applied loading. Fatigue Fract. Engng. Mater. Struct. 12, 363-376.
202. Kang, K. J., Song, J. H. and Earmme, Y. Y. (1990) Fatigue crack growth and closure behaviour through a compressive residual stress field. Fatigue Fract. Engng. Mater. Struct. 13, 1-13.
203. Ohta, A., Kosuge, M., Mawari, T. and Nishijima, S. (1988) Fatigue crack propagation in tensile residual stress fields of welded joints under fully compressive cycling. Int. J. Fatigue, 10, 237-242.
204. Ohta, A., McEvily, A. J. and Suzuki, N. (1993) Fatigue crack propagation in a tensile residual stress field under a two-step programmed test. Int. J. Fatigue, 5, 9-12.
205. Beghini, M. and Bertini, L. (1990) Fatigue crack propagation through residual stress fields with closure phenomena. Engng. Fract. Mech. 36, 379-387.
206. Beghini, M., Bertini, L. and Vitale, E. (1994) Fatigue crack growth in residual stress fields: Experimental results and modeling. Fatigue Fract. Engng. Mater. Struct. 17, 1433-1444.
207. Wang, G. S. (1996) To analyse fatigue crack growth in residual stress field at welded joints. In: Proceedings of the of the 6th International Fatigue Congress - Fatigue '96, Berlin, Germany (Edited by G. Lütjering and H. Nowack), Pergamon, Vol. II, pp. 1219-1224.
208. Wang, G. S. (1999) A strip yield analysis of fatigue crack growth in the residual stress field. Int. J. Fract. 96, 247-277.
209. Iida, K., Yamamoto, S. and Takanashi, M. (1997) Residual stress relaxation by reversed loading. Welding in the World/Le Soudage dans le Monde, 39, 138-144.
210. Iida, K. and Takanashi, M. (1998) Relaxation of welding residual stresses by reversed and repeated loadings. Welding in the World/Le Soudage dans le Monde, 41, 314-327.
211. Takanashi, M., Kamata, K. and Kunihiro, I. (2000) Relaxation behavior of welding residual stresses by fatigue loading in smooth longitudinal butt welded joints. Welding World, 44, 28-34.
212. Nitschke-Pagel, Th. and Wohlfahrt, H. (2000) Residual stress relaxation in welded high strength steels under different loading conditions. In: Proceedings of the 6th International Conference on Residual Stresses: ICRS-6, Oxford, UK, pp. 1495-1502.
213. Lachmann, C., Nitschke-Pagel, Th. and Wohlfahrt, H. (2000) Characterisation of residual stress relaxation in fatigue loaded welded joints by x-ray diffraction and barkhausen noise method. In: ECRS 5, Proceedings of the 5th European Conference on Residual Stresses, Delft-Noordwijkerhout, the Netherlands, Mater. Sci. Forum, 347, 374-379.
214. Han, S. T. Lee and Shin, B. (2002) Residual stress relaxation of welded steel components under cyclic load. Mater. Technol. 73, 414-420.
215. Dattoma, V., De Giorgi, M. and Nobile, R. (2004) Numerical evaluation of residual stress relaxation by cyclic load. J. Strain Anal. 39, 663-672.
216. Blom, A. F. (1995) Spectrum fatigue behaviour of welded joints. Int. J. Fatigue, 17, 485-491.
217. Lopez Martinez, L., Lin, R., Want, D. and Blom, A. F. (1997) Investigation of residual stresses in as-welded and TIG-dressed specimens subjected to static/spectrum loading. In: Proceedings of the of the North European Engineering and Science Conference (NESC): Welded High-Strength Steel Structures, Stockholm, Sweden (Edited by A. F. Blom), EMAS Publishing, London, UK.
218. Khanna, S. K., He, C. and Agrawal, H. N. (2001) Residual stress measurement in spot welds and the effect of fatigue loading on redistribution of stresses using high sensitivity moire interferometry. J. Engng. Mater. Technol. 123, 132-138.
219. Fukuda, S. and Tsuruta, Y. (1979) A preliminary study of the influence of welding residual stress upon fatigue crack propagation. In: Recent Research on Mechanical Behavior of Solids, University of Tokyo Press, pp. 401-419.
220. Fukuda, S. (1989) Analysis of crack propagation in residual stress field using computer algebra. Nucl. Engng. Des. 111, 21-15.
221. Park, E. J., Kim, E. J. and Yoo, S. H. (2004) Prediction of the crack opening behaviour for the fatigue crack propagating in welding residual stress field. Key Engng. Mater. 270-273, 96-101.
222. Terada, H. (2005) Stress intensity factor analysis and fatigue behavior of a crack in the residual stress field of welding. J. ASTM Int. 2, Paper ID JAI12558.
223. James, M. R. (1982) The relaxation of residual stresses during fatigue. In: Residual Stress and Stress Relaxation, Proceedings of the 28th Sagamore Army Materials Research Conference, Lake Placid, New York, pp. 297-314.
224. James, M. R. and Morris, W. L. (1981) The relaxation of machining stresses in aluminum alloys during fatigue. In: Residual Stress for Designers and Metallurgists, ASM, pp. 169-188.
225. Flavenot, J. F. and Skalli, N. (1988) Effects of grinding conditions on fatigue behavior of 42CD4 grade steel; comparison of different fatigue criteria incorporating residual stresses. In: Mechanical Relaxation of Residual Stresses, ASTM STP 993 (Edited by L. Mordfin), American Society for Testing and Materials, pp. 91-111.
226. Kuhn, G., Hoffmann, J. E., Eifler, D., Scholtes, B. and Macherauch, E. (1991) Instability of machining residual stresses in differently heat treated notched parts of SAE 1045 during cyclic deformation. In: Residual Stresses-III: Science and Technology, Proceedings of the International Conference on Residual Stresses, Elsevier Applied Science, Vol. 2, pp. 1294-1301.
227. Alam, A. M., Chieragatti, R. and Lavelle, B. (2000) A new device for in situ residual stress measurement during fatigue testing. Mater. Sci. Forum, 347/349, 358-362.
228. Morrow, J. and Sinclair, G. M. (1958) Cycle-dependent stress relaxation. In: Symposium on Basic Mechanisms of Fatigue, ASTM STP 237, American Society for Testing and Materials, pp. 83-99.
229. Ross, A. S. and Morrow, J. (1960) Cycle-dependent stress relaxation of A-286 alloy. J. Bas. Engng. pp. 654-660.
230. Morrow, J., Ross, A. S. and Sinclair, G. M. (1960) Relaxation of residual stresses due to fatigue loading. SAE Trans. 68, 40-48.
231. Martin, J. F., Topper, T. H. and Sinclair, G. M. (1971) Computer based simulation of cyclic stress-strain behavior with applications to fatigue. Mater. Res. Std. 11, 23-28.
232. Jhansale, H. R. and Topper, T. H. (1973) Engineering analysis of the inelastic stress response of a structural metal under variable cyclic strains. In: Cyclic Stress-Strain Behavior-Analysis, Experimentation, and Failure Prediction, ASTM STP 519, American Society for Testing and Materials, pp. 246-270.
233. Taira, S., Honda, K. and Abe, T. (1964) X-ray investigation on fatigue damage of metals (on the changes in half-value breadth of x-ray diffraction line and macro-residual stress in torsional fatigue with mean stress). In: Proceedings of the 7th Japan Congress on Testing Materials, Society of Materials Science, Kyoto, pp. 26-30.
234. Gong, Y. and Norton, M. (1999) Cyclic response and fatigue of steels subjected to strain control with non-zero means. J. Testing Eval. 27, 15-30.
235. Lindgren, M. and Lepistö, T. (2002) Effect of mean stress on residual stress relaxation in steel specimens. Mater. Sci. Technol. 18, 845-849.
236. Pattinson, E. J. and Dugdale, D. S. (1962) Fading of residual stresses due to repeated loading. Metallurgia, 66, 228-230.
237. Gould, R. W. and Pittella, C. F. (1972) An x-ray investigation of fatigue behavior of cold worked aluminum. In: Proc eedings of the 21st Annual Conference on Applications of X-Ray Analysis, Denver, Colorado (Edited by L. S. Birks, C. S. Barrett, J. B. Newkirk and C. O. Ruud) Plenum Press, Advances in X-Ray Analysis, Vol. 16, pp. 354-366.
238. Radhakrishnan, V. M. and Prasad, C. R. (1976) Relaxation of residual stress with fatigue loading. Engng. Fract. Mech. 8, 593-597.
239. Underwood, J.H., Pook L.P., and Sharples J.K. (1977) Fatigue-crack propagation through a measured residual stress field in alloy steel In: Flaw Growth and Fracture, ASTM STP 631, American Society for Testing and Materials, pp. 402-415