Characterisation of cracks in thermal barrier coatings using impedance spectroscopy

Ceramic Engineering and Science Proceedings

Volumn 27, Issue 3, 2006, Pages 191-206

  Deng, Lifen ^a   Zhao, Xiaofeng ^a   Xiao, Ping ^a  

^a UNIVERSITY OF MANCHESTER   (United Kingdom)

Author keywords

[No Author keywords available]

Indexed keywords

CRACK PROPAGATION; CRACKS; FINITE ELEMENT METHOD; SPECTROSCOPIC ANALYSIS;

CRACK SIZE; CRACK THICKNESS; IMPEDANCE SPECTRA; IMPEDANCE SPECTROSCOPY;

THERMAL BARRIER COATINGS;

EID: 33845938988     PISSN: 01966219     EISSN: None     Source Type: Conference Proceeding    
DOI: None     Document Type: Conference Paper

References (24)

1. S. Nusier,G. Newaz, "Analysis of interfacial cracks in a TBC/superalloy system under thermal loading," Eng. Fract. Mech. 60, 577-81 (1998).
2. D. R. Clarke, R. J. Christensen,V. Tolpygo, "The evolution of oxidation stresses in zirconia thermal barrier coated superalloy leading to spolling failure," Surf. Coat Tech. 94-95, 89-93 (1997).
3. A. G. Evans, D. R. Mumm, J. W. Hutchinson, G. H. Meier,F. S. Pettit, "Mechanisms controlling the durability of thermal barrier coatings, "Prog. Mater. Sci. 46, 505-53 (2001).
4. D. R. Mumm,A. G. Evans, "On the role of imperfections in the failure of a thermal barrier coating made by electron beam deposition," Acta Mater. 48, 1815-27 (2000).
5. G. Qian, T. Nakamura,C. C. Berndt, "Effects of thermal gradient and residual stresses on thermal barrier coating fracture," Mech. of Mater. 27, 91-110 (1998).
6. A. Rabiei,A. G. Evans, "Failure mechanisms associated with the thermally grown oxide in plasma-sprayed thermal barrier coatings, "Acta Mater. 48, 3963-76 (2000).
7. D. R. Clarke,S. R. Phillpot, "Thermal barrier coating materials," Mater. Today. 8, 22-29 (2005).
8. Y. C. Zhou,T. Hashida, " Thermal fatigue failure induced by delamination in thermal barrier coating," Int. J. Fatigue. 24, 407-17 (2002).
9. N. Mesrati, Q. Saif, D. Treheux, A. Moughil, G Fantozzi,A. Vincent, "Characterisation of thermal fatigue damage of thermal barrier produced by atmospheric plasma spraying," Surf.& Coat. Tech. 187, 185-93 (2004).
10. G. Newaz,X. Chen, "Progressive damage assessment in thermal barrier coatings using thermal wave imaging technique," Surf Coat Tech. 190, 7-14 (2005).
11. M. M. Gentleman,D. R. Clarke, "Concepts for luminescence sensing of thermal barrier coatings, " Surf Coat Tech. 188-189, 93-100 (2004).
12. V. K. Tolpygo, D. R. Clarke,K. S. Murphy, "Evaluation of interface degradation during cyclic oxidation of EB-PVD thermal barrier coatings and correlation with TGO luminescence, " Surf. Coat. Tech. 188-189, 62-70 (2004).
13. B. Jayaraj, S. Vishweswaraiah, V. H. Desai.Y. H. Sohn, "Electrochemical impedance spectroscopy of thermal barrier coatings as a function of isothermal and cyclic thermal exposure," Surf Coat Tech. 177-178, 140-51 (2004).
14. M. S. Ali, A novel technique for evaluating the degradation of engine components non-destructivtely, in Department of Mechanical Engineering. 2002, Brunel University: London.
15. M. S. Ali, S. Song, P. Xiao, "Evaluation of degradation of thermal barrier coatings using impedance spectroscopy," J. Eur. Ceram. Soc. 22, 101-07 (2002).
16. X. Wang, J. Mei, P. Xiao, "Determining oxide growth in thermal barrier coatings (TBCs) non-destructively using impedance spectroscopy, " J. Mater. Sci. Lett. 20, 47-49 (2001).
17. P. S. Anderson, X. Wang,P. Xiao, "Impedance spectroscopy study of plasma sprayed and EB-PVD thermal barrier coatings, "Surf. Coat. Tech. 185, 106-19 (2004).
18. P. S. Anderson, X. Wang, P. Xiao, "Effect of isothermal heat treatment on plasma-sprayedyttria-stabili-ed Zirconia studied by impedance spectroscopy," J. Am.Ceram.Soc. 88, 324-30 (2005).
19. J. Fleig,J. Maier, "Finite element calculations of impedance effects at point contacts, "Electrochemica Acta. 41, 1003-09 (1995).
20. J. Fleig,J. Maier, "The impedance of ceramics with highly resistive grain boundaries: validity and limits of the brick layer model," J. Eur. Ceram. Soc. 19, 693-96 (1999).
21. J.-S. Lee, J. R. Fleig,J. Maier, "Conventional and microcontact impedance studies of Mn-Zn ferrite ceramics," J. Mater. Res. 19, 864-71 (2004).
22. D. R. Lide, CRC Handbook of Chemistry and Physics. 85th ed. 2004: CRC press LLC. 12-52.
23. X. Wang, Non-Destructive Characterisation of Structural Ceramics Using Impedance Spectroscopy, in Department of Mechanical Engineering. 2001, Brunel University: London, p. 8.
24. M. Okazaki,H. Yamano, "Mechanisms and mechanics of early growth of debonding crack in an APSed Ni-base superalloy TBCs under cyclic load." Int. J. Fatigue. 27, 1613-22 (2005).